WO2016175745A1 - Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol - Google Patents

Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol Download PDF

Info

Publication number
WO2016175745A1
WO2016175745A1 PCT/US2015/027818 US2015027818W WO2016175745A1 WO 2016175745 A1 WO2016175745 A1 WO 2016175745A1 US 2015027818 W US2015027818 W US 2015027818W WO 2016175745 A1 WO2016175745 A1 WO 2016175745A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
total
acetic acid
ethanol
cobalt
Prior art date
Application number
PCT/US2015/027818
Other languages
English (en)
Inventor
Heiko Weiner
Zhenhua Zhou
Victor Johnston
Original Assignee
Celanese International Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Celanese International Corporation filed Critical Celanese International Corporation
Priority to PCT/US2015/027818 priority Critical patent/WO2016175745A1/fr
Publication of WO2016175745A1 publication Critical patent/WO2016175745A1/fr

Abstract

L'invention concerne un procédé de production d'éthanol consistant à mettre en contact de l'acide acétique et de l'hydrogène dans un réacteur en présence d'un catalyseur comprenant un liant, un oxyde mixte, et au moins deux métaux promoteurs comprenant le ruthénium et le bismuth. L'oxyde mixte comprend également, de préférence, du cobalt et de l'étain.
PCT/US2015/027818 2015-04-27 2015-04-27 Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol WO2016175745A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2015/027818 WO2016175745A1 (fr) 2015-04-27 2015-04-27 Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2015/027818 WO2016175745A1 (fr) 2015-04-27 2015-04-27 Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol

Publications (1)

Publication Number Publication Date
WO2016175745A1 true WO2016175745A1 (fr) 2016-11-03

Family

ID=53180819

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2015/027818 WO2016175745A1 (fr) 2015-04-27 2015-04-27 Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol

Country Status (1)

Country Link
WO (1) WO2016175745A1 (fr)

Citations (35)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4398039A (en) 1981-05-18 1983-08-09 The Standard Oil Company Hydrogenation of carboxylic acids
US4517391A (en) 1982-06-04 1985-05-14 Basf Aktiengesellschaft Continuous preparation of ethanol
EP0175558A1 (fr) 1984-09-17 1986-03-26 EASTMAN KODAK COMPANY (a New Jersey corporation) Procédé d'hydrogénation en phase gazeuse d'acides carboxyliques en esters et alcools
US4777303A (en) 1985-04-13 1988-10-11 Bp Chemicals Limited Alcohols production by hydrogenation of carboxylic acids
US4918248A (en) 1988-06-02 1990-04-17 Kao Corporation Process for preparation of alcohols
US5149680A (en) 1987-03-31 1992-09-22 The British Petroleum Company P.L.C. Platinum group metal alloy catalysts for hydrogenation of carboxylic acids and their anhydrides to alcohols and/or esters
USRE35377E (en) 1993-05-27 1996-11-12 Steinberg; Meyer Process and apparatus for the production of methanol from condensed carbonaceous material
US5821111A (en) 1994-03-31 1998-10-13 Bioengineering Resources, Inc. Bioconversion of waste biomass to useful products
US6204417B1 (en) 1997-05-16 2001-03-20 Basf Aktiengesellschaft Method for producing aliphatic alcohols
US6232352B1 (en) 1999-11-01 2001-05-15 Acetex Limited Methanol plant retrofit for acetic acid manufacture
US6495730B1 (en) 1999-09-21 2002-12-17 Asahi Kasei Kabushiki Kaisha Catalysts for hydrogenation of carboxylic acid
US6657078B2 (en) 2001-02-07 2003-12-02 Celanese International Corporation Low energy carbonylation process
US6685754B2 (en) 2001-03-06 2004-02-03 Alchemix Corporation Method for the production of hydrogen-containing gaseous mixtures
US7608744B1 (en) 2008-07-31 2009-10-27 Celanese International Corporation Ethanol production from acetic acid utilizing a cobalt catalyst
US20100030001A1 (en) 2008-07-31 2010-02-04 Laiyuan Chen Process for catalytically producing ethylene directly from acetic acid in a single reaction zone
US20100030002A1 (en) 2008-07-31 2010-02-04 Johnston Victor J Ethylene production from acetic acid utilizing dual reaction zone process
WO2010146332A1 (fr) 2009-06-19 2010-12-23 Bp P.L.C. Procédé de déshydratation de l'éthanol pour produire de l'éthylène
US7863489B2 (en) 2008-07-31 2011-01-04 Celanese International Corporation Direct and selective production of ethanol from acetic acid utilizing a platinum/tin catalyst
US8080694B2 (en) 2008-07-31 2011-12-20 Celanese International Corporation Catalyst for gas phase hydrogenation of carboxylic acids having a support modified with a reducible metal oxide
US20120010438A1 (en) 2010-07-09 2012-01-12 Celanese International Corporation Reduced Energy Alcohol Separation Process
US20120277490A1 (en) 2011-04-26 2012-11-01 Celanese International Corporation Process to Recover Alcohol From An Ethyl Acetate Residue Stream
US20120277497A1 (en) 2011-04-26 2012-11-01 Celanese International Corporation Process to Recover Alcohol with Reduced Water From Overhead of Acid Column
US8304586B2 (en) 2010-02-02 2012-11-06 Celanese International Corporation Process for purifying ethanol
US8304587B2 (en) 2010-05-07 2012-11-06 Celanese International Corporation Process for producing ethanol using an extractive distillation column
US8309773B2 (en) 2010-02-02 2012-11-13 Calanese International Corporation Process for recovering ethanol
US8338650B2 (en) 2008-07-31 2012-12-25 Celanese International Corporation Palladium catalysts for making ethanol from acetic acid
US8350886B2 (en) 2007-02-16 2013-01-08 Autonetworks Technologies, Ltd. Vehicle-mounted video communication system and vehicle-mounted image pickup system
US8471075B2 (en) 2008-07-31 2013-06-25 Celanese International Corporation Processes for making ethanol from acetic acid
US20130178663A1 (en) 2012-01-06 2013-07-11 Celanese International Corporation Cobalt-containing hydrogenation catalysts and processes for making same
US20130190527A1 (en) * 2012-01-23 2013-07-25 Celanese International Corporation Bismuth Catalyst Composition and Process For Manufacturing Ethanol Mixture
US8501652B2 (en) 2008-07-31 2013-08-06 Celanese International Corporation Catalysts for making ethanol from acetic acid
CN103785415A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸加氢制备醇的钴铋催化剂
CN103785418A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸加氢制备醇的钴锡催化剂
CN103787827A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸选择加氢制备醇的方法
US8865609B2 (en) 2012-01-06 2014-10-21 Celanese International Corporation Hydrogenation catalysts

Patent Citations (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4398039A (en) 1981-05-18 1983-08-09 The Standard Oil Company Hydrogenation of carboxylic acids
US4517391A (en) 1982-06-04 1985-05-14 Basf Aktiengesellschaft Continuous preparation of ethanol
EP0175558A1 (fr) 1984-09-17 1986-03-26 EASTMAN KODAK COMPANY (a New Jersey corporation) Procédé d'hydrogénation en phase gazeuse d'acides carboxyliques en esters et alcools
US4777303A (en) 1985-04-13 1988-10-11 Bp Chemicals Limited Alcohols production by hydrogenation of carboxylic acids
US4804791A (en) 1985-04-13 1989-02-14 Bp Chemicals Limited Alcohols production by hydrogenation of carboxylic acids
US5149680A (en) 1987-03-31 1992-09-22 The British Petroleum Company P.L.C. Platinum group metal alloy catalysts for hydrogenation of carboxylic acids and their anhydrides to alcohols and/or esters
US4918248A (en) 1988-06-02 1990-04-17 Kao Corporation Process for preparation of alcohols
USRE35377E (en) 1993-05-27 1996-11-12 Steinberg; Meyer Process and apparatus for the production of methanol from condensed carbonaceous material
US5821111A (en) 1994-03-31 1998-10-13 Bioengineering Resources, Inc. Bioconversion of waste biomass to useful products
US6204417B1 (en) 1997-05-16 2001-03-20 Basf Aktiengesellschaft Method for producing aliphatic alcohols
US6495730B1 (en) 1999-09-21 2002-12-17 Asahi Kasei Kabushiki Kaisha Catalysts for hydrogenation of carboxylic acid
US6232352B1 (en) 1999-11-01 2001-05-15 Acetex Limited Methanol plant retrofit for acetic acid manufacture
US6657078B2 (en) 2001-02-07 2003-12-02 Celanese International Corporation Low energy carbonylation process
US6685754B2 (en) 2001-03-06 2004-02-03 Alchemix Corporation Method for the production of hydrogen-containing gaseous mixtures
US8350886B2 (en) 2007-02-16 2013-01-08 Autonetworks Technologies, Ltd. Vehicle-mounted video communication system and vehicle-mounted image pickup system
US7863489B2 (en) 2008-07-31 2011-01-04 Celanese International Corporation Direct and selective production of ethanol from acetic acid utilizing a platinum/tin catalyst
US8501652B2 (en) 2008-07-31 2013-08-06 Celanese International Corporation Catalysts for making ethanol from acetic acid
US7608744B1 (en) 2008-07-31 2009-10-27 Celanese International Corporation Ethanol production from acetic acid utilizing a cobalt catalyst
US20100030001A1 (en) 2008-07-31 2010-02-04 Laiyuan Chen Process for catalytically producing ethylene directly from acetic acid in a single reaction zone
US8080694B2 (en) 2008-07-31 2011-12-20 Celanese International Corporation Catalyst for gas phase hydrogenation of carboxylic acids having a support modified with a reducible metal oxide
US8338650B2 (en) 2008-07-31 2012-12-25 Celanese International Corporation Palladium catalysts for making ethanol from acetic acid
US20100030002A1 (en) 2008-07-31 2010-02-04 Johnston Victor J Ethylene production from acetic acid utilizing dual reaction zone process
US8471075B2 (en) 2008-07-31 2013-06-25 Celanese International Corporation Processes for making ethanol from acetic acid
US8309772B2 (en) 2008-07-31 2012-11-13 Celanese International Corporation Tunable catalyst gas phase hydrogenation of carboxylic acids
WO2010146332A1 (fr) 2009-06-19 2010-12-23 Bp P.L.C. Procédé de déshydratation de l'éthanol pour produire de l'éthylène
US8309773B2 (en) 2010-02-02 2012-11-13 Calanese International Corporation Process for recovering ethanol
US8304586B2 (en) 2010-02-02 2012-11-06 Celanese International Corporation Process for purifying ethanol
US8304587B2 (en) 2010-05-07 2012-11-06 Celanese International Corporation Process for producing ethanol using an extractive distillation column
US20120010438A1 (en) 2010-07-09 2012-01-12 Celanese International Corporation Reduced Energy Alcohol Separation Process
US20120277490A1 (en) 2011-04-26 2012-11-01 Celanese International Corporation Process to Recover Alcohol From An Ethyl Acetate Residue Stream
US20120277497A1 (en) 2011-04-26 2012-11-01 Celanese International Corporation Process to Recover Alcohol with Reduced Water From Overhead of Acid Column
US20130178663A1 (en) 2012-01-06 2013-07-11 Celanese International Corporation Cobalt-containing hydrogenation catalysts and processes for making same
US8865609B2 (en) 2012-01-06 2014-10-21 Celanese International Corporation Hydrogenation catalysts
US8975200B2 (en) 2012-01-06 2015-03-10 Celanese International Corporation Hydrogenation catalysts with cobalt-modified supports
US20130190527A1 (en) * 2012-01-23 2013-07-25 Celanese International Corporation Bismuth Catalyst Composition and Process For Manufacturing Ethanol Mixture
CN103785415A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸加氢制备醇的钴铋催化剂
CN103785418A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸加氢制备醇的钴锡催化剂
CN103787827A (zh) 2012-10-31 2014-05-14 中国石油化工股份有限公司 羧酸选择加氢制备醇的方法

Similar Documents

Publication Publication Date Title
US9024087B2 (en) Process for making ethanol from acetic acid using acidic catalysts
US9458072B2 (en) Hydrogenation catalysts comprising a mixed oxide and processes for producing ethanol
AU2011213050B2 (en) Process for purifying ethanol
US8071806B2 (en) Integrated process for the production of vinyl acetate from acetic acid via ethylene
US8350098B2 (en) Ethanol production from acetic acid utilizing a molybdenum carbide catalyst
US8710277B2 (en) Process for making diethyl ether from acetic acid
CA2778959A1 (fr) Procede de fabrication d'ethanol a partir d'acide acetique a l'aide de catalyseurs acides
US9024088B1 (en) Hydrogenation catalysts comprising a mixed oxide comprising nickel
US8575404B2 (en) Process for recycling gas from acetic acid hydrogenation
US9353035B2 (en) Process for producing ethanol with zonal catalysts
US9382177B2 (en) Hydrogenation catalysts comprising a mixed oxide comprising a promoter metal
AU2011213125B2 (en) Process for purifying ethanol
US9540297B2 (en) Ruthenium-bismuth mixed oxide hydrogenation catalysts and processes for producing ethanol
WO2011097190A2 (fr) Procédés de maximisation de la formation d'éthanol dans l'hydrogénation d'acide acétique
US8754267B2 (en) Process for separating acetaldehyde from ethanol-containing mixtures
WO2016175747A1 (fr) Catalyseurs d'hydrogénation comprenant un oxyde mixte contenant du bismuth et procédé de production d'éthanol
WO2016175745A1 (fr) Catalyseurs d'hydrogénation d'oxyde mixte de ruthénium-bismuth et procédés pour la production d'éthanol
WO2015168021A1 (fr) Procédé de production d'éthanol avec des catalyseurs zonaux

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15722829

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15722829

Country of ref document: EP

Kind code of ref document: A1