WO2017149082A1

WO2017149082A1 - Piston ring

Info

Publication number: WO2017149082A1
Application number: PCT/EP2017/054925
Authority: WO
Inventors: Thomas Smith; Thomas Stong
Original assignee: Mahle International GmbH
Current assignee: Mahle International GmbH
Priority date: 2016-03-04
Filing date: 2017-03-02
Publication date: 2017-09-08
Anticipated expiration: 2018-09-04
Also published as: US20170254418A1; US10030773B2

Abstract

A piston ring (110) for a piston (14) of a reciprocating internal combustion engine. The piston ring comprises a body having an outer contact surface. A tribological coating (126) is formed on the outer contact surface of the body. The tribological coating (126)comprises a quaternary Cr-V-Ti-N system. In one form, the tribological coating is deposited on the outer contact surface of the body as a stack of multiple layers (128,130).

Description

PISTON RING

TECHNICAL FIELD

[0001] The present invention generally relates to a piston ring for a piston of a reciprocating engine, and more particularly, to a coating for a piston ring.

BACKGROUND

[0002] A piston ring is an open-ended ring that fits into an annular groove in an outer circumference of a piston of a reciprocating engine, such as an internal combustion engine. When disposed within a cylinder of the engine, the piston ring is compressed around the piston and the intrinsic spring force of the ring ensures sufficient contact between an outer circumferential surface of the ring and an inner wall of the cylinder. During engine operation, the piston moves up and down within the cylinder and the pressure exerted on the cylinder wall by the piston ring provides a seal around the piston between the combustion chamber and the crankcase, which helps prevent escape of combustion gases from the combustion chamber and helps control oil consumption. Piston rings also may help transfer heat away from the piston to the cylinder wall and may be configured to regulate the amount of oil on the cylinder wall by distributing it on and wiping it off the cylinder wall.

[0003] Metallic and/or ceramic coatings may be applied to contact surfaces of various sliding components to improve the tribological properties thereof. For example, chromium platings are commonly applied to the outer circumferential surfaces of piston rings for increased wear resistance. Graphite, phosphate, or molybdenum coatings may be used to reduce the sliding friction between an outer contact surface of a piston ring and an interior surface of a cylinder wall.

SUMMARY

[0004] According to an aspect of the invention, there is provided a piston ring comprising a body having an outer contact surface. A tribological coating is formed on the outer contact surface of the body. The tribological coating comprises a quaternary Cr-V-Ti-N system. [0005] In accordance with an embodiment of the invention, the quaternary Cr-V-Ti-N system comprises 15^15at% chromium (Cr), 10-20at% vanadium (V), 5-15at% titanium (Ti), and 40- 50at% nitrogen (N).

[0006] In accordance with an embodiment of the invention, a nitrided layer is formed at an exterior surface of the body of the piston ring, with the tribological coating formed over the nitrided layer.

[0007] In accordance with an embodiment of the invention, an intermediate coating is disposed between the body of the piston ring and the tribological coating.

[0008] In accordance with an embodiment of the invention, the tribological coating comprises a stack of multiple layers.

[0009] The piston ring, as described above, may be used in combination with a piston and disposed within a cylinder of a reciprocating internal combustion engine to form a seal around the piston between the combustion chamber and the crankcase. The piston ring, as described above, is generally more robust than prior art piston rings due to the presence of the tribological coating on the contact surface of the piston ring. In particular, the presence of the tribological coating on the contact surface of the piston ring may provide the piston ring with enhanced wear resistance, scuff resistance, high hardness, and low friction properties, which may allow the piston ring to more effectively and efficiently function in the relatively harsh operating environments of modern combustion engines and also may increase the service life of the piston ring.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] Preferred exemplary embodiments of the invention will hereinafter be described in conjunction with the appended drawings, wherein like designations denote like elements, and wherein:

[001 1] FIG. 1 is a side elevation of a piston and connecting rod assembly for an internal combustion engine;

[0012] FIG. 2 is a perspective view of a piston ring;

[0013] FIG. 3 is a cross-sectional view of the piston ring of FIG. 2 taken along line 3-3; and [0014] FIG. 4 is a magnified partial cross-sectional view of the piston ring.

DETAILED DESCRIPTION

[0015] The presently disclosed tribological coating may be formed on a contact surface of a sliding component, such as a piston ring for a piston of a reciprocating internal combustion engine. When the tribological coating is formed on an outer circumferential surface of a piston ring, such as an upper compression ring, the tribological coating may provide the piston ring with certain desirable properties. For example, the presently disclosed tribological coating may be formulated to enhance the wear resistance, scuff resistance, and hardness of the piston ring, while reducing sliding friction between the piston ring and the inner wall of the cylinder, which may allow the piston ring to better withstand the relatively harsh operating environments of modern combustion engines. In addition, the formulation of the tribological coating may provide the coating with improved ductility and a reduced amount of internal stress at high temperatures, as compared to conventional piston ring coatings, which may help reduce cracking and spalling of the coating.

[0016] FIG. 1 illustrates a piston and connecting rod assembly 10 for use in a cylinder 12 of a reciprocating internal combustion engine (not shown). The assembly 10 has a central longitudinal axis A and comprises a piston 14 and a connecting rod 16. The piston 14 has a body including an upper crown 18 and a lower skirt 20. A plurality of annular grooves 22 are formed about an outer circumference of the crown 18 of the piston 14 and are sized to accommodate three piston rings: an upper compression ring 24, a lower compression ring 26, and an oil control ring 28. Each of the piston rings 24, 26, 28 has an outer circumferential surface or contact surface that is adapted to contact and slide along an inner wall of the cylinder 12. A pin bore 30 is formed in the skirt 20 of the piston 14 and is sized to receive a piston pin 32 for connecting the piston 14 to a small end of the connecting rod 16.

[0017] FIGS. 2 and 3 illustrate a piston ring 110 for a piston of a reciprocating internal combustion engine, such as the piston 14 illustrated in FIG. 1. The piston ring 1 10 comprises a split annular body 1 12 having an exterior surface that includes an upper surface 1 14, a lower surface 1 16, an inner circumferential surface 118, and an outer circumferential surface or contact surface 120 extending between the upper and lower surfaces 114, 1 16. The piston ring 1 10 illustrated in FIGS. 2 and 3 has a keystone or trapezoidal shaped cross-section, with tapered upper and lower surfaces 1 14, 1 16. However, in other embodiments, the piston ring 1 10 may exhibit various other cross-sectional shapes, e.g., rectangular. The annular body 1 12 may be made of cast iron (e.g., gray or nodular cast iron), steel (e.g., stainless steel), or any other suitable ferrous metal or alloy.

[0018] A diffusion nitrided layer 122 may be formed at the exterior surface of the annular body 1 12, although this is not necessarily required. The nitrided layer 122 may be formed by any known nitriding process. For example, the nitrided layer 122 may be formed by heating the annular body 1 12 to a suitable temperature and exposing the annular body 1 12 to a nitrogen-containing gas, e.g., ammonia (NH₃). The nitrided layer 122 may extend from the exterior surface of the annular body 112 of the piston ring 1 10 at a depth in the range of 10-170 μηι. The actual depth of the nitrided layer 122 at the exterior surface of the body 1 12 may be selected based upon the size of the piston ring 1 10 and also may be selected to impart certain desirable mechanical and/or physical properties to the piston ring 1 10, including high hardness, wear resistance, scuff resistance, and improved fatigue life. In other embodiments, the exterior surface of the annular body 112 may be subjected to a different type of thermochemical surface treatment process to produce a different type of diffusion layer at the exterior surface of the annular body 112.

[0019] Referring now to FIG. 3, in one form, an intermediate coating 124 and a tribological coating 126 are formed on the exterior surface of the annular body 1 12 over the nitrided layer 122. The tribological coating 126 may be formed on the exterior surface of the annular body 1 12 over the intermediate coating 124 and/or over one or more other coating layers already present on the exterior surface of the annular body 1 12. Or the tribological coating 126 may be formed directly on the exterior surface of the annular body 1 12. In such case, the intermediate coating 124 is omitted. Forming the tribological coating 126 directly on the exterior surface of the annular body 1 12 may or may not include forming the tribological coating 126 over the nitrided layer 122 or some other type of diffusion layer. This will depend upon whether the annular body 1 12 has or has not been subjected to a nitriding process or some other type of thermochemical surface treatment process prior to deposition of the tribological coating 126. [0020] In the embodiment illustrated in FIG. 3, the intermediate coating 124 and the tribological coating 126 are formed on the outer circumferential surface 120 of the annular body 1 12. In particular, the intermediate coating 124 and the tribological coating 126 are formed on the outer circumferential surface 120 of the annular body 1 12 such that the intermediate coating 124 and the tribological coating 126 both extend from the upper surface 1 14 to the lower surface 1 16 of the annular body 1 12. In other embodiments, the intermediate coating 124 and/or the tribological coating 126 may be additionally or alternatively formed over one or more other exterior surfaces of the annular body 112, including the upper surface 1 14, the lower surface 1 16, and/or the inner circumferential surface 1 18 of the body 1 12. In addition, in the embodiment illustrated in FIG. 3, the intermediate coating 124 is disposed between the nitrided layer 122 and the tribological coating 126 on the outer circumferential surface 120 of the annular body 1 12. However, in other embodiments, the intermediate coating 124 may be omitted and the tribological coating 126 may be formed directly on the outer circumferential surface 120 of the annular body 112.

[0021] The intermediate coating 124 may help improve adhesion of the tribological coating 126 to the exterior surface of the annular body 1 12 and may comprise at least one of chromium (Cr), nickel ( i), cobalt (Co), titanium (Ti), and vanadium (V). For example, in some embodiments, the intermediate coating 124 may comprise a combination of chromium (Cr), titanium (Ti), and vanadium (V). In other embodiments, the intermediate coating 124 may consist essentially of elemental chromium (Cr). The intermediate coating 124 may be formed on the exterior surface of the annular body 1 12 by a thermal spray process (e.g., a flame spraying process, a high velocity oxy-fuel (HVOF) process, or a plasma spraying process), a physical vapor deposition (PVD) process, or by any other suitable process. A suitable thickness for the intermediate coating 124 may be in the range of 1-10 μηι. However, in other forms, the thickness of the intermediate coating 124 may be somewhat more or less than this amount depending on the application method used to form the intermediate coating 124 on the exterior surface of the annular body 112.

[0022] The tribological coating 126 may improve the wear resistance, scuff resistance, hardness, and frictional properties of the piston ring 1 10 and may comprise a quaternary chromium (Cr), vanadium (V), titanium (Ti), and nitrogen ( i)-containing system (Cr-V-Ti-N system). The amount of chromium (Cr) in the quaternary Cr-V-Ti-N system, as a percentage of the total number of atoms in the system, may be: greater than or equal to 15.0at%, 25.0at%, or 30.0at%; less than or equal to 45.0at%, 40.0at%, or 35.0at%; or between 15.0-45.0at%, 25.0-40.0at%, or 30.0-35.0at%. The amount of vanadium (V) in the quaternary Cr-V-Ti-N system, as a percentage of the total number of atoms in the system, may be: greater than or equal to 5.0at%, 10.0at%, or 13.0at%; less than or equal to 20.0at%, 15.0at%, or 13.0at%; or between 5.0- 20.0at%, 10.0-15.0at%, or 12.0-13.0at%. The presence of vanadium (V) in the quaternary Cr- V-Ti-N system may help lower the frictional properties and increase the scuff resistance of the tribological coating 126. The amount of titanium (Ti) in the quaternary Cr-V-Ti-N system, as a percentage of the total number of atoms in the system, may be: greater than or equal to 0.0at%, 5.0at%, or 6.0at%; less than or equal to 15.0at%, 10.0at%, or 8.0at%; or between 0.0-15.0at%, 5.0-10.0at%, or 6.0-8.0at%. In particular, the presence of about 5.0-15.0at% titanium (Ti) in the quaternary Cr-V-Ti-N system may effectively enhance the hardness and wear resistance of the tribological coating 126 without adversely affecting other desirable properties of the coating 126 including internal stress. The amount of nitrogen (N) in the quaternary Cr-V-Ti-N system, as a percentage of the total number of atoms in the system, may be: greater than or equal to 40.0at%, 42.5at%, or 45.0at%; less than or equal to 50.0at%, 47.5at%, or 47.0at%; or between 40.0-50.0at%, 42.5-47.5at%, or 45.0-47.0at%. In one specific embodiment, the tribological coating 126 may comprise about 34.5at% chromium (Cr), 12.5at% vanadium (V), about 7.0at% titanium (Ti), and about 46.0at% nitrogen (N). The Cr:V:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be about 5:2:1. For example, the Cr:V:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be in the range of 4-6:1-3:0-2. The Cr:V atomic ratio in the quaternary Cr-V-Ti-N system may be about 3:1. For example, the Cr: V atomic ratio in the quaternary Cr-V-Ti-N system may be in the range of 1.5-4.5: 1. The Cr:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be about 5:1. For example, the Cr:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be in the range of 4- 6:1. The V:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be about 2:1. For example, the V:Ti atomic ratio in the quaternary Cr-V-Ti-N system may be in the range of 1- 3:1. [0024] The quaternary Cr-V-Ti-N system may be doped with one or more doping elements. For example, the quaternary Cr-V-Ti-N system may be doped with at least one of oxygen (O), carbon (C), and boron (B). The amount of the one or more doping elements in the quaternary Cr-V-Ti-N system, as a percentage of the total number of atoms in the system, may be: greater than or equal to 0.1 at%, 0.5at%, or 2at%; less than or equal to 10at%, 8at%, or 3at%; or between 0.1-10at%, 2-8at%, or 0.5-3at%. In some forms, the amount of oxygen (O), carbon (C), and/or boron (B) doping of the quaternary Cr-V-Ti-N system may be somewhat greater than 10at% depending on the application of use and/or the desired characteristics of the tribological coating 126.

[0025] The tribological coating 126 may additionally include one or more elements or compounds of molybdenum (Mo), niobium (Nb), zirconium (Zr), tungsten (W), tantalum (Ta), aluminum (Al), and silicon (Si). For example, the tribological coating 126 may include one or more nitrides of molybdenum (Mo), niobium (Nb), zirconium (Zr), tungsten (W), tantalum (Ta), aluminum (Al), and silicon (Si). Such elements and/or compounds may be present in the tribological coating 126 in an amount greater than or equal to 0.0at%, 5.0at%, or 6.0at%; less than or equal to 15.0at%, 10.0at%, or 8.0at%; or between 0.0-15.0at%, 5.0-10.0at%, or 6.0-8.0at%.

[0026] In one form, the tribological coating 126 may consist essentially of a quaternary chromium (Cr), vanadium (V), titanium (Ti), and nitrogen (Ni)-containing system (Cr-V-Ti-N system). For example, the quaternary Cr-V-Ti-N system may account for greater than or equal to 90at%, greater than or equal to 95at%, greater than or equal to 99at%, greater than or equal to 99.9at% of the tribological coating 126.

[0027] The tribological coating 126 may be formed on the exterior surface of the annular body 1 12 via any suitable physical vapor deposition (PVD) process (e.g., cathodic arc or sputtering), reactive electric arc process, or chemical vapor deposition (CVD) process. The tribological coating 126 may have an overall thickness in the range of about 5-100 μιη. For example, in one form, the overall thickness of the tribological coating 126 may be in the range of about 20^-0 μηι. The overall thickness of the tribological coating 126 may be somewhat more or less than this amount depending on the particular application of use. [0028] The tribological coating 126 may be deposited on the exterior surface of the annular body 1 12 as a single layer or as a stack of multiple successively applied layers, wherein the number of layers in the stack can be any integer greater than one. Forming the tribological coating 126 as a stack of multiple layers may provide the coating 126 with certain desirable attributes. For example, depositing the tribological coating 126 on the exterior surface of the annular body 1 12 as a stack of multiple layers may help reduce the overall internal stress of the tribological coating 126, which may help reduce the incidence of spalling. In addition, the composition of the layers in the stack of multiple layers may be formulated to allow for the formation of a relatively thick tribological coating 126 without creating an undue amount of internal stress within the coating 126.

[0029] In embodiments where the tribological coating 126 comprises a stack of multiple layers, each individual layer in the stack may have a generally uniform thickness and a generally uniform chemical composition. But the thickness and/or the chemical composition of each of the individual layers may be the same or different from that of the one or more other layers in the stack. In one form, the thickness of each of the individual layers in the stack of multiple layers that make up the tribological coating 126 may be in the range of 5-200 nm. The stack of multiple layers that make up the tribological coating 126 may comprise a quaternary Cr-V-Ti-N system. This may mean that the overall chemical composition of the stack of multiple layers comprises a quaternary Cr-V-Ti-N system when the composition of each of the individual layers is grouped together as a whole. Or, this may mean that one or more of the individual layers in the stack of multiple layers comprises a quaternary Cr-V-Ti-N system. In some forms, it may be desirable for a Cr-V-Ti-N-containing layer to form the outermost layer in the stack of multiple layers that make up the tribological coating 126.

[0030] In one form, the tribological coating 126 may comprise a stack of multiple layers that includes two, three, four, or more individual layers, with each of the individual layers having a different chemical composition than the others. In another form, the tribological coating 126 may comprise a stack of multiple layers wherein two or more of the individual layers have the same chemical composition, but at least one of the other individual layers has a different chemical composition. For example, the tribological coating 126 may comprise a stack of multiple layers that includes a series of two alternately and repeatedly applied individual layers having different chemical compositions. As another example, the tribological coating 126 may comprise a stack of multiple layers that includes a series of three or more sequentially and repeatedly applied layers, with each of the layers in the series having a different chemical composition.

[0031] Referring now to FIG. 4, in one form, the tribological coating 126 comprises a stack of multiple layers that includes a first layer 128 and a subsequently applied second layer 130. The tribological coating 126 is formed by alternately and repeatedly applying the first layer 128 and the second layer 130 to the exterior surface of the annular body 112. For example, the first and second layers 128, 130 may be alternately and repeatedly applied to the exterior surface of the annular body 1 12 a sufficient number of times for the tribological coating 126 to reach a final desired thickness. This may mean that each of the first and second layers 128, 130 is individually applied to the exterior surface of the annular body 112 two, three, four, or more times. The thickness of the first layer 128 may be the same or different from that of the second layer 130. In one form, the first layer 128 may have a thickness in the range of 5-150 nm and the second layer 130 may have a thickness in the range of 5-150 nm, with the thickness of the first layer 128 being different from that of the second layer 130. In one form, the chemical composition of the first layer 128 is different from that of the second layer 130. For example, the first layer 128 may comprise a quaternary Cr-V-Ti-N system and the second layer 130 may comprise one or more other metal nitrides, for example, binary metal nitrides. As another example, the first layer 128 may comprise one or more metal nitrides, for example, binary metal nitrides, and the second layer 130 may comprise a quaternary Cr-V-Ti-N system. Some examples of suitable metal nitrides for the first and second layers 128, 130 include chromium nitride (CrN and/or Cr₂N), vanadium nitride (VN), and/or titanium nitride (TiN). The first layer 128 and/or the second layer 130 also may include one or more elements or compounds of molybdenum (Mo), niobium (Nb), zirconium (Zr), tungsten (W), tantalum (Ta), aluminum (Al), and silicon (Si).

[0032] In one form, each layer in the stack of multiple layers that make up the tribological coating 126 may comprise a quaternary Cr-V-Ti-N system. In such case, the overall chemical composition of the tribological coating 126 may be generally uniform and may be the same regardless of whether the coating 126 is deposited as a single layer or in multiple layers on the exterior surface of the annular body 112. [0033] It is to be understood that the foregoing is a description of one or more preferred exemplary embodiments of the invention. The invention is not limited to the particular embodiment(s) disclosed herein, but rather is defined solely by the claims below. Furthermore, the statements contained in the foregoing description relate to particular embodiments and are not to be construed as limitations on the scope of the invention or on the definition of terms used in the claims, except where a term or phrase is expressly defined above. Various other embodiments and various changes and modifications to the disclosed embodiment(s) will become apparent to those skilled in the art. All such other embodiments, changes, and modifications are intended to come within the scope of the appended claims.

[0034] As used in this specification and claims, the terms "for example," "e.g.," "for instance," "such as," and "like," and the verbs "comprising," "having," "including," and their other verb forms, when used in conjunction with a listing of one or more components or other items, are each to be construed as open-ended, meaning that the listing is not to be considered as excluding other, additional components or items. Other terms are to be construed using their broadest reasonable meaning unless they are used in a context that requires a different interpretation.

Claims

1. A piston ring comprising:

a body having an outer contact surface; and

a tribological coating overlying the outer contact surface of the body, wherein the tribological coating comprises a quaternary Cr-V-Ti-N system.

2. The piston ring set forth in claim 1 wherein the quaternary Cr-V-Ti-N system comprises 15^5at% chromium (Cr), 10-20at% vanadium (V), 5-15at% titanium (Ti), and 40-50at% nitrogen (N).

3. The piston ring set forth in claim 1 wherein the tribological coating is doped with 0.1- 10at% of at least one doping element selected from the group consisting of oxygen (O), carbon (C), and boron (B).

4. The piston ring set forth in claim 1 wherein the tribological coating comprises 5-15at% of at least one element or compound selected from the group consisting of molybdenum (Mo), niobium (Nb), zirconium (Zr), tungsten (W), tantalum (Ta), aluminum (Al), and silicon (Si).

5. The piston ring set forth in claim 1 comprising:

a nitrided layer formed at an exterior surface of the body, wherein the tribological coating is formed over the nitrided layer.

6. The piston ring set forth in claim 1 comprising:

an intermediate coating disposed between the body and the tribological coating, wherein the intermediate coating comprises at least one of chromium (Cr), titanium (Ti), and vanadium (V).

7. The piston ring set forth in claim 1 wherein the tribological coating is formed on the outer contact surface of the body by a physical vapor deposition (PVD) process.

8. The piston ring set forth in claim 1 wherein the body comprises a split annular body and the tribological coating is formed on an outer circumferential surface of the annular body.

9. The piston ring set forth in claim 1 wherein the tribological coating has a thickness in the range of 5-100 μηι.

10. The piston ring set forth in claim 1 wherein the tribological coating comprises a stack of multiple layers that includes a first layer and a second layer, with the first layer having a different chemical composition than that of the second layer.

1 1. The piston ring set forth in claim 10 wherein at least one of the layers in the stack of multiple layers that make up the tribological coating comprises a quaternary Cr-V-Ti-N system.

12. The piston ring set forth in claim 10 wherein at least one of the layers in the stack of multiple layers that make up the tribological coating comprises a binary metal nitride.

13. A piston ring comprising:

a split annular body having an upper surface, a lower surface, an inner circumferential surface, and an outer circumferential surface extending between the upper and lower surfaces; and

a tribological coating overlying the outer circumferential surface of the annular body, wherein the tribological coating comprises a quaternary Cr-V-Ti-N system and is formed on the outer circumferential surface of the annular body as a stack of multiple layers.

14. The piston ring set forth in claim 13 wherein the quaternary Cr-V-Ti-N system comprises 15^5at% chromium (Cr), 10-20at% vanadium (V), 5-15at% titanium (Ti), and 40- 50at% nitrogen (N).

15. The piston ring set forth in claim 13 wherein at least one of the layers in the stack of multiple layers that make up the tribological coating comprises a quaternary Cr-V-Ti-N system.

16. The piston ring set forth in claim 13 wherein at least one of the layers in the stack of multiple layers that make up the tribological coating comprises a binary metal nitride.

17. The piston ring set forth in claim 13 wherein the stack of multiple layers includes a first layer and a second layer, with the first layer having a different chemical composition than that of the second layer.

18. The piston ring set forth in claim 17 wherein the first layer and the second layer are individually and alternately applied to the outer circumferential surface of the annular body at least two times.

19. The piston ring set forth in claim 13 comprising:

a nitrided layer formed at an exterior surface of the annular body; and

an intermediate coating formed on the outer circumferential surface of the annular body over the nitrided layer,

wherein the tribological coating is formed over the intermediate coating on the outer circumferential surface of the annular body.

20. The piston ring set forth in claim 13 wherein the quaternary Cr-V-Ti-N system is doped with 0.1-10at% of at least one doping element selected from the group consisting of oxygen (O), carbon (C), and boron (B).