WO2016109544A1 - Coextruded, crosslinked multilayer polyolefin foam structures from recycled polyolefin material and methods of making the same - Google Patents
Coextruded, crosslinked multilayer polyolefin foam structures from recycled polyolefin material and methods of making the same Download PDFInfo
- Publication number
- WO2016109544A1 WO2016109544A1 PCT/US2015/067875 US2015067875W WO2016109544A1 WO 2016109544 A1 WO2016109544 A1 WO 2016109544A1 US 2015067875 W US2015067875 W US 2015067875W WO 2016109544 A1 WO2016109544 A1 WO 2016109544A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- foam
- polypropylene
- polyethylene
- multilayer
- Prior art date
Abstract
Description
Claims