WO2015196342A1 - Painted polyolefin articles - Google Patents
Painted polyolefin articles Download PDFInfo
- Publication number
- WO2015196342A1 WO2015196342A1 PCT/CN2014/080543 CN2014080543W WO2015196342A1 WO 2015196342 A1 WO2015196342 A1 WO 2015196342A1 CN 2014080543 W CN2014080543 W CN 2014080543W WO 2015196342 A1 WO2015196342 A1 WO 2015196342A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- paint
- substrate
- olefin
- block copolymer
- polypropylene
- Prior art date
Abstract
Description
Claims