WO2019101766A1 - Process for the production of ceramic bodies consisting of nanofibers of silicon nitride and ceramic bodies thus obtained - Google Patents
Process for the production of ceramic bodies consisting of nanofibers of silicon nitride and ceramic bodies thus obtained Download PDFInfo
- Publication number
- WO2019101766A1 WO2019101766A1 PCT/EP2018/082003 EP2018082003W WO2019101766A1 WO 2019101766 A1 WO2019101766 A1 WO 2019101766A1 EP 2018082003 W EP2018082003 W EP 2018082003W WO 2019101766 A1 WO2019101766 A1 WO 2019101766A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymer
- precursor
- process according
- ceramic
- temperature
- Prior art date
Abstract
Description
Claims