WO2018060287A1 - Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé - Google Patents

Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé Download PDF

Info

Publication number
WO2018060287A1
WO2018060287A1 PCT/EP2017/074551 EP2017074551W WO2018060287A1 WO 2018060287 A1 WO2018060287 A1 WO 2018060287A1 EP 2017074551 W EP2017074551 W EP 2017074551W WO 2018060287 A1 WO2018060287 A1 WO 2018060287A1
Authority
WO
WIPO (PCT)
Prior art keywords
tissue
tcp
silicate
amino acid
composition according
Prior art date
Application number
PCT/EP2017/074551
Other languages
English (en)
Inventor
Philip Procter
Håkan ENGQVIST
Michael PUJARI-PALMER
Gerard Insley
Original Assignee
Gpbio Ltd.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from SE1651271A external-priority patent/SE1651271A1/en
Application filed by Gpbio Ltd. filed Critical Gpbio Ltd.
Priority to EP23171337.1A priority Critical patent/EP4233923A1/fr
Priority to CN201780059294.7A priority patent/CN110062635B/zh
Priority to EP17772726.0A priority patent/EP3518995B1/fr
Priority to US16/337,355 priority patent/US20200038545A1/en
Priority to ES17772726T priority patent/ES2949193T3/es
Publication of WO2018060287A1 publication Critical patent/WO2018060287A1/fr

Abstract

La présente invention concerne une composition aqueuse comprenant une solution aqueuse, de l'α-TCP, un composé silicaté et un acide aminé phosphorylé. La composition présente une résistance mécanique améliorée et est facilement appliquée et peut être utilisée en tant qu'adhésif tissulaire, implant ou matériau de remplissage.
PCT/EP2017/074551 2016-09-27 2017-09-27 Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé WO2018060287A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP23171337.1A EP4233923A1 (fr) 2016-09-27 2017-09-27 Composition de a-tcp, silicate et acide aminé phosphorylé
CN201780059294.7A CN110062635B (zh) 2016-09-27 2017-09-27 α-TCP、硅酸盐和磷酸化氨基酸的组合物
EP17772726.0A EP3518995B1 (fr) 2016-09-27 2017-09-27 Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé
US16/337,355 US20200038545A1 (en) 2016-09-27 2017-09-27 Composition of alpha-tcp, silicate and phosphorylated amino acid
ES17772726T ES2949193T3 (es) 2016-09-27 2017-09-27 Composicion de alpha-TCP, silicato y aminoacido fosforilado

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
SE1651271A SE1651271A1 (en) 2016-09-27 2016-09-27 Composition of alfa-tcp, silicate and phosphorylated amino acid
SE1651271-7 2016-09-27
SE1651727 2016-12-22

Publications (1)

Publication Number Publication Date
WO2018060287A1 true WO2018060287A1 (fr) 2018-04-05

Family

ID=61759312

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/EP2017/074553 WO2018060289A1 (fr) 2016-09-27 2017-09-27 COMPOSITION D'ADHÉSIF POUR TISSU MOU À BASE DE α-TCP ET D'ACIDE AMINÉ PHOSPHORYLÉ
PCT/EP2017/074551 WO2018060287A1 (fr) 2016-09-27 2017-09-27 Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/EP2017/074553 WO2018060289A1 (fr) 2016-09-27 2017-09-27 COMPOSITION D'ADHÉSIF POUR TISSU MOU À BASE DE α-TCP ET D'ACIDE AMINÉ PHOSPHORYLÉ

Country Status (1)

Country Link
WO (2) WO2018060289A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP4091599A1 (fr) 2021-05-18 2022-11-23 Karl Leibinger Medizintechnik Gmbh & Co. Kg Composition polymérisable à base de thiol-en

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120288446A1 (en) 2011-05-13 2012-11-15 Garigapati Venkat R Organophosphorous & multivalent metal compound compositions & methods
US20130122057A1 (en) 2011-11-10 2013-05-16 Venkat R. Garigapati Organophosphorous, Multivalent Metal Compounds, and Bioactive Glass Material Macromolecular Network Compositions and Methods

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE202004005420U1 (de) * 2004-03-31 2005-08-18 Technische Universität Dresden Modifizierter Calciumphosphatzement

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20120288446A1 (en) 2011-05-13 2012-11-15 Garigapati Venkat R Organophosphorous & multivalent metal compound compositions & methods
US8765189B2 (en) 2011-05-13 2014-07-01 Howmedica Osteonic Corp. Organophosphorous and multivalent metal compound compositions and methods
US20130122057A1 (en) 2011-11-10 2013-05-16 Venkat R. Garigapati Organophosphorous, Multivalent Metal Compounds, and Bioactive Glass Material Macromolecular Network Compositions and Methods

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
DANIEL CORREA ET AL: "-dicalcium silicate and tricalcium aluminate: Physicochemical characterization, in vitro bioactivity and cytotoxicity : [alpha]-C 3 P Cements with [beta]-Dicalcium Silicate and Tricalcium Aluminate", JOURNAL OF BIOMEDICAL MATERIALS RESEARCH. PART B: APPLIED BIOMATERIALS, vol. 103, no. 1, 1 January 2015 (2015-01-01), US, pages 72 - 83, XP055427677, ISSN: 1552-4973, DOI: 10.1002/jbm.b.33176 *
WOLFGANG SCHNEIDERS ET AL: "Effect of modification of hydroxyapatite/collagen composites with sodium citrate, phosphoserine, phosphoserine/RGD-peptide and calcium carbonate on bone remodelling", BONE, vol. 40, no. 4, 1 April 2007 (2007-04-01), GB, pages 1048 - 1059, XP055426963, ISSN: 8756-3282, DOI: 10.1016/j.bone.2006.11.019 *

Also Published As

Publication number Publication date
WO2018060289A1 (fr) 2018-04-05

Similar Documents

Publication Publication Date Title
EP3518995B1 (fr) Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé
US20210275717A1 (en) Organophosphorous, multivalent metal compounds, & polymer adhesive interpenetrating network compositions & methods
EP2365994B1 (fr) Compositions organophosphorées à base de phosphate tétracalcique et procédés d'utilisation de celles-ci
US20130122057A1 (en) Organophosphorous, Multivalent Metal Compounds, and Bioactive Glass Material Macromolecular Network Compositions and Methods
EP3717027B1 (fr) Composition d'un phosphate de calcium et d'un composé additif contenant un groupe phosphate ou phosphonate
WO2018060287A1 (fr) Composition d'alpha-tcp, de silicate et d'acide aminé phosphorylé
EP3518996B1 (fr) Composition d'adhésif pour tissu mou à base de -tcp et d'acide aminé phosphorylé

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17772726

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 2017772726

Country of ref document: EP

Effective date: 20190429