WO2016091691A1 - Procédé fischer-tropsch utilisant un catalyseur réduit en cobalt supporté - Google Patents

Procédé fischer-tropsch utilisant un catalyseur réduit en cobalt supporté Download PDF

Info

Publication number
WO2016091691A1
WO2016091691A1 PCT/EP2015/078415 EP2015078415W WO2016091691A1 WO 2016091691 A1 WO2016091691 A1 WO 2016091691A1 EP 2015078415 W EP2015078415 W EP 2015078415W WO 2016091691 A1 WO2016091691 A1 WO 2016091691A1
Authority
WO
WIPO (PCT)
Prior art keywords
cobalt
catalyst
carbon monoxide
gas
hydrogen
Prior art date
Application number
PCT/EP2015/078415
Other languages
English (en)
Inventor
Ewen Ferguson
Piotr KRAWIEC
Matthew James WELLS
Original Assignee
Bp P.L.C.
Johnson Matthey Davy Technologies Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bp P.L.C., Johnson Matthey Davy Technologies Limited filed Critical Bp P.L.C.
Publication of WO2016091691A1 publication Critical patent/WO2016091691A1/fr

Abstract

L'invention concerne un procédé pour la conversion de charge comprenant un mélange d'hydrogène et de monoxyde de carbone en hydrocarbures, l'hydrogène et le monoxyde de carbone dans la charge étant présents dans un rapport de 1:9 à 9:1 en volume, le procédé comprenant l'étape consistant à mettre en contact la charge à température élevée et à pression atmosphérique ou élevée avec un catalyseur comprenant de l'oxyde de zinc et du cobalt, le catalyseur comprenant initialement de 20 % à 95 % de cobalt métallique en poids de cobalt.
PCT/EP2015/078415 2014-12-12 2015-12-02 Procédé fischer-tropsch utilisant un catalyseur réduit en cobalt supporté WO2016091691A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP14197776 2014-12-12
EP14197776.9 2014-12-12

Publications (1)

Publication Number Publication Date
WO2016091691A1 true WO2016091691A1 (fr) 2016-06-16

Family

ID=52354670

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2015/078415 WO2016091691A1 (fr) 2014-12-12 2015-12-02 Procédé fischer-tropsch utilisant un catalyseur réduit en cobalt supporté

Country Status (1)

Country Link
WO (1) WO2016091691A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0261870A1 (fr) 1986-09-26 1988-03-30 The British Petroleum Company p.l.c. Catalyseur pour la conversion de gaz de synthèse, sa préparation et son utilisation
US20040116277A1 (en) * 2001-04-18 2004-06-17 Clarkson Jay Simon Catalyst activation process
US20040171703A1 (en) * 2001-05-25 2004-09-02 Barry Nay Fischer-tropsch process
WO2008075023A1 (fr) * 2006-12-19 2008-06-26 Bp Exploration Operating Company Limited Catalyseur de fischer-tropsch

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0261870A1 (fr) 1986-09-26 1988-03-30 The British Petroleum Company p.l.c. Catalyseur pour la conversion de gaz de synthèse, sa préparation et son utilisation
US20040116277A1 (en) * 2001-04-18 2004-06-17 Clarkson Jay Simon Catalyst activation process
US20040171703A1 (en) * 2001-05-25 2004-09-02 Barry Nay Fischer-tropsch process
WO2008075023A1 (fr) * 2006-12-19 2008-06-26 Bp Exploration Operating Company Limited Catalyseur de fischer-tropsch

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
BARTHOLOMEW ET AL., JOURNAL OF CATALYSIS, vol. 128, 1991, pages 231 - 247

Similar Documents

Publication Publication Date Title
US20210001322A1 (en) Fischer-tropsch process using reduced cobalt catalyst
JP2018158915A (ja) ヒドロホルミル化混合物のクロムおよびニッケル不要の水素化
Beerthuis et al. Particle size effects in copper-catalyzed hydrogenation of ethyl acetate
EP2694205B1 (fr) Catalyseurs pour la conversion de gaz de synthèse en alcools
Maniecki et al. Copper-supported catalysts in methanol synthesis and water gas shift reaction
AU2015359691B2 (en) Fischer-Tropsch process using reductively-activated cobalt catalyst
Peláez et al. Synthesis of formaldehyde from dimethyl ether on alumina-supported molybdenum oxide catalyst
WO2016091696A1 (fr) Procédé de fabrication d'un catalyseur de synthèse fischer-tropsch partiellement activé par réduction et procédé de production d'hydrocarbures l'utilisant
WO2016091695A1 (fr) Processus de production d'un catalyseur de synthèse fischer-tropsch à activation réductrice, et processus de production d'hydrocarbures utilisant celui-ci
WO2012134492A1 (fr) Catalyseurs pour la conversion de gaz de synthèse en alcools
WO2016091691A1 (fr) Procédé fischer-tropsch utilisant un catalyseur réduit en cobalt supporté
WO2016091692A1 (fr) Processus de production d'un catalyseur de synthèse fischer-tropsch à activation réductrice, et processus de production d'hydrocarbures utilisant celui-ci
WO2016091694A1 (fr) Procédé de production d'un catalyseur de synthèse de fischer-tropsch supporté, partiellement activé par réduction, et procédé de production d'hydrocarbures faisant appel à celui-ci
EA041101B1 (ru) Способ фишера-тропша, проводимый с применением восстановленного катализатора на основе кобальта
JP5776872B2 (ja) 多価アルコールからのヒドロキシケトンの製造方法
Sahoo et al. Activated Carbon Supported Cesium-Promoted Molybdenum Sulfide Catalysts for Higher Alcohol Synthesis from Syngas
WO2014157015A1 (fr) Procédé de fabrication d'un composé acétylène

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15804752

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15804752

Country of ref document: EP

Kind code of ref document: A1