WO2017026588A1 - Procédé de préparation de film composite comprenant des fibres de carbone et une résine d'uréthane, et film composite préparé au moyen de ce dernier - Google Patents
Procédé de préparation de film composite comprenant des fibres de carbone et une résine d'uréthane, et film composite préparé au moyen de ce dernier Download PDFInfo
- Publication number
- WO2017026588A1 WO2017026588A1 PCT/KR2015/013212 KR2015013212W WO2017026588A1 WO 2017026588 A1 WO2017026588 A1 WO 2017026588A1 KR 2015013212 W KR2015013212 W KR 2015013212W WO 2017026588 A1 WO2017026588 A1 WO 2017026588A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- urethane resin
- composite film
- urethane
- carbon fiber
- film
- Prior art date
Abstract
L'invention concerne un procédé de préparation de film composite, comprenant les étapes suivantes : imprégner une résine d'uréthane liquide avec des fibres de carbone; sécher la résine d'uréthane liquide qui a été imprégnée avec les fibres de carbone, en évaporant ainsi un solvant dans la résine d'uréthane liquide; et coller un film d'uréthane sur les fibres de carbone.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2015-0112518 | 2015-08-10 | ||
KR20150112518 | 2015-08-10 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2017026588A1 true WO2017026588A1 (fr) | 2017-02-16 |
Family
ID=57983257
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2015/013212 WO2017026588A1 (fr) | 2015-08-10 | 2015-12-04 | Procédé de préparation de film composite comprenant des fibres de carbone et une résine d'uréthane, et film composite préparé au moyen de ce dernier |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2017026588A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2011093175A (ja) * | 2009-10-29 | 2011-05-12 | Inoac Corp | 繊維強化成形体及びその製造方法 |
KR20110115850A (ko) * | 2010-04-16 | 2011-10-24 | (주)월드튜브 | 나노카본액 조성물, 나노카본 수지 조성물, 나노카본 고형체, 나노카본 수지체 및 이들의 제조방법 |
KR101380173B1 (ko) * | 2013-12-18 | 2014-04-01 | (주)엠텍스텍 | 자착형 우레탄 시트 및 그것의 부착 방법 |
KR101470803B1 (ko) * | 2013-10-07 | 2014-12-08 | 주식회사 동성화학 | 열가소성 탄소섬유강화 복합재료 및 그 제조방법 |
JP2015120837A (ja) * | 2013-12-24 | 2015-07-02 | 保土谷化学工業株式会社 | 微細炭素繊維含有水系ポリウレタン樹脂溶液及びそれを用いた導電膜 |
-
2015
- 2015-12-04 WO PCT/KR2015/013212 patent/WO2017026588A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2011093175A (ja) * | 2009-10-29 | 2011-05-12 | Inoac Corp | 繊維強化成形体及びその製造方法 |
KR20110115850A (ko) * | 2010-04-16 | 2011-10-24 | (주)월드튜브 | 나노카본액 조성물, 나노카본 수지 조성물, 나노카본 고형체, 나노카본 수지체 및 이들의 제조방법 |
KR101470803B1 (ko) * | 2013-10-07 | 2014-12-08 | 주식회사 동성화학 | 열가소성 탄소섬유강화 복합재료 및 그 제조방법 |
KR101380173B1 (ko) * | 2013-12-18 | 2014-04-01 | (주)엠텍스텍 | 자착형 우레탄 시트 및 그것의 부착 방법 |
JP2015120837A (ja) * | 2013-12-24 | 2015-07-02 | 保土谷化学工業株式会社 | 微細炭素繊維含有水系ポリウレタン樹脂溶液及びそれを用いた導電膜 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
CN104527190A (zh) | 一种储油囊用tpu复合材料 | |
US10307994B2 (en) | Composite board composed of wood material | |
CA2507779A1 (fr) | Composition d'appret et ses utilisations | |
CN102164725A (zh) | 具有性质提高的表面树脂膜用于改善的性质的半预浸料材料 | |
EP3027392A1 (fr) | Procédé servant à mouler un corps dans un moule | |
EP3174681A1 (fr) | Procédé servant à mouler un corps dans un moule | |
TW201414615A (zh) | 用於提高複合材料的浸漬性的功能性膜及利用上述膜的複合材料的製備方法 | |
CN106471088A (zh) | 包含填料的聚氨酯层压粘合剂 | |
MX2010007567A (es) | Producto textil semiacabado con por lo menos una superficie provista de un adhesivo. | |
DE102014208111A1 (de) | Verfahren zur Herstellung einer Verklebung auf Permeat sensiblen Oberflächen | |
JP2007268774A (ja) | 床基材、その製造方法及び床材 | |
KR101813939B1 (ko) | 모재 재료의 공급 공간을 형성하기 위한 가요성 시트 형태의 재료와 그 제조 방법 | |
CN108589322A (zh) | 一种双面合成革及其制备方法 | |
KR20170055616A (ko) | 프리프레그, 이를 이용한 복합재 및 이의 제조 방법 | |
RU2686919C1 (ru) | Эпоксидное клеевое связующее, пленочный клей и клеевой препрег на его основе | |
WO2010042334A1 (fr) | Pellicule de polyoléfines comportant une couche barrière améliorée pour application de type airbag | |
US20160157532A1 (en) | Environmentally Friendly Wetsuit and the Fabrication Process Thereof | |
WO2017026588A1 (fr) | Procédé de préparation de film composite comprenant des fibres de carbone et une résine d'uréthane, et film composite préparé au moyen de ce dernier | |
JP6558121B2 (ja) | 化粧シート及び化粧板 | |
EP4058299B1 (fr) | Film de transfert permettant le transfert de matériaux de revêtement sur des éléments | |
JP2006263977A (ja) | 化粧板及びその製造方法 | |
US10189217B2 (en) | Method for preparing thermoplastic prepreg and thermoplastic prepreg prepared thereby | |
EP3325567A1 (fr) | Ruban adhésif pouvant notamment être employé dans un procédé de moulage d'un corps dans un moule | |
CN108597358A (zh) | 硫化轮胎标签 | |
US11001018B2 (en) | Surface-modifiable injection-molded body and method for its production |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 15901070 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 15901070 Country of ref document: EP Kind code of ref document: A1 |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 15901070 Country of ref document: EP Kind code of ref document: A1 |