WO2015172233A1

WO2015172233A1 - Method and system for manufacturing a composite tube node

Info

Publication number: WO2015172233A1
Application number: PCT/CA2015/000319
Authority: WO
Inventors: Todd Deaville; Andrea Pretzler
Original assignee: Magna International Inc
Current assignee: Magna International Inc
Priority date: 2014-05-16
Filing date: 2015-05-14
Publication date: 2015-11-19
Anticipated expiration: 2016-11-16
Also published as: DE112015002298T5; CN106457702A; US10328642B2; DE112015002298B4; US20170080652A1; CN106457702B

Abstract

A process includes disposing a mandrel assembly within a mold cavity bounded by mold forming surfaces. The mold is closed, first portions of the mandrel assembly seal against mold forming surfaces, and a continuous volume shaped as a node element is defined between second portions of the mandrel and the mold forming surfaces. A composite material is injected into the mold cavity filling the continuous volume, and cured forming the node element. The mandrel assembly is removed in sections exposing a node element opening. Tube-skeletons are inserted one each into openings of the node element, each tube-skeleton comprises foam core supported glass or carbon fabric materials. A resin material is injected into the mold cavity, such that the resin material permeates through the fabric material into a node element interior via the openings. The injected resin material is cured, thereby forming tube elements joined to the node element.

Description

METHOD AND SYSTEM FOR MANUFACTURING A COMPOSITE TUBE

NODE

CROSS-REFERENCE TO PRIOR APPLICATION

This PCT patent application claims the benefit of U.S. Provisional Patent Application Serial No. 61/994,463 filed May 16, 2014, entitled "METHOD AND SYSTEM FOR MANUFACTURING A COMPOSITE TUBE NODE", the entire disclosure of the application being considered part of the disclosure of this application and hereby incorporated by reference.

FIELD OF THE INVENTION

[0001] The present invention relates to methods and systems for forming frames having a generally tubular construction. More particularly, the present invention relates to methods and systems for forming a composite tube node and integrated composite tubes for use in vehicular applications, including bicycles and motorcycles.

BACKGROUND OF THE INVENTION

(0002] Bicycles and motorcycles typically are built on a frame comprising metallic tubular members that are either welded together or joined using lugs or other connectors. The frame may include various other elements, such as for instance a head tube for holding the front fork and for allowing it to pivot and a seat tube for receiving a seat post, etc. Other systems and assemblies are attached to the frame, such as for instance suspension systems, braking assemblies, electrical systems, a motorcycle fuel tank, etc. Further, the frame provides rigidity, dissipates vibrations, and protects other systems in the event of a crash, etc.

[0003] Composite materials are also used in the construction of bicycle and motorcycle frames. Tubes are fabricated from fiber-reinforced resin materials and are joined together, typically using a connector element that is molded and bonded to the tubes that are being joined. By way of a few specific and non-limiting examples, cast aluminum or reinforced plastic shells may be used. Unfortunately, this assembly process is slow and expensive, requires additional tooling, and results in a relatively week connection since the connector element usually must be split to go over the tubes. Further, connecting tubes in this way produces a step in the resulting joint, which is aesthetically unpleasant.

[0004) In a different approach, an entire composite frame may be fabricated as a single part. This approach involves joining together tubular structural members, either by laying up several layers of an epoxy-containing carbon-fiber strip as described in U.S. 4,900,048, or by using a complex mold with appropriate internal pressurization bladders to form pre-preg blanks into the desired shape as described in U.S. 6,340,509. Unfortunately, the above-noted approaches are labor intensive, require complex and specialized tooling, and are unsuitable for some applications.

[0005] It would therefore be beneficial to overcome at least some of the above- mentioned limitations and disadvantages.

SUMMARY OF THE INVENTION

[0006) According to an aspect of at least one embodiment of the instant invention, a process is disclosed comprising: disposing a multi-part mandrel within a cavity that is defined between opposite forming surfaces of a mold, each part of the multi-part mandrel comprising a first portion that is dimensioned to form a seal with the forming surfaces of the mold, and a second portion that is dimensioned to define a space between the multi-part mandrel and the forming surfaces of the mold; forming a composite node element in a first molding step, comprising providing a composite material within the space between each part of the multi-part mandrel and the forming surfaces of the mold, and curing the composite material with the multi-part mandrel in place; withdrawing each part of the multi-part mandrel away from the formed node element, wherein withdrawing each part exposes an opening of the node element; assembling a tube-framework, comprising inserting tube-skeletons into the openings of the node element while the node element is within the mold, each tube-skeleton comprising a foam core supporting a tube-shaped covering of a fiber-containing fabric extending along a length of the foam core; and forming a composite tube element on each of the tube-skeletons in a second molding step, comprising injecting a resin material into the mold cavity such that the resin material permeates through the fiber- containing fabric and into an interior of the node element v ia the openings, thereby joining the formed tube elements to the node element. |0007| According to an aspect of at least one embodiment of the instant invention, a process is disclosed comprising: disposing a mandrel assembly within a mold cavity that is bounded by forming surfaces of a mold; closing the mold such that first portions of the mandrel assembly seal against the forming surfaces of the mold, and such that a continuous volume having the shape of a node element is defined between second portions of the mandrel and the forming surfaces of the mold; injecting a composite material into the mold cavity to fill the continuous volume; curing the injected composite material to form the node element; removing the mandrel assembly in sections, wherein removing each mandrel section exposes an opening of the node element; inserting tube-skeletons into the openings of the node element, each tube-skeleton comprising a glass or carbon fabric material supported on a foam core; and injecting a resin material into the mold cavity such that the resin material permeates through the glass or carbon fabric material and into an interior of the node element via the openings; and curing the injected resin material, thereby forming tube elements joined to the node element.

[0008] According to an aspect of at least one embodiment of the instant invention, a system is disclosed comprising: a mold having opposite forming surfaces that define a mold cavity when the mold is in a closed condition, the opposite forming surfaces comprising first features for forming an outer surface of a node element and comprising second features for forming a first portion of an outer surface of each one of a plurality of tube elements; a multi-part mandrel fabricated from a resilient material and comprising first portions that are dimensioned for sealing against the second features of the forming surfaces of the mold, and comprising second portions that are dimensioned to define a continuous volume between the multi-part mandrel and the first features of the forming surfaces of the mold, the continuous volume having the shape of the node element; and a plurality of tube-skeletons, each tube- skeleton comprising a foam core that is encased by a fiber-containing fabric material, and each tube-skeleton being dimensioned at least at one end thereof substantially the same as the second portions of the multi-part mandrel.

[0009] According to an aspect of at least one embodiment of the instant invention, a system is disclosed comprising: a first mold having opposite forming surfaces that define a first mold cavity when the first mold is in a closed condition, the opposite forming surfaces comprising first features for forming an outer surface of a node element and comprising second features for forming a first portion of an outer surface of each tube element of a plurality of tube elements; a multi-part mandrel shaped to define a continuous volume between the multi-part mandrel and the first features of the forming surfaces of the mold, the continuous volume having the shape of the node element; a plurality of second molds, each second mold detachably mountable to the first mold and having opposite forming surfaces comprising third features for forming a second portion of the outer surface of a respective one of the plurality of tube elements; and a plurality of tube-skeletons, each tube-skeleton dimensioned to engage an inner surface of the node element, to extend away from the node element out of the first mold, and to extend into a respective second mold of the plurality of second molds, wherein the first portion and the second portion of the outer surface of each tube element of the plurality of tube elements is formed in a single molding step.

BRIEF DESCRIPTION OF THE DRAWINGS

[0010] The instant invention will now be described by way of example only, and with reference to the attached drawings, wherein similar reference numerals denote similar elements throughout the several views. It should be understood that the drawings are not necessarily to scale. In certain instances, details that are not necessary for an understanding of the disclosure or that render other details difficult to perceive have been omitted.

[001 1 ] FIG. 1A is a simplified perspective diagram showing a multi-part mandrel within a mold cavity of a first mold.

[0012) FIG. I B is a cross-sectional view taken along the line A— A in FIG. 1 A.

[0013] FIG. 2A is a simplified perspective diagram showing a composite node element fabricated with the multi-part mandrel of FIG. 1 A in place.

[0014] FIG. 2B is a cross-sectional view taken along the line B— B in FIG. 2A.

[0015] FIG. 3 A is a simplified perspective diagram showing a plurality of tube- skeletons inserted into openings of the composite node element subsequent to removing the multi-part mandrel of FIG. 1 A. [0016] FIG. 3B is a cross-sectional view taken along the line C— C in FIG. 3 A.

[0017] FIG. 4A is a simplified perspective diagram showing a plurality of second molds releasably mounted to the first mold of FIG. 1A.

[0018) FIG. 4B is a cross-sectional view taken along the line D— D in FIG. 4A.

[0019] FIG. 5A is a simplified perspective diagram showing a finished composite tube node with integrally formed composite tube sections.

[0020] FIG. 5B is a cross-sectional view taken along the line E— E in FIG. 5A.

[0021] FIG. 6 is a simplified flow diagram for a process according to an embodiment of the invention.

[0022] FIG. 7 is a simplified flow diagram for another process according to an embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0023] The following description is presented to enable a person skilled in the art to make and use the invention, and is provided in the context of a particular application and its requirements. Various modifications to the disclosed embodiments will be readily apparent to those skilled in the art, and the general principles defined herein may be applied to other embodiments and applications without departing from the scope of the invention. Thus, the present invention is not intended to be limited to the embodiments disclosed, but is to be accorded the widest scope consistent with the principles and features disclosed herein.

[0024] FIG. 1A is a simplified perspective diagram showing a multi-part mandrel 100 disposed within a mold cavity of a first mold 102, the mold cavity being defined betw een opposite forming surfaces of an upper mold part 102A and a lower mold part 102B. In the specific and non-limiting example that is illustrated in FIG. 1 A, the multi-part mandrel 100 includes three mandrel parts or segments 100A, 100B and l OOC. The mold 102 also includes external tool-locating features 104, which are used for positioning and securing additional molds (not shown in FIG. 1 A) adjacent to the mold 102, as discussed in greater detail in the following sections. Further, the mold 102 includes internal heating elements (not illustrated) for heat-curing composite materials within the mold during molding steps. Optionally, the parts lOOA-C of the multi-part mandrel 100 are pinned together or otherwise temporarily joined using not illustrated fasteners, so as to facilitate placing the multi-part mandrel 100 into the mold cavity.

[0025] Referring now to FIG. 1 B, shown is a cross-sectional view taken along the line A— A in FIG. 1 A. The mandrel part 100A is shown disposed within mold cavity 106, which is defined between a forming surface 108 A of the upper mold part 102 A and an opposite forming surface 108B of the lower mold part 102B. As shown in FIG. I B, the mandrel part 100 A has a first portion 1 10 that is dimensioned for sealing with the forming surfaces 108 A and 108B of the mold 102, a second portion 1 12 that is dimensioned to define a space 1 14 between the mandrel part 100 A and the forming surfaces 108A and 108B of the mold 102, and a third portion 1 16 joining the first portion 1 10 and the second portion 1 12. More particularly, the third portion 1 16 defines a tapered mandrel surface 1 18 between the first portion 1 10 and the second portion 1 12. As will be discussed in the following sections, the tapered mandrel surface 1 18 is for forming an inner beveled surface at a respective opening of a node element.

[0026] As is shown in FIG. 1A, each of the three mandrel parts 100A, 100B and l OOC comprises a first portion, a second portion and a third portion (not labeled in FIG. 1 A). The space that is defined between the second portion of each mandrel part 100 A, 100B and lOOC and the forming surfaces 108 A and 108B of the mold define, in aggregate, a continuous volume having the shape of the node element. In this simplified example each one of the mandrel parts 100A-C has a circular shaped cross- section in a plane that is perpendicular to a length of the respective mandrel part. As such, a generally annular space is defined between the second portion of each of the mandrel parts 100A-C and the forming surfaces 108 A and 108B of the mold 102. Optionally, at least one mandrel part has a non-circular shaped cross-section in a plane that is perpendicular to a length of said at least one mandrel part.

[0027] FIG. 2A is a simplified perspective diagram show ing a composite node element 200 that has been fabricated in the mold 102, with the multi-part mandrel 100 of FIG. 1 A in place. More particularly, a composite material is placed within the continuous volume that is defined between the second portions of each of the mandrel parts 100A-C and the forming surfaces 108A and 108B of the mold 102. The composite material substantially fills the volume between the multi-part mandrel 100 and the forming surfaces of the mold 102, and extends to the tapered mandrel surface 1 1 8 of each of the mandrel parts 100A-C. The composite material is then heat-cured using internal heating elements (not shown) of mold 102, thereby forming the node element 200.

[0028] Referring now to FIG. 2B, shown is a cross-sectional view taken along the line B— B in FIG. 2A. The node element 200 is shown between the upper and lower mold parts 102 A and 102B, respectively, and the mandrel part 100A. More particularly, the node element 200 is molded around the mandrel part 100 A, such that the mandrel part 100A forms an opening of the node 200. Further, the tapered mandrel surface 1 18 of the mandrel part 100 A forms a beveled inner surface 202 at the opening of the node 200.

[0029] By way of a specific and non-limiting example, a composite material comprising e.g., glass-fiber or carbon-fiber filled urethane or epoxy resin is injected into the volume via a resin injection port (not shown). The fibers in this specific example are relatively short, such as for instance 0.2 - 4 mm. The composite material continues to be injected until the volume is substantially filled. In this example, the multi-part mandrel 100 is optionally fabricated from silicone rubber or another material with a high coefficient of thermal expansion. During the heat-curing step the mandrel material expands and presses the composite material against the forming surfaces of the mold 102. Alternatively, the multi-part mandrel 100 is fabricated from carbon composite, steel, aluminum or another suitable material with a low coefficient of thermal expansion. In this case, the composite material is injected under sufficiently high pressure to ensure that the composite material is pressed against the forming surfaces of the mold 102.

[0030] By way of another specific and non-limiting example, a pre-preg material comprising glass- fiber or carbon-fiber in an epoxy matrix material is wrapped around the second portions of the mandrel parts 100A-C. When the multi-part mandrel 100 is placed in the mold 102 and the mold 102 is closed, the pre-preg material substantially fills the volume that has the shape of the node element. In this example, the multipart mandrel 100 is fabricated from silicone rubber or another material with a high coefficient of thermal expansion. During the heat-curing step the mandrel material expands and presses the pre-preg material against the forming surfaces of the mold 102.

[00311 Subsequent to performing the heat-curing step, and with the formed node element 200 still in the mold 102, the mandrel parts lOOA-C are withdrawn away from the formed node element 200. Removing the mandrel parts 100A-C exposes corresponding openings of the node element 200, which are in communication with one another via an open interior structure of the node element 200. FIG. 3A is a simplified perspective diagram showing a plurality of tube-skeletons 300 A, 300B and 300C inserted into the openings of the composite node element 200, subsequent to removing the multi-part mandrel 100 of FIG. 1 A.

[0032J Referring now to FIG. 3B, shown is a cross-sectional view taken along the line C— C in FIG. 3A. The tube-skeleton 300A in FIG. 3B, which is considered to be representative of the tube skeletons 300A-C, comprises a foam core 302 that supports a braided or non-woven carbon or glass fabric material 304. The foam core 302 has a first portion 306 that is dimensioned larger than a second portion 308, and a third portion 3 10 that joins the first portion 306 and the second portion 308 and that defines a tapered core surface 3 12. When the tube-skeleton 300A is inserted into the opening of the node element 200, as is illustrated in FIG. 3B, the fabric material 304 occupies the spaces between the foam core 302 and either the interior surfaces of the node element 200 or the forming surfaces 108A and 108B of the mold 102. The tapered core surface 3 12 of the foam core 302 is complementary to the inner beveled surface 202 at the opening of the node element 200. As will be apparent to one of ordinary skill in the art, the tapered core surface 3 12 and the inner beveled surface 202 facilitates the joining of the tube element to the node element absent a material step at the joint seam.

[0033] FIG. 4A is a simplified perspective diagram show ing a plurality of second molds 400 A-C releasably mounted to the first mold 102 of FIG. 1 A. In particular, each second mold 400A-C comprises a tool-locating feature (not labled) for interlocking with one of the tool-locating features 104 of the mold 102. Each second mold 400 has a mold cavity that is defined between opposite forming surfaces thereof, the mold cavity of each second mold 400A-C being aligned with a portion of the mold cavity 106 of mold 102, when in the assembled condition that is shown in FIG. 4A. Also shown in FIG. 4A is the plurality of tube-skeletons 300A-C, each of which extends out of the mold cavity 106 of mold 102 and into the mold cavity of an adjacent one of the second molds 400A-C. The mold assembly that is show n in FIG. 4A is used to form composite tube elements in a second molding step, subsequent to forming the node element 200 in a first molding step.

[0034] The second molding step comprises injecting resin via a resin injection port 402 of the second mold 400A. The resin is injected under a pressure that is sufficient to cause the resin to permeate through the fabric material 304 that is supported on the foam core 302 of tube-skeleton 300A. The resin continues to permeate through the fabric material 304, through the interior of node element 200, and then through the fabric material 304 that is supported by the foam core 302 of each of the tube- skeletons 300B and 300C. Vacuum/vent ports 404 of the second molds 400B and 400C facilitate movement of the injected resin through the mold assembly. For instance, vacuum is applied via the vacuum/vent ports 404 in order to draw the resin through the fabric material 304 and out of the second molds 400B and 400C. The injected resin is subsequently heat-cured and bonds with the node element 200, such that an integrated node/tube assembly is formed.

[0035] Referring to FIG. 4B, shown is a cross-sectional view taken along the line D— D in FIG. 4A. In particular, FIG. 4B shows injected resin material 406 that has permeated through the fabric material 304 only as far as the vertical dashed line. The resin material 406 has advanced past the inner beveled surface 202 at the opening of the node element 202, and has entered into the interior of the node element 200. As additional resin material 406 is injected via the resin source 402, the resin material 406 will continue to permeate through the fabric material 304, advancing further through the interior of the node element 200 and eventually being drawn through the second molds 400B and 400C. As noted above, the injected resin material is subsequently heat-cured to form the integrated node/tube assembly.

[0036] Fig. 5A shows the integrated node/tube assembly 500 after it has been removed from the mold assembly of FIG. 4A. FIG. 5B is a cross-sectional view taken along the line E— E in FIG. 5A. As is shown most clearly in FIG. 5B, the composite tube element 502 A and the node element 200 are joined with a step-less seam 504, and the composite tube element 502A extends through the opening and into the interior of the node element 200. In the specific and non-limiting example that is shown in FIG. 5B, the foam core 302 remains inside the composite tube element 502A subsequent to the second molding step. Optionally, the foam core 302 is removed such as for instance by using a suitable solvent liquid.

[0037] The system and method described with reference to FIGS. 1 A-5A and 1B-5B uses a first mold to form both the node element 200 as well as a portion of each of the composite tube elements 502A-C. This approach reduces the tooling that is required, results in a stronger part and reduces the finishing steps (i.e. requires no adhesives, allows less edge trimming, reduces fitting issues, etc.). The use of the releasably mounted second molds allows large and complicated tube/node assemblies to be fabricated without the need for multiple tooling sets, fitting, etc.

[0038] Referring now to FIG. 6, shown is a simplified flow diagram of a process according to an embodiment of the invention. At 600 a multi-part mandrel is disposed within a mold cavity that is defined between opposite forming surfaces of a mold. As discussed in the preceding paragraphs, each part of the multi-part mandrel comprises a first portion that is dimensioned to form a seal with the forming surfaces of the mold, and a second portion that is dimensioned to define a space between the multi-part mandrel and the forming surfaces of the mold. The individual parts of the multi-part mandrel are optionally pinned together to prevent them from separating as the multipart mandrel is being placed into the mold cavity. Optionally, the multi-part mandrel is fabricated from a material with a relatively high coefficient of thermal expansion (e.g., silicone rubber) or from a material with a relatively low coefficient of thermal expansion (e.g., carbon composite).

[0039] At 602, in a first molding step, a composite node element is formed within the space between the parts of the multi-part mandrel and the forming surfaces of the mold. More particularly, a composite material is provided w ithin the space and heat and pressure are applied in order to cure the composite material while the multi-part mandrel is in place. Optionally, the composite material is provided in the form of a glass or carbon filled urethane or epoxy resin that is injected into the space, in which case the glass or carbon fibers are relatively short (e.g. 0. 1 -4 mm). Alternatively, the composite material is provided in the form of a pre-preg material that is wrapped around the multi-part mandrel prior to disposing the multi-part mandrel in the mold cavity, in which case the glass or carbon fibers are relatively long (greater than 4 mm). When the composite material is provided in the form of a pre-preg material, then the mandrel should be fabricated from silicone rubber or another material that expands, upon heating, by an amount that is sufficient to press the pre-preg material against the forming surfaces of the mold.

[0040J At 604 each part of the multi-part mandrel is withdrawn away from the formed node element, thereby exposing openings of the node element. The openings of the node element are in communication with one another via an open internal structure of the node element, which is the result of the presence of the mandrel within the mold cavity during the first molding step. At 606 a tube-framework is assembled, which comprises inserting tube-skeletons into the openings of the node element while the node element is still within the mold. In particular, each tube- skeleton comprises a foam core supporting a tube-shaped covering of a fiber- containing fabric extending along a length of the foam core. At 608, in a second molding step, a composite tube element is formed on each of the tube-skeletons, which comprises injecting a resin material into the mold cavity such that the resin material permeates through the fiber-containing fabric and into an interior of the node element via the openings. The injected resin material is heat-cured, thereby joining the formed tube elements to the node element to form an integrated node/tube assembly.

[004 lj Referring now to FIG. 7, shown is a simplified flow diagram of a process according to an embodiment of the invention. At 700 a mandrel assembly is disposed within a mold cavity that is bounded by forming surfaces of a mold. In particular, the mandrel assembly is a multi-part mandrel. The mandrel assembly comprises first portions that are dimensioned to form a seal with the forming surfaces of the mold, and second portions that are dimensioned to define a space between the multi-part mandrel and the forming surfaces of the mold. The individual parts of the multi-part mandrel are optionally pinned together to prevent them from separating as the multipart mandrel is being placed into the mold cavity. Optionally, the multi-part mandrel is fabricated from a material with a relatively high coefficient of thermal expansion (e.g., silicone rubber) or from a material with a relatively low coefficient of thermal expansion (e.g., carbon).

[0042] At 702 the mold is closed, such that the first portions of the mandrel assembly seal against the forming surfaces of the mold, and such that a continuous volume having the shape of a node element is defined between the second portions of the mandrel and the forming surfaces of the mold. At 704 a composite material is injected into the mold cavity to fill the continuous volume. For instance, the composite material is a glass or carbon fiber-filled urethane or epo y resin. At 706 the injected composite material is cured, so as to form the node element. At 708 the mandrel assembly is removed in sections, wherein removing each mandrel section exposes an opening of the node element. At 710 tube-skeletons are inserted into the openings of the node element, each tube-skeleton comprising a glass or carbon fabric material that is supported on a foam core. At 712 a resin material is injected into the mold cavity such that the resin material permeates through the glass or carbon fabric material and into an interior of the node element via the openings. At 714 the injected resin material is cured, thereby forming tube elements joined to the node element.

[0043] While the above description constitutes a plurality of embodiments of the present invention, it will be appreciated that the present invention is susceptible to further modification and change without departing from the fair meaning of the accompanying claims.

Claims

CLAIMS What is claimed is:

1. A process, comprising:

disposing a multi-part mandrel within a cavity that is defined between opposite forming surfaces of a mold, each part of the multi-part mandrel comprising a first portion that is dimensioned to form a seal with the forming surfaces of the mold, and a second portion that is dimensioned to define a space between the multi-part mandrel and the forming surfaces of the mold;

forming a composite node element in a first molding step, comprising providing a composite material within the space between each part of the multi-part mandrel and the forming surfaces of the mold, and curing the composite material with the multi-part mandrel in place;

withdrawing each part of the multi-part mandrel away from the formed node element, wherein withdrawing each part exposes an opening of the node element; assembling a tube-framework, comprising inserting tube-skeletons into the openings of the node element while the node element is within the mold, each tube- skeleton comprising a foam core supporting a tube-shaped covering of a fiber- containing fabric extending along a length of the foam core; and

forming a composite tube element on each of the tube-skeletons in a second molding step, comprising injecting a resin material into the mold cavity such that the resin material permeates through the fiber-containing fabric and into an interior of the node element via the openings, thereby joining the formed tube elements to the node element.

2. The process according to claim 1, wherein the space between each part of the multipart mandrel and the forming surfaces of the mold, in aggregate, define a continuous volume having the shape of the node element.

3. The process according to claim 2, wherein providing the composite material comprises providing a prepreg material within the space between each part of the multi-part mandrel and the forming surfaces of the mold.

4. The process according to claim 3, wherein the multi-part mandrel is fabricated from silicone rubber.

5. The process according to claim 2, wherein providing the composite material comprises injecting a fiber-filled resin material into the space between each part of the multi-part mandrel and the forming surfaces of the mold.

6. The process according to claim 1 , wherein each part of the multi-part mandrel comprises a third portion joining the first portion and the second portion, the third portion defining a tapered surface between the first portion and the second portion, the third portion for forming an inner beveled surface at the respective opening of the node element.

7. The process according to claim 6, wherein the foam core of each tube-skeleton comprises a first portion dimensioned for being received within a respective opening of the node element, a second portion dimensioned larger than the respective opening, and a third portion joining the first portion and second portion, the third portion of the tube-skeleton for overlapping with the beveled surface at the respective opening when the first portion is received within the respective opening.

8. The process according to claim 1 , wherein the node element is formed within a portion of the mold and wherein the tube elements are formed within respective portions of the same mold.

9. The process according to claim 1 , wherein forming the composite tube element on at least one of the tube-skeletons in the second molding step comprises disposing a second mold adjacent to the mold such that the at least one of the tube-skeletons extends out of the mold and into the second mold, and wherein the injected resin material permeates through the fiber-containing fabric between the mold and the second mold.

10. A process, comprising:

disposing a mandrel assembly within a mold cavity that is bounded by forming surfaces of a mold; closing the mold such that first portions of the mandrel assembly seal against the forming surfaces of the mold, and such that a continuous volume having the shape of a node element is defined between second portions of the mandrel and the forming surfaces of the mold;

injecting a composite material into the mold cavity to fill the continuous volume;

curing the injected composite material to form the node element;

removing the mandrel assembly in sections, wherein removing each mandrel section exposes an opening of the node element;

inserting tube-skeletons into the openings of the node element, each tube- skeleton comprising a glass or carbon fabric material supported on a foam core; and injecting a resin material into the mold cavity such that the resin material permeates through the glass or carbon fabric material and into an interior of the node element via the openings; and

curing the injected resin material, thereby forming tube elements joined to the node element.

1 1 . The process according to claim 10, wherein the mandrel assembly is fabricated from silicone rubber.

12. The process according to claim 10, wherein each mandrel section comprises a feature that is shaped to form an inner beveled surface at the respective opening of the node element.

13. The process according to claim 12, wherein the foam core of each tube-skeleton comprises a first portion dimensioned for being received within a respective opening of the node element, a second portion dimensioned larger than the respective opening, and a third portion joining the first portion and second portion, the third portion of the tube-skeleton for overlapping with the beveled surface at the respective opening when the first portion is received within the respective opening.

14. The process according to claim 10, wherein the node element is formed within a portion of the mold and wherein the tube elements are formed within respective portions of the same mold.

15. The process according to claim 10, wherein forming at least one of the tube elements comprises disposing a second mold adjacent to the mold, and wherein the injected resin material permeates through the glass or carbon fabric material between the mold and the second mold during forming of the at least one of the tube elements.

16. A system, comprising:

a mold having opposite forming surfaces that define a mold cavity when the mold is in a closed condition, the opposite forming surfaces comprising first features for forming an outer surface of a node element and comprising second features for forming a first portion of an outer surface of each one of a plurality of tube elements; a multi-part mandrel fabricated from a resilient material and comprising first portions that are dimensioned for sealing against the second features of the forming surfaces of the mold, and comprising second portions that are dimensioned to define a continuous volume between the multi-part mandrel and the first features of the forming surfaces of the mold, the continuous volume having the shape of the node element; and

a plurality of tube-skeletons, each tube-skeleton comprising a foam core that is encased by a fiber-containing fabric material, and each tube-skeleton being dimensioned at least at one end thereof substantially the same as the second portions of the multi-part mandrel.

17. The system according to claim 16, wherein the multi-part mandrel is fabricated from silicone rubber.

18. The system according to claim 16, wherein each part of the multi-part mandrel comprises a third portion, the third portion joining a respective first portion and a respective second portion and defining a tapered surface between the respective first portion and the respective second portion, the third portion for forming an inner beveled surface at a respective opening of the node element.

19. The system according to claim 1 8, wherein the foam core of each tube-skeleton comprises a complementary feature for seating against the inner beveled surface at the respective opening of the node element.

20. The system according to claim 16, comprising a second mold having opposite forming surfaces that define a second mold cavity when the second mold is in a closed condition, the opposite forming surfaces of the second mold comprising third features for forming a second portion of the outer surface of one of the plurality of tube elements, wherein the first portion and the second portion of the outer surface of the one of the plurality of tube elements is formed in a single molding step.

21 . The system according to claim 20, wherein the mold comprises a tool-locating feature and wherein the second mold comprises a complementary feature for releasably engaging the tool-locating feature such that the second mold cavity is aligned with the mold cavity.

22. A system, comprising:

a first mold having opposite forming surfaces that define a first mold cavity when the first mold is in a closed condition, the opposite forming surfaces comprising first features for forming an outer surface of a node element and comprising second features for forming a first portion of an outer surface of each tube element of a plurality of tube elements;

a multi-part mandrel shaped to define a continuous volume between the multi-part mandrel and the first features of the forming surfaces of the mold, the continuous volume having the shape of the node element;

a plurality of second molds, each second mold detachably mountable to the first mold and having opposite forming surfaces comprising third features for forming a second portion of the outer surface of a respective one of the plurality of tube elements; and

a plurality of tube-skeletons, each tube-skeleton dimensioned to engage an inner surface of the node element, to extend away from the node element out of the first mold, and to extend into a respective second mold of the plurality of second molds,

wherein the first portion and the second portion of the outer surface of each tube element of the plurality of tube elements is formed in a single molding step. a plurality of second molds, each second mold detachably mountable to the first mold and having opposite forming surfaces comprising third features for forming a second portion of the outer surface of a respective one of the plurality of tube elements; and

a plurality of tube-skeletons, each tube-skeleton dimensioned to engage an inner surface of the node element, to extend away from the node element out of the first mold, and to extend into a respective second mold of the plurality of second molds, wherein the first portion and the second portion of the outer surface of each tube element of the plurality of tube elements is formed in a single molding step.

23. The system according to claim 22, wherein the multi-part mandrel is fabricated from silicone rubber.

24. The system according to claim 22, wherein the multi-part mandrel comprises first portions that are dimensioned for sealing against the second features of the opposite forming surfaces of the mold, and second portions that are dimensioned to define the continuous volume between the multi-part mandrel and the first features of the opposite forming surfaces of the mold.

25. The system according to claim 24, wherein each part of the multi-part mandrel comprises a third portion, the third portion joining a respective first portion and a respective second portion and defining a tapered surface between the respective first portion and the respective second portion, the third portion for forming an inner beveled surface at a respective opening of the node element.

26. The system according to claim 25, wherein each tube-skeleton comprising a foam core that is encased by a fiber-containing fabric material.

27. The system according to claim 26, wherein the foam core of each tube-skeleton comprises a complementary feature for seating against the inner beveled surface at the respective opening of the node element.