WO2017133833A1

WO2017133833A1 - Preparation of matt paints and printing inks

Info

Publication number: WO2017133833A1
Application number: PCT/EP2017/000098
Authority: WO
Inventors: Volker Jurgens; Frank Mersch
Original assignee: Kronos International, Inc.
Priority date: 2016-02-02
Filing date: 2017-01-27
Publication date: 2017-08-10
Also published as: TWI716535B; ZA201804841B; JP2019510122A; BR112018015582A2; KR20180104742A; RU2708605C1; PL3411439T3; PT3411439T; MY191492A; WO2017133833A8; AU2017213599A1; US20170218210A1; MX2018009472A; EP3411439A1; TW201800502A; EP3202858A1; US10533102B2; EP3411439B1; CN109071963A; UA124006C2

Abstract

The invention relates to a pigment composition for preparing pigmented matt coatings, such as matt paints and printing inks. Further, the invention relates to a process for preparing such pigment composition, and to a coating formulation containing such composition. Finally, the invention is directed to a pigmented matt surface of a substrate, and to the use of the pigment compositions disclosed herein for matting substrates.

Description

Preparation of matt paints and printing inks

Field of the invention

Technological background of the invention

Matting a surface is achieved by selectively roughening the surface in the micro range. Thus, impinging light is no longer reflected directionally, but diffusely. The height, shape and number of the surface structures determine the degree of gloss of the paint film or printing ink.

Specific matting agents are usually added to the paint or printing ink composition to achieve a mat surface. The usual matting agents are spherical particles with a particle size within a range of from 1 to about 20 pm, as a function of the film layer thickness. In practice, precipitated or pyrogenic silicas or silica gels are predominantly used as matting agents, but also matting agents based on duromers, waxes, or thermoplasts are used. Further known is the suitability of silicates, calcium carbonate, and different kinds of hollow spheres.

Thus, EP 1 398 301 B1 discloses matting agents for paints and lacquers based on precipitated silicas having particle sizes (d50) within a range of from 5 to 15 pm and a specific surface (BET) of from 350 to 550 m²/g. The silicas are optionally coated with wax.

DE 195 16 253 A1 discloses matting agents based on spray-dried silica gel. In order to ensure sufficient stability of the aggregates, a binder, such as a layer silicate, pyrogenic silica or organic polymer, is used. The agent has a particle size of from 1 to 20 pm and a specific pore volume of from 0.4 to 2.5 ml/g. In general, the matting effect increases with the dosage of the matting agent. Larger particles have a greater matting effect, but lead to a less smooth surface, which is undesirable. Further, both higher contents of matting agent and a longer dispersing time result in increasing viscosities of the paint systems, thus creating processing problems. Further, the known matting agents based on silica are difficult to handle because of a strong tendency to dusting, and are therefore disadvantageous.

According to the patent application EP 1 500 3103, these disadvantages are avoided by using pigment agglomerates having a mean size d50 of from 2 pm to 200 pm in the preparation of matt paints and printing inks. The process is characterized in that the pigment agglomerates partially decay during the dispersing, for example, in a bead mill, but no increase of viscosity occurs. A further feature of the process is that the matting agent and the pigment have the same chemical compositions and surface properties. A drawback of the process is that the degree of matting depends significantly on the input of dispersing energy due to the partial decay of the pigment agglomerates.

Therefore, there is a need in the art for a matting agent for preparing matt coatings that is little dusting, dispersion-stable, and further reproducibly enables surfaces having a homogeneous matt appearance. Additionally, there is a need for a process for preparing matt pigmented coatings in which the matting agent has the similar composition as the pigment, but the matting effect is not affected by the dispersing method.

Problem and brief description of the invention

The technical problem underlying the invention is to provide a pigment composition for preparing pigmented matt coatings, a process for preparing such a composition, and a coating formulation containing such pigment composition, and the use of said composition for matting substrates.

The problem is solved by a pigment composition for preparing matt coatings, characterized in that said pigment composition comprises inorganic pigment particles having a bimodal mass- related particle size distribution, in which the first particle fraction has a pigmentary particle size, and in which the second particle fraction has a mean particle size (d50) within a range of from 2 to 200 pm, preferably from 2 to 100 pm, more preferably from 2 to 50 pm, and most preferably from 2 to 20 pm, and in which the first and second particle fractions have been subjected to a surface treatment.

The pigment composition according to the invention has good matting properties and an excellent opacity. Further, the composition has a high impact and abrasion resistance, and an improved chemical stability. The incorporation of the composition does not significantly change neither the matting effect nor the viscosity of the coating formulation, as the particles do not decay, so that the formulation is readily prepared and easily handled and applied. Further, only a slight adaptation of the formulation from glossy paints is required because of a similar viscosity and matrix behavior, which makes the composition according to the invention practicable.

Therefore, in a first aspect, the invention relates to a pigment composition for preparing matt coatings, characterized in, that said pigment composition comprises inorganic pigment particles having a bimodal mass-related particle size distribution, in which the first particle fraction has a pigmentary particle size, and in which the second particle fraction has a mean particle size (d50) within a range of from 2 to 200 pm, preferably from 2 to 100 pm, more preferably from 2 to 50 pm, and most preferably from 2 to 20 pm, and in which the first and second particle fractions have been subjected to a surface treatment.

In a further aspect, the invention relates to a process for producing a pigment composition for matt coatings, comprising the steps of

(a) providing a first inorganic pigment particle fraction with a pigmentary particle size;

(b) providing a second inorganic pigment particle fraction with a mean particle size (d50) within a range of from 2 to 200 pm, preferably from 2 to 100 pm, more preferably from 2 to 50 pm, and most preferably from 2 to 20 pm; and

(c) subjecting the first and second pigment particle fractions to a surface treatment in aqueous suspension.

In another aspect, the invention relates to a coating formulation comprising the pigment composition according to the invention.

In yet another aspect, the present invention is directed to a pigmented matt surface of a substrate, characterized in that said surface is coated with a coating formulation according to to the invention. In another aspect, the invention refers to pigmented matt coatings, such as paints and printing inks, characterized in that a pigment composition according to the invention is employed.

In a further aspect, the present invention is directed to a plastic comprising a matting agent, characterized in that said plastic comprises a pigment composition according to the invention.

Finally, in another aspect, the invention relates to the use of a pigment composition for matting substrates.

Further advantageous embodiments of the invention are stated in the dependent claims.

Description of the invention

These and further aspects, features, and advantages of the invention become apparent to the skilled person from a study of the following detailed description and claims. Each feature from one aspect of the invention may also be used in any other aspect of the invention. Further, of course, the examples contained herein are intended to merely describe and illustrate the invention, but not to limit it, and in particular, the invention is not limited to such examples. Numerical ranges stated in the form "from x to y" include the values mentioned and those values that lie within the range of the respective measurement accuracy as known to the skilled person. If several preferred numerical ranges are stated in this form, of course, all the ranges formed by a combination of the different end points are also included.

All percentages stated in connection with the compositions herein described relate to percent by weight unless explicitly stated otherwise, respectively based on the mixture or composition in question.

"At least one" as used herein means 1 or more, i.e., 1 , 2, 3, 4, 5, 6, 7, 8, 9, or more. With respect to an ingredient, the value relates to the species of the ingredient rather than the absolute number of molecules. Together with weight statements, the value relates to all compounds of the stated kind that are contained in the composition/formulation, which means that the composition/formulation does not contain any further compounds of this kind beyond the stated amount of the corresponding compounds. Within the scope of the invention, the "mean particle size" means the mass-related median d50, hereinafter d50. The particle size distribution and the mass-related median d50 were determined by sedimentation techniques as described herein.

"Pigment", as used herein, relates to inorganic or organic colorants that are virtually insoluble in the application medium according to DIN 55 943, which are neither chemically nor physically changed in the application medium and retain their particulate structure. They are employed for coloring, which is based on the interaction of the pigment particles with the visible light by absorption and remission. Further, "pigmentary particle size", as used herein, refers to an average particle size (d50) within a range of from 0.01 to 1 μιτπ, preferably from 0.2 to 0.5 pm, and more preferably from 0.2 to 0.4 μηη.

Any inorganic pigment known in the prior art and suitable for the purpose according to the invention can be employed as said inorganic pigment particle. Preferably, said inorganic pigment particle is a metal salt, and more preferably, said metal salt is a metal oxide.

Suitable inorganic pigments include, without limitation, white pigments, such as titanium dioxide (C.I. Pigment White 6), zinc white, leaded zinc oxide; zinc sulfide, lithopone; black pigments, such as iron oxide black (C.I. Pigment Black 1 1 ), iron manganese black, spinel black (C.I. Pigment Black 27); carbon black (C.I. Pigment Black 7); color pigments, such as chromium oxide, chromium oxide hydrate green; chromium green (C.I. Pigment Green 48); cobalt green (C.I. Pigment Green 50); ultramarine green; cobalt blue (C.I. Pigment Blue 28 and 36; C.I. Pigment Blue 72); ultramarine blue; manganese blue; ultramarine violet; cobalt and manganese violet; iron oxide red (C.I. Pigment Red 101 ); cadmium sulfoselenide (C.I. Pigment Red 108); cerium sulfide (C.I. Pigment Red 265); molybdate red (C.I. Pigment Red 104); ultramarine red; iron oxide brown (C.I. Pigment Brown 6 and 7), mixed brown, spinel and corundum phases (C.I. Pigment Brown, 29, 31 , 33, 34, 35, 37, 39 and 40), chromium titanium yellow (C.I. Pigment Brown 24), chromium orange; cerium sulfide (C.I. Pigment Orange 75); iron oxide yellow (C.I. Pigment Yellow 42); nickel titanium yellow (C.I. Pigment Yellow 53 ; C.I. Pigment Yellow 157, 158, 159, 160, 161 , 162, 163, 164 and 189); chromium titanium yellow; spinel phases (C.I. Pigment Yellow 119); cadmium sulfide and cadmium zinc sulfide (C.I. Pigment Yellow 37 and 35); chromium yellow (C.I. Pigment Yellow 34), and bismuth vanadate (C.I. Pigment Yellow 184). Further, inorganic pigment particles that are conventionally used as fillers, such as aluminum oxide, aluminum hydroxide, zinc sulfide, natural and precipitated chalk and barium sulfate, may also be employed.

Preferably, the pigment particle is selected from the group consisting of magnesium carbonate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, huntite, lead white, lithopone, cristobal- ite, china clay, and mixtures thereof. Among all pigment particles disclosed herein, titanium dioxide is most preferred because of its pigment properties and its high Mohs hardness. Titanium dioxide may be present in the crystal structures of rutile, anatase or brookite, usually in the crystal structures of rutile or anatase. Rutile is particularly suitable as compared to anatase because of its lower photolytic catalytic activity.

In the case where titanium dioxide is used, untreated titanium dioxide particles (titanium dioxide base pigment), usually prepared by the sulfate or chloride process, are used as the starting material for the first particle fraction according to the invention. Pigmentary titanium dioxide base pigment usually has a mean particle size d50 of from 0.2 to 0.5 pm, preferably from 0.2 to 0.5 pm, and more preferably from 0.2 to 0.4 pm. A non-pigmentary coarse titanium dioxide base pigment having a mean particle size d50 of from 2 to 200 pm, preferably from 2 to 100 pm, more preferably from 2 to 50 pm, and most preferably from 2 to 20 pm, is employed as said second particle fraction. For example, said coarse titanium dioxide base pigment may be a rutile prepared by the sulfate or chloride process. The particles may have a particle size d50 of up to about 2 mm and are optionally ground to the desired particle size range, optionally followed by classification, for example, by screening. The grinding may be effected, for example, in an agitator bead mill, pendulum mill, or roller mill. In a titanium dioxide production by the sulfate process, the desired particle size is achieved during calcination by the addition of particular additives, by longer calcination times and/or higher calcination temperatures. The particles produced are characterized by stronger sintering, and therefore, they are very stable during the subsequent dispersion within the scope of application in coatings, i.e., they do not decay. In a particular embodiment, titanium dioxide particles from a chloride process subjected to a sintering process may be employed.

Preferably, the pigment particles of the coating substances have been surface-treated with compounds of aluminum, silicon, titanium, zirconium, tin, cerium or phosphorus, and/or with organic compounds selected from the group of silanes, siloxanes, TMPs, TMEs, and HMPs. Further, in a preferred embodiment of the invention, the first and second particle fractions have been subjected to the same surface treatment. In this way, both particle fractions have approximately identical surface properties, such as matrix compatibility, especially towards surface-active additives, so that their manageability is significantly improved.

Preferably, the second particle fraction is present in the pigment composition in an amount of from 1 to 10% by weight, preferably from 1 to 6% by weight, based on the total weight of the pigment composition.

The process according to the invention for producing a pigment composition for matt coatings comprises the steps of:

(b) providing a second inorganic pigment particle fraction with a mean particle size (d50) within a range of from 2 to 200 μηι, preferably from 2 to 100 m, more preferably from 2 to 50 μιτι, and most preferably from 2 to 20 μηι; and

In titanium dioxide production by the sulfate process, the desired particle size is achieved during calcination by the addition of particular additives, by longer calcination times and/or higher calcination temperatures. The particles produced are characterized by stronger sintering, and therefore, they are very stable during the subsequent dispersion within the scope of application in coatings, i.e., they do not decay. In a particular embodiment, titanium dioxide particles from a chloride processsubjected to a sintering process may be employed.

Subsequently, the pigment particles are surface-treated with inorganic and/or organic compounds. The surface treatment corresponds to the surface coating usually applied with pigments. The coating substances include, for example, Si, Al, Ti, Zr, Sn, Ce, or P compounds, or organic compounds, such as silanes, siloxanes, trimethylolpropane (TMP), trimethylolethane (TME), hexametaphosphate (HMP), etc. In this way, the matting agent has similar surface properties as a usually employed pigment, for example, in terms of matrix compatibility, especially towards surface-active additives.

In the surface treatment, one or more layers or mixed layers of the coating substances may be applied. In a particular embodiment of the invention, the outer layer of the surface-treated particle contains Al compounds, especially aluminum oxide or water-containing aluminum oxide. The surface treatment is performed, for example, by precipitating the coating substances onto the particles in aqueous suspension. These methods are known, in particular, from titanium dioxide pigment technology, and can be applied according to the invention. The layer thickness of the surface coating applied to the particles within the scope of the surface treatment is within the nanometer range, preferably smaller than 10 nm, more preferably from 1 nm to 10 nm, so that the particle size of the surface-treated particles does not change significantly as compared to the untreated particles.

The surface treatment of both particle fractions is preferably effected in the same way by either treating both particle fractions together in the same suspension, or by treating each particle fraction separately in a suspension each. In the first case, a suspension of both particle fractions with a proportion of the second particle fraction of from 1 to 10% by weight, preferably from 1 to 6% by weight, based on the total particle weight, is prepared. Subsequently, the particles are surface-treated in the suspension and separated off, washed and dried as usual, and micronized as usual. In the second case, each particle fraction is surface-treated separately in a suspension, then separated off, washed, dried, micronized, and finally mixed in a dry state in the desired quantitative ratio.

Subsequently to the surface treatment, the particles are separated off, filtered, washed and dried, and optionally micronized, for example, in a steam jet mill. The micronization is usually effected through a steam jet mill, in the course of which an organic compound, such as TMP or TME, may be added. Those skilled in the art are aware of such methods.

The present invention further relates to coating formulations for preparing pigmented matt surfaces, containing the pigment composition as described herein. The composition may be contained in the coating formulation in an amount of from 0.1 to 98% by weight, preferably from 1 to 50% by weight, more preferably from 2 to 25% by weight, most preferably from 3 to 23% by weight, based on the total weight of the coating formulation. In addition to the pigment composition according to the invention, the formulation may have a usual pigment composition, and pigments. Preferably, the formulation does not contain any further pigment compositions.

Further, the formulation comprises usual components. Any components known in the prior art that are suitable for the purpose according to the invention may be employed as components. Preferably, the formulation comprises at least one component selected from the group consisting of a binder, defoamer, dispersant, filler, solvent, preservative, auxiliary film forming agent, and rheology additive. The preservatives also include usual fungicides. The coating formulations include lacquers, paints, and printing inks.

The present invention further relates to pigmented matt surfaces of a substrate, wherein said surface is characterized in that said surface is coated with a coating formulation as disclosed herein. The formulations may be in the form of the established one-part, two-part, and multicomponent paints in the usual compositions. The paints are applied to the substrate by the usual techniques, and methods, and cured as a function of the paint composition, especially the binder, for example, by means of UV irradiation or drying. The substrates include without limitation wood, plastics, metals, paper, glass fabric, and mixtures thereof.

In the finished coating, the first, pigmentary pigment particle fraction (first particle fraction) provides for pigmentation, and the second, coarser pigment particle fraction (d50 within a range of from 2 to 200 pm) provides for the sought surface roughness.

The invention still further relates to a plastic characterized in that said plastic comprises a pigment composition according to the invention. Any plastic known in the prior art and suitable for the purpose according to the invention can be employed as the plastic. "Plastic", as used herein, relates to a material containing at least 50% by weight of a polymer, based on the total weight of the plastic. Said polymer may be a homopolymer, a copolymer, or a grafted polymer. Further, the polymer may be an atactic, isotactic, or syndiotactic polymer. Further, the plastic is a thermoplast, elastomer, duroplast or thermoplastic elastomer, preferably a thermoplast. Without limitation, the polymer is selected from the group consisting of polyolefins, polystyrene, polyamide, polyketone, polyester, polyurethane, poly(meth)acrylate, and mixtures thereof. Without limitation, the polyolefin is selected from the group consisting of polymethylene, polyethylene, polypropylene, polybutylene, and mixtures thereof. The composition according to the invention can be incorporated in the plastic by known techniques and methods, for example, by extruding. The composition described herein is advantageous in the extruding process, in particular, because it does not decay therein, and the extruding has no influence on the matting effect. The matting agent is processed into the plastic in the usual amounts. Thus, the plastic obtained contains from 0.1 to 30% by weight, preferably from 1 to 25% by weight, of the agent according to the invention, based on the total weight of the plastic.

Finally, the invention further relates to the use of a pigment composition for matting substrates. As described above, the substrates include without limitation wood, plastics, metals, paper, glass fabric, and mixtures thereof. Test methods

Particle size distribution and mass-related median d50

This method uses the concentration shift of a suspension of particles in water, which sediments by effecting of gravity, for the calculation of its particle size distribution. The change of concentration was detected by means of x-ray. The loss of intensity by absorption at the particles is a degree for the solid concentration in the beam path. The calculation of the particle size is based on the laws of Stokes out of the fixed sedimentation rates of the particles.

Flow viscosity

The flow viscosity was determined by using the method DIN 5321 1. The finished paint is poured into a flow cup of defined geometry with 4 mm diameter outlet capillary. When the outlet is opened, the fluid flows through the central outlet opening in the bottom of the cup under its own weight. The flow time is measured by optical scanning of the emerging fluid stream using Cuptimer 243 T automatic flow time measuring station, the measured time being immediately displayed on the unit.

Contrast ratio

The contrast ratio was measured by standard technique using apparatus Color guide sphere from Byk gardner and foil Hostaphan RN 23 commercially available from Jakob Benn & Sonne.

Example 1a

A coarse grain, non-pigmentary titanium dioxide was sintered in a kiln. The sintered material (220 g) was grinded and the particle size was classified by sedimentation technique Atterberg sedimentation. The obtained aggregates had a particle size d50m of 17 (+/-2) μιη. This fraction was post-treated with an alumina layer. The amount of alumina was calculated to a similar layer thickness like the used white pigment. Example 1b

Example 1b includes the preparation of Example 1a, except that no post treatment was conducted.

Example 2

A standard formulation is based on nitro cellulose, which is supplied in the form of chips, that are dissolved in ethanol, and ethyl acetate. Other components are plasticizers, and additives for improving the surface and gloss. After preparing the vehicle and weighting in the pigment composition the formulation is dispersed in a Skandex disperser using milling beads.

Comparative Example 1

Comparative Example 1 includes the preparation of the standard formulation as described in Example 2, wherein the pigment composition is titanium dioxide pigment in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina. The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1.

Comparative Example 2

Comparative Example 2 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (97 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and commercially available matting agent Acematt TS100 (3 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1.

Comparative Example 3

Comparative Example 5 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (94 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and commercially available matting agent Acematt TS100 (6 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1. Example 3

Example 3 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (97 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and the material of Example 1 b (3 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1.

Example 4

Example 4 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (94 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and the material of Example 1 b (6 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1.

Example 5

Example 5 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (97 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and the material of Example 1a (3 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1.

Example 6

Example 6 includes the preparation of the standard formulation as described in Example 2, the pigment composition is titanium dioxide pigment (94 wt.% based on the total amount of said composition) in the rutile crystal modification, commercially available under the product name Kronos 2066 from Kronos International Inc., which is post-treated with alumina, and the material of Example 1a (6 wt.% based on the total amount of said composition). The flow viscosity and the gloss (20°, 60°, 85°) were determined as described above. The data can be seen from Table 1. Table 1

As compared to the comparative paints prepared with commercially available titanium dioxide pigment, and additionally with commercially available matting agent (Comparative Examples 2, 3), the paints prepared according to the invention (Examples 3, 4, 5, 6) have a lower viscosity As compared to the glossy paint prepared with commercially available titanium dioxide that does not contain any matting agent (Comparative Example 1 ), the mat paints prepared according to the invention (Examples 3, 4, 5, 6) do not show any significant increase in viscosity, but a good matting effect. Further, the paints according to the invention comprising particles, which were subjected to similar post treatment (Examples 5, 6), exhibit improved viscosity properties compared to those paints according to the invention comprising particles, which were not subjected to similar post treatment (Examples 3, 4).

Claims

C L A I M S :

1. A pigment composition for preparing matt coatings, characterized in that

said pigment composition comprises inorganic pigment particles having a bimodal mass-related particle size distribution,

in which the first particle fraction has a pigmentary particle size, and

in which the second particle fraction has a mean particle size (d50) within a range of from 2 to 200 μητι, preferably from 2 to 100 pm, more preferably from 2 to 50 pm, and most preferably from 2 to 20 pm, and

in which the first and second particle fractions have been subjected to a surface treatment.

2. The pigment composition according to claim 1 , characterized in that

said inorganic pigment particles are a metal salt.

3. The pigment composition according to claim 2, characterized in that said

metal salt is a metal oxide.

4. The pigment composition according to claim 3, characterized in that

said metal oxide is titanium dioxide.

5. The pigment composition according to any of claims 1 to 4, characterized in that

said pigment particles have been surface-treated with compounds of aluminum, silicon, titanium, zirconium, tin, cerium or phosphorus, and/or

with organic compounds selected from the group of silanes, siloxanes, TMPs, TMEs and HMPs.

6. The pigment composition according to any of claims 1 to 5, characterized in that

the first and second particle fractions have been subjected to the same surface treatment; and/or

the pigment composition contains from 1 to 8% by weight, preferably from 3 to 6% by weight, particles of the second particle fraction.

7. A process for producing a pigment composition for matt coatings, comprising the steps of:

(a) providing a first inorganic pigment particle fraction with a pigmentary particle size; (b) providing a second inorganic pigment particle fraction with a mean particle size (d50) within a range of from 2 to 200 pm, preferably from 2 to 100 pm, more preferably from 2 to 50 m, and most preferably from 2 to 20 pm; and

8. The process according to claim 7, characterized in that

said particles of the first and second particle fractions are metal oxides; and/or said particles of the first and second particle fractions are metal salts; and/or said particles of the first and second particle fractions are titanium dioxide.

9. The process according to claim 7 or 8, characterized in that

said surface treatment is an inorganic and/or organic surface treatment; and/or the particles of the first and second particle fractions have been surface-treated with compounds of aluminum, silicon, titanium, zirconium, tin, cerium or phosphorus, and/or with organic compounds selected from the group of silanes, siloxanes, TMPs, TMEs, and HMPs.

10. The process according to any of claims 7 to 9, characterized in that

either the first and second particle fractions are surface-treated together; or

the first and second particle fractions have been surface-treated separately, but in the same way.

11. A coating formulation for preparing pigmented matt surfaces, characterized in that

said formulation comprises a pigment composition according to any of claims 1 to 6.

12. A pigmented matt surface of a substrate, characterized in that said surface is coated with a coating formulation according to claim 11.

13. Pigmented matt coatings, such as paints and printing inks, characterized in that

a pigment composition according to any of claims 1 to 6 is employed.

14. A plastic comprising a matting agent, characterized in that said plastic comprises a pigment composition according to any of claims 1 to 6.