WO2018034222A1 - Room temperature curable organopolysiloxane composition for protecting electric/electronic parts - Google Patents
Room temperature curable organopolysiloxane composition for protecting electric/electronic parts Download PDFInfo
- Publication number
- WO2018034222A1 WO2018034222A1 PCT/JP2017/029043 JP2017029043W WO2018034222A1 WO 2018034222 A1 WO2018034222 A1 WO 2018034222A1 JP 2017029043 W JP2017029043 W JP 2017029043W WO 2018034222 A1 WO2018034222 A1 WO 2018034222A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- parts
- room temperature
- mass
- electronic parts
- Prior art date
Abstract
Description
Patent Document 2: Japanese Unexamined Patent Application Publication No. 2006-316184
Patent Document 3: Japanese Unexamined Patent Application Publication No. 2012-251058
Patent Document 4: Japanese Unexamined Patent Application Publication No. Sho 59-80463
(A) 100 parts by mass of an organopolysiloxane having a viscosity at 25°C of 20 to 1,000,000 mPa・s and having at least two silicon atom-bonded hydroxyl groups or silicon atom-bonded alkoxy groups in a molecule;
(B) 0.5 to 15 parts by mass of an alkoxysilane represented by the following general formula or a partial hydrolysis condensation product thereof:
R1 aSi(OR2)(4-a)
wherein R1 is a monovalent hydrocarbon group having a carbon number of 1 to 12, R2 is an alkyl group having a carbon number of 1 to 3, and “a” is an integer of 0 to 2;
(C) 0.001 to 0.5 parts by mass of a mercaptobenzothiazole based compound;
(D) 0.1 to 30 parts by mass of zinc oxide powder and/or zinc carbonate powder; and
(E) 0.1 to 10 parts by mass of a catalyst for condensation reactions.
methylvinylsiloxane copolymer having both molecular chain terminals blocked with trimethoxysiloxy groups, a dimethylsiloxane・methylphenylsiloxane copolymer having both molecular chain terminals blocked with trimethoxysiloxy groups, a dimethylsiloxane・methyl(3,3,3-trifluoropropyl)siloxane copolymer having both molecular chain terminals blocked with trimethoxysiloxy groups, a dimethylpolysiloxane having both molecular chain terminals blocked with trimethoxysilylethyldimethylsiloxy groups, a dimethylsiloxane・methylvinylsiloxane copolymer having both molecular chain terminals blocked with trimethoxysilylethyldimethylsiloxy groups, a dimethylsiloxane・methylphenylsiloxane copolymer having both molecular chain terminals blocked with trimethoxysilylethyldimethylsiloxy groups, a dimethylsiloxane・methyl(3,3,3-trifluoropropyl)siloxane copolymer having both molecular chain terminals blocked with trimethoxysilylethyldimethylsiloxy groups, and mixtures of two or more thereof.
R1 aSi(OR2)(4-a).
The room temperature curable organopolysiloxane composition prepared in Practical Examples and Comparative Examples was applied on a silver plated copper plate so as to have a thickness of 2 mm, and cured to manufacture a test piece. Subsequently, this test piece, along with 0.2 g of sulfur powder, was placed in a 100 cc glass bottle, sealed, heated to 70°C, and left to stand for 72 hours, after which the cured product was peeled and the degree of corrosion of the silver plating, as well as the state thereof, was visually observed and evaluated as follows.
○: corrosion is absent
×: corrosion is present (blackening)
Regarding the silver plated part obtained by peeling the cured product in the abovementioned sulfur corrosion test, the resistance value (Ω) at a distance of 2 cm between electrodes was measured using an electric tester.
While moisture shielded, 100 parts by mass of dimethylpolysiloxane having both molecular chain terminals blocked with trimethoxysiloxy groups and having a viscosity of 700 mPa・s, 4 parts by mass of hydrophobic fumed silica having a BET specific surface area of 200 m2/g, 2 parts by mass of methyltrimethoxysilane, 0.02 parts by mass of mercaptobenzothiazole, 1.1 parts by mass of zinc oxide powder having a BET specific surface area of 75 m2/g, and 2 parts by mass of diisopropoxybis(ethylacetoacetate)titanium were mixed to prepare a room temperature curable organopolysiloxane composition. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 1, except that the blending amount of zinc oxide powder was 5.7 parts by mass. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 1, except that the blending amount of zinc oxide powder was 12.0 parts by mass. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 1, except that mercaptobenzothiazole and zinc oxide powder were not blended. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 1, except that zinc oxide powder was not blended. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 1, except that mercaptobenzothiazole was not blended. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 2, except that mercaptobenzothiazole was not blended. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 3, except that mercaptobenzothiazole was not blended. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
A room temperature curable organopolysiloxane composition was prepared as in Practical Example 2, except that benzotriazole was blended instead of mercaptobenzothiazole. A test piece was manufactured using this composition to carry out sulfur corrosion testing. The results of sulfur corrosion testing, as well as the resistance value, are shown in Table 1.
Claims (3)
- A room temperature curable organopolysiloxane composition for protecting electric/electronic parts, comprising:
(A) 100 parts by mass of an organopolysiloxane having a viscosity at 25°C of 20 to 1,000,000 mPa・s and having at least two silicon atom-bonded hydroxyl groups or silicon atom-bonded alkoxy groups in a molecule;
(B) 0.5 to 15 parts by mass of an alkoxysilane represented by the following general formula or a partial hydrolysis condensation product thereof:
R1 aSi(OR2)(4-a)
wherein R1 is a monovalent hydrocarbon group having a carbon number of 1 to 12, R2 is an alkyl group having a carbon number of 1 to 3, and “a” is an integer of 0 to 2;
(C) 0.001 to 0.5 parts by mass of a mercaptobenzothiazole based compound;
(D) 0.1 to 30 parts by mass of zinc oxide powder and/or zinc carbonate powder; and
(E) 0.1 to 10 parts by mass of a catalyst for condensation reactions. - The room temperature curable organopolysiloxane composition for protecting electric/electronic parts according to Claim 1, wherein component (C) is mercaptobenzothiazole, dibenzothiazyl disulfide, a sodium salt of mercaptobenzothiazole, a zinc salt of mercaptobenzothiazole, a cyclohexylamine salt of mercaptobenzothiazole, morpholinodithiobenzothiazole, N-cyclohexyl-benzothiazolyl sulfenamide, N-oxydiethylene-benzothiazolyl sulfenamide, or N-tert-butylbenzothiazolyl sulfenamide.
- The room temperature curable organopolysiloxane composition for protecting electric/electronic parts according to Claim 1, wherein component (D) is zinc oxide powder having a BET specific surface area of at least 10 m2/g.