WO2019002368A1 - Glycosaminoglycanes réticulés et fonctionnalisés - Google Patents

Glycosaminoglycanes réticulés et fonctionnalisés Download PDF

Info

Publication number
WO2019002368A1
WO2019002368A1 PCT/EP2018/067251 EP2018067251W WO2019002368A1 WO 2019002368 A1 WO2019002368 A1 WO 2019002368A1 EP 2018067251 W EP2018067251 W EP 2018067251W WO 2019002368 A1 WO2019002368 A1 WO 2019002368A1
Authority
WO
WIPO (PCT)
Prior art keywords
glycosaminoglycan
aminodextran
hyaluronic acid
dextran
amide
Prior art date
Application number
PCT/EP2018/067251
Other languages
English (en)
Inventor
Johan Olsson
Hotan MOJARRADI
Craig Steven Harris
Original Assignee
Nestlé Skin Health Sa
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nestlé Skin Health Sa filed Critical Nestlé Skin Health Sa
Publication of WO2019002368A1 publication Critical patent/WO2019002368A1/fr

Abstract

L'invention concerne un procédé de préparation d'un produit hydrogel comprenant des molécules de glycosaminoglycanes réticulés, ledit procédé consistant à : (i) utiliser un glycosaminoglycane réticulé par amide ; (ii) activer les groupes carboxyle sur le glycosaminoglycane avec un agent de couplage pour former un glycosaminoglycane activé ; (iii) greffer un aminodextrane au glycosaminoglycane activé par l'intermédiaire des groupes carboxyle activés, et un produit hydrogel comprenant un glycosaminoglycane réticulé par amide, greffé avec un dextrane, ledit dextrane étant lié de manière covalente au glycosaminoglycane par des liaisons amide.
PCT/EP2018/067251 2017-06-28 2018-06-27 Glycosaminoglycanes réticulés et fonctionnalisés WO2019002368A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP17178479 2017-06-28
EP17178479.6 2017-06-28

Publications (1)

Publication Number Publication Date
WO2019002368A1 true WO2019002368A1 (fr) 2019-01-03

Family

ID=59350623

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2018/067251 WO2019002368A1 (fr) 2017-06-28 2018-06-27 Glycosaminoglycanes réticulés et fonctionnalisés

Country Status (1)

Country Link
WO (1) WO2019002368A1 (fr)

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3659632A1 (fr) * 2018-11-29 2020-06-03 Nestlé Skin Health SA Dégradation partielle post-réticulation d'hydrogels d'amide réticulés
WO2021111303A1 (fr) * 2019-12-02 2021-06-10 Galderma Holding SA Compositions esthétiques de poids moléculaire élevé
CN113384497A (zh) * 2021-07-30 2021-09-14 上海新高姿化妆品有限公司 一种双重保湿修复和改善皮肤弹性的组合物及化妆品
CN114395593A (zh) * 2022-03-03 2022-04-26 山东福洋生物制造工程研究院 一种交联海藻糖的制备方法
US11530301B2 (en) 2015-12-29 2022-12-20 Galderma Holding SA Carbohydrate crosslinker

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000046252A1 (fr) * 1999-02-05 2000-08-10 Vitrolife Uk Limited Procede de reticulation d'acide hyaluronique avec des polymeres
WO2001085801A1 (fr) * 2000-05-10 2001-11-15 Aquisitio S.P.A. Polymeres reticules pour des utilisations pharmaceutiques, medicales et cosmetiques
US20070053987A1 (en) * 2005-09-02 2007-03-08 Thomas Bayer Cross-linked polysacharide and protein matrices and methods for their preparation
WO2015181369A1 (fr) * 2014-05-29 2015-12-03 Galderma S.A. Acide hyaluronique réticulé greffé à du dextrane
WO2015181366A1 (fr) * 2014-05-29 2015-12-03 Galderma S.A. Mélange de polymère réticulé d'acide hyaluronique et de dextrane greffé avec des cyclodextrines et leur utilisations
WO2016107834A1 (fr) * 2014-12-29 2016-07-07 Galderma S.A. Hydrogels de chondroïtine réticulée par ses groupes carboxyle et leur utilisation pour des applications dans des tissus mous

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2000046252A1 (fr) * 1999-02-05 2000-08-10 Vitrolife Uk Limited Procede de reticulation d'acide hyaluronique avec des polymeres
WO2001085801A1 (fr) * 2000-05-10 2001-11-15 Aquisitio S.P.A. Polymeres reticules pour des utilisations pharmaceutiques, medicales et cosmetiques
US20070053987A1 (en) * 2005-09-02 2007-03-08 Thomas Bayer Cross-linked polysacharide and protein matrices and methods for their preparation
WO2015181369A1 (fr) * 2014-05-29 2015-12-03 Galderma S.A. Acide hyaluronique réticulé greffé à du dextrane
WO2015181366A1 (fr) * 2014-05-29 2015-12-03 Galderma S.A. Mélange de polymère réticulé d'acide hyaluronique et de dextrane greffé avec des cyclodextrines et leur utilisations
WO2016107834A1 (fr) * 2014-12-29 2016-07-07 Galderma S.A. Hydrogels de chondroïtine réticulée par ses groupes carboxyle et leur utilisation pour des applications dans des tissus mous

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
KEISUKE KURITA; NAOKO MASUDA; SADAFUMI AIBE; KAORI MURAKAMI; SHIGERU ISHII; SHIN-ICHIRO NISHIMURAT: "Synthetic Carbohydrate Polymers Containing Trehalose Residues in the Main Chain: Preparation and Characteristic Properties", MACROMOLECULES, vol. 27, 1994, pages 7544 - 7549, XP000485396, DOI: doi:10.1021/ma00104a007

Cited By (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11643509B2 (en) 2015-12-29 2023-05-09 Galderma Holding SA Carbohydrate crosslinker
US11939433B2 (en) 2015-12-29 2024-03-26 Galderma Holding S.A. Method for preparing acylated crosslinked glycosaminoglycans
US11780970B2 (en) 2015-12-29 2023-10-10 Galderma Holding S.A. Carbohydrate crosslinker
US11708461B2 (en) 2015-12-29 2023-07-25 Galderma Holding SA Method for preparing acylated crosslinked glycosaminoglycans
US11530301B2 (en) 2015-12-29 2022-12-20 Galderma Holding SA Carbohydrate crosslinker
WO2020110007A1 (fr) * 2018-11-29 2020-06-04 Nestlé Skin Health S.A. Dégradation partielle post-réticulation d'hydrogels réticulés à l'aide d'un amide
EP3659632A1 (fr) * 2018-11-29 2020-06-03 Nestlé Skin Health SA Dégradation partielle post-réticulation d'hydrogels d'amide réticulés
US11730691B2 (en) 2019-12-02 2023-08-22 Galderma Holding SA High molecular weight esthetic compositions
CN115335414A (zh) * 2019-12-02 2022-11-11 高德美控股有限公司 高分子量美容组合物
CN115335414B (zh) * 2019-12-02 2024-03-19 高德美控股有限公司 高分子量美容组合物
WO2021111303A1 (fr) * 2019-12-02 2021-06-10 Galderma Holding SA Compositions esthétiques de poids moléculaire élevé
CN113384497A (zh) * 2021-07-30 2021-09-14 上海新高姿化妆品有限公司 一种双重保湿修复和改善皮肤弹性的组合物及化妆品
CN114395593A (zh) * 2022-03-03 2022-04-26 山东福洋生物制造工程研究院 一种交联海藻糖的制备方法

Similar Documents

Publication Publication Date Title
Rinaudo Main properties and current applications of some polysaccharides as biomaterials
US7651702B2 (en) Crosslinking hyaluronan and chitosanic polymers
WO2019002368A1 (fr) Glycosaminoglycanes réticulés et fonctionnalisés
JP6479783B2 (ja) 架橋ヒアルロン酸生成物を調製するための方法
EP2643029B1 (fr) Préparations et/ou formulations à base de protéines réticulées avec des polysaccharides
EP3148511A1 (fr) Acide hyaluronique réticulé greffé à du dextrane
CN112041378B (zh) 可注射凝胶产品
US20210308332A1 (en) Hydrogel compositions encapsulating solid particles
WO2017016917A1 (fr) Procédé de réticulation efficace d'acide hyaluronique
WO2019002369A1 (fr) Hydrogel de glycosaminoglycane avec dextrane ou cyclodextrine greffé
US20200140626A1 (en) Method of preparing a hydrogel product
Rinaudo Properties and degradation of selected polysaccharides: hyaluronan and chitosan
WO2019002370A1 (fr) Glycosaminoglycanes réticulés et fonctionnalisés
US20230346680A1 (en) High molecular weight esthetic compositions
Wang A novel hydrogel crosslinked hyaluronan with glycol chitosan
WO2019001784A1 (fr) Gel d'acide hyaluronique avec un cation divalent
EP3252081A1 (fr) Hydrolyse de liaisons esters de glycosaminoglycanes réticulés par des liaisons amides
EP3252080A1 (fr) Procédé de préparation de glycosaminoglycanes réticulés acylés
EP3252082A1 (fr) Procédé pour la désacétylation de biopolymères
RU2783125C2 (ru) Инъекционный гелевый продукт
WO2019002371A1 (fr) Gel de glycosaminoglycane avec tampon bis-tris
EP3886930A1 (fr) Dégradation partielle post-réticulation d'hydrogels réticulés à l'aide d'un amide

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18734803

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18734803

Country of ref document: EP

Kind code of ref document: A1