WO2019036370A1 - Procédés pour des implants dentaires personnalisés constitués d'un matériau composite biomimétique et leurs procédés de fabrication - Google Patents

Procédés pour des implants dentaires personnalisés constitués d'un matériau composite biomimétique et leurs procédés de fabrication Download PDF

Info

Publication number
WO2019036370A1
WO2019036370A1 PCT/US2018/046515 US2018046515W WO2019036370A1 WO 2019036370 A1 WO2019036370 A1 WO 2019036370A1 US 2018046515 W US2018046515 W US 2018046515W WO 2019036370 A1 WO2019036370 A1 WO 2019036370A1
Authority
WO
WIPO (PCT)
Prior art keywords
tooth
dentin
dental implant
composite material
cement
Prior art date
Application number
PCT/US2018/046515
Other languages
English (en)
Inventor
Amir FAKHRZADEH
Original Assignee
Rutgers, The State University Of New Jersey
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rutgers, The State University Of New Jersey filed Critical Rutgers, The State University Of New Jersey
Priority to EP18846032.3A priority Critical patent/EP3668445A4/fr
Publication of WO2019036370A1 publication Critical patent/WO2019036370A1/fr
Priority to US16/791,090 priority patent/US11406478B2/en

Abstract

La présente invention concerne des procédés et un matériau composite d'application d'un remplacement immédiat de dent, comprenant l'étape de traitement de la dentine humaine à partir d'une dent extraite et sa combinaison avec un ciment bioactif pour former un matériau composite biomimétique qui est reconstruit en un implant en forme de dent. Le matériau composite biomimétique peut être constitué d'un matériau de ciment à base de silicate de calcium disponible dans le commerce, qui produit un matériau composite qui est beaucoup plus proche des dents naturelles en termes de composition, de couleur et de propriétés mécaniques.
PCT/US2018/046515 2017-08-14 2018-08-13 Procédés pour des implants dentaires personnalisés constitués d'un matériau composite biomimétique et leurs procédés de fabrication WO2019036370A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
EP18846032.3A EP3668445A4 (fr) 2017-08-14 2018-08-13 Procédés pour des implants dentaires personnalisés constitués d'un matériau composite biomimétique et leurs procédés de fabrication
US16/791,090 US11406478B2 (en) 2017-08-14 2020-02-14 Methods for customized dental implants formed of a biometric composite material and methods of manufacture thereof

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201762545113P 2017-08-14 2017-08-14
US62/545,113 2017-08-14

Related Child Applications (1)

Application Number Title Priority Date Filing Date
US16/790,202 Continuation-In-Part US11291612B2 (en) 2017-08-14 2020-02-13 Injectable hybrid cement for dental implants and methods of manufacture thereof

Publications (1)

Publication Number Publication Date
WO2019036370A1 true WO2019036370A1 (fr) 2019-02-21

Family

ID=65362736

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2018/046515 WO2019036370A1 (fr) 2017-08-14 2018-08-13 Procédés pour des implants dentaires personnalisés constitués d'un matériau composite biomimétique et leurs procédés de fabrication

Country Status (2)

Country Link
EP (1) EP3668445A4 (fr)
WO (1) WO2019036370A1 (fr)

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4051598A (en) * 1974-04-23 1977-10-04 Meer Sneer Dental implants
US20080090207A1 (en) * 2006-10-16 2008-04-17 Ruedger Rubbert Customized dental prosthesis for periodontal- or osseointegration, and related systems and methods
US20100086618A1 (en) * 2008-10-08 2010-04-08 Medical College Of Georgia Research Institute, Inc Methods and Systems for Mineralization of Demineralized Tissue
US20100215617A1 (en) * 2009-01-03 2010-08-26 Wasielewski Ray C Enhanced medical implant
US20120156308A1 (en) * 2009-08-29 2012-06-21 Dentosolve Mineral trioxide aggregate (mta) composition and use

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20130143179A1 (en) * 2010-08-05 2013-06-06 In Woong Um Method for processing bone graft material using teeth, and bone graft material processed thereby

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4051598A (en) * 1974-04-23 1977-10-04 Meer Sneer Dental implants
US20080090207A1 (en) * 2006-10-16 2008-04-17 Ruedger Rubbert Customized dental prosthesis for periodontal- or osseointegration, and related systems and methods
US20100086618A1 (en) * 2008-10-08 2010-04-08 Medical College Of Georgia Research Institute, Inc Methods and Systems for Mineralization of Demineralized Tissue
US20100215617A1 (en) * 2009-01-03 2010-08-26 Wasielewski Ray C Enhanced medical implant
US20120156308A1 (en) * 2009-08-29 2012-06-21 Dentosolve Mineral trioxide aggregate (mta) composition and use

Non-Patent Citations (6)

* Cited by examiner, † Cited by third party
Title
FONTAINE ET AL.: "New calcium carbonate-based cements for bone reconstruction", KEY ENGINEERING MATERIALS (SCIENTIFIC.NET), vol. 284-286, 30 April 2005 (2005-04-30), pages 105 - 108, XP055571185, Retrieved from the Internet <URL:https://doi.org/10.4028/www.scientific.net/KEM.284-286.105> *
GRAFTYS, GRAFTY'S PRODUCTS, 2019, XP055571166, Retrieved from the Internet <URL:https://www.graftys.com/injectable-ceramic-products/> *
GURTU ET AL.: "Evaluation of effect of dentin powder on antibacterial properties of Mineral Trioxide Aggregate - An in vitro study", ENDODONTOLOGY, vol. 26, no. 1, 20 June 2014 (2014-06-20), XP055571160 *
HILLEY ET AL.: "Bioceramics in Endodontics", CLINICAL UPDATENAVAL POSTGRADUATE DENTAL SCHOOLNAVY MEDICINE PROFESSIONAL DEVELOPMENT CENTER, vol. 35, no. 4, 2013, XP055571175 *
See also references of EP3668445A4 *
YAKOOB ET AL.: "Evaluate the use of fresh Autogenous cement and dentine as bone graft to repair bone defects in dogs: experimental study", INTERNATIONAL DENTAL JOURNAL OF STUDENT RESEARCH, vol. 4, no. 2, 30 June 2016 (2016-06-30), pages 97 - 100, XP055571199 *

Also Published As

Publication number Publication date
EP3668445A4 (fr) 2021-04-21
EP3668445A1 (fr) 2020-06-24

Similar Documents

Publication Publication Date Title
Zoidis et al. Modified PEEK resin-bonded fixed dental prosthesis as an interim restoration after implant placement
US10350030B2 (en) Methods of designing and manufacturing customized dental prosthesis for periodontal or osseointegration and related systems
US20180008213A1 (en) Customized Dental Prosthesis for Periodontal or Osseointegration, and Related Systems
EP2063804B1 (fr) Prothèse dentaire sur mesure pour intégration parodontale et osteointegration et systèmes et procédés associes
US20170156824A1 (en) Customized Dental Prosthesis For Periodontal or Osseointegration and Related Systems
Zita Gomes et al. Alveolar ridge reconstruction with titanium meshes and simultaneous implant placement: a retrospective, multicenter clinical study
Felice et al. Reconstruction of an atrophied posterior mandible with the inlay technique and inorganic bovine bone block: a case report.
Diéguez-Pereira et al. Monolithic and minimally veneered zirconia complications as implant-supported restorative material: A retrospective clinical study up to 5 years
Sivolella et al. Maxillary sinus augmentation with bovine bone and simultaneous dental implant placement in conditions of severe alveolar atrophy: A retrospective analysis of a consecutively treated case series.
Abichandani et al. Abutment selection, designing, and its influence on the emergence profile: A comprehensive review
US11406478B2 (en) Methods for customized dental implants formed of a biometric composite material and methods of manufacture thereof
Majewski Piezoelectric surgery in autogenous bone block grafts.
US11291612B2 (en) Injectable hybrid cement for dental implants and methods of manufacture thereof
Ali et al. Clinical and radiographic outcomes of polyetheretherketone (PEEK) hybrid prosthesis used for “All on four” rehabilitation of edentulous maxilla. A short-term case series study
WO2019036370A1 (fr) Procédés pour des implants dentaires personnalisés constitués d&#39;un matériau composite biomimétique et leurs procédés de fabrication
Ghuneim In situ tooth replica custom implant: rationale, material, and technique
Oliva et al. Zirconia implants and all-ceramic restorations for the esthetic replacement of the maxillary central incisors.
RU2182817C1 (ru) Внутрикостный корневой остеокондуктивный дентальный имплантат и материал для его изготовления
Kim et al. Zirconia/alumina composite dental implant abutments
Östman On various protocols for direct loading of implant-supported fixed prostheses
Hamdi et al. The use of PEEK in implantology: a narrative review
MEHROTRA et al. Multidisciplinary Approach in the Management of Maxillary Anterior Region Dental Trauma: A Case Report.
Müller et al. Implant-prosthetic rehabilitation using individualized allogeneic bone blocks for bone defects caused by peri-implantitis
Liu et al. Comparative Study of the Efficacy of Autologous Tooth Bone Powder and Inorganic Bovine Bone Powder on the Repair of Jaw Defects.
Kaneko et al. A Novel Open-Tray Impression Technique for Fabrication of a Provisional Prosthesis on Immediate Load Implants in a Completely Edentulous Arch.

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18846032

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2018846032

Country of ref document: EP

Effective date: 20200316