WO2017129135A1

WO2017129135A1 - Luminescent tetradentate gold (iii) compounds for organic light-emitting devices and their preparation

Info

Publication number: WO2017129135A1
Application number: PCT/CN2017/072639
Authority: WO
Inventors: Wing-Wah Vivian YAM; Hok Lai Wong; Yiu Wing Wong; Mei Yee CHAN
Original assignee: University of Hong Kong HKU
Current assignee: University of Hong Kong HKU
Priority date: 2016-01-29
Filing date: 2017-01-25
Publication date: 2017-08-03
Anticipated expiration: 2018-07-29
Also published as: US20170222164A1; KR102773350B1; US20210249612A1; US11765971B2; CN109153913B; US11018310B2; KR20180109950A; CN109153913A

Abstract

A highly rigid tetradentate ligand is combined with a gold (III) ion as a thermally stable tetradentate gold (III) complex. The tetradentate gold (III) complex is a tetradentate gold (III) compound that can be used as a light-emitting material which can be used for fabricated of light-emitting devices such as an organic light-emitting diode (OLED). The tetradentate gold (III) compound can be deposited as a layer or a component of a layer using a solution-process or a vacuum deposition process. The luminescent tetradentate gold (III) compounds are robust and can provide electroluminescence (EL) with a high efficiency and brightness.

Description

LUMINESCENT TETRADENTATE GOLD (III) COMPOUNDS FOR ORGANIC LIGHT-EMITTING DEVICES AND THEIR PREPARATION

CROSS-REFERENCE TO A RELATED APPLICATION

This application claims the benefit of U.S. Provisional Application Serial No. 62/288,514, filed January 29, 2016, the disclosure of which is hereby incorporated by reference in its entirety, including all figures, tables and drawings.

TECHNICAL FIELD

Cyclometalated tetradentate gold (III) compounds, their synthesis, and their use as light-emitting material in phosphorescence-based organic light-emitting devices (OLEDs) are described.

BACKGROUND OF INVENTION

In recent years, extensive attention has been drawn towards the research and development of OLEDs. The enormous size and scope of research is related to potential applications of OLEDs in commercial flat panel displays and solid-state lighting systems. Because of their low cost, light weight, low operating voltage, high brightness, robustness, wide color tunability, wide viewing angle, ease of fabrication onto flexible substrates and low energy consumption, OLEDs are remarkably attractive candidates for flat panel display technologies.

Typically, an OLED contains several layers of semiconductor materials sandwiched between two conducting electrodes. The cathode is composed of a low work function metal alloy deposited by vacuum evaporation, whereas the anode is a transparent conductor such as indium tin oxide (ITO) . Upon application of a DC voltage, holes injected by the ITO electrode and electrons injected by the metal electrode recombine to form excitons. Subsequent relaxation of excitons results in the generation of electroluminescence (EL) .

To achieve higher OLED performance, multiple layers of functional materials can be incorporated that further separate the two electrodes. There are two main categories of materials that are used as these functional layers, namely vacuum-deposited small molecules and spin-coated polymeric materials. Both fabrication methods have their respective advantages. Vacuum deposition generally allows better control over layer thickness and uniformity while spin coating generally offers a less complex fabrication process having lower production cost [Burrows, P.E.； Forrest, S.R.； Thompson, M.E. Curr. Opin. Solid State Mater. Sci. 2, 236 (1997) ] .

In spite of the fact that EL from organic polymers was initially reported in the 1970s [Kaneto, K.； Yoshino, K.； Koa, K.； Inuishi, Y. Jpn. J. Appl. Phys. 18, 1023 (1974) ] , it was only after a report on yellow-green EL from poly (p-phenylenenvinylene) (PPV) that light-emitting polymers and OLEDs received much attention [Burroughs, J.H.； Bradley, D.D.C.； Brown, A.R.； Marks, N； Friend, R.H.； Burn, P.L.； Holmes, A.B. Nature 347, 539 (1990) ] . Subsequently, similar studies reported PPV derivatives as light-emitting polymers [Braun, D.； Heeger, A.J. Appl. Phys. Lett. 58, 1982 (1991) ] . Since then, many new electroluminescent polymers have been investigated with improved photophysical properties.

EL from organic materials was first discovered in anthracene crystals immersed in liquid electrolyte in 1965 [Helfruch, W.； Schneider, W.G. Phys. Rev. Lett. 14, 229 (1965) ] . Although lower operating voltages were achieved by using a thin film of anthracene with solid electrodes, very low efficiencies were encountered with these single-layer devices. High-performance green EL from an organic small molecule, tris- (8-hydroxyquinoline) aluminum (Alq₃) , was first reported in 1987 [Tang, C.W.； Van Slyke, S.A. Appl. Phys. Lett. 51, 913 (1987) ] . A double-layer OLED with high efficiency and low operating voltage was described where Alq₃ was utilized as an emitting layer and as an electron transporting layer with diamine as hole transporting layer. Subsequent modification of the device architecture to produce a triple-layer structure gave better performance with higher efficiency.

Superior performance of phosphorescence-based OLEDs can be realized when the emissive materials have short radiative lifetimes. Short radiative lifetimes can be achieved by mixing singlet and triplet excited states and exploiting spin-orbit (L-S) coupling. In the presence of a heavy metal center, the propensity of spin-orbit coupling can be greatly enhanced. Hence, the use of heavy metal complexes in OLEDs is generally advantageous relative to the use of pure organic materials. The lowest energy excited state of an organometallic compound with π-acceptor ligand is commonly a metal-to-ligand charge transfer (MLCT) triplet state, which can mix with the excited singlet state through L-S coupling, resulting in higher photoluminescence efficiencies [Baldo, M.A.； Thompson, M.E.； Forrest, S.R. Pure Appl. Chem. 71, 2095 (1999) ] . In 1998, Baldo et al. demonstrated a phosphorescent EL device with high internal quantum efficiency by using platinum (II) 2, 3, 7, 8, 12, 13, 17, 18-octaethyl-21H, 23H-porphyrin (PtOEP) as a dopant [Baldo, M.A.； O'Brien, D.F.； You, Y； Shoustikow, A.； Sibley, S.； Thompson, M.E.； Forrest, S.R. Nature 395, 151 (1998) ； O'Brien, D.F.； Baldo, M.A.； Thompson, M.E.； Forrest, S.R. Appl. Phys. Lett. 74, 442 (1999) ] . A multilayer device consisting of an emitting layer of Alq₃ doped with PtOEP showed a strong emission at 650 nm attributed to the triplet excitons of PtOEP.

Cyclometalated iridium (III) compounds show intense phosphorescence and are another class of materials widely used in the fabrication of high efficiency OLEDs. The use of fac-tri (2-phenylpyridine) iridium (III) [Ir (ppy) ₃] as phosphorescent emitting dopant in a 4, 4’-N, N’-diarbazole-biphenyl (CBP) host yields high efficiency OLEDs [Baldo, M.A.； Lamansky, S.； Burrows, P.E.； Thompson. M.E.； Forrest, S.R. Appl. Phys. Lett. 75, 4 (1999) ] . In light of the rich photoluminescence properties of [Ir (ppy) ₃] , there has been a growing interest in the incorporation of 2-phenylpyridine derivatives into iridium (III) center to prepare triplet emitters for OLED applications. Another triplet emitter is the sky-blue light-emitting complex, iridium (III) bis [2- (4’, 6’-difluorophenyl) pyridinato-N, C²] -picolinate [Ir (4, 6-dFppy) ₂ (pic) ] , which exhibits a very high photoluminescence quantum yield of about 60％in solution and nearly 100％in a solid film when doped into high triplet energy host [Rausch, A.F.； Thompson, M.E.； Yersin, H. Inorg. Chem. 48, 1928 (2009) ； Adachi, C； Kwong, R.C.； Djurovich, P.I.； Adamovich, V.； Baldo, M.A.； Thompson, M.E.； Forrest, S.R. Appl. Phys. Lett. 79, 2082 (2001) ； Kawamura, Y.； Goushi K.； Brooks, J.； Brown, J.J.； Sasabe, H.； Adachi, C. Appl. Phys. Lett. 86, 071104 (2005) ] . In spite of the extensive use of 2-phenylpyridine and its derivatives in iridium (III) systems for the fabrication of OLEDs, the use of phosphors containing alternative metal centers with these ligands remains under-explored and under-developed.

In addition to enhancing the external quantum efficiencies (EQE) , the ability to vary the emission color is desirable. Most approaches to color variance involve use of multi-component blended mixtures of light-emitting materials with different emission characteristics or different light-emitting materials for color tuning. Examples of a single light-emitting material as dopant to generate more than one emission color are rare. Recent studies have shown that different emission colors from a single emissive dopant can be generated by using a phosphorescent material, by changing the bias direction or by changing the dopant concentration. An OLED can be fabricated from a semiconducting polymer PPV and phosphorescent ruthenium polypyridine dopant [Welter, S.: Krunner, K.； Hofstraat, J.W.； De Cola, L. Nature 421, 54 (2003) ] . Under a forward bias, red emission from the excited state of the phosphorescent ruthenium polypyridine dopant was observed while the OLED emitted a green emission under reverse bias where the lowest excited singlet state of PPV was populated. A series of phosphorescent platinum (II) [2- (4, 6-difluorophenyl) pyridinato-N, C] -β-diketones as single emissive dopants has been demonstrated in OLEDs [Adamovieh, V.； Brooks, J.； Tamayo, A.； Alexander, A.M.: Djurovich. P.R.； D’Andrade, B.W.； Adachi, C.； Forrest, S.R.； Thompson, M.E. New J. Chem. 26, 1171 (2002) ] . Both blue emission from monomeric species and orange emission from the aggregates were observed in such OLED where the relative intensity of the orange emission increased as the doping level increased. As a result, the EL color can be tuned by changing the dopant concentration with equal intensities of the monomeric and aggregate bands. In both cases, the change of EL color in an OLED can be accomplished by varying the external stimulus or fabrication conditions while employing the same light-emittingmaterial.

Emitting materials that have long EL device operational lifetimes as well as high EL performances are crucial. These properties are closely related to the structure of the metal complexes. It appears that for square-planar metal complexes, their thermal stability and rigidity are of great importance in the device performance as well as the operational lifetime. Greater stability as well as a lowering of non-radiative decay rate can be achieved by employing rigid tetradentate ligands to confine the metal center. The first tetradentate metal complex used as emitting material was a zinc (II) Schiff base complex, in which a blue-emitting OLED was fabricated by vacuum vapor deposition [Hamada, Y.； Takeshi, S.； Fujita, M.； Fujii, T.； Nishio, Y.； Shibata, K. Jpn. J. Appl. Phys. 32, L511 (1993) ] . However, device performance based on this emitter was found to be poor due to the lack of triplet exciton harvesting. Later, a porphyrin-based platinum (II) triplet emitter, PtOEP, was employed [Baldo, M.A.； O'Brien, D.F.； You, Y； Shoustikow, A.； Sibley, S.； Thompson, M.E.； Forrest, S.R. Nature 395, 151 (1998) ] . This device showed peak external and internal quantum efficiencies of 4％and 23％, respectively. The low device performance is believed to be limited by low photoluminescence quantum yields of the emitter. Recently, rigid tetradentate O^N^C^N platinum (II) complexes were reported to have a photoluminescence quantum yields of 90％and display good thermal stability. Because if these advantages, phosphorescent OLEDs (PHOLEDs) with high device efficiency and stability have been achievedwith EQE of 18.2％and current efficiency of 66.7 cd A^–1 [Kui, S.C.F.； Chow, P.K.； Cheng, G.C.； Kwok, C. -C.； Kwong, C.L.； Low, K. -H.； Che, C. -M. Chem. Comm. 49, 1497 (2013) ] .

Even with an increased interest in electrophosphorescent materials, particularly metal complexes with heavy metal centers, most developments have focused on the use of iridium (III) , platinum (II) and ruthenium (II) centers, while the use of other metal centers has been much less explored. In contrast to isoelectronic platinum (II) compounds, which are known to exhibit rich luminescence properties, very few examples of luminescent gold (III) complexes have been reported, probably due to the presence of low-energy d-d ligand field (LF) states and the electrophilicity of the gold (III) metal center. One way to enhance the luminescence of gold (III) complexes is through the introduction of strongσ-donating ligands, as was first demonstrated for stable gold (III) aryl and alkyl compounds found to display interesting photoluminescence properties at room temperature [Yam, V.W. -W.； Choi, S.W. -K.； Lai, T. -F.； Lee, W. -K.J. Chem. Soc., Dalton Trans. 1001 (1993) ] . Subsequently, a series of bis-cyclometalated alkynylgold (III) compounds with various strongσ-donating alkynyl ligands were found to exhibit rich luminescence behaviors at room temperature and below in various media [Yam, V.W. -W.； Wong, K.M. -C.； Hung, L. -L, .； Zhu, N. Angew. Chem. Int. Ed. 44, 3107 (2005) ； Wong, K, M. -C.； Hung, L, -L.； Lam, W.H.； Zhu, N.； Yam, V.W. -W.J. Am. Chem. Soc. 129, 4350 (2007) ] . This class of highly luminescent gold (III) compounds were first employed as dopants for emissive layers of OLEDs, displaying a high brightness and EQE of 10,000 cd m^–2 and 5.5％, respectively [Wong, K.M. -C.； Zhu, X.； Hung, L. -L.； Zhu, N.； Yam, V.W. -W.； Kwok, H. -S. Chem. Comm. 2906 (2005) ] . A class of phosphorescent material of cyclometalated alkynylgold (III) compounds has been fabricated as emissive dopants of OLEDs by vapor deposition where the optimized OLED reached an EQE of 11.5％and a current efficiency of 37.4 cd A^–1 [Au, K. -M.； Wong, K.M. -C.； Tsang, D.P. -K.； Chan, M.Y.； Yam, V.W. -W.J. Am. Chem. Soc. 132, 14273 (2010) ] . Hence, alkynylgold (III) complexes are promising phosphorescent materials in terms of efficiency and thermal stability. A series of dendritic luminescent gold (III) complexes with very good solubilities as well as very high luminescence quantum yields have been prepared and employed in the fabrication of high-performance solution-processed devices that display a high EQE of 7.8％and a current efficiency of 24.0 cd A^–1 [Tang, M. -C.； Tsang, D.P. -K.； Chan, M.M. -Y., Wong, K.M. -C.； Yam, V.W. -W. Angew. Chem. Int. Ed. 52, 446 (2013) ] . By changing the dendritic alkynyl ligand to a bipolar ligand containing triphenylamine and benzimidazole, gold (III) complexes demonstrate higher photoluminescence quantum yields, of up to 75％, in spin-coated thin films. OLEDs based on these complexes exhibited an EQE of 10.0％and a current efficiency of 33.6 cd A^–1. More importantly, such OLEDs exhibit an extremely small efficiency roll-off, of less than 1％at brightness of 1,000 cd m^–2. [Tang, M. -C.； Tsang, D.P. -K.； Chan, M.M. -Y., Wong, K.M. -C.； Yam, V.W. -W J. Am. Chem. Soc. 136, 17861 (2014) ] . Apart from bidentate and tridentate ligands, gold (III) compounds with tetradentate ligands have not been reported.

BRIEF SUMMARY

Embodiments of the invention are directed to highly rigid tetradentate ligands and their use in the synthesis of thermally stable tetradentate gold (III) complexes and their applications in the fabrication of OLEDs using solution-processing or vacuum deposition techniques. These robust luminescent gold (III) compounds with tetradentate ligands provide EL with high efficiency and brightness when used as light-emitting materials in OLEDs.

The novel class of luminescent tetradentate gold (III) compounds comprise a tetradentate ligand containing four ligating sites coordinated to a gold (III) metal center. The ligation site consists of coordinating atoms that can be, for example, nitrogen, carbon, orσ-donating groups, for example, alkynyl and aryl groups.

The compounds according to an embodiment of the invention, have the chemical structure shown in Formula I:

wherein:

(a) W, X, Y and Z are independently selected from C, O, N, P, C–C≡C (alkynyl) , C–N≡C (isocyanide) or C–C≡N (cyanide) , where the atom that is in bold-faced represents the coordinating site；

(b) A, B, C and D are independently a cyclic derivatives selected from substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, or substituted or unsubstituted polycyclic group, or any combinations thereof；

(c) αandβare each independently a cyclic structure, an acyclic structure, or mixtures of thereof, wherein the cyclic structure can be a substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, substituted or unsubstituted cycloalkyl group, or substituted or unsubstituted polycyclic group, and the acyclic structure can be a substituted or unsubstituted alkynyl, substituted or unsubstituted arylalkynyl, substituted or unsubstituted alkyl, substituted or unsubstituted alkylaryl, substituted or unsubstituted alkoxy, substituted or unsubstituted arylalkoxy, and substituted or unsubstituted derivatives thereof；

(d) each G is independently a non-coordination site, and can be CRR’, C＝O, NR, O, PR, P (＝O) R, BR, S, SO, SO₂, SiRR′, Se, AsR,

where R and R'are independent selected from hydrogen, halogen, aryl, alkyl, heteroaryl, nitro, trifluoromethyl, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, a heterocyclic group and derivatives thereof； and

(e) p, q, r and s are each independently 0–3.

The luminescent tetradentate gold (III) compounds, according to embodiments of the invention, show strong photoluminescence upon photo-excitation, or EL upon applying a direct current voltage. The tetradentate gold (III) compounds, according to embodiments of the invention, are thermally stable and sufficiently volatile to form a thin layer by sublimation or vacuum deposition. Alternatively, the tetradentate gold (III) compounds can be doped into a host matrix for thin film deposition by spin-coating, inkjet printing, or any other known fabrication method. The tetradentate gold (III) compounds can be used for the fabrication of OLEDs as phosphorescent emitters or dopants to generate EL.

An OLED, according to an embodiment of the invention, employs the luminescent tetradentate gold (III) compound as a light-emitting layer. The OLED comprises the luminescent tetradentate gold (III) compounds and can comprise a layer structure having a cathode layer, an electron transporting layer, the luminescent tetradentate gold (III) compound as the light-emitting layer, a carrier confinement layer, a hole transporting layer, and an anode.

The present invention comprises the following embodiments:

1. A luminescent tetradentate gold (III) compound comprising the chemical structure represented by the following general Formula I,

wherein:

(a) W, X, Y and Z are independently selected from C, O, N, P, C-C≡C (alkynyl) , C-N≡C (isocyanide) or C-C≡N (cyanide) , and the atom that is in bold-faced represents a coordinating site；

(b) A, B, C and D are each independently cyclic structure derivatives of substituted or unsubstituted pyridine groups, substituted or unsubstituted phenyl groups, substituted or unsubstituted heteroaryl groups, or substituted or unsubstituted polycyclic groups；

(c) αandβare each independently cyclic structure, acyclic structure derivatives or mixtures thereof, wherein the cyclic structure includes substituted or unsubstituted pyridine groups, substituted or unsubstituted phenyl groups, substituted or unsubstituted heteroaryl groups, substituted or unsubstituted cycloalkyl or substituted or unsubstituted polycyclic groups, and the acyclic structure includes substituted or unsubstituted alkynyl, substituted or unsubstituted arylalkynyl, substituted or unsubstituted alkyl, substituted or unsubstituted alkylaryl, substituted or unsubstituted alkoxy, substituted or unsubstituted arylalkoxy, and substituted or unsubstituted derivatives thereof；

where R and R'are independent selected from hydrogen, halogen, aryl, alkyl, heteroaryl, nitro group, trifluoromethane group, cyano group, aryl or alkyl or heteroaryl ether group, diarylamine group, dialkylamine group, diheteroarylamine group, diarylborane group, triaryl or trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, a heterocyclic group and derivatives thereof；

(e) p, q, r and s are each independently 0-3.

2. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein in the case ofαandβbeing cyclic structures, rings A, B, C, D, αandβ， or in the case ofαandβbeing acyclic structures, rings A, B, C and D are cyclic structure derivatives where the cyclic structures are independently selected from arene, heteroarene, heterocycle or polycyclic unit as known skilled in the art, where, in the case ofαandβbeing cyclic structures, rings A, B, C, D, αandβ， or in the case ofαandβbeing acyclic structures, rings A, B, C and D can be each independently selected from heteroatom containing heteroarenes or heterocycles； the arene or heteroarene can be benzene, pyridine, thiophene, furan, pyrazole, oxadiazole, thiadiazole, imidazole, oxazole, isoxazole, thiazole, isothiazole, isoquinoline, pyrrole, pyrazine, pyridazine, pyrimidine, benzimidazole, benzofuran, benzothiazole, indole, indolocarbazole, benzopyrrolizinophenoxazine, naphthalene, anthracene, pyrene, triazole, tetrazole, pyran, thiapyran, oxadiazole, triazine, tetrazine, carbazole, dibenzothiophene, dibenzofuran, fluorene and derivatives thereof.

3. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein in the case ofαandβbeing cyclic structures, rings A, B, C, D, αandβ， or in the case ofαandβbeing acyclic structures, rings A, B, C and D can be unsubstituted or be substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

4. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein any two adjacent substituted positions of rings A, B, C, D, αandβ， in the case ofαandβbeing cyclic structures, or rings A, B, C, D， in the case ofαandβbeing acyclic structures, together form, independently, fused 5-to 6-membered cyclic groups, wherein the said cyclic group is cycloalkyl, cycloheteroalkyl, aryl, or heteroaryl, and wherein the fused 5-to 6-membered cyclic group can be unsubstituted or be substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

5. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the gold (III) compounds can be one of

wherein, G, G′, G″and G″′are independently selected from CRR’, C＝O, NR, O, BR, S, SO, SO₂, SiRR′, Se and AsR, where R and R′are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof； and, R¹ to R²³ are each independently selected from alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

6. The tetradentate gold (III) compound of any one of the above embodiment (s) , wherein two, three or more of the compounds are connected through a bridging substituent as a dimer, trimer, oligomer or polymer.

7. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the compound is deposited as a thin layer on a substrate layer.

8. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the layer is deposited by spin-coating, inkjet printing, or vacuum deposition.

9. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound has photoluminescence properties within a range from about 380 to about 1050 nm.

10. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound emits lights in response to the passage of an electric current or to a strong electric field.

11. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound is used to fabricate an OLED.

12. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound serves as the light-emitting layer of the OLED.

13. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound serves as a dopant in the light-emitting layer of the OLED.

14. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the emission energy of the compound varies with the concentration of tetradentate gold (III) compound dopant.

15. A method for the preparation of luminescent tetradentate gold (III) compound according to any one of the above embodiment (s) , comprising the preparation of tetradentate gold (III) compound by intramolecular cyclization reaction of a gold (III) precursor compound bearing a combination of monodentate, bidentate or tridentate ligands, wherein the luminescence tetradentate gold (III) compound according to any one of the above embodiment (s) is formed.

16. The method of any one of the above embodiment (s) , wherein the reaction occurs in the presence of base (s) , catalyst (s) or both of them.

17. The method of any one of the above embodiment (s) , wherein the base (s) can be organic base (s) , inorganic base (s) or both of them； and wherein catalyst can be metal based catalyst (s) , organic based catalyst (s) , organometallic based catalyst (s) or mixtures of them.

18. The method according to any one of the above embodiment (s) , wherein reaction occurs in solution.

19. The method according to any one of the above embodiment (s) , comprising purifying the tetradentate gold (III) compound by chromatography, extraction, crystallization, sublimation or any combination.

20. The method of modification of the tetradentate gold (III) compound, wherein substituents can be introduced to the tetradentate gold (III) compound according to any one of the above embodiment (s) is formed.

21. The method according to any one of the above embodiment (s) , comprising purifying the substituted tetradentate gold (III) compound by chromatography, extraction, crystallization, sublimation or any combination thereof.

22. The method according to any one of the above embodiment (s) , wherein luminescent compound is prepared.

23. The method according to any one of the above embodiment (s) , wherein the gold (III) compound comprises a light-emitting layer of a light-emitting device.

24. The methods according to any one of the above embodiment (s) , wherein the gold (III) compound comprises a layer of a light emitting device.

25. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the tetradentate gold (III) compound is a dopant included in the light-emitting layer of the light-emitting device.

26. The methods according to any one of the above embodiment (s) , wherein the gold (III) compound is a dopant included in the light-emitting device.

27. A light-emitting device with an ordered structure comprising an anode, hole-transporting layer, a light-emitting layer and a cathode wherein, the light-emitting layer comprises a tetradentate gold (III) compound having a chemical structure according to any one of the above embodiment (s) .

In addition, the present invention further comprises the following embodiments:

wherein:

(a) W, X, Y and Z are independently selected from C, O, N, P, C–C≡C (alkynyl) , C–N≡C (isocyanide) or C–C≡N (cyanide) ；

(b) A, B, C and D are independently a cyclic structure selected from substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, or substituted or unsubstituted polycyclic group；

(c) αandβare independently a cyclic structure, acyclic structure, or any derivative thereof, wherein the cyclic structure is selected from a substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, substituted or unsubstituted cycloalkyl group, and substituted or unsubstituted polycyclic group, and wherein the acyclic structure is selected from substituted or unsubstituted alkynyl, substituted or unsubstituted arylalkynyl, substituted or unsubstituted alkyl, substituted or unsubstituted alkylaryl, substituted or unsubstituted alkoxy, and substituted or unsubstituted arylalkoxy；

wherein R and R'are independent selected from hydrogen, halogen, aryl, alkyl, heteroaryl, nitro, trifluoromethyl, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclyl, and derivatives thereof；

(e) p, q, r and s are each independently 0–3.

2. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein A, B, C, D, optionallyαand optionallyβ, are independently selected benzene, pyridine, thiophene, furan, pyrazole, oxadiazole, thiadiazole, imidazole, oxazole, isoxazole, thiazole, isothiazole, isoquinoline, pyrrole, pyrazine, pyridazine, pyrimidine, benzimidazole, benzofuran, benzothiazole, indole, indolocarbazole, benzopyrrolizinophenoxazine, naphthalene, anthracene, pyrene, triazole, tetrazole, pyran, thiapyran, oxadiazole, triazine, tetrazine, carbazole, dibenzothiophene, dibenzofuran, fluorene and derivatives thereof.

3. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein one or more of A, B, C, D, optionallyαand optionallyβ, are substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’or derivatives thereof； and R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane. Trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

4. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein independently any two adjacent substituted positions of at least two of A, B, C, D, optionallyαand optionallyβ, form a fused 5-to 6-membered cyclic group selected from cycloalkyl, cycloheteroalkyl, aryl, and heteroaryl, wherein the fused 5-to 6-membered cyclic group is unsubstituted or substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’or derivatives thereof； wherein R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

5. The tetradentate gold (III) compound according to any one of the above embodiment (s) , wherein the gold (III) compounds is selected from:

wherein, G, G′, G″and G″′are independently selected from CRR’, C＝O, NR, O, BR, S, SO, SO₂, SiRR′, Se and AsR, wherein R and R′are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, and derivatives thereof； and, R¹ to R²³ are each independently selected from hydrogen, deuterium, alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof, wherein R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

6. The tetradentate gold (III) compound of any one of the above embodiment (s) , wherein at least one substituent of A, B, C, D, optionallyαand optionallyβ, is further derived to form a bridging substituent wherein two or more of the tetradentate gold (III) are combined as a dimer, trimer, oligomer, or polymer.

7. A method for the preparation of luminescent tetradentate gold (III) compound according to any one of the above embodiment (s) , comprising:

Providing a gold (III) precursor compound comprising a combination of monodentate, bidentate or tridentate ligands； and

intramolecularly cyclizating the gold (III) precursor compound to form a tetradentate gold (III) compound.

8. The method of any one of the above embodiment (s) , further comprising adding at least one base, catalyst or combination thereof to the gold (III) precursor compound.

9. The method of any one of the above embodiment (s) , wherein the base is selected from an organic base, an inorganic base, or a combination thereof.

10. The method of any one of the above embodiment (s) , wherein the catalyst is selected from a metal based catalyst, organic based catalyst, organometallic based catalyst, or any combination thereof.

11. The method according to any one of the above embodiment (s) , further comprising adding a solvent to the gold (III) precursor compound to form a solution.

12. The method according to any one of the above embodiment (s) , further comprising isolating the tetradentate gold (III) compound according to any one of the above embodiment (s) by chromatography, extraction, crystallization, sublimation or any combination thereof.

13. The method according to any one of the above embodiment (s) , further comprising adding or substituting a substituent to the gold (III) precursor, the gold (III) precursor comprising a different tetradentate gold (III) compound according to any one of the above embodiment (s) .

14. A luminescent material, comprising a tetradentate gold (III) compound according to any one of the above embodiment (s) .

15. A light-emitting device, comprising at least one tetradentate gold (III) compound according to any one of the above embodiment (s) .

16. The light-emitting device according to any one of the above embodiment (s) , wherein the at least one gold (III) compound comprises a light-emitting layer.

17. The light-emitting device according to any one of the above embodiment (s) , wherein the gold (III) compound comprises a dopant in the light-emitting layer.

18. The light-emitting device according to any one of the above embodiment (s) , further comprising an anode, a hole-transporting layer, and a cathode.

19. The light-emitting device according to any one of the above embodiment (s) , wherein the light-emitting layer is a spin-coated, inkjet printed, or vacuum deposited light-emitting layer.

20. The light-emitting device according to any one of the above embodiment (s) , wherein the light-emitting device is an organic light-emitting diode (OLED) .

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic diagram of the basic structure of an organic electroluminescence device, in accordance with an embodiment of the present invention.

FIG. 2 shows UV-vis absorption spectra of compounds 3–5 in dichloromethane (CH₂Cl₂) at 298 K, in accordance with an embodiment of the present invention.

FIG. 3 shows UV-vis absorption spectra of

compounds

2, 6 and 7 in dichloromethane at 298 K, in accordance with an embodiment of the present invention.

FIG. 4 shows UV-vis absorption spectra of compounds 8–11 in dichloromethane at 298 K, in accordance with an embodiment of the present invention.

FIG. 5 shows UV-vis absorption spectra of

compounds

12 and 13 in dichloromethane at 298 K, in accordance with an embodiment of the present invention.

FIG. 6 shows the normalized photoluminescence spectra of compounds 3–5 in dichloromethane at 298 K, in accordance with an embodiment of the present invention.

FIG. 7 shows the normalized photoluminescence spectra of

compounds

FIG. 8 shows the normalized photoluminescence spectra of compounds 8–11 in dichloromethane at 298 K, in accordance with an embodiment of the present invention.

FIG. 9 shows the normalized photoluminescence spectra of

compounds

FIG. 10 shows the normalized photoluminescence spectra of 5

wt％compounds

2, 6 and 7 doped into N, N’-dicarbazolyl-3, 5-benzene (MCP) thin film, in accordance with an embodiment of the present invention.

FIG. 11 shows the normalized photoluminescence spectra of 5 wt％compounds 8–11 doped into MCP thin films, in accordance with an embodiment of the present invention.

FIG. 12 shows the thermogravimetric analysis (TGA) analysis of compound 9, in accordance with an embodiment of the present invention.

FIG. 13 shows the TGA analysis of compound 13, in accordance with an embodiment of the present invention.

FIG. 14 shows the EQE of the device with compound 10 doped into MCP as light-emitting layer, in accordance with an embodiment of the present invention.

FIG. 15 shows the EQE of the device with compound 11 doped into MCP as light-emitting layer and the electroluminescence spectra of device compound 10 as light-emitting layer, in accordance with an embodiment of the present invention.

DETAILED DESCRIPTION

Embodiments of the invention are directed towards robust luminescent gold (III) compounds comprising tetradentate ligand. Other embodiments of the invention are directed to modification of the luminescent tetradentate gold (III) compounds. The luminescent tetradentate gold (III) compounds comprise:

at least one gold metal center having a+3 oxidation state and four coordination sites；

a tetradentate ligand bearing coordinating atoms or functional groups as ligating site to coordinate to the gold center； and the coordinating sites are connected directly or via an aromatic system or spacer to form a rigid tetradentate ligand having four coordination sites.

The tetradentate gold (III) compounds have the chemical structure shown in Formula I:

wherein:

(a) W, X, Y and Z are independently selected from C, O, N, P, C–C≡C (alkynyl) , C–N≡C (isocyanide) or C–C≡N (cyanide) , where the bold-faced atom represents the coordinating site；

(b) A, B, C and D are independently cyclic derivatives of substituted or unsubstituted pyridine groups, substituted or unsubstituted phenyl groups, substituted or unsubstituted heteroaryl groups, or substituted or unsubstituted polycyclic groups；

(e) p, q, r and s are each independently 0–3.

A, B, C, D, optionallyα, and optionallyβor in the case ofαandβbeing acyclic structures, rings A, B, C and D are cyclic structure derivatives where the cyclic structures are independently selected from arene, heteroarene, heterocycle or polycyclic unit as known to those skilled in the art. A, B, C, D, optionallyαand optionallyβcan be independently selected from heteroatom containing heteroarenes or heterocycles. The arene or heteroarene can be benzene, pyridine, thiophene, furan, pyrazole, oxadiazole, thiadiazole, imidazole, oxazole, isoxazole, thiazole, isothiazole, isoquinoline, pyrrole, pyrazine, pyridazine, pyrimidine, benzimidazole, benzofuran, benzothiazole, indole, indolocarbazole, benzopyrrolizinophenoxazine, naphthalene, anthracene, pyrene, triazole, tetrazole, pyran, thiapyran, oxadiazole, triazine, tetrazine, carbazole, dibenzothiophene, dibenzofuran, fluorene and derivatives thereof.

A, B, C, D, optionallyα, and optionallyβcan be unsubstituted or substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl or alkyl or heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triaryl or trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

Additionally, or alternatively, any two adjacent substituted positions of rings A, B, C, D, optionallyα, and optionallyβ, together form, independently, fused 5-to 6-membered cyclic groups, wherein the said cyclic group is cycloalkyl, cycloheteroalkyl, aryl, or heteroaryl, and wherein the fused 5-to 6-member cyclic group can be unsubstituted or be substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

Specific examples of the luminescent tetradentate gold (III) compounds of Formula I include the following:

wherein, G, G′, G″and G″′are independently selected from CRR’, C＝O, NR, O, BR, S, SO, SO₂, SiRR′, Se and AsR, where R and R′are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, a heterocyclic group and derivatives thereof； and, R¹ to R²³ are each independently selected from alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilne, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

In the present disclosure the following terms are used.

The term "halo" or "halogen" as used herein includes fluorine, chlorine, bromine and iodine.

The term "alkyl" as used herein includes straight and branched chain alkyl groups, as well as cycloalkyl group with cyclic structure of alkyl groups. Alkyl groups are those containing from one to eighteen carbon atoms and includes methyl, ethyl, propyl, isopropyl, butyl, isobutyl, tert-butyl, and the like. In addition, the alkyl group can be unsubstituted or substituted with one or more substituents including hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "alkenyl" as used herein includes both straight and branched chain alkene radicals. Alkenyl groups are those containing two to eighteen carbon atoms. In addition, the alkenyl group can be unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "alkynyl" as used herein includes alkyne and polyalkyne that have a straight chain of two to eighteen or more carbon atoms. The alkynyl group can be unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "arylalkynyl" as used herein includes an alkynyl group which has an aromatic group as a substituent. In addition, the arylalkynyl group can be unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "alkylaryl" as used herein includes an alkyl group which has an aromatic group as a substituent. In addition, the alkylaryl group can be unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "cycloalkyl" as used herein includes cyclic alkylgroups. Cycloalkyl groups can contain 3 to 7 or more carbon atoms and includes cyclopropyl, cyclopentyl, cyclohexyl, and the like. Cycloalkyl group can be unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

The term "alkoxy" as used herein includes linear or branched alkoxy groups of 1 to 18 or more carbon atoms, and unsubstituted or substituted with one or more substituents including alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof； and R and R’are independently selected from hydrogen atom, deuterium atom, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, heterocyclic and derivatives thereof.

Aryl alone or in combination includes carbocyclic aromatic systems. The systems may contain one, two or three rings wherein each ring may be attached together in a pendent manner or may be fused. Preferably the rings are 5-or 6-membered rings. Aryl groups include, but are not exclusive to, unsubstituted or substituted derivatives of benzene, naphthylene, pyrene, anthracene, pentacene, benzo [a] pyrene, chrysene, coronene, corannulene, naphthacene, phenanthrene, triphenyklene, ovalene, benzophenanthrene, perylene, benzo [g, h, i] perylene, antanthrene, pentaphene, picene, dibenzo [3, 4； 9, 10] pyrene, benzo [3, 4] pyrene, dibenzo [3, 4； 8, 9] pyrene, dibenzo [3, 4； 6, 7] pyrene, dibenzo [1, 2； 3, 4] pyrene, and naphto [2, 3； 3, 4] pyrene； wherein the positions of attachment and substitution can be at any carbon of the group that does not sterically inhibit formation of compound of Formula I, as can be appreciated by one skilled in the art.

Heteroaryl alone or in combination includes heterocyclic aromatic systems. The systems may contain one, two or three rings wherein each ring may be attached together in a pendent manner or may be fused. Preferably the rings are 5-or 6-membered rings. Heterocyclic and heterocycle refer to a 3 to 7-membered ring containing at least one heteroatom. Heteroaryl groups include, but are not exclusive to, unsubstituted or substituted derivatives of pyridine, thiophene, furan, pyrazole, imidazole, oxazole, isoxazole, thiazole, isothiazole, pyrrole, pyrazine, pyridazine, pyrimidine, benzimidazole benzofuran, benzothiazole, benzopyrrolizinophenoxazine, indolocarbazole, oxadiazole, thiadiazole, indole, triazole, tetrazole, pyran, thiapyran, oxadiazole, triazine, tetrazine, carbazole, dibenzothiophene, dibenzofuran, isoindole, quinoline, isoquinoline, chromene, isochromene and non-aromatic rings piperazine, piperidine, or pyrrolidine； wherein the position of attachment or substitution can be at any carbon of the group that does not sterically inhibit formation of compound of Formula I, as can be appreciated by one skilled in the art.

Heteroatom refers to S, O, N, P, Si, B, or Se.

Substituted refers to any level of substitution. Mono-, di-and tri-substitutions are readily prepared. Substituents including hydrogen, halogen, aryl, alkyl, heteroaryl, nitro group, trifluoromethane group, cyano group, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitro, nitroso, oxadiazole, thiadiazole, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, heteroaryl, substituted heteroaryl, or heterocyclic group, that are readily prepared.

Benzene includes substituted or unsubstituted benzene. Pyridine includes substituted or unsubstituted pyridine. Thiophene includes substituted or unsubstituted thiophene. Furan includes substituted or unsubstituted furan. Pyrazole includes substituted or unsubstituted pyrazole. Imidazole includes substituted or unsubstituted imidazole. Oxazole includes substituted or unsubstituted oxazole. Isoxazole includes substituted or unsubstituted isoxazole. Thiazole includes substituted or unsubstituted thiazole. Isothiazole includes substituted or unsubstituted isothiazole. Pyrrole includes substituted or unsubstituted pyrrole. Pyrazine includes substituted or unsubstituted pyrazine. Pyridazine includes substituted or unsubstituted pyridazine. Pyrimidine includes substituted or unsubstituted pyrimidine. Benzimidazole includes substituted or unsubstituted benzimidazole. Benzofuran includes substituted or unsubstituted benzofuran. Benzothiazole includes substituted or unsubstituted benzothiazole. Indole includes substituted or unsubstituted indole. Naphthalene includes substituted or unsubstituted naphthalene. Triazole includes substituted or unsubstituted triazole. Tetrazole includes substituted or unsubstituted tetrazole. Pyran includes substituted or unsubstituted pyran. Thiapyran includes substituted or unsubstituted thiapyran. Oxadiazole includes substituted or unsubstituted oxadiazole. Triazine includes substituted or unsubstituted triazine. Tetrazine includes substituted or unsubstituted tetrazine. Carbazole includes substituted or unsubstituted carbazole. Dibenzothiophene includes substituted or unsubstituted dibenzothiophene. Dibenzofuran includes substituted or unsubstituted dibenzofuran. Piperazine includes substituted or unsubstituted piperazine. Piperidine includes substituted or unsubstituted piperidine. Pyrrolidine includes substituted or unsubstituted pyrrolidine. Indolocarbazole includes substituted or unsubstituted indolocarbazole. Benzopyrrolizinophenoxazine includes substituted or unsubstituted benzopyrrolizinophenoxazine. Oxadiazole includes substituted or unsubstituted oxadiazole. Thiadiazole includes substituted or unsubstituted thiadiazole.

Embodiments of the invention are illustrated, but not limited to, the following examples. It is to be understood that changes and variations can be made therein without deviating from the scope and the spirit of the invention as hereinafter claimed. It is also understood that various theories as to why the invention works are not intended to be limiting. Unless otherwise indicated in the following examples and elsewhere in the application text, all parts and percentages are by weight, all temperatures are in degrees Centigrade, and pressure is at or near atmospheric pressure.

In some embodiments of the invention, the luminescent tetradentate gold (III) compounds of Formula I are prepared in high purity. The compounds are represented throughout by their monomeric structure. As is well known to those skilled in the art, the compounds may also be present as dimers, trimers, oligomers or dendrimers, where two or more substituents can be coupled by an addition or condensation reaction between two or more tetradentate gold (III) compounds or the tetradentate gold (III) compounds and a divalent or polyvalent reagent, such a, but not limited to, an alklene, diaminoalkane, dihydroxyalkane, dicarboxyalkane, diaminoarene, dihydroxyarene, or dicarboxyarene. Reactions that can be used include, but are not limited to, olefin metathesis, a alkene oligomerization or polymerization, amidation, esterification, urethane formation, urea formation, and eterification.

The luminescent tetradentate gold (III) compounds can be used to form thin films by spin-coating, vacuum deposition or other known fabrication methods and be applied in OLEDs. Referring to FIG. 1, an organic EL device has, in order, substrate, hole-injecting anode, hole transporting layer, light-emitting layer, electron transporting layer, and electron-injecting cathode. The substrate is electrically insulated and can be either optically transparent, comprising glass, plastic foil, or other appropriate material. Alternatively, the substrate may be opaque and comprises one or more semiconducting materials or ceramics. In one embodiment of the invention, the EL emission is viewed through the substrate, or through both sides of the device, and the substrate comprises a transparent glass substrate or a plastic foil. In other embodiments of the invention, the EL emission is viewed only through the top electrode, and the substrate comprises an opaque semiconductor or ceramic wafers. Hole-injecting anode injects holes into the organic electroluminescence layer when anode is positively biased. The anode is composed of a conductive and optionally transmissive layer. In one embodiment of the invention, the EL emission is viewed through the substrate and the hole-injecting anode is transparent. In another embodiment of the inveniton, the EL emission is viewed through the top electrode and the transmissive characteristics of anode are immaterial and, therefore, any appropriate materials including metals or metal compounds having a work function of greater than 4.1 eV. Appropriate metals include gold, iridium, molybdenum, palladium, and platinum. When the anode is transmissive, suitable materials are metal oxides, including ITO, aluminum-or indium-doped zinc oxide, tin oxide, magnesium-indium oxide, nickel-tungsten oxide, and cadmium-tin oxide. The preferred metals and metal oxides can be deposited by evaporation, sputtering, laser ablation, and chemical vapor deposition. Suitable materials for a hole-transporting layer include polycyclic aromatic compounds, for example, but not limited to, 4, 4'-bis [N- (1-naphthyl) -N-phenylamino] biphenyl (NPB) , 4, 4'-bis [N- (3-methylphenyl) N-phenylamino] biphenyl (TPD) , 4, 4', 4″-tris [ (3-methylphenyl) phenylamino] triphenylamine (MTDATA) , and di- [4- (N, N-ditolyl-amino) phenyl] cyclohexane (TAPC) . Polymeric hole-transporting materials can be used, including, but not limited to, poly (N-vinylcarbazole) (PVK) , polythiophene, polypyrrole, polyaniline, and copolymers including poly (3, 4-ethylenedioxythiophene) : poly (4-styrene-surlfonate) (PEDOT: PSS) .

The light-emitting layer in FIG. 1 is formed by doping the phosphorescent gold (III) compounds as a dopant into a host compound. Suitable host materials should be selected so that the triplet exciton can be transferred efficiently from the host material to the phosphorescent dopant material. Suitable host materials include certain aryl amines, triazoles and carbazole compounds. Examples of desirable hosts are CBP, MCP, 3- (4-biphenylyl) -4-phenyl-5-tert-butylphenyl-1, 2-butylphenyl-1, 2, 4-triazole (TAZ) 4, 4', 4"-tris (carbazol-9-yl) triphenylamine (TCTA) , p-bis- (triphenylsilyl) benzene (UGH2) , and PVK.

The electron-transporting layer consists of materials or mixtures of materials having a high ionization potential and wide optical band gap. Suitable electron-transporting materials include, but are not limited to bis (2-methyl-8-quinolinolate) -4- (phenylphenolate) aluminum (BAlq) , bathocuproine (BCP) , 1, 3, 5-tris (phenyl-2-benzimidazolyl) -benzene (TPBI) , 1, 3, 5-tri [ (3-pyridyl) -phen-3-yl] benzene (TmPyPB) , bathophenanthroline (BPhen) and tris- [2, 4, 6-trimethyl-3- (pyridin-3-yl) phenyl] borane (3TPyMB) , and 1, 3-bis [3, 5-di (pyridin-3-yl) phenyl] benzene (BmPyPhB) . In an embodiment of the inveniton, the electron transporting layer is prepared from an organic film by thermal evaporation, spin-coating, ink-jet printing from a solution, or other known fabrication methods. The electron-injecting cathode acts as a transmissive electron injector that injects electrons into the organic electroluminescence layer of anode when the cathode is negatively biased. The cathode optionally comprises a thin fluoride layer and a metal or metal alloy, preferably having a work function of less than 4 eV. Suitable materials include Mg: Ag, Ca, Li: Al, Al.

In some embodiments of the invention, luminescent tetradentate gold (III) compounds are a primary luminescent material or a secondary luminescent material in device, as shown in FIG. 1. In some embodiments of the invention, the tetradentate gold (III) compounds are employed as electrophosphorescent dopants in multilayer OLED with an EQE of up to 11.1 ％. Advantageously, the tetradentate gold (III) compounds can be deposited in the OLEDs by spin-coating, screen printing, ink-jet printing and vacuum deposition. In addition, the modular molecular design of tetradentate gold (III) compounds, as shown in Formula I, allows independent optimization of electronic and processing properties producing OLEDs having various emission colors.

In general, the emissive layer is sandwiched between the hole-transporting layer and the electron-transporting layer. To ensure an efficient exothermic energy transfer between the host material and the dopant material, the triplet energy of the host material is larger than that of the dopant material. In addition, the ionization potential and the electron affinity of the host material is larger than those of the dopant material in order to achieve efficient

resonance energy transfer from the host to the dopant. In order to confine triplet excitons within emissive layer, the triplet energy of the hole-transporting material and electron-transporting material is larger than that of the dopant material.

In some embodiments of the invention, the luminescent tetradentate gold (III) compounds of Formula I are prepared in high purity. The synthetic method involves providing the luminescent tetradentate gold (III) compounds of Formula I from the cyclomatelated gold (III) precursor compounds or their equivalents. The gold (III) precursor compounds can be prepared by any methods known to those skilled in the art, for example, but not limited to, the methods disclosed in Krohnke, F. Synthesis 1 (1976) ； Wong, K.H.； Cheung, K.K.； Chan, M.C.； Che, C.M. Organometallics, 17, 5305 (1998) ； Yam, V.W. -W.； Wong, K.M. -C.； Hung, L. -L.； Zhu, N. Angew. Chem. Int. Ed. 44, 3107 (2005) ； Au, V.K. -M.； Wong, K.M. -C.； Zhu, N.； Yam, V.W. -W. Chem. Eur. J. 17, 130 (2011) ；

D. -A.； Smith, D.A.； Bochmann, M. Chem. Comm. 48, 7247 (2012) ； David, B.； Monkowius, U.； Rust, J.； Lehmann, C.W.； Hyzak, L.； Mohr, F. Dalton Trans. 43, 11059 (2014) ； Maity, A.； Sulicz, A.N.；Deligonul, N.； Zeller, M.； Hunter, A.D.； Gray, T.G. Chem. Sci. 6, 981 (2015) ； Kumar, R.； Linden, A.； Nevado, C. Angew. Chem. Int. Ed. 54, 14287 (2015) .

The target compounds can be synthesized by intramolecular cyclization, for example gold (III) precursor compounds undergo intramolecular cyclization reaction in the presence of base (s) or the intramolecular cyclization reaction in the presence of one or more catalyst or in the presence of both base and catalyst, as shown in Schemes 1–4, wherein the base is an organic base or inorganic base and the catalyst can be metal-based catalyst, organic-based catalyst, organometallic-based catalyst or mixtures thereof. Although the method can vary depending upon the ligand, in general the reaction is carried out in solution. The reactions are generally carried out above room temperature, for example 90℃. Specific conditions of solvent and temperature vary depending upon the structure of the desired gold (III) compound, as can be appreciated by those skilled in the art.

In some parts of the invention, the tetradentate gold (III) compounds can be further modified by incorporation of the substituents to the tetradentate gold (III) compounds, as can be appreciated upon inspection of Scheme 3.

In some parts of the invention, purification can be carried out by any method or combination of methods, including chromatography, extraction, crystallization, sublimation or any combination thereof.

EXAMPLE 1

Compounds 1–13 and 6p were prepared according to the following methodology as illustrated in Scheme 1, whereas compound 6 was prepared according to Scheme 2. The precursor compounds were prepared as disclosed in Yam, V.W. -W.； Wong, K.M. -C.； Hung, L. -L.； Zhu, N. Angew. Chem. Int. Ed. 44, 3107 (2005) . All the tetradentate complexes were synthesized by cyclization reaction of the respective precursor compounds with Cs₂CO₃, or with NaO^tBu, Pd₂ (dba) ₃ and phosphine ligand (s) . Modification of the tetradentate compound 6p to compound 6 was carried out by Buchwald-Hartwig amination using NaO^tBu, Pd₂ (dba) ₃ and phosphine ligand (s) . For example, to prepare compound 1, degassed dimethylformamide (DMF) was added to the flask containing the precursor of compound 1 and Cs₂CO₃, and the reaction mixture was heated to 90℃ for 2 days. The crude product was purified by column chromatography on silica gel using dichloromethane and hexane as eluent. Yellow crystals were obtained from layering of methanol onto the concentrated ethyl acetate solution of the compounds.

The characteristic spectroscopic properties of compounds 1-13 and6p are as follows:

Compound 1: Yield: 110 mg, 65％. ¹H NMR (400 MHz, CDCl₃) : δ1.41 (s, 9H) 6.88–6.94 (m, 1H) , 7.17 (d, J＝7.8 Hz) , 7.22 (d, J＝8.0 Hz, 1H) , 7.26–7.29 (m, 1H) , 7.31–7.36 (m, 2H) , 7.39–7.49 (m, 5H) , 7.49–7.55 (m, 4H) 7.68–7.73 (m, 2H) , 7.75–7.79 (m, 1H) , 7.88 (s, 1H) , 8.08 (s, 1H) , 8.77–8.79 (m, 1H) . Positive FAB-MS: m/z 750 ( [M+H] ⁺) .

Compound 2: Yield: 90 mg, 42％. ¹HNMR (400 MHz, CD₂Cl₂) : δ1.43 (s, 9H) , 6.58–6.62 (m, 1H) , 7.00–7.02 (m, 1H) , 7.07–7.09 (m, 2H) , 7.10–7.13 (m, 6H) , 7.14–7.22 (m, 4H) , 7.29–7.35 (m, 4H) , 7.37–7.38 (m, 3H) , 7.41–7.42 (m, 1H) , 7.43–7.53 (m, 4H) , 7.54–7.59 (m, 2H) , 7.84–7.90 (m, 4H) , 8.01 (s, 1H) , 8.05 (s, 1H) , 8.11 (s, 1H) , 8.80–8.83 (m, 1H) . Positive FAB-MS: m/z 1080 ( [M+H] ⁺) .

Compound 3: Yield: 87 mg, 51％. ¹HNMR (400 MHz, [D₆] -DMSO) : δ1.28 (s, 9H) , 6.41 (dd, J＝8.5, 2.6 Hz, 1H) , 7.14 (d, J＝2.6 Hz, 1H) , 7.20–7.26 (m, 2H) , 7.31–7.37 (m, 3H) , 7.37–7.44 (m, 4H) , 7.47–7.50 (m, 2H) , 7.53–7.60 (m, 5H) , 7.76 (d, J＝8.5 Hz, 1H) , 7.81–7.85 (m, 1H) , 7.93–7.96 (m, 1H) , 8.12–8.15 (m, 1H) . Positive FAB-MS: m/z 806 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₄₃H₃₀AuNOS·0.5H₂O: C, 63.39； H, 3.84； N, 1.72； found: C, 63.41； H, 3.77； N, 1.90.

Compound 4: Yield: 96 mg, 50％. ¹H NMR (400 MHz, CDCl₃) : δ1.28 (s, 9H) , 6.56 (dd, J＝ 8.5, 2.6 Hz) , 6.88–6.90 (m, 1H) , 6.95–6.97 (m, 1H) , 7.11–7.15 (m, 1H) , 7.17 (d, J＝8.5 Hz, 1H) , 7.23–7.25 (m, 1H) 7.29–7.33 (m, 1H) 7.36–7.48 (m, 7H) 7.69 (d, J＝8.3 Hz, 2H) , 7.78–7.82 (m, 1H) , 7.92 (d, J＝2.6 Hz, 1H) , 7.93–7.98 (m, 1H) , 8.26–8.30 (m, 1H) . ¹⁹F {¹H} NMR (376 MHz, CDCl₃) : δ–61.52 (s) . Positive FAB-MS: m/z 874 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₄₄H₂₉AuF₃NOS·H₂O: C, 59.26； H, 3.50； N, 1.57； found: C, 59.39； H, 3.37； N, 1.87.

Compound 5: Yield: 80 mg, 57％. ¹H NMR (400 MHz, CDCl₃) : δ1.38 (s, 9H) , 1.44 (s, 9H) , 6.57 (dd, J＝8.5, 2.6 Hz, 1H) , 6.80–6.82 (m, 1H) , 6.91–6.93 (m, 1H) , 7.08 (d, J＝8.5 Hz, 1H) , 7.10–7.14 (m, 1H) , 7.16–7.20 (m, 2H) , 7.21 (s, 1H) , 7.24 (d, J＝2.0 Hz, 1H) , 7.33–7.41 (m, 5H) , 7.43 (d, J＝8.4 Hz, 2H) , 7.78–7.81 (m, 1H) , 7.82 (d, J＝2.6 Hz, 1H) , 7.91–7.96 (m, 1H) , 8.24–8.26 (m, 1H) . Positive FAB-MS: m/z 862 ( [M+H] ⁺) .

Compound 6p: Yield: 98 mg, 59％. ¹H NMR (400 MHz, CDCl₃) : δ1.39 (s, 9H) , 6.51–6.57 (m, 1H) , 6.78–6.90 (m, 2H) , 7.07–7.17 (m, 3H) , 7.19–7.24 (m, 2H) , 7.36–7.40 (m, 2H) , 7.42–7.51 (m, 4H) , 7.53–7.60 (m, 2H) , 7.78–7.82 (m, 1H) , 7.90–7.93 (m, 2H) , 8.32–8.34 (m, 1H) . Positive FAB-MS: m/z 884 ( [M+H] ⁺) .

Compound6: Yield: 56 mg, 43％. ¹HNMR (400 MHz, CDCl₃) : δ1.35 (s, 27H) , 6.52 (dd, J＝8.5, 2.6 Hz, 1H) , 6.85 (d, J＝8.8 Hz, 2H) , 7.02 (d, J＝8.8 Hz, 2H) , 7.10–7.14 (m, 5H) , 7.15–7.19 (m, 5H) , 7.34–7.39 (m, 6H) , 7.44 (d, J＝2.6 Hz, 1H) , 7.45–7.50 (m, 2H) , 7.77–7.82 (m, 1H) , 7.90–7.92 (s, 1H) , 7.95–7.99 (m, 1H) , 8.34–8.36 (m, 1H) . Positive FAB-MS: m/z 1085 ( [M+H] ⁺) .

Compound 7: Yield: 50 mg, 43％. ¹H NMR (400 MHz, [D₆] -DMSO) : δ0.69 (m, 3H) , 0.82–1.08 (m, 8H) , 1.34 (s, 9H) , 4.15 (t, J＝7.0 Hz, 2H) , 6.45 (dd, J＝8.5, 2.6 Hz, 1H) , 7.07 (d, J ＝2.6 Hz, 1H) , 7.13 (t, J＝7.9 Hz, 1H) , 7.20–7.31 (m, 3H) , 7.327–7.37 (m, 1H) , 7.44–7.48 (m, 1H) , 7.51 (d, J＝8.5 Hz, 1H) , 7.55 (t, J＝7.9 Hz, 1H) , 7.68 (d, J＝8.2 Hz, 2H) , 7.70–7.75 (m, 3H) , 7.80 (s, 1H) , 7.84–7.86 (m, 1H) , 7.89 (d, J＝7.9 Hz, 1H) , 7.93 (d, J＝8.2 Hz, 2H) . ¹⁹F {¹H} NMR (376 MHz, [D₆] -DMSO) : δ–61.39 (s) . Positive FAB-MS: m/z 997 ( [M+H] ⁺) .

Compound 8: Yield: 104 mg, 68％. ¹H NMR (400 MHz, CDCl₃) : δ1.40 (s, 9H) , 2.44 (s, 3H) , 6.52 (dd, 1H, J＝8.6, 2.8 Hz) , 6.74–6.76 (m, 1H) , 7.21–7.25 (m, 2H) , 7.26–7.36 (m, 8H) , 7.36–7.41 (m, 2H) , 7.47–7.55 (m, 4H) , 7.66–7.71 (m, 2H) , 7.75–7.80 (m, 1H) , 7.86–7.90 (m, 1H) , 8.05 (d, J＝2.0 Hz, 1H) , 8.36–8.42 (m, 1H) , 9.06 (d, J＝2.8 Hz, 1H) . Positive FAB-MS: m/z 895 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₅₀H₃₆AuN₂S·H₂O: C, 65.78； H, 4.31； N, 3.07； found: C, 65.77； H, 4.04； N, 3.12.

Compound 9: Yield: 110 mg, 67％. ¹H NMR (400 MHz, CDCl₃) δ1.38 (s, 9H) , 1.43 (s, 9H) , 2.45 (s, 3H) , 6.55 (dd, J＝8.6, 2.8 Hz, 1H) , 6.78–6.82 (m, 1H) , 7.26–7.29 (m, 1H) , 7.32–7.35 (m, 5H) , 7.35–7.40 (m, 5H) , 7.49–7.51 (m, 1H) , 7.58 (d, J＝8.5 Hz, 2H) , 7.63 (d, J＝8.6 Hz, 1H) , 7.70 (d, J＝8.5 Hz, 2H) , 7.81–7.90 (m, 2H) , 8.04–8.06 (m, 1H) , 8.39–8.41 (m, 1H) , 9.04 (d, J＝2.8 Hz, 1H) . Positive FAB-MS: m/z 951 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₅₄H₄₅AuN₂S·0.5H₂O: C, 67.56； H, 4.83； N, 2.92； found: C, 67.60； H, 4.84； N, 2.98.

Compound 10: Yield: 108 mg, 72％. ¹H NMR (400 MHz, CDCl₃) : δ1.31 (s, 9H) , 2.44 (s, 3H) , 6.47 (dd, J＝8.6, 2.8 Hz, 1H) , 6.71–6.75 (m, 1H) , 7.04–7.08 (m, 1H) , 7.16–7.19 (m, 1H) , 7.21–7.24 (m, 2H) , 7.27–7.31 (m, 3H) , 7.31–7.36 (m, 2H) , 7.36–7.41 (m, 3H) , 7.43 (d, J＝8.4, 2H) , 7.55–7.62 (m, 3H) , 7.77–7.80 (m, 1H) , 7.80–7.84 (m, 1H) , 8.11 (m, 1H) , 8.23–8.26 (m, 1H) , 8.88 (d, J＝2.8 Hz, 1H) . ¹⁹F {¹H} NMR (376 MHz, CDCl₃) : δ–62.47 (s) . Positive FAB-MS: m/z 963 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₅₁H₃₆AuF₃N₂S·0.5H₂O: C, 63.03； H, 3.84； N, 2.88； found: C, 63.01； H, 3.79； N, 3.01.

Compound 11: Yield: 110 mg, 99％. ¹H NMR (400 MHz, CDCl₃) : δ0.63–0.91 (m, 10H) , 1.03–1.20 (m, 12H) , 1.36 (s, 9H) , 1.90–2.03 (m, 4H) , 6.65 (dd, J＝8.6, 2.8 Hz, 1H) , 6.75–6.79 (m, 1H) , 7.20–7.25 (m, 2H) , 7.27–7.29 (m, 1H) , 7.34–7.39 (m, 5H, C^N^C) , 7.39–7.45 (m, 3H) 7.45–7.49 (m, 2H) , 7.51 (d, J＝8.5 Hz, 2H) , 7.62 (d, J＝8.5 Hz, 2H) , 7.68 (d, J＝8.6 Hz, 1H) , 7.71–7.74 (m, 1H) , 7.77–7.81 (m, 2H) , 7.87–7.91 (m, 1H) , 8.18–8.22 (m, 1H) , 8.34–8.37 (m, 1H) , 9.07 (d, J＝2.8 Hz, 1H. ¹⁹F {¹H} NMR (376 MHz, CDCl₃) : δ–62.53 (s) . Positive FAB-MS: m/z 1205 ( [M+H] ⁺) . Elemental analysis calcd (％) for C₆₉H₆₂AuF₃N₂S·H₂O: C, 67.75； H, 5.27； N, 2.29； found: C, 67.99； H, 5.24； N, 2.44.

Compound 12: Yield: 120 mg, 65％. ¹H NMR (400 MHz, CDCl₃) : δ1.41 (s, 9H) , 1.52 (s, 9H) , 2.47 (s, 3H) , 3.02–3.08 (m, 4H) , 6.87–6.91 (m, 1H) , 6.93–6.98 (m, 1H) , 6.99–7.03 (m, 1H) , 7.15–7.20 (m, 1H) , 7.30–7.35 (m, 3H) , 7.35–7.40 (m, 3H) , 7.45 (d, J＝8.4 Hz, 2H) , 7.50 (s, 1H) , 7.58 (d, J＝8.4 Hz, 2H) , 7.72 (d, J＝8.2 Hz, 1H) , 7.83–7.88 (m, 1H) , 8.77 (d, J ＝1.9 Hz, 1H) . HRMS (Positive ESI) calcd. for C₄₈H₄₃AuN₂S: m/z＝876.2807； found: 976.2793 [M] ⁺.

Compound 13: Yield: 200 mg, 70％. ¹H NMR (400 MHz, CDCl₃) : δ0.57–0.72 (m, 4H) , 0.75 (t, J＝7.1 Hz, 6H) , 0.96–1.03 (m, 8H) , 1.05–1.14 (m, 4H) , 1.39 (s, 9H) , 1.53 (s, 9H) , 1.89–2.00 (m, 4H) , 2.95–3.06 (m, 4H) , 6.68 (d, J＝8.2 Hz, 1H) , 6.74–6.79 (m, 1H) , 6.88 (d, J＝8.7 Hz, 1H) , 7.06–7.11 (m, 1H) , 7.19 (d, J＝8.7 Hz, 1H) , 7.31–7.34 (m, 1H) , 7.35–7.37 (m, 3H) , 7.37–7.40 (m, 3H) , 7.41 (s, 1H) , 7.48–7.53 (m, 3H) , 7.63 (d, J＝8.2 Hz, 1H) , 7.75–7.79 (m, 1H) , 7.80–7.86 (m, 2H) , 8.86 (d, J＝1.9 Hz, 1H) . HRMS (Positive ESI) calcd. for C₆₆H₆₉AuN₂S: m/z＝1118.4842； found: 1118.4819 [M] ⁺.

EXAMPLE 2

UV-Vis Absorption Properties

The electronic absorption spectra of the tetradentate gold (III) compounds 2–13 in dichloromethane solution at 298 K showed intense absorption bands at ca. 300–400 nm with extinction coefficients in the order of 10⁴ dm^–3mol^–1cm^–1, and a moderately intense absorption band at ca. 420–500 nm, as listed in

, below, and FIGs. 2–5. Compounds 2–5 showed a vibronic-structured low-energy absorption band with vibrational progressional spacings of 1,250 cm^–1, corresponding to the skeletal vibrational frequencies of the diarylpyridine ligand. The origin of this absorption band is tentatively assigned as the intraligand (IL) [π→π*] transition of the diarylpyridine ligand. Compounds 6–11 showed a broad structureless low-energy absorption band, and the origin is tentatively assigned as intraligand charge transfer (ILCT) transition. For compound 6, due to the presence of the electron-donating triphenylamine group at the 4-position of pyridine, the transition is tentatively assigned as ILCT [π (triphenylamine) →π*(diarylpyridine) ] transition. For compound 7, since the electron-donating thieno [3, 2-b] indole unit is introduced into the alkynyl framework, the presence of a low-lying [π (alkynyl-thieno [3, 2-b] indole) →π* (diarylpyridine) ] ILCT transition is possible. For compounds 8–11, in view of the presence of the electron-donating amine group attached to the diarylpyridine core, the transition is possibly originated from an ILCT [π (phenylamine) →π* (diarylpyridine) ] transition.

Compounds

12 and 13 showed the structureless lower-energy absorption band at 482 nm and 490 nm, respectively, which was tentatively assigned as the ILCT [π (diarylamine) →π* (diarylpyridine) ] transition.

EXAMPLE 3

Photoluminescenceproperties

Tetradentate gold (III) compounds of the present invention exhibit rich luminescence at both room temperature and low temperature in various media. Upon photo-excitation in dichloromethane solution at room temperature, compounds 2–13 showed intense luminescence at 509–653 nm as shown in FIGs. 6–9. A vibronic-structured emission band with band maximum at ca. 545 nm was observed for compounds 3–5 as shown in FIG. 6, whereas compound 2 showed a structured emission band at ca. 509 nm. Vibrational progressional spacings of ca. 1,100 cm^–1 were observed in these three compounds. These vibronic-structured emission bands are tentatively assigned as derived from metal-perturbed ³IL [π→π*] state of the diarylpyridine framework. Upon introducing electron-donating group, compounds 4–11 showed a structureless emission at ca. 542–620 nm, which is tentatively assigned as derived from an excited state of metal-perturbed ILCT origin from the electron-rich arylamino functional group to the diarylpyridine. Besides, compounds 12 and 13 exhibited a structureless emission band at ca. 655 nm, derived from the ³ILCT [π (diarylamine) →π* (diarylpyridine) ] excited state.

Table 1

^a Relative luminescence photoluminescence quantum yield, measured at room temperature using [Ru (bpy) ₃] Cl₂ in aqueous state as the reference. The absolute photoluminescence quantum yield of thin films was measured on a Hammamatsu C9920-03 Absolute Photoluminescence Quantum Yield Measurement System.

FIG. 10 shows the normalized emission spectra of

compounds

2, 6 and 7 doped in MCP thin films. For compound 2, both the emission of the thin film and solution displayed vibronic-structured emission bands, and the emission spectrum in the thin film state showed a hypsochromic shift of 155 cm^–1 compared to the emission spectrum in dichloromethane solution. The vibronic emission of compound 2 is tentatively assigned as derived from metal-perturbed IL ³ [π→π*] state of the diarylpyridine framework. A structureless emission band was observed for compound 6 doped into MCP film. The origin of this emission band is tentatively assigned as ILCT state derived from [π (triphenylamine) →π* (diarylpyridine) ] transition. Furthermore, compounds 8–11 exhibit structureless emission bands at ca. 560–581 nm as shown in FIG. 11. These emission bands are tentatively assigned as originating from ILCT [π (phenylamine) →π* (diarylpyridine) ] state.

EXAMPLE 4

The decomposition temperature of the tetradentate gold (III) compound had been measured by thermogravitic analysis (TGA) . All the compounds are thermally stable and exhibit high decomposition temperature, which is defined as the temperature at which the material shows a 5％weight loss. FIGs. 12 and 13 show the TGA curves of the selected

compounds

9 and 13, respectively. Notably, high decomposition temperatures of 498℃ and 457℃ were found for

compounds

9 and 13, respectively.

EXAMPLE 5

An organic EL device according to an embodiment of the invention was constructed in the following manner:

(a) A transparent anode ITO-coated borosilicate glass substrate (38 mm×38 mm) with sheet resistance of 30 Ωsquare^–1 was ultra-sonicated in the commercial detergent Decon 90, rinsed in deionized water having a resistivity of 18.2 MΩfor 15 minutes, and then dried in an oven at 120℃ for an hour. The substrate was next subjected to an UV-ozone treatment in a Jelight 42-220 UVO-Cleaner equipped with a mercury grid lamp for 15 minutes in order to increase the work function of the ITO-coated glass substrate for better hole injection into the organic layer.

(b) A 40-nm thick PEDOT: PSS hole-transporting layer was spin-coated by using a Laurell WS-400Ez6NPP-Lit2 single wafer spin processor at 7000 rpm for 30 seconds onto the ITO-coated glass substrate of step (a) and baked at 110 degree C for 10 minutes in air.

(c) A 30-nm thick light-emitting layer was spin coated by using a Laurell WS-400Ez-6NPP-Lit2 single wafer spin processor at 6000 rpm for 25 seconds onto PEDOT: PSS layer of step (b) , and baked at 80 degree C for 10 minutes in air, in which compound 10 was doped into light-emitting MCP layer at different concentrations in the range from 5 to 20％；

(d) The substrate was put into a vacuum chamber, and the chamber was pumped down from 1 bar to 5×10^–6 mbar；

(e) A 5-nm thick 3TPyMB carrier confinement layer and a 30-nm thick TmPyPB electron-transporting layer were deposited by thermal evaporation on doped CBP light-emitting layer.

(f) A 0.8-nm thick LiF layer and an 80 nm thick Al layer were deposited by thermal evaporation on the TmPyPB layer to form an electron-injecting cathode.

3TPyMB, TmPyPB, LiF and Al were prepared by thermal evaporation from tantalum boats by applying current through the tantalum boats. Deposition rates were monitored with a quartz oscillation crystal and a Sigma SQM-242 quartz crystal card and controlled at 0.1–0.2 nm s^–1 for both organic and metal layers. Current density–voltage–luminance characteristics of organic electroluminescence devices were measured with a programmable Keithley model 2420 power source and a Spectrascan PR-655 colorimeter under ambient air conditions. OLEDs doped with 20％compound 10 showed a saturated yellow color with the Commission Internationale de L’Eclairage coordinates of (0.54, 0.46) and a maximum EQE of 7.2％as shown in FIG. 14.

EXAMPLE 6

The same materials and processing procedures were employed as described in Example 4 except that compound 11 was doped into MCP as light emissive layer. Device doped with 20％of compound 11 shows a structureless orange emission with peak maximum at 590 nm and a high EQE of 11.1％, as shown in FIG. 15. In some embodiments of the invention, these tetradentate gold (III) compounds possess desirable electrophosphorescent properties, and are candidates as electrophosphorescent dopants for OLEDs.

With respect to any FIG. or numerical range for a given characteristic, a FIG. or a parameter from one range may be combined with another FIG. or a parameter from a different range for the same characteristic to generate a numerical range.

Other than in the operating examples, or where otherwise indicated, all numbers, values and/or expressions referring to quantities of ingredients, reaction conditions, etc., used in the application text are to be understood as modified in all instances by the term "about" .

It should be understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be included within the spirit and purview of this application.

Claims

A luminescent tetradentate gold (III) compound comprising the chemical structure represented by the following general Formula I,

wherein:

(a) W, X, Y and Z are independently selected from C, O, N, P, C–C≡C, C–N≡C or C–C≡N；

(b) A, B, C and D are independently a cyclic structure selected from substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, or substituted or unsubstituted polycyclic group；

(c) α and β are independently a cyclic structure, acyclic structure, or any derivative thereof, wherein the cyclic structure is selected from a substituted or unsubstituted pyridine group, substituted or unsubstituted phenyl group, substituted or unsubstituted heteroaryl group, substituted or unsubstituted cycloalkyl group, and substituted or unsubstituted polycyclic group, and wherein the acyclic structure is selected from substituted or unsubstituted alkynyl, substituted or unsubstituted arylalkynyl, substituted or unsubstituted alkyl, substituted or unsubstituted alkylaryl, substituted or unsubstituted alkoxy, and substituted or unsubstituted arylalkoxy；

(d) each G is independently a non-coordination site, and can be CRR’, C＝O, NR, O, PR, P (＝O) R, BR, S, SO, SO₂, SiRR′, Se, AsR,
wherein R and R'are independent selected from hydrogen, halogen, aryl, alkyl, heteroaryl, nitro, trifluoromethyl, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, substituted aryl, substituted heteroaryl, heterocyclyl, and derivatives thereof；

(e) p, q, r and s are each independently 0–3.
The tetradentate gold (III) compound according to claim 1, wherein A, B, C, D, optionally α and optionally β, are independently selected benzene, pyridine, thiophene, furan, pyrazole, oxadiazole, thiadiazole, imidazole, oxazole, isoxazole, thiazole, isothiazole, isoquinoline, pyrrole, pyrazine, pyridazine, pyrimidine, benzimidazole, benzofuran, benzothiazole, indole, indolocarbazole, benzopyrrolizinophenoxazine, naphthalene, anthracene, pyrene, triazole, tetrazole, pyran, thiapyran, oxadiazole, triazine, tetrazine, carbazole, dibenzothiophene, dibenzofuran, fluorene and derivatives thereof； and/or

wherein one or more of A, B, C, D, optionally α and optionally β, are substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, substituted aryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’or derivatives thereof； and R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic and derivatives thereof； and/or

wherein independently any two adjacent substituted positions of at least two of A, B, C, D, optionally α and optionally β, form a fused 5-to 6-membered cyclic group selected from cycloalkyl, cycloheteroalkyl, aryl, and heteroaryl, wherein the fused 5-to 6-membered cyclic group is unsubstituted or substituted with one or more of alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’or derivatives thereof； wherein R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic and derivatives thereof.
The tetradentate gold (III) compound according to claim 1, which is selected from, but not limited to the following:

wherein, G, G′, G″and G″′are independently selected from CRR’, C＝O, NR, O, BR, S, SO, SO₂, SiRR′, Se and AsR, wherein R and R′are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic, and derivatives thereof； and, R¹ to R²³ are each independently selected from hydrogen, deuterium, alkyl, alkenyl, alkynyl, alkylaryl, cycloalkyl, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic, NRR’, SR, C (O) R, COOR, C (O) NR₂, SOR, SO₃R, BRR’and derivatives thereof, wherein R and R’are independently selected from hydrogen, deuterium, formaldehyde, cyano, alkylalkynyl, substituted alkylalkynyl, arylalkynyl, substituted arylalkynyl, heteroarylalkynyl, substituted heteroarylalkynyl, condensed polycyclic, substituted condensed polycyclic, aryl, alkyl, heteroaryl, nitro, trifluoromethane, cyano, aryl ether, alkyl ether, heteroaryl ether, diarylamine, dialkylamine, diheteroarylamine, diarylborane, triarylsilane, trialkylsiliane, alkenyl, alkylaryl, cycloalkyl, haloformyl, hydroxyl, aldehyde, carboxamide, amine, amino, alkoxy, azo, benzyl, carbonate ester, carboxylate, carboxyl, ketamine, isocyanate, isocyanide, isothiocyanate, nitrile, nitroso, phosphine, phosphate, phosphono, pyridyl, sulfonyl, sulfo, sulfinyl, sulfhydryl, halo, aryl, substituted aryl, substituted heteroaryl, heterocyclic and derivatives thereof.
The tetradentate gold (III) compound according to claim 1, wherein at least one substituent of A, B, C, D, optionally α and optionally β, is further derived to form a bridging substituent wherein two or more of the tetradentate gold (III) compounds are combined as a dimer, trimer, oligomer, or polymer.
A method for the preparation of luminescent tetradentate gold (III) compound according to claim 1 or 2, comprising:

providing a gold (III) precursor compound comprising a combination of monodentate, bidentate or tridentate ligands； and

intramolecularly cyclizating the gold (III) precursor compound to form a tetradentate gold (III) compound.
The method of claim 5, wherein the method further comprises adding at least one base, catalyst or combination thereof to the gold (III) precursor compound； and/or

wherein the base is selected from an organic base, an inorganic base, or a combination thereof； and/or

wherein the catalyst is selected from a metal based catalyst, organic based catalyst, organometallic based catalyst, or any combination thereof.
The method according to claim 5, wherein the method further comprises adding a solvent to the gold (III) precursor compound to form a solution； and/or

wherein the method further comprises isolating the tetradentate gold (III) compound according to claim 1 by chromatography, extraction, crystallization, sublimation or any combination thereof； and/or

wherein the method further comprises adding or substituting a substituent to the gold (III) precursor, the gold (III) precursor comprising a different tetradentate gold (III) compound according to claim 1.
A luminescent material, comprising a tetradentate gold (III) compound according to any one of claims 1 to 4.
A light-emitting device, comprising at least one tetradentate gold (III) compound according to any one of claims 1 to 4； and/or

wherein at least one gold (III) compound comprises a light-emitting layer； and/or wherein the light-emitting device is an organic light-emitting diode.
The light-emitting device according to claim 9, wherein the gold (III) compound comprises a dopant in the light-emitting layer； and/or

wherein the light-emitting device further comprises an anode, a hole-transporting layer, and a cathode； and/or

wherein the light-emitting layer is a spin-coated, inkjet printed, or vacuum deposited light-emitting layer.