WO2019040686A1 - Unité de rétroéclairage comprenant une plaque guide de lumière - Google Patents

Unité de rétroéclairage comprenant une plaque guide de lumière Download PDF

Info

Publication number
WO2019040686A1
WO2019040686A1 PCT/US2018/047635 US2018047635W WO2019040686A1 WO 2019040686 A1 WO2019040686 A1 WO 2019040686A1 US 2018047635 W US2018047635 W US 2018047635W WO 2019040686 A1 WO2019040686 A1 WO 2019040686A1
Authority
WO
WIPO (PCT)
Prior art keywords
pattern
microstructures
guide plate
light guide
backlight
Prior art date
Application number
PCT/US2018/047635
Other languages
English (en)
Inventor
Dmitri Vladislavovich Kuksenkov
David August Sniezek Loeber
Xiang-Dong Mi
Original Assignee
Corning Incorporated
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Corning Incorporated filed Critical Corning Incorporated
Publication of WO2019040686A1 publication Critical patent/WO2019040686A1/fr

Abstract

La présente invention porte sur un rétroéclairage (100) comprenant une pluralité de sources de lumière (5) et une plaque guide de lumière à motifs (30) présentant un premier motif de microstructures (33) sur une surface supérieure ou inférieure dans le but d'extraire la lumière de la pluralité de sources de lumière, un deuxième motif de microstructures (32) sur la surface inférieure, et un troisième motif de microstructures (31) sur la surface supérieure à proximité ou au-dessus des sources de lumière. La pluralité de sources de lumière (5) sont situées directement derrière la plaque guide de lumière à motifs (30), et des rayons dominants de la pluralité de sources de lumière (5) sont transmis par le deuxième motif et réfléchis par le troisième motif (31) de sorte que plus de 60 % des rayons dominants se déplacent latéralement dans la plaque guide de lumière à motifs (30) en raison de la réflexion interne totale.
PCT/US2018/047635 2017-08-24 2018-08-23 Unité de rétroéclairage comprenant une plaque guide de lumière WO2019040686A1 (fr)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
US201762549576P 2017-08-24 2017-08-24
US62/549,576 2017-08-24
US201862649210P 2018-03-28 2018-03-28
US62/649,210 2018-03-28

Publications (1)

Publication Number Publication Date
WO2019040686A1 true WO2019040686A1 (fr) 2019-02-28

Family

ID=63490727

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2018/047635 WO2019040686A1 (fr) 2017-08-24 2018-08-23 Unité de rétroéclairage comprenant une plaque guide de lumière

Country Status (2)

Country Link
TW (1) TW201921008A (fr)
WO (1) WO2019040686A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020236549A1 (fr) * 2019-05-23 2020-11-26 Corning Incorporated Lunettes à décalage de couleur négative et plaques de guidage de lumière
US11880057B2 (en) 2019-06-26 2024-01-23 Corning Incorporated Display device and backlight unit therefor
US11927791B2 (en) 2020-02-10 2024-03-12 Corning Incorporated Backlights including patterned reflectors

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010058625A1 (fr) * 2008-11-20 2010-05-27 シャープ株式会社 Dispositif d’illumination, dispositif d’affichage et dispositif de réception de télévision
US20120013811A1 (en) * 2009-04-03 2012-01-19 Sharp Kabushiki Kaisha Lighting device, display device and television receiver
WO2012064007A1 (fr) * 2010-11-10 2012-05-18 Lg Innotek Co., Ltd. Unité de rétro-éclairage

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010058625A1 (fr) * 2008-11-20 2010-05-27 シャープ株式会社 Dispositif d’illumination, dispositif d’affichage et dispositif de réception de télévision
US20120013811A1 (en) * 2009-04-03 2012-01-19 Sharp Kabushiki Kaisha Lighting device, display device and television receiver
WO2012064007A1 (fr) * 2010-11-10 2012-05-18 Lg Innotek Co., Ltd. Unité de rétro-éclairage

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020236549A1 (fr) * 2019-05-23 2020-11-26 Corning Incorporated Lunettes à décalage de couleur négative et plaques de guidage de lumière
CN114007992A (zh) * 2019-05-23 2022-02-01 康宁公司 负色偏移玻璃及光导板
CN114007992B (zh) * 2019-05-23 2023-10-03 康宁公司 负色偏移玻璃及光导板
TWI838528B (zh) * 2019-05-23 2024-04-11 美商康寧公司 負色偏移玻璃及光導板
US11880057B2 (en) 2019-06-26 2024-01-23 Corning Incorporated Display device and backlight unit therefor
US11927791B2 (en) 2020-02-10 2024-03-12 Corning Incorporated Backlights including patterned reflectors

Also Published As

Publication number Publication date
TW201921008A (zh) 2019-06-01

Similar Documents

Publication Publication Date Title
JP7266584B2 (ja) ２ｄローカルディミングを備えた直接発光バックライトユニット
TWI772501B (zh) 用於直接發光的背光的多層反射器
EP3469252A1 (fr) Plaques de guidage de lumière présentant des microstructures et des motifs, et dispositifs comprenant lesdites plaques de guidage
JP2019523970A (ja) 微細構造化された導光板およびそれを含む装置
JP7169274B2 (ja) 微細構造を有する導光板、およびそれを含む装置
WO2018144509A1 (fr) Unité de rétroéclairage avec gradation locale 2d
WO2017106124A2 (fr) Plaques de guidage de lumière et dispositifs d'affichage les comprenant
TW201814340A (zh) 邊緣光照導光板以及包含彼之裝置
WO2019040686A1 (fr) Unité de rétroéclairage comprenant une plaque guide de lumière
WO2018144720A1 (fr) Ensembles guides de lumière comprenant des caractéristiques de manipulation optique
US9846271B2 (en) Display device having a patterned glass light guide and CTE-matched TFT
WO2018156547A1 (fr) Dispositifs comprenant une unité de rétroéclairage intégrée et un panneau d'affichage
WO2019217408A1 (fr) Unité de rétroéclairage dotée d'une gradation locale 2d améliorée

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18765282

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18765282

Country of ref document: EP

Kind code of ref document: A1