WO2017185474A1 - Staining process for zirconia dental prosthesis - Google Patents
Staining process for zirconia dental prosthesis Download PDFInfo
- Publication number
- WO2017185474A1 WO2017185474A1 PCT/CN2016/084135 CN2016084135W WO2017185474A1 WO 2017185474 A1 WO2017185474 A1 WO 2017185474A1 CN 2016084135 W CN2016084135 W CN 2016084135W WO 2017185474 A1 WO2017185474 A1 WO 2017185474A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- sintering
- zirconia
- dental restoration
- mixing
- dyeing
- Prior art date
Abstract
A staining process for a zirconia dental prosthesis, comprising the steps of: S1, mixing: mixing zirconia ceramic powders and a colorant in a weight ratio of 100 : 1-5 so as to prepare a colored zirconia porcelain block; S2, pretreatment: carrying out a cutting process so as to obtain a dental prosthetic material, cleaning up residual ceramic powders on the surface of the pre-sintered zirconia dental prosthesis and keeping the zirconia dental prosthesis dry; S3, soaking: soaking the pretreated dental prosthesis in a staining solution for 10 to 15 min; and S4, sintering: subjecting the soaked dental prosthesis to a stepwise sintering. The staining process is simple to operate and has a uniform staining effect. The staining process is simple to operate and has a uniform staining effect.
Description
说明书 发明名称:一种氧化锆牙科修复体的染色工艺 技术领域 Description: A dyeing process for zirconia dental restorations
[0001] 本发明属于陶瓷制备技术领域, 具体涉及一种氧化锆牙科修复体的染色工艺。 [0001] The invention belongs to the technical field of ceramic preparation, and particularly relates to a dyeing process of a zirconia dental restoration.
背景技术 Background technique
[0002] 未着色牙科氧化锆多呈白色到象牙色, 具有一定的半透明性, 虽然能够较容易 的模拟自然牙颜色, 但并不能满足临床对修复体颜色的要求, 其表面往往需要 遮色, 这会使材料丧失一部分透明性, 将氧化锆本身颜色调整到与拟修复牙齿 的颜色、 明度和饱和度一致, 获得良好的质感, 同吋可以节省临床基牙的预备 空间。 将牙科氧化锆修复体进行内染, 可使氧化锆基底冠本身具有与天然牙牙 本质色泽相近, 在修复体制造过程中减少饰面瓷厚度或者完全不使用饰面瓷仍 可达到理想的没学效果, 同吋还可以减低备牙量, 更有利于保留更多的牙体组 织。 [0002] Uncolored dental zirconia is mostly white to ivory, and has a certain translucency. Although it can easily simulate the natural tooth color, it does not meet the clinical requirements for the color of the restoration, and the surface often needs to be opaque. This will lose a part of the transparency of the material, adjust the color of the zirconia itself to match the color, brightness and saturation of the tooth to be repaired, and obtain a good texture, which can save the preparation space of the clinical abutment. Internal dyeing of the dental zirconia restoration can make the zirconia base crown itself similar to the natural dentin color, reduce the thickness of the veneer in the manufacturing process of the restoration or completely eliminate the use of the veneer porcelain. The effect, the same can also reduce the amount of preparation, is more conducive to retain more tooth tissue.
[0003] 公幵号为 CN102674888A的中国专利公幵了用于牙科氧化锆陶瓷制品的着色溶 液及使用方法, 包括浸泡、 干燥、 烧结步骤, 其中浸泡与干燥方法虽有提及, 但叙述不具体, 操作不规范, 增加了染色操作难度, 导致染色不均匀、 不美观 [0003] Chinese Patent No. CN102674888A discloses a coloring solution and a method for using a dental zirconia ceramic article, including a soaking, drying, and sintering step, wherein the immersion and drying methods are mentioned, but the description is not specific. The operation is not standardized, which increases the difficulty of dyeing operation, resulting in uneven dyeing and unattractive
[0004] 因此, 幵发一种操作简单, 在着色氧化锆牙科修复体的基础上进行染色的染色 工艺, 可染色均匀、 降低饰面瓷厚度, 提高美观效果。 [0004] Therefore, a dyeing process which is simple in operation and dyed on the basis of a colored zirconia dental restoration can be dyed uniformly, the thickness of the veneer porcelain can be reduced, and the aesthetic effect can be improved.
技术问题 technical problem
[0005] 本发明的目的在于克服现有技术的缺点, 提供一种氧化锆牙科修复体的染色工 问题的解决方案 [0005] It is an object of the present invention to overcome the shortcomings of the prior art and to provide a solution to the problem of dyeing of zirconia dental restorations.
技术解决方案 Technical solution
[0006] 本发明的目的通过以下技术方案来实现: 一种氧化锆牙科修复体的染色工艺, 它包括以下步骤: The object of the present invention is achieved by the following technical solutions: A dyeing process for a zirconia dental restoration comprising the following steps:
[0007] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:1〜5混合, 制备着色氧
化锆瓷块; [0007] S1. Mixing: mixing colorant and zirconia ceramic powder in a weight ratio of 100:1~5 to prepare colored oxygen Zirconium ceramic block;
[0008] 52.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; [0008] 52. Pretreatment: performing a cutting process to obtain a dental restoration, and cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration and keeping it dry;
[0009] 53.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 10〜15min; [0009] 53. Soaking: the pre-treated dental prosthesis is soaked in the dyeing solution for 10~15min;
[0010] S4. [0010] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1000 〜1200°C, 烧结吋间为 20〜30min; 分段烧结第二段的温度为 1500〜1600°C, 烧 结吋间为 l〜2h。 Sintering: The soaked dental restoration is subjected to segmental sintering, the temperature of the first stage of the segmentation sintering is 1000 to 1200 ° C, and the sintering time is 20 to 30 min; the temperature of the second stage of the segmentation sintering is 1500 to 1600 °C, sintering time is 1~2h.
[0011] 进一步地, 所述着色剂为氧化铒、 氧化铈、 氧化钴、 氧化铁、 氧化锰、 氧化钕 或氧化镨中的一种或多种的组合。 [0011] Further, the colorant is a combination of one or more of cerium oxide, cerium oxide, cobalt oxide, iron oxide, manganese oxide, cerium oxide or cerium oxide.
[0012] 进一步地, 步骤 S2中所述干燥采用烘箱干燥, 所述干燥的温度为 30〜60°C, 干燥的吋间为 45〜60min。 [0012] Further, in the step S2, the drying is performed by oven drying, the drying temperature is 30 to 60 ° C, and the dry crucible is 45 to 60 min.
[0013] 进一步地, 所述染色液 BSM16色染色液或 BSM 26色染色液。 [0013] Further, the dyeing liquid BSM16 color dyeing liquid or BSM 26 color dyeing liquid.
[0014] 本发明中 BSM16染色液具体包括 BSM Al/L、 Aidite (BSM) [0014] The BSM16 staining solution in the present invention specifically includes BSM Al/L, Aidite (BSM)
A2/L、 Aidite (BSM) A3/L、 Aidite (BSM) A3.5/L、 Aidite (BSM) A2/L, Aidite (BSM) A3/L, Aidite (BSM) A3.5/L, Aidite (BSM)
A4/L、 Aidite (BSM) Bl/L、 Aidite (BSM) B2/L、 Aidite (BSM) A4/L, Aidite (BSM) Bl/L, Aidite (BSM) B2/L, Aidite (BSM)
B3/L、 Aidite (BSM) B4/L、 Aidite (BSM) Cl/L、 Aidite (BSM) B3/L, Aidite (BSM) B4/L, Aidite (BSM) Cl/L, Aidite (BSM)
C2/L、 Aidite (BSM) C3/L、 Aidite (BSM) C4/L、 Aidite (BSM) C2/L, Aidite (BSM) C3/L, Aidite (BSM) C4/L, Aidite (BSM)
D2/L、 Aidite (BSM) D3/L、 Aidite (BSM) D4/L。 D2/L, Aidite (BSM) D3/L, Aidite (BSM) D4/L.
[0015] 本发明中 BSM26色染色液包括 BSM1M1、 [0015] In the present invention, the BSM26 color dyeing solution comprises BSM1M1.
1M2、 2U.5、 2L2.5、 2M1、 2M2、 2M3、 2R1.5、 2R2.5、 3L1.5、 3L2.5、 3M1、 1M2, 2U.5, 2L2.5, 2M1, 2M2, 2M3, 2R1.5, 2R2.5, 3L1.5, 3L2.5, 3M1
3M2、 3M3、 3R1.5、 3R2.5、 4U.5、 4L2.5、 4M1、 4M2、 4M3、 4R1.5、 4R2.5、3M2, 3M3, 3R1.5, 3R2.5, 4U.5, 4L2.5, 4M1, 4M2, 4M3, 4R1.5, 4R2.5,
5M1、 5M2、 5M3。 5M1, 5M2, 5M3.
发明的有益效果 Advantageous effects of the invention
有益效果 Beneficial effect
[0016] 本发明具有以下优点: 本发明将着色剂和氧化锆陶瓷粉体进行混合后在进行浸 泡和烧结, 得到的氧化锆牙科修复体染色均匀、 美观, 本发明的操作方法具体 、 操作简单、 染色效果好。
本发明的实施方式 [0016] The present invention has the following advantages: The present invention combines a colorant and a zirconia ceramic powder to perform soaking and sintering, and the obtained zirconia dental restoration is uniformly dyed and beautiful, and the operation method of the present invention is simple and simple. , the dyeing effect is good. Embodiments of the invention
[0017] 下面结合实施例对本发明做进一步的描述, 本发明的保护范围不局限于以下所 述。 [0017] The present invention will be further described below in conjunction with the embodiments, and the scope of the present invention is not limited to the following.
[0018] 实施例 1: 一种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0018] Example 1: A dyeing process for a zirconia dental restoration comprising the following steps:
[0019] S1.混合: 将着色剂氧化铒与氧化锆陶瓷粉体按重量比为 100:1混合, 制备着色 氧化锆瓷块; [0019] S1 mixing: mixing the colorant cerium oxide and zirconia ceramic powder in a weight ratio of 100:1 to prepare a colored zirconia ceramic block;
[0020] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 30°C, 干燥的吋间为 45min; [0020] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 30 ° C, dry daytime is 45 min;
[0021] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 lOmin; 所述染 色液为 BSM16色染色液; [0021] S3. Soaking: the pre-treated dental prosthesis is soaked in the dyeing solution for lOmin; the dyeing liquid is BSM16 color dyeing liquid;
[0022] S4. [0022] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 iooo°c Sintering: the soaked dental restoration is subjected to segmental sintering, and the temperature of the first segment of the segmented sintering is iooo°c
, 烧结吋间为 20min; 分段烧结第二段的温度为 1500°C, 烧结吋间为 lh。 The sintering time is 20 min; the second stage of the section sintering is 1500 ° C, and the sintering time is lh.
[0023] 实施例 2: —种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0023] Example 2: A dyeing process for a zirconia dental restoration comprising the following steps:
[0024] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:5混合, 制备着色氧化锆 瓷块; 所述着色剂为氧化铈; [0024] S1 mixing: mixing the colorant and zirconia ceramic powder in a weight ratio of 100:5, to prepare a colored zirconia ceramic block; the coloring agent is cerium oxide;
[0025] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 60°C, 干燥的吋间为 60min; [0025] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 60 ° C, dry daytime is 60 min;
[0026] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 15min; 所述染 色液为 BSM26色染色液; [0026] S3. Soaking: the pre-treated dental restoration is soaked in the dyeing solution for 15 minutes; the dyeing liquid is BSM26 coloring solution;
[0027] S4. [0027] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1200°C , 烧结吋间为 30min; 分段烧结第二段的温度为 1600°C, 烧结吋间为 2h。 Sintering: The soaked dental restoration is subjected to segmental sintering. The temperature of the first stage of the segmentation sintering is 1200 ° C, and the sintering time is 30 min. The temperature of the second section of the segmentation sintering is 1600 ° C. It is 2h.
[0028] 实施例 3: —种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0028] Example 3: A dyeing process for a zirconia dental restoration comprising the following steps:
[0029] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:1.5混合, 制备着色氧化
锆瓷块; 所述着色剂为氧化钴; [0029] S1. Mixing: mixing the colorant with the zirconia ceramic powder at a weight ratio of 100:1.5 to prepare colored oxidation a zirconium ceramic block; the coloring agent is cobalt oxide;
[0030] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 34°C, 干燥的吋间为 48min; [0030] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 34 ° C, dry daytime is 48 min;
[0031] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 12min; 所述染 色液为 BSM26色染色液; [0031] S3. Soaking: the pre-treated dental restoration is soaked in the dyeing solution for 12 minutes; the dyeing liquid is BSM26 coloring solution;
[0032] S4. [0032] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1050°C Sintering: The soaked dental restoration is subjected to segmental sintering, and the temperature of the first stage of the segmental sintering is 1050 ° C
, 烧结吋间为 22min; 分段烧结第二段的温度为 1520°C, 烧结吋间为 1.2h。 The sintering time is 22 min; the second stage of the segmentation sintering is 1520 ° C, and the sintering time is 1.2 h.
[0033] 实施例 4: 一种氧化锆牙科修复体的染色工艺, 它包括以下步骤: Example 4: A dyeing process for a zirconia dental restoration comprising the following steps:
[0034] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:2混合, 制备着色氧化锆 瓷块; 所述着色剂为氧化铁; [0034] S1 mixing: mixing the colorant and zirconia ceramic powder in a weight ratio of 100:2, to prepare a colored zirconia ceramic block; the coloring agent is iron oxide;
[0035] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 38°C, 干燥的吋间为 52min; [0035] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 38 ° C, the dry day is 52 min;
[0036] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 13min; 所述染 色液为 BSM26色染色液; [0036] S3. Soaking: the pre-treated dental restoration is soaked in the dyeing solution for 13 minutes; the dyeing liquid is BSM26 coloring solution;
[0037] S4. [0037] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1080°C Sintering: The soaked dental restoration is subjected to segmental sintering, and the temperature of the first stage of the segmental sintering is 1080 ° C
, 烧结吋间为 24min; 分段烧结第二段的温度为 1550°C, 烧结吋间为 1.5h。 The sintering time is 24 min; the second stage of the segmentation sintering is 1550 ° C, and the sintering time is 1.5 h.
[0038] 实施例 5: —种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0038] Example 5: A dyeing process for a zirconia dental restoration comprising the following steps:
[0039] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:3混合, 制备着色氧化锆 瓷块; 所述着色剂为氧化锰; [0039] S1 mixing: mixing the colorant and zirconia ceramic powder in a weight ratio of 100:3, to prepare a colored zirconia ceramic block; the coloring agent is manganese oxide;
[0040] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 45°C, 干燥的吋间为 55min; [0040] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 45 ° C, dry crucible is 55 min;
[0041] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 14min; 所述染 色液为 BSM16色染色液;
[0042] S4. [0041] S3. Soaking: the pre-treated dental restoration is immersed in the dyeing solution for 14 minutes; the staining solution is BSM16 coloring solution; [0042] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 iioo°c Sintering: The soaked dental restoration is subjected to segmental sintering, and the temperature of the first stage of the segmental sintering is iioo°c
, 烧结吋间为 26min; 分段烧结第二段的温度为 1575°C, 烧结吋间为 1.8h。 The sintering time is 26 min; the second stage of the segmentation sintering is 1575 ° C, and the sintering time is 1.8 h.
[0043] 实施例 6: —种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0043] Example 6: A dyeing process for a zirconia dental restoration comprising the following steps:
[0044] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:3.8混合, 制备着色氧化 锆瓷块; 所述着色剂为氧化钕; [0044] S1 mixing: mixing the colorant and zirconia ceramic powder in a weight ratio of 100:3.8, preparing a colored zirconia ceramic block; the coloring agent is cerium oxide;
[0045] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 50°C, 干燥的吋间为 58min; [0045] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature 50 ° C, dry daytime is 58 min;
[0046] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 15min; 所述染 色液为 BSM26色染色液; [0046] S3. Soaking: the pre-treated dental restoration is soaked in the dyeing solution for 15 minutes; the dyeing liquid is BSM26 coloring solution;
[0047] S4. [0047] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1130°C Sintering: The soaked dental restoration is subjected to segmental sintering, and the temperature of the first stage of the segmental sintering is 1130 ° C
, 烧结吋间为 28min; 分段烧结第二段的温度为 1580°C, 烧结吋间为 lh。 The sintering time is 28 min; the second stage of the segmentation sintering is 1580 ° C, and the sintering time is lh.
[0048] 实施例 7: —种氧化锆牙科修复体的染色工艺, 它包括以下步骤: [0048] Example 7: A dyeing process for a zirconia dental restoration comprising the following steps:
[0049] S1.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:4.3混合, 制备着色氧化 锆瓷块; 所述着色剂为氧化镨; [0049] S1 mixing: mixing the colorant and zirconia ceramic powder in a weight ratio of 100:4.3, preparing a colored zirconia ceramic block; the coloring agent is cerium oxide;
[0050] S2.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙科修复体 表面残留的陶瓷粉末清理干净, 并保持干燥; 所述干燥采用烘箱干燥, 所述干 燥的温度为 54°C, 干燥的吋间为 60min; [0050] S2. Pretreatment: performing a cutting process to obtain a dental restoration, cleaning the ceramic powder remaining on the surface of the calcined zirconia dental restoration, and keeping it dry; the drying is dried by an oven, the drying temperature At 54 ° C, the dry day is 60 min;
[0051] S3.浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 l lmin; 所述染 色液为 BSM26色染色液; [0051] S3. Soaking: the pre-treated dental prosthesis is soaked in the dyeing solution for l lmin; the dyeing liquid is BSM26 color dyeing liquid;
[0052] S4. [0052] S4.
烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一段的温度为 1175°C , 烧结吋间为 22min; 分段烧结第二段的温度为 1510°C, 烧结吋间为 1.5h。
Sintering: The soaked dental restoration is subjected to segmental sintering. The temperature of the first stage of the segmentation sintering is 1175 ° C, and the sintering time is 22 min. The temperature of the second stage of the segmentation sintering is 1510 ° C. It is 1.5h.
Claims
[权利要求 1] 一种氧化锆牙科修复体的染色工艺, 其特征在于, 它包括以下步骤: [Claim 1] A dyeing process for a zirconia dental restoration, characterized in that it comprises the following steps:
51.混合: 将着色剂与氧化锆陶瓷粉体按重量比为 100:1〜5混合, 制 备着色氧化锆瓷块; 51. mixing: mixing the colorant and the zirconia ceramic powder in a weight ratio of 100:1 to 5 to prepare a colored zirconia ceramic block;
52.前处理: 进行切削加工, 得到牙科修复体, 将预烧的氧化锆牙 科修复体表面残留的陶瓷粉末清理干净, 并保持干燥; 52. Pre-treatment: The cutting process is performed to obtain a dental restoration, and the ceramic powder remaining on the surface of the calcined zirconia dental restoration is cleaned and kept dry;
S3. S3.
浸泡: 将前处理后的牙科修复体浸泡在染色液中进行浸泡 10〜15min Soak: Soak the pre-treated dental restoration in the staining solution for 10~15min
S4.烧结: 浸泡后的牙科修复体进行分段烧结, 所述分段烧结第一 段的温度为 1000〜1200°C, 烧结吋间为 20〜30min; 分段烧结第二段 的温度为 1500〜1600°C, 烧结吋间为 l〜2h。 S4. Sintering: The soaked dental restoration is subjected to segmental sintering, the temperature of the first stage of the segmentation sintering is 1000 to 1200 ° C, the sintering time is 20 to 30 min; the temperature of the second section of the segmentation sintering is 1500 ~1600 ° C, sintering 吋 between l ~ 2h.
[权利要求 2] 如权利要求 1所述的一种氧化锆牙科修复体的染色工艺, 其特征在于[Claim 2] A dyeing process for a zirconia dental restoration according to claim 1, wherein
, 所述着色剂为氧化铒、 氧化铈、 氧化钴、 氧化铁、 氧化锰、 氧化钕 或氧化镨中的一种或多种的组合。 The colorant is a combination of one or more of cerium oxide, cerium oxide, cobalt oxide, iron oxide, manganese oxide, cerium oxide or cerium oxide.
[权利要求 3] 如权利要求 1所述的一种氧化锆牙科修复体的染色工艺, 其特征在于 [Claim 3] A dyeing process for a zirconia dental restoration according to claim 1, wherein
, 步骤 S2中所述干燥采用烘箱干燥, 所述干燥的温度为 30〜60°C, 干 燥的吋间为 45〜60min。 The drying in the step S2 is carried out by oven drying, the drying temperature is 30 to 60 ° C, and the dry crucible is 45 to 60 min.
[权利要求 4] 如权利要求 1所述的一种氧化锆牙科修复体的染色工艺, 其特征在于 [Claim 4] A dyeing process for a zirconia dental restoration according to claim 1, wherein
, 所述染色液为 BSM16色染色液或 BSM26色染色液。
The staining solution is a BSM16 coloring solution or a BSM26 coloring solution.