WO2017102004A1 - Procédé de soudage de rails - Google Patents

Procédé de soudage de rails Download PDF

Info

Publication number
WO2017102004A1
WO2017102004A1 PCT/EP2015/080181 EP2015080181W WO2017102004A1 WO 2017102004 A1 WO2017102004 A1 WO 2017102004A1 EP 2015080181 W EP2015080181 W EP 2015080181W WO 2017102004 A1 WO2017102004 A1 WO 2017102004A1
Authority
WO
WIPO (PCT)
Prior art keywords
welding
laser
previous
rails
arc
Prior art date
Application number
PCT/EP2015/080181
Other languages
English (en)
Inventor
David Jan VERMEIJ
Arie Gerrit OVEREEM
Jaap Marinus MICHORIUS
Original Assignee
Strukton Rail B.V.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Strukton Rail B.V. filed Critical Strukton Rail B.V.
Priority to PCT/EP2015/080181 priority Critical patent/WO2017102004A1/fr
Publication of WO2017102004A1 publication Critical patent/WO2017102004A1/fr

Abstract

La présente invention concerne un procédé de soudage de rails à des extrémités frontales opposées espacées des rails pendant lequel un matériau de soudage est introduit dans un espacement entre lesdites extrémités frontales. Une partie du soudage desdites extrémités frontales est effectuée au moyen d'un faisceau laser pour exécuter un processus de soudage au laser et une autre partie du soudage desdites extrémités frontales et de la distribution de matériau de soudage est effectuée par un processus de soudage à l'arc.
PCT/EP2015/080181 2015-12-17 2015-12-17 Procédé de soudage de rails WO2017102004A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/EP2015/080181 WO2017102004A1 (fr) 2015-12-17 2015-12-17 Procédé de soudage de rails

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/EP2015/080181 WO2017102004A1 (fr) 2015-12-17 2015-12-17 Procédé de soudage de rails

Publications (1)

Publication Number Publication Date
WO2017102004A1 true WO2017102004A1 (fr) 2017-06-22

Family

ID=55069824

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2015/080181 WO2017102004A1 (fr) 2015-12-17 2015-12-17 Procédé de soudage de rails

Country Status (1)

Country Link
WO (1) WO2017102004A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020233945A1 (fr) * 2019-05-22 2020-11-26 Stahlkontor Gmbh & Co. Kg Procédé hybride laser double
CN114059405A (zh) * 2021-12-10 2022-02-18 芜湖越捷锻造有限公司 一种用于轨道高效无缝焊接装置

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5605283A (en) * 1991-12-03 1997-02-25 Fronius Schweissmaschinen Kg. Austria Weld joint between two rails arranged behind each other along a rail track
US6166347A (en) * 1999-07-16 2000-12-26 Lincoln Global, Inc. Method and system for welding steel rails
US20120261389A1 (en) * 2011-04-13 2012-10-18 General Electric Company Hybrid welding apparatus and system and method of welding
FR3008635A1 (fr) * 2013-07-16 2015-01-23 Areva Np Dispositif de soudage en chanfrein etroit

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5605283A (en) * 1991-12-03 1997-02-25 Fronius Schweissmaschinen Kg. Austria Weld joint between two rails arranged behind each other along a rail track
US6166347A (en) * 1999-07-16 2000-12-26 Lincoln Global, Inc. Method and system for welding steel rails
US20120261389A1 (en) * 2011-04-13 2012-10-18 General Electric Company Hybrid welding apparatus and system and method of welding
FR3008635A1 (fr) * 2013-07-16 2015-01-23 Areva Np Dispositif de soudage en chanfrein etroit

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020233945A1 (fr) * 2019-05-22 2020-11-26 Stahlkontor Gmbh & Co. Kg Procédé hybride laser double
CN114059405A (zh) * 2021-12-10 2022-02-18 芜湖越捷锻造有限公司 一种用于轨道高效无缝焊接装置
CN114059405B (zh) * 2021-12-10 2023-09-01 株洲三龙特种精密铸造有限公司 一种用于轨道高效无缝焊接装置

Similar Documents

Publication Publication Date Title
US8884183B2 (en) Welding process and a welding arrangement
EP1534460B2 (fr) Soudage laser par oscillation du faisceau
US20040188395A1 (en) Laser-hybrid welding with beam oscillation
US20170252848A1 (en) Method and system of using comsumable with weld puddle
EP0098306B1 (fr) Procede de soudage utilisant un rayon laser
US7253377B2 (en) System and method of joining overlapping workpieces
EP2698223B1 (fr) Procédé de soudage pour la réparation de sections épaisses utilisant deux dispositifs de soudage à l'arc et un dispositif de soudage laser
CN101362256A (zh) 一种激光-电弧复合热源窄间隙精密焊接方法
JP2015525676A (ja) ホットワイヤで接合部を形成するためのシステム及び方法
CA2942755A1 (fr) Methode et systeme d'utilisation d'une forme d'onde de soudage en courant alternatif et produit consomptible ameliore pour ameliorer le soudage d'une piece a usiner galvanisee
WO2007120408A2 (fr) Électrode à âme métallique pour soudure par passe de fond ouvert
EP2596896B1 (fr) Système et procédé de soudage avec un dispositif laser, un dispositif MIG/MAG et un dispositif TIG
US20060261045A1 (en) Multi-heat source laser brazing system and method
JP5812527B2 (ja) ホットワイヤレーザ溶接方法と装置
CN108453388A (zh) 一种t型结构件双激光诱导电弧穿透焊接方法及焊接装置
Lamas et al. Gap bridging for two modes of laser arc hybrid welding
CN114012265A (zh) 一种双束激光电弧复合单面横焊方法及装置
CN104785931B (zh) 一种等离子-埋弧复合焊接系统及其焊接方法
JP2014018816A (ja) 溶接鋼管およびその製造方法
WO2017102004A1 (fr) Procédé de soudage de rails
US8853594B2 (en) Welding method and apparatus therefor
RU2668625C1 (ru) Способ лазерно-дуговой сварки плавящимся электродом в среде защитного газа стыкового соединения сформованной трубной заготовки
JP2003001453A (ja) 複合熱源溶接法
JPH06198472A (ja) 高速レーザ溶接法
JP6092163B2 (ja) 溶接装置及び溶接方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15820093

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15820093

Country of ref document: EP

Kind code of ref document: A1