WO2017160290A1 - Composants de fond de trou revêtus - Google Patents
Composants de fond de trou revêtus Download PDFInfo
- Publication number
- WO2017160290A1 WO2017160290A1 PCT/US2016/022745 US2016022745W WO2017160290A1 WO 2017160290 A1 WO2017160290 A1 WO 2017160290A1 US 2016022745 W US2016022745 W US 2016022745W WO 2017160290 A1 WO2017160290 A1 WO 2017160290A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polymeric surface
- component
- cable
- hydrophilic polymeric
- coated
- Prior art date
Abstract
Cette invention concerne un procédé comprenant : le revêtement d'une surface polymère hydrophile d'un composant d'un système de pompe électrique immergée par une dispersion aqueuse polymère pour former un composant revêtu ; et le frittage du composant revêtu pour former un composant revêtu fritté qui comprend une surface polymère moins hydrophile, qui peut être une surface polymère hydrophobe.
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2016/022745 WO2017160290A1 (fr) | 2016-03-17 | 2016-03-17 | Composants de fond de trou revêtus |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
PCT/US2016/022745 WO2017160290A1 (fr) | 2016-03-17 | 2016-03-17 | Composants de fond de trou revêtus |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017160290A1 true WO2017160290A1 (fr) | 2017-09-21 |
Family
ID=59851358
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2016/022745 WO2017160290A1 (fr) | 2016-03-17 | 2016-03-17 | Composants de fond de trou revêtus |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2017160290A1 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11414967B2 (en) * | 2017-01-05 | 2022-08-16 | Halliburton Energy Services, Inc. | Dynamic power optimization system and method for electric submersible motors |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070051510A1 (en) * | 2005-09-07 | 2007-03-08 | Veneruso Anthony F | Polymer protective coated polymeric components for oilfield applications |
US20120063934A1 (en) * | 2010-09-13 | 2012-03-15 | Baker Hughes Incorporated | Electrical Submersible Pump System Having High Temperature Slot, End Bell and Phase-to-Phase Insulation |
US20140027152A1 (en) * | 2012-07-24 | 2014-01-30 | Jason Holzmueller | Power Cable System |
US20140042835A1 (en) * | 2012-08-11 | 2014-02-13 | Schlumberger Technology Corporation | Equipment including epitaxial co-crystallized material |
US20140154113A1 (en) * | 2012-12-05 | 2014-06-05 | Ge Oil & Gas Esp, Inc. | High temperature downhole motors with advanced polyimide insulation materials |
-
2016
- 2016-03-17 WO PCT/US2016/022745 patent/WO2017160290A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20070051510A1 (en) * | 2005-09-07 | 2007-03-08 | Veneruso Anthony F | Polymer protective coated polymeric components for oilfield applications |
US20120063934A1 (en) * | 2010-09-13 | 2012-03-15 | Baker Hughes Incorporated | Electrical Submersible Pump System Having High Temperature Slot, End Bell and Phase-to-Phase Insulation |
US20140027152A1 (en) * | 2012-07-24 | 2014-01-30 | Jason Holzmueller | Power Cable System |
US20140042835A1 (en) * | 2012-08-11 | 2014-02-13 | Schlumberger Technology Corporation | Equipment including epitaxial co-crystallized material |
US20140154113A1 (en) * | 2012-12-05 | 2014-06-05 | Ge Oil & Gas Esp, Inc. | High temperature downhole motors with advanced polyimide insulation materials |
Cited By (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US11414967B2 (en) * | 2017-01-05 | 2022-08-16 | Halliburton Energy Services, Inc. | Dynamic power optimization system and method for electric submersible motors |
US11613974B2 (en) | 2017-01-05 | 2023-03-28 | Halliburton Energy Services, Inc. | Dynamic power optimization system and method for electric submersible motors |
US20230184071A1 (en) * | 2017-01-05 | 2023-06-15 | Halliburton Energy Services, Inc. | Dynamic power optimization system and method for electric submersible motors |
US11795808B2 (en) | 2017-01-05 | 2023-10-24 | Halliburton Energy Services, Inc. | Dynamic power optimization system and method for electric submersible motors |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US20160293294A1 (en) | Cable for downhole equipment | |
US9634535B2 (en) | Equipment including epitaxial co-crystallized material | |
US11025118B2 (en) | Polymeric materials | |
US20170244294A1 (en) | Equipment including polytetrafluoroethylene | |
US20160217888A1 (en) | Power cable gas barrier | |
US11646134B2 (en) | Armored submersible power cable | |
US10204715B2 (en) | Submersible power cable | |
CA2810093C (fr) | Systeme et procede d'isolation de fils magnetiques amelioree | |
CN109643868B (zh) | 用于潜油电动机的耐气体电缆头系统和方法 | |
US9455069B2 (en) | Power cable system | |
WO2016032469A1 (fr) | Isolation de conducteur électrique améliorée | |
US20140154113A1 (en) | High temperature downhole motors with advanced polyimide insulation materials | |
US20090317264A1 (en) | Esp motor windings for high temperature environments | |
WO2016094244A1 (fr) | Revêtement résistant à la corrosion et conducteur | |
US20140152155A1 (en) | High temperature downhole motors with advanced polyimide insulation materials | |
WO2016089938A1 (fr) | Polymères pour moteurs électriques de fond de trou | |
WO2017058647A1 (fr) | Câble de puissance submersible à haute température | |
WO2017160290A1 (fr) | Composants de fond de trou revêtus | |
US20190228879A1 (en) | Methods of manufacturing coated conductors | |
GB2506513B (en) | Equipment including epitaxial co-crystallised material | |
WO2016191508A1 (fr) | Bande formant barrière en alliage de plomb | |
US20240136879A1 (en) | Polymeric materials | |
WO2016024939A1 (fr) | Élément d'étanchéité conjointement moulé | |
CA2916162A1 (fr) | Moteurs de fond de trou a haute temperature ayant des materiaux d'isolation de polyimide avances |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 16894749 Country of ref document: EP Kind code of ref document: A1 |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 16894749 Country of ref document: EP Kind code of ref document: A1 |