WO2015114222A1 - Duplex stainless steel - Google Patents
Duplex stainless steel Download PDFInfo
- Publication number
- WO2015114222A1 WO2015114222A1 PCT/FI2015/050065 FI2015050065W WO2015114222A1 WO 2015114222 A1 WO2015114222 A1 WO 2015114222A1 FI 2015050065 W FI2015050065 W FI 2015050065W WO 2015114222 A1 WO2015114222 A1 WO 2015114222A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- stainless steel
- less
- austenitic stainless
- steel according
- Prior art date
Abstract
Description
Claims