WO2018031828A1 - Fabrication de structures de gradient de matériaux tridimensionnelles par durcissement en vol d'aérosols - Google Patents

Fabrication de structures de gradient de matériaux tridimensionnelles par durcissement en vol d'aérosols Download PDF

Info

Publication number
WO2018031828A1
WO2018031828A1 PCT/US2017/046381 US2017046381W WO2018031828A1 WO 2018031828 A1 WO2018031828 A1 WO 2018031828A1 US 2017046381 W US2017046381 W US 2017046381W WO 2018031828 A1 WO2018031828 A1 WO 2018031828A1
Authority
WO
WIPO (PCT)
Prior art keywords
droplets
materials
aerosol
substrate
aerosol droplets
Prior art date
Application number
PCT/US2017/046381
Other languages
English (en)
Inventor
Michael J. Renn
Douglas John WELTER
Original Assignee
Optomec. Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Optomec. Inc. filed Critical Optomec. Inc.
Publication of WO2018031828A1 publication Critical patent/WO2018031828A1/fr

Abstract

La présente invention concerne un procédé de fabrication de structures tridimensionnelles. Le chauffage l'évaporation ou l'éclairage UV en vol modifie les propriétés de gouttelettes d'aérosol lorsqu'elles sont projetées sur une surface cible. La lumière UV durcit au moins partiellement les gouttelettes photopolymère ou en variante, fait en sorte que des gouttelettes de dispersions de nanoparticules à base de solvant sèchent rapidement en vol, et la viscosité accrue résultante des gouttelettes d'aérosol facilite la formation de structures en trois dimensions autoportantes. Cette fabrication en 3D peut être effectuée à l'aide d'une grande variété de photopolymères, de dispersions de nanoparticules et de matières composites. Les formes 3D résultantes peuvent être autonomes, fabriquées sans supports, et peuvent parvenir à des formes arbitraires par manipulation de la buse d'impression par rapport au substrat cible. De multiples matériaux peuvent être mélangés et déposés pour former des structures avec des profils de matériau à gradient de composition, par exemple des réseaux de Bragg dans un conduit de lumière ou une fibre optique, des interconnexions optiques et des lentilles plates.
PCT/US2017/046381 2016-08-10 2017-08-10 Fabrication de structures de gradient de matériaux tridimensionnelles par durcissement en vol d'aérosols WO2018031828A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201662372955P 2016-08-10 2016-08-10
US62/372,955 2016-08-10

Publications (1)

Publication Number Publication Date
WO2018031828A1 true WO2018031828A1 (fr) 2018-02-15

Family

ID=61163134

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2017/046381 WO2018031828A1 (fr) 2016-08-10 2017-08-10 Fabrication de structures de gradient de matériaux tridimensionnelles par durcissement en vol d'aérosols

Country Status (2)

Country Link
TW (1) TW201811543A (fr)
WO (1) WO2018031828A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019165205A1 (fr) 2018-02-23 2019-08-29 Commscope Technologies Llc Face d'extrémité de connecteur de fibre optique imprimée en 3d et procédé de fabrication
WO2019177666A1 (fr) * 2018-03-15 2019-09-19 Hewlett-Packard Development Company, L.P. Impression en trois dimensions

Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08156106A (ja) * 1992-11-13 1996-06-18 Japan Atom Energy Res Inst ３次元物体製作法
US6144008A (en) * 1996-11-22 2000-11-07 Rabinovich; Joshua E. Rapid manufacturing system for metal, metal matrix composite materials and ceramics
US7164818B2 (en) * 2001-05-03 2007-01-16 Neophontonics Corporation Integrated gradient index lenses
US7171093B2 (en) * 2001-06-11 2007-01-30 Optoplan, As Method for preparing an optical fibre, optical fibre and use of such
US20070240454A1 (en) * 2006-01-30 2007-10-18 Brown David P Method and apparatus for continuous or batch optical fiber preform and optical fiber production
US7469558B2 (en) * 2001-07-10 2008-12-30 Springworks, Llc As-deposited planar optical waveguides with low scattering loss and methods for their manufacture
US7938079B2 (en) * 1998-09-30 2011-05-10 Optomec Design Company Annular aerosol jet deposition using an extended nozzle
US20120177319A1 (en) * 2009-07-16 2012-07-12 Hamidreza Alemohammad Optical fiber sensor and methods of manufacture
US8383014B2 (en) * 2010-06-15 2013-02-26 Cabot Corporation Metal nanoparticle compositions
US8796146B2 (en) * 2004-12-13 2014-08-05 Optomec, Inc. Aerodynamic jetting of blended aerosolized materials

Patent Citations (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08156106A (ja) * 1992-11-13 1996-06-18 Japan Atom Energy Res Inst ３次元物体製作法
US6144008A (en) * 1996-11-22 2000-11-07 Rabinovich; Joshua E. Rapid manufacturing system for metal, metal matrix composite materials and ceramics
US7938079B2 (en) * 1998-09-30 2011-05-10 Optomec Design Company Annular aerosol jet deposition using an extended nozzle
US7164818B2 (en) * 2001-05-03 2007-01-16 Neophontonics Corporation Integrated gradient index lenses
US7171093B2 (en) * 2001-06-11 2007-01-30 Optoplan, As Method for preparing an optical fibre, optical fibre and use of such
US7469558B2 (en) * 2001-07-10 2008-12-30 Springworks, Llc As-deposited planar optical waveguides with low scattering loss and methods for their manufacture
US8796146B2 (en) * 2004-12-13 2014-08-05 Optomec, Inc. Aerodynamic jetting of blended aerosolized materials
US20070240454A1 (en) * 2006-01-30 2007-10-18 Brown David P Method and apparatus for continuous or batch optical fiber preform and optical fiber production
US20120177319A1 (en) * 2009-07-16 2012-07-12 Hamidreza Alemohammad Optical fiber sensor and methods of manufacture
US8383014B2 (en) * 2010-06-15 2013-02-26 Cabot Corporation Metal nanoparticle compositions

Cited By (8)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019165205A1 (fr) 2018-02-23 2019-08-29 Commscope Technologies Llc Face d'extrémité de connecteur de fibre optique imprimée en 3d et procédé de fabrication
EP3756037A4 (fr) * 2018-02-23 2021-11-17 CommScope Technologies LLC Face d'extrémité de connecteur de fibre optique imprimée en 3d et procédé de fabrication
WO2019177666A1 (fr) * 2018-03-15 2019-09-19 Hewlett-Packard Development Company, L.P. Impression en trois dimensions
US11534824B2 (en) 2018-03-15 2022-12-27 Hewlett-Packard Development Company, L.P. Composition
US11684978B2 (en) 2018-03-15 2023-06-27 Hewlett-Packard Development Company, L.P. Build material composition
US11998977B2 (en) 2018-03-15 2024-06-04 Hewlett-Packard Development Company, L.P. Build material composition with metal powder and freeze-dried heteropolymer
US12042859B2 (en) 2018-03-15 2024-07-23 Hewlett-Packard Development Company, L.P. Build material composition
US12042860B2 (en) 2018-03-15 2024-07-23 Hewlett-Packard Development Company, L.P. Build material composition

Also Published As

Publication number Publication date
TW201811543A (zh) 2018-04-01

Similar Documents

Publication Publication Date Title
EP3256308B1 (fr) Fabrication de structures tridimensionnelles par durcissement en vol d'aérosols
US20170348903A1 (en) Fabrication of Three-Dimensional Materials Gradient Structures by In-Flight Curing of Aerosols
Farahani et al. Three-dimensional printing of freeform helical microstructures: a review
Gao et al. 3D printed optics and photonics: Processes, materials and applications
US9579829B2 (en) Method for manufacturing an optical element
Magazine et al. 3D inkjet-printing of photo-crosslinkable resins for microlens fabrication
US7658603B2 (en) Methods and systems for integrating fluid dispensing technology with stereolithography
CA2447850C (fr) Impression structuree tridimensionnelle
Behroodi et al. A compact LED-based projection microstereolithography for producing 3D microstructures
US20040207123A1 (en) 3-D model maker
Jiang et al. Continuous high‐throughput fabrication of architected micromaterials via in‐air photopolymerization
CN110505953B (zh) 使用喷墨打印制造复合组件
WO2018031828A1 (fr) Fabrication de structures de gradient de matériaux tridimensionnelles par durcissement en vol d'aérosols
Malinauskas et al. Nanophotonic lithography: a versatile tool for manufacturing functional three-dimensional micro-/nano-objects
Kronenfeld et al. Roll-to-roll, high-resolution 3D printing of shape-specific particles
Wu et al. Interfacial Regulation for 3D Printing based on Slice‐Based Photopolymerization
Maruo Stereolithography and two-photon polymerization
Seok et al. Micro/nanoscale 3-dimensional fabrication using multi-photons polymerization
Esteve et al. Micro-additive manufacturing technology
NL2027000B1 (en) A method and system for producing polymer micro-bodies
Mishra et al. Additive Manufacturing (3D Printing): A Review on the Micro Fabrication Methods
Wasley Digitally driven microfabrication of 3D multilayer embedded electronic systems
US20240157637A1 (en) System and methods for high resolution microfluidic channel fabrication via co-phase flow enabled additive manufacturing
Xiao Metallization Process for 3D Printed Electronics: from i3DP II to 3D Co-printing Technology
CN108274738B (zh) 一种多尺度可见光波段梯度折射率透镜的制备方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17840311

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17840311

Country of ref document: EP

Kind code of ref document: A1