WO2017125059A1 - Non-powered purifier device for air inlet/outlet and manufacturing method of multifunctional honeycomb activated carbon thereof - Google Patents
Non-powered purifier device for air inlet/outlet and manufacturing method of multifunctional honeycomb activated carbon thereof Download PDFInfo
- Publication number
- WO2017125059A1 WO2017125059A1 PCT/CN2017/071816 CN2017071816W WO2017125059A1 WO 2017125059 A1 WO2017125059 A1 WO 2017125059A1 CN 2017071816 W CN2017071816 W CN 2017071816W WO 2017125059 A1 WO2017125059 A1 WO 2017125059A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- activated carbon
- honeycomb activated
- magnetic ring
- outlet
- magnetic ball
- Prior art date
Abstract
A non-powered purifier device for an air inlet/outlet comprises a housing (1), a multifunctional honeycomb activated carbon component (2), a back cover (3), a magnetic ring (4) and a universal magnetic joint clip (5). The multifunctional honeycomb activated carbon component (2) is installed within the housing (1), the back cover (3) is engaged and mounted on the housing (1), the magnetic ring (4) is disposed on the back cover (3), the universal magnetic joint clip (5) is installed on the magnetic ring (4), the back cover is provided with dense air inlet holes (7) thereon, and the housing is provided with dense air outlet holes (6) thereon. The non-powered purifier device for the air inlet/outlet is not power-driven, has a simple structure, and is easy to use. The manufactured multifunctional honeycomb activated carbon component (2) has high density and functions of sterilization and degradation of formaldehyde, and has good air convection speed and purifying effects, and long service life.
Description
本发明涉及空气净化领域,具体为一种无电进出风口净化装置及其多性能蜂窝活性炭的制作方法。The invention relates to the field of air purification, in particular to a non-electric inlet and outlet tuyere purifying device and a multi-performance honeycomb activated carbon manufacturing method thereof.
目前随着环境污染的严重,越来越多的汽车和室内空调出入风口需配备有空气净化装置,目前的空气净化装置一般都为电动净化装置,设备成本大、噪声大,其次净化装置内的净化层一般为颗粒状活性炭,气流导速和净化性能单一效果差,。At present, with the serious environmental pollution, more and more automobile and indoor air conditioning air inlets and outlets need to be equipped with air purification devices. Currently, air purification devices are generally electric purification devices, which have high equipment cost and high noise, and secondly in the purification device. The purification layer is generally granular activated carbon, and the air conduction rate and purification performance are single effect poor.
发明内容Summary of the invention
本发明的目的在于提供一种无电进出风口净化装置,以解决上述背景技术中提出的问题。It is an object of the present invention to provide an electroless inlet and outlet tuyere purification apparatus to solve the problems set forth in the background art described above.
为实现上述目的,本发明提供如下技术方案:一种无电进出风口净化装置,包括外壳、多性能性蜂窝活性炭、后盖、磁环和万向磁球夹,所述多性能性蜂窝活性炭安装在外壳内,后盖卡装在外壳上,所述后盖上设有磁环,磁环上安装有万向磁球夹,所述后盖上设有密集的进气孔,所述外壳上设有密集的出气孔,所述多性能蜂窝活性炭上镶嵌有一组除菌模块。In order to achieve the above object, the present invention provides the following technical solution: an electric inlet and outlet tuyere purifying device, comprising a casing, a multi-performance honeycomb activated carbon, a back cover, a magnetic ring and a universal magnetic ball clamp, and the multi-performance honeycomb activated carbon is installed. In the outer casing, the rear cover is snapped onto the outer casing, and the rear cover is provided with a magnetic ring, the universal magnetic ball clamp is mounted on the magnetic ring, and the rear cover is provided with a dense air inlet hole on the outer casing. A dense vent is provided, and the multi-performance honeycomb activated carbon is embedded with a set of sterilization modules.
优先的,所述万向磁球夹由磁球和安装在磁球上的安装夹组成,所述磁球安装在磁环上,所述后盖上设有塑料橡胶扣,所述磁环可拆卸安装在塑料橡胶扣内。Preferably, the universal magnetic ball clamp is composed of a magnetic ball and a mounting clip mounted on the magnetic ball, the magnetic ball is mounted on the magnetic ring, and the back cover is provided with a plastic rubber buckle, and the magnetic ring can be Remove and install in plastic rubber buckle.
优选的,所述多性能蜂窝活性炭的透气孔为圆形、正六边形或矩形。Preferably, the vent hole of the multi-performance honeycomb activated carbon is circular, regular hexagon or rectangular.
多性能性蜂窝活性炭的制作方法如下:The multi-performance honeycomb activated carbon is produced as follows:
S1,椰壳10-30份、棕榈壳10-25份、核桃壳25-40份、煤质5-15份的原料进行配置混合,获得混合原料;S1, 10-30 parts of coconut shell, 10-25 parts of palm shell, 25-40 parts of walnut shell, 5-15 parts of coal material are mixed and configured to obtain mixed raw materials;
S2,将混合原料研磨粉碎至粉状,过滤除去大颗粒物质,获得研磨粉;
S2, the mixed raw material is ground and pulverized to a powder form, and the large particulate matter is removed by filtration to obtain an abrasive powder;
S3,将研磨粉加入乳化剂水溶液,将其加入捏合机中搅拌均匀,获得乳化粉末;S3, adding the grinding powder to the emulsifier aqueous solution, adding it to the kneader and stirring uniformly to obtain an emulsified powder;
S4,将乳化粉末加入装有60至4000目孔蜂窝钢模具的挤出成型机中,进行成型,得到湿的蜂窝体;S4, adding the emulsified powder to an extrusion molding machine equipped with a 60-4000 mesh honeycomb steel mold, and molding to obtain a wet honeycomb body;
S5,干燥:湿的蜂窝体干燥至水分低于3%;S5, drying: the wet honeycomb is dried to a moisture content of less than 3%;
S6,炭化及活化:按升温速度4℃/min加热到600℃,并且在此温度下炭化3小时;然后按升温速度5℃/min升温到750-850℃,持续2小时;S6, carbonization and activation: heating to 600 ° C at a heating rate of 4 ° C / min, and carbonization at this temperature for 3 hours; then heating at a temperature increase rate of 5 ° C / min to 750-850 ° C for 2 hours;
S7,置于纯净水雾化厢,并在洁净厢中24小时转入高压箱体植入甲醛催化剂;S7, placed in a pure water atomization chamber, and transferred to a high-pressure tank for implantation of formaldehyde catalyst in a clean room for 24 hours;
S8,嵌入广谱灭菌材料,封装多层过滤粗细颗粒棉。S8, embedded in a broad-spectrum sterilizing material, encapsulating multi-layer filtered coarse-grain cotton.
与现有技术相比,本发明的有益效果是:无电进出风口净化装置,无需电力驱动,结构简单,使用方便,采用本工艺制作的多性能蜂窝活性炭,致密度大,灭菌,除甲醛,气流导速和净化效果好,使用寿命长。Compared with the prior art, the beneficial effects of the invention are: no electricity inlet and outlet tuyere purifying device, no electric drive, simple structure, convenient use, multi-performance honeycomb activated carbon produced by the process, high density, sterilization, formaldehyde removal The air flow has a good speed and purification effect and a long service life.
图1为本发明的净化装置结构示意图;Figure 1 is a schematic structural view of a purification device of the present invention;
图2为净化装置无后盖结构示意图;2 is a schematic view showing the structure of the cleaning device without a back cover;
图3为万向磁球夹和磁环安装的结构示意图;3 is a schematic structural view of a universal magnetic ball clamp and a magnetic ring installation;
图4为磁环和塑料橡胶扣安装结构示意图。Figure 4 is a schematic view showing the installation structure of the magnetic ring and the plastic rubber buckle.
下面将结合本发明实施例中的附图,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。The technical solutions in the embodiments of the present invention are clearly and completely described in the following with reference to the accompanying drawings in the embodiments of the present invention. It is obvious that the described embodiments are only a part of the embodiments of the present invention, but not all embodiments. All other embodiments obtained by those skilled in the art based on the embodiments of the present invention without creative efforts are within the scope of the present invention.
请参阅图1、图2、图3和图4,一种无电进出风口净化装置,包括外壳1、多性能蜂窝活性炭2、后盖3、磁环4和万向磁球夹5,所述多性能蜂窝活
性炭2安装在外壳1内,后盖3卡装在外壳1上,所述后盖3上设有磁环4,磁环4上安装有万向磁球夹5,所述后盖3上设有密集的进气孔7,所述外壳1上设有密集的出气孔6,所述多性能蜂窝活性炭2上镶嵌有一组除菌模块8。Referring to FIG. 1 , FIG. 2 , FIG. 3 and FIG. 4 , an electric inlet and outlet tuyere purifying device comprises a casing 1 , a multi-performance honeycomb activated carbon 2 , a back cover 3 , a magnetic ring 4 and a universal magnetic ball clamp 5 , Multi-performance cellular live
The carbon 2 is mounted on the outer casing 1 , and the rear cover 3 is mounted on the outer casing 1 . The rear cover 3 is provided with a magnetic ring 4 . The magnetic ring 4 is mounted with a universal magnetic ball clamp 5 , and the rear cover 3 is mounted thereon. A dense air inlet hole 7 is provided, and the outer casing 1 is provided with a dense air outlet hole 6, and the multi-performance honeycomb activated carbon 2 is embedded with a group of sterilization modules 8.
万向磁球夹5由磁球10和安装在磁球上的安装夹9组成,磁球安装在磁环4上,所述后盖3上设有塑料橡胶扣11,所述磁环4可拆卸安装在塑料橡胶扣11内。The universal magnetic ball clamp 5 is composed of a magnetic ball 10 and a mounting clip 9 mounted on the magnetic ball. The magnetic ball is mounted on the magnetic ring 4. The rear cover 3 is provided with a plastic rubber buckle 11, and the magnetic ring 4 can be It is disassembled and installed in the plastic rubber buckle 11.
多性能蜂窝活性炭2的透气孔为圆形、正六边形或矩形。The venting holes of the multi-performance honeycomb activated carbon 2 are circular, regular hexagon or rectangular.
一种多性能蜂窝活性炭的制作方法如下:A multi-performance honeycomb activated carbon is produced as follows:
实施例1Example 1
S1,椰壳12份、棕榈壳20份、核桃壳30份、煤质12份的原料进行配置混合,获得混合原料;S1, 12 parts of coconut shell, 20 parts of palm shell, 30 parts of walnut shell, 12 parts of coal material are mixed and configured to obtain mixed raw materials;
S2,将混合原料研磨粉碎至粉状,过滤除去大颗粒物质,获得研磨粉;S2, the mixed raw material is ground and pulverized to a powder form, and the large particulate matter is removed by filtration to obtain an abrasive powder;
S3,将研磨粉加入乳化剂水溶液,将其加入捏合机中搅拌均匀,获得乳化粉末;S3, adding the grinding powder to the emulsifier aqueous solution, adding it to the kneader and stirring uniformly to obtain an emulsified powder;
S4,将乳化粉末加入装有60至4000目孔蜂窝钢模具的挤出成型机中,进行成型,得到湿的蜂窝体;S4, adding the emulsified powder to an extrusion molding machine equipped with a 60-4000 mesh honeycomb steel mold, and molding to obtain a wet honeycomb body;
S5,干燥:湿的蜂窝体干燥至水分低于3%;S5, drying: the wet honeycomb is dried to a moisture content of less than 3%;
S6,炭化及活化:按升温速度4℃/min加热到600℃,并且在此温度下炭化3小时;然后按升温速度5℃/min升温到750-850℃,持续2小时;S6, carbonization and activation: heating to 600 ° C at a heating rate of 4 ° C / min, and carbonization at this temperature for 3 hours; then heating at a temperature increase rate of 5 ° C / min to 750-850 ° C for 2 hours;
S7,置于纯净水雾化厢,并在洁净厢中24小时转入高压箱体植入甲醛催化剂;S7, placed in a pure water atomization chamber, and transferred to a high-pressure tank for implantation of formaldehyde catalyst in a clean room for 24 hours;
S8,嵌入广谱灭菌材料,封装多层过滤粗细颗粒棉。S8, embedded in a broad-spectrum sterilizing material, encapsulating multi-layer filtered coarse-grain cotton.
实施例2Example 2
S1,椰壳12份、棕榈壳21份、核桃壳28份、煤质12份的原料进行配置混合,获得混合原料;
S1, 12 parts of coconut shell, 21 parts of palm shell, 28 parts of walnut shell, 12 parts of coal material are mixed and configured to obtain mixed raw materials;
S2,将混合原料研磨粉碎至粉状,过滤除去大颗粒物质,获得研磨粉;S2, the mixed raw material is ground and pulverized to a powder form, and the large particulate matter is removed by filtration to obtain an abrasive powder;
S3,将研磨粉加入乳化剂水溶液,将其加入捏合机中搅拌均匀,获得乳化粉末;S3, adding the grinding powder to the emulsifier aqueous solution, adding it to the kneader and stirring uniformly to obtain an emulsified powder;
S4,将乳化粉末加入装有60至4000目孔蜂窝钢模具的挤出成型机中,进行成型,得到湿的蜂窝体;S4, adding the emulsified powder to an extrusion molding machine equipped with a 60-4000 mesh honeycomb steel mold, and molding to obtain a wet honeycomb body;
S5,干燥:湿的蜂窝体干燥至水分低于3%;S5, drying: the wet honeycomb is dried to a moisture content of less than 3%;
S6,炭化及活化:按升温速度4℃/min加热到700℃,并且在此温度下炭化3小时;然后按升温速度5℃/min升温到780℃,持续2小时;S6, carbonization and activation: heating to 700 ° C at a heating rate of 4 ° C / min, and carbonization at this temperature for 3 hours; then heating at a temperature increase rate of 5 ° C / min to 780 ° C for 2 hours;
S7,置于纯净水雾化厢,并在洁净厢中24小时转入高压箱体植入甲醛催化剂;S7, placed in a pure water atomization chamber, and transferred to a high-pressure tank for implantation of formaldehyde catalyst in a clean room for 24 hours;
S8,嵌入广谱灭菌材料,封装多层过滤粗细颗粒棉。S8, embedded in a broad-spectrum sterilizing material, encapsulating multi-layer filtered coarse-grain cotton.
实施例3Example 3
S1,椰壳23份、棕榈壳23份、核桃壳35份、煤质12份的原料进行配置混合,获得混合原料;S1, 23 parts of coconut shell, 23 parts of palm shell, 35 parts of walnut shell, 12 parts of coal material are mixed and arranged to obtain mixed raw materials;
S2,将混合原料研磨粉碎至粉状,过滤除去大颗粒物质,获得研磨粉;S2, the mixed raw material is ground and pulverized to a powder form, and the large particulate matter is removed by filtration to obtain an abrasive powder;
S3,将研磨粉加入乳化剂水溶液,将其加入捏合机中搅拌均匀,获得乳化粉末;S3, adding the grinding powder to the emulsifier aqueous solution, adding it to the kneader and stirring uniformly to obtain an emulsified powder;
S4,将乳化粉末加入装有60至4000目孔蜂窝钢模具的挤出成型机中,进行成型,得到湿的蜂窝体;S4, adding the emulsified powder to an extrusion molding machine equipped with a 60-4000 mesh honeycomb steel mold, and molding to obtain a wet honeycomb body;
S5,干燥:湿的蜂窝体干燥至水分低于3%;S5, drying: the wet honeycomb is dried to a moisture content of less than 3%;
S6,炭化及活化:按升温速度4℃/min加热到700℃,并且在此温度下炭化3小时;然后按升温速度5℃/min升温到810℃,持续2小时;S6, carbonization and activation: heating to 700 ° C at a heating rate of 4 ° C / min, and carbonization at this temperature for 3 hours; then heating at a temperature increase rate of 5 ° C / min to 810 ° C for 2 hours;
S7,置于纯净水雾化厢,并在洁净厢中24小时转入高压箱体植入甲醛催化剂;S7, placed in a pure water atomization chamber, and transferred to a high-pressure tank for implantation of formaldehyde catalyst in a clean room for 24 hours;
S8,嵌入广谱灭菌材料,封装多层过滤粗细颗粒棉。
S8, embedded in a broad-spectrum sterilizing material, encapsulating multi-layer filtered coarse-grain cotton.
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
While the embodiments of the present invention have been shown and described, it will be understood by those skilled in the art The scope of the invention is defined by the appended claims and their equivalents.
Claims (4)
- 一种无电进出风口净化装置,其特征在于:包括外壳(1)、多性能蜂窝活性炭(2)、后盖(3)、磁环(4)和万向磁球夹(5),所述多性能蜂窝活性炭(2)安装在外壳(1)内,后盖(3)卡装在外壳(1)上,所述后盖(3)上设有磁环(4),磁环(4)上安装有万向磁球夹(5),所述后盖(3)上设有密集的进气孔(7),所述外壳(1)上设有密集的出气孔(6),所述多性能蜂窝活性炭(2)上镶嵌有一组除菌模块(8)。An electric inlet and outlet tuyere purifying device, comprising: a casing (1), a multi-performance honeycomb activated carbon (2), a back cover (3), a magnetic ring (4) and a universal magnetic ball clamp (5), The multi-performance honeycomb activated carbon (2) is installed in the outer casing (1), the rear cover (3) is mounted on the outer casing (1), and the rear cover (3) is provided with a magnetic ring (4), a magnetic ring (4) Mounted thereon is a universal magnetic ball clamp (5), the rear cover (3) is provided with a dense air inlet hole (7), and the outer casing (1) is provided with a dense air outlet hole (6), A multi-performance honeycomb activated carbon (2) is embedded with a set of sterilization modules (8).
- 根据权利要求1所述的无电进出风口净化装置,其特征在于:所述万向磁球夹(5)由磁球(10)和安装在磁球上的安装夹(9)组成,所述磁球安装在磁环(4)上,所述后盖(3)上设有塑料橡胶扣(11),所述磁环(4)可拆卸安装在塑料橡胶扣(11)内。The electric inlet and outlet tuyere purifying apparatus according to claim 1, wherein the universal magnetic ball clamp (5) is composed of a magnetic ball (10) and a mounting clip (9) mounted on the magnetic ball, The magnetic ball is mounted on the magnetic ring (4), and the back cover (3) is provided with a plastic rubber buckle (11), and the magnetic ring (4) is detachably mounted in the plastic rubber buckle (11).
- 根据权利要求1所述的无电进出风口净化装置,其特征在于:所述多性能蜂窝活性炭(2)的透气孔为圆形、正六边形或矩形。The electric inlet and outlet tuyere purifying apparatus according to claim 1, characterized in that the vent hole of the multi-performance honeycomb activated carbon (2) is circular, regular hexagon or rectangular.
- 一种权利要求1所述的多性能蜂窝活性炭的制作方法,其特征在于:A method for fabricating a multi-performance honeycomb activated carbon according to claim 1, wherein:S1,椰壳10-30份、棕榈壳10-25份、核桃壳25-40份、煤质5-15份的原料进行配置混合,获得混合原料;S1, 10-30 parts of coconut shell, 10-25 parts of palm shell, 25-40 parts of walnut shell, 5-15 parts of coal material are mixed and configured to obtain mixed raw materials;S2,将混合原料研磨粉碎至粉状,过滤除去大颗粒物质,获得研磨粉;S2, the mixed raw material is ground and pulverized to a powder form, and the large particulate matter is removed by filtration to obtain an abrasive powder;S3,将研磨粉加入乳化剂水溶液,将其加入捏合机中搅拌均匀,获得乳化粉末;S3, adding the grinding powder to the emulsifier aqueous solution, adding it to the kneader and stirring uniformly to obtain an emulsified powder;S4,将乳化粉末加入装有60至4000目孔蜂窝钢模具的挤出成型机中,进行成型,得到湿的蜂窝体;S4, adding the emulsified powder to an extrusion molding machine equipped with a 60-4000 mesh honeycomb steel mold, and molding to obtain a wet honeycomb body;S5,干燥:湿的蜂窝体干燥至水分低于3%;S5, drying: the wet honeycomb is dried to a moisture content of less than 3%;S6,炭化及活化:按升温速度4℃/min加热到600℃,并且在此温度下炭化3小时;然后按升温速度5℃/min升温到750-850℃,持续2小时;S6, carbonization and activation: heating to 600 ° C at a heating rate of 4 ° C / min, and carbonization at this temperature for 3 hours; then heating at a temperature increase rate of 5 ° C / min to 750-850 ° C for 2 hours;S7,置于纯净水雾化厢,并在洁净厢中24小时转入高压箱体植入甲醛催化剂; S7, placed in a pure water atomization chamber, and transferred to a high-pressure tank for implantation of formaldehyde catalyst in a clean room for 24 hours;S8,嵌入广谱灭菌材料,封装多层过滤粗细颗粒棉。 S8, embedded in a broad-spectrum sterilizing material, encapsulating multi-layer filtered coarse-grain cotton.