WO2016039800A1 - Enhanced color-preference led light sources using lag, nitride and pfs phosphors - Google Patents
Enhanced color-preference led light sources using lag, nitride and pfs phosphors Download PDFInfo
- Publication number
- WO2016039800A1 WO2016039800A1 PCT/US2015/012286 US2015012286W WO2016039800A1 WO 2016039800 A1 WO2016039800 A1 WO 2016039800A1 US 2015012286 W US2015012286 W US 2015012286W WO 2016039800 A1 WO2016039800 A1 WO 2016039800A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- light source
- composite light
- phosphor
- range
- lag
- Prior art date
Abstract
Description
Claims