WO2015113128A1 - Product from precipitated calcium carbonate, or so-called lime sludge, produced in the causticizing system in the cellulose industry, and used as an anti-pitch product in the manufacture of cellulose - Google Patents
Product from precipitated calcium carbonate, or so-called lime sludge, produced in the causticizing system in the cellulose industry, and used as an anti-pitch product in the manufacture of cellulose Download PDFInfo
- Publication number
- WO2015113128A1 WO2015113128A1 PCT/BR2014/000376 BR2014000376W WO2015113128A1 WO 2015113128 A1 WO2015113128 A1 WO 2015113128A1 BR 2014000376 W BR2014000376 W BR 2014000376W WO 2015113128 A1 WO2015113128 A1 WO 2015113128A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- product
- cellulose
- calcium carbonate
- manufacture
- pitch
- Prior art date
Abstract
The present invention patent relates to a product to be used as an anti-pitch product in the manufacture of cellulose, this product being precipitated calcium carbonate, the so-called lime sludge produced in the causticizing system in the cellulose industry, and product obtained by this process, pertaining to the chemical field, specifically generated and produced during the causticizing process.
Description
PRODUTO A SER UTILIZADO COMO ANTI PITCH NA PRODUCT TO BE USED AS ANTI PITCH IN
FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE MANUFACTURE OF CELLULOSE WITH THAT CARBONATE
CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFICAÇÃO DO PROCESSO DAPRECIPITATED CALCIUM KNOWN AS THE "LIME MUD" GENERATED IN THE PROCESS OF CAUSIFICATION OF THE
INDÚSTRIA DA CELULOSE CELLULOSE INDUSTRY
[1] Trata-.se a presente patente de invenção, de um produto a ser utilizado como anti pitch na fabricação de celulose sendo esse o carbonato de cálcio precipitado conhecido como "lama de cal" gerado no sistema de caustificação do processo da indústria da celulose, pertencente ao setor químico, particularmente trata-se de um processo para aplicar o produto obtido, especificamente no licor de lignificação da madeira. [1] The present invention is a product to be used as an anti-pitch in the manufacture of cellulose, which is the precipitated calcium carbonate known as "lime sludge" generated in the process industry's caustic system. Cellulose, belonging to the chemical sector, is particularly a process to apply the obtained product, specifically in the lignification liquor of the wood.
SINOPSE DO ANTI PITCH ANTI PITCH SYNOPSIS
[2] Problemas com pitch coloidal e seu respectivo controle em indústrias de celulose e papel são relativamente comuns. [2] Problems with colloidal pitch and their control in the pulp and paper industries are relatively common.
[3] A intensidade e a metodologia dos tratamentos para seu controle dependem de vários autores relacionados com o processo e características operacionais de cada indústria. [3] The intensity and methodology of treatments for their control depend on several authors related to the process and operational characteristics of each industry.
[4] Em muitos casos, indústrias que anteriormente não apresentavam problemas com pitch, passam na atualidade a tentar conviver com estes problemas. [4] In many cases, industries that previously had no pitch problems now try to cope with these problems.
[5] Em gerai, esta situação é causada pelo aumento de produção industrial, associada em muitos casos com aumento da produção acima da capacidade nominal da indústria e pelo fechamento do circuito de efluentes industriais, assim como alta exigência de qualidade dos papéis e/ou mudança da característica da madeira utilizada para produção de celulose. [5] In general, this situation is caused by increased industrial production, often associated with increased production above industry nominal capacity and the closure of the industrial effluent circuit, as well as high demands on paper and / or paper quality. change in the characteristic of wood used for pulp production.
[6] Pitch é considerado ser uma mistura de hidrocarbonetos
resinosos com variações de composição originados basicamente da fração de extrativos da madeira. [6] Pitch is considered to be a hydrocarbon mixture. resinous with variations in composition originated basically from the fraction of wood extractives.
[7] Pitch aglomera e acumula outros materiais indesejáveis no processo formando pintas e outros tipos de sujeiras no produto final. Também se depositam em telas, feltros e em outros equipamentos do sistema industrial resultando maior manutenção e consequentemente perdas de produção. [7] Pitch agglomerates and accumulates other undesirable materials in the process by forming specks and other dirt in the final product. They are also deposited on screens, felts and other equipment of the industrial system resulting in greater maintenance and consequently production losses.
[8] Embora, existam outros meios de controle de pitch, a prática de utilização de minerais com propriedades adsorventes tem sido considerada pela indústria celulósica papeleira as mais comuns e eficientes. [8] Although there are other means of pitch control, the practice of using minerals with adsorbing properties has been considered by the paper pulp industry to be the most common and efficient.
[9] Dentre as vantagens técnicas além do controle de pitch e eliminação de outros tipos de sujeiras, os agentes adsorventes podem melhorar a alvura da polpa ou papel. A vantagem económica se origina da sua retenção pelo fato de ser de menor custo em relação à polpa. [9] Among the technical advantages beyond pitch control and elimination of other dirt, adsorbing agents can improve the whiteness of pulp or paper. The economic advantage stems from its retention because it is less expensive than pulp.
[10] Sua aplicação pode também melhorar as propriedades de maciez e opacidade, sem, entretanto afetar as propriedades de resistências dos papéis. Além desses fatos, a utilização desses agentes minerais adsorventes em combinação com agentes dispersantes pode aumentar a eficiência da remoção de micelas de pitch do sistema em um processo produtivo. [10] Its application can also improve the softness and opacity properties without, however, affecting the strength properties of papers. In addition to these facts, the use of these adsorbent mineral agents in combination with dispersing agents can increase the efficiency of removing micelles of pitch from the system in a production process.
[11] O processo de branqueamento da celulose naturalmente é utilizado através de várias fases e uma das mais importantes é a utilização de matérias primas minerais. Especificamente na aplicação de insumo como anti pitch. [11] The pulp bleaching process is naturally used through several stages and one of the most important is the use of mineral raw materials. Specifically in the application of input as anti pitch.
[12] Utiliza-se atualmente em todo o mundo o Talco (silicato de magnésio), matéria prima essa obtida de jazidas naturais e beneficiadas por grandes mineradoras que vendem com o intuito
desse mineral ser aplicado como anti pitch na fabricação da celulose. [12] Talc (magnesium silicate) is currently used worldwide, a raw material obtained from natural deposits and benefited by large mining companies that sell for this purpose. of this mineral be applied as anti pitch in the manufacture of cellulose.
[13] O pitch são miceías contidas na celulose oriundas da lignina da madeira com características oleosas e de cor escura. Por se tratar de uma contaminação na celulose as indústrias de celulose utilizam o talco para absorver essas miceías reduzindo os pitches da celulose deixando-a mesma mais branca. [13] Pitches are miceías contained in wood pulp from lignin of wood with oily characteristics and dark color. Because it is a contamination in the pulp, the pulp industries use talc to absorb these mice reducing the pitches of the pulp making it even whiter.
[14] O talco tem características tísicas muito peculiares para essa aplicação dentre elas são: [14] Talc has very peculiar physical characteristics for this application among them are:
- Forma cristalina lamelar; - Lamellar crystalline form;
- Tamanho de partícula médio entre 1 ,5 a 3 mícrons; - average particle size between 1.5 to 3 microns;
- Alvura mínima de 84 (ISO); - Minimum brightness of 84 (ISO);
- Alta absorção em óleo devido a sua porosidade natural; - High absorption in oil due to its natural porosity;
- Aspect ratio mínimo de 15:1 ; - Minimum aspect ratio of 15: 1;
- Fácil dispersão em água. - Easy dispersion in water.
[15] Portanto, essa patente trata e mostra que o produto carbonato de cálcio ppt com nome de Ecofill S tem as condições ideais para ser usado como anti pitch, devido a suas características físico e químicas entre outras, pois através do sistema de processo abaixo descrito o produto obtido atinge as seguintes condições físicas principais para a aplicação: [15] Therefore, this patent treats and shows that the ppt calcium carbonate product named Ecofill S has the ideal conditions to be used as anti pitch due to its physical and chemical characteristics among others, because through the process system below. described the product obtained meets the following main physical conditions for the application:
- Aspect ratio de mínimo 15:1 devido ao sistema de moagem diferenciado; - Aspect ratio of minimum 15: 1 due to differentiated grinding system;
- Alta absorção em óleo devido a sua porosidade obtida naturalmente na sua geração; - High absorption in oil due to its naturally obtained porosity in its generation;
- Tamanho de partícula médio entre 2 a 3 mícrons controlado pelo sistema de moagem; - Average particle size between 2 and 3 microns controlled by the grinding system;
- Forma cristalina prismática cuja tem a mesma característica de performance que a lamelar - Prismatic crystalline form which has the same performance characteristics as lamellar
- Alvura mínima de 84 (ISO).
FUNDAMENTOS DA TÉCNICA - Minimum brightness of 84 (ISO). TECHNICAL BACKGROUNDS
[16] A classificação dos minerais usados na indústria de transformação tem atingido volumes enormes nos últimos anos e a preocupação com o meio ambiente tem sido ainda maior. [16] The classification of minerals used in the manufacturing industry has reached huge volumes in recent years and concern for the environment has been even greater.
[17] De acordo com as novas tendências do mercado mundial produtivo, podemos considerar que as empresas que transformam matérias primas nobres em produto acabado de consumo deveriam ser auto-sustentáveis, ou seja, dando destino correto ao seu insumo gerado e não destinando os mesmos para aterros sanitários e nem mesmo para aplicações das quais podem comprometer o meio ambiente, devido a esse motivo o Ecofill S é uma inovação de produto obtido pela geração da indústria de celulose e através da tecnologia aplicada o mesmo poderá ser utilizado no seu mesmo processo como anti pitch, tornando o sistema totalmente auto-sustentável, 100% ecológico e com ciclo fechado de seu sistema. [17] According to new trends in the world productive market, we can consider that companies that transform noble raw materials into finished consumer products should be self-sustaining, that is, giving their generated input the correct destination and not destining them. for landfills and not even for applications that may compromise the environment, for this reason Ecofill S is a product innovation obtained by the pulp industry generation and through the applied technology it can be used in its same process as anti pitch, making the system fully self-sustaining, 100% eco-friendly and closed-loop in your system.
P8] Característica do produto carbonato de cálcio anti pitch: O carbonato de cálcio ppt da indústria de celulose é considerado atualmente um grande problema para a indústria de celulose devido ao alto teor de contaminantes, dentre eles o sódio, e têm também como característica em sua geração o fato de estar em meio líquido, ou seja, em suspensão. Isso dificulta ainda mais a sua destinação, pois, o teor de sólidos desse resíduo é muito baixo e é necessário usar desaguadores para aumentar o teor de sólidos do mesmo a fim de destiná-lo a aterros em caminhões caçamba. P8] Product Feature Calcium carbonate anti pitch: Calcium carbonate ppt from the pulp industry is currently considered a major problem for the pulp industry due to the high content of contaminants, including sodium, and also have as their characteristic generation the fact that it is in liquid medium, ie in suspension. This makes it even more difficult to dispose of because the solids content of this waste is very low and it is necessary to use dewaterers to increase the solids content of the waste in order to be landfilled on dump trucks.
[19] Sua classificação como resíduo é de alta segurança sendo um contaminante classe 2A, no entanto, é necessário um trabalho extremamente direcionado e rigoroso para sua aplicação. [19] Its classification as a waste is highly safe and a class 2A contaminant, however, extremely targeted and rigorous work is required for its application.
[20] O alto teor de sódio contido na sua composição é um fator de alto risco ao meio ambiente e a possibilidade de contaminação em
sistema produtivo é alto devido a sua fácil dispersão em meio aquoso. [20] The high sodium content of its composition is a high risk factor for the environment and the possibility of contamination in productive system is high due to its easy dispersion in aqueous medium.
[21 J Nos últimos 50 anos a indústria de celulose tem gerado esse resíduo e até o presente momento as aplicações mais comuns desse resíduo tem sido a mistura do mesmo junto a cinzas e outros onde da mesma forma ele é destinado para aterros sendo diluído em grandes proporções nos [21 J Over the last 50 years the pulp industry has generated this waste and to date the most common applications of this waste have been mixing it together with ashes and others where it is similarly intended for landfill being diluted into large proportions in
[22] De acordo com os resultados obtidos e gerações de grande escala o resíduo tem em sua composição um teor de carbonato em torno de 85%, aproximadamente 10% de sódio livre, e magnésio e sílica como os restante. [22] According to the results obtained and large-scale generations the residue has in its composition a carbonate content of around 85%, approximately 10% free sodium, and magnesium and silica as the rest.
[23] O mercado mundial tem sido bastante rigoroso com o controle de destinação desse resíduo, em específico devido ao seu alto teor de contaminante em volumes expressivos, perto de 500 mil toneladas ano. [23] The world market has been very strict with the control of disposal of this waste, in particular due to its high contaminant content in expressive volumes, close to 500 thousand tons per year.
[24] Atualmente se tenta usar a lama de carbonato na composição de compostagem, o mesmo tem aprovação devidoi sua composição química que tem componentes cujo podem ser agregados a fertilizantes, portanto não podem ser usados em grande escala nesse sistema como composto de fertilizante devido à ; necessidade de diluição por não poder ultrapassar a percentuais mínimos para não contaminar o solo com excesso de sódio [24] Currently trying to use carbonate sludge in the composting composition, it is approved because of its chemical composition which has components whose components can be added to fertilizers, so they cannot be used on a large scale in this system as a fertilizer compost due to ; need for dilution because it cannot exceed the minimum percentages so as not to contaminate the soil with excess sodium
[25] Assim, a presente patente de invenção tem como objetivo aplicar 100% do carbonato de cálcio transformando-o como matéria prima nobre para aplicações como anti pitch. [25] Thus, the present invention aims to apply 100% of calcium carbonate transforming it as prime material for anti pitch applications.
DESCRIÇÃO RESUMIDA DA INVENÇÃO BRIEF DESCRIPTION OF THE INVENTION
[26] A presente invenção apresenta um Produto a ser utilizado como anti pitch na fabricação de celulose sendo esse o carbonato de cálcio precipitado conhecido como "lama de cal" gerado1 no sistema de caustificação do processo da indústria da celulose que compreende
uma fase de preparação da lama, após o produto é enviado para o sistema de e moagem, armazenagem a úmído ou secagem e ensaque. [26] The present invention provides a product for use as anti pitch for pulp being the precipitated calcium carbonate known as "lime mud" 1 generated in the causticizing system pulp industry process comprising a sludge preparation phase, after the product is sent to the milling, wet storage or drying and bagging system.
[27] Trata-se de outra forma de tratamento para aplicação especifica. [27] This is another form of treatment for specific application.
[28] Esse processo se descreve para a aplicação especifica em anti pitch na fabricação de celulose. [28] This process is described for specific anti-pitch application in pulp making.
[29] Prepara-se o carbonato, usando o mesmo tal qual recebido, ou seja, em forma de lama. [29] Carbonate is prepared using the same as received, ie in sludge form.
[30] Através do sistema de micronização trata-se o produto para tingir uma curva granulométrica com tamanho médio de 2,0 ate 3,0 microns tamanho médio conforme anexo 1 . [30] The micronization system treats the product to dye a particle size curve with an average size of 2.0 to 3.0 average microns as shown in Annex 1.
[31] O material ao passar pelo moinho a úmido irá receber dois aditivos para manter sua performance de fluidez.utilíza-se 0,15% de poliacrilato de sódio e 0, 15% de policloreto de alumínio, onde o material ficara com viscosidade em torno de 100 a 150 cps. [31] The material passing through the wet mill will receive two additives to maintain its flow performance. 0.15% sodium polyacrylate and 0.15% aluminum polychloride are used, where the material will be viscous in viscosity. around 100 to 150 cps.
[32] Após essa ação transfere-se o material via gravidade para uma peneira vibratória de 325# e em seguida alimenta-se um tanque estático com volume de 5 m3. [32] After this action the material is transferred via gravity to a 325 # vibrating screen and then fed to a static tank with a volume of 5 m3.
[33] Após o tanque estático descarregasse o material que é transferido e estocado em tq de armazenamento de 30 m3 com agitação. Para setores que necessitam do material seco foi elaborado o processo de secagem em secadores Drum Dryer que recebe o material com máximo de 40% sólidos, essa suspensão é aspergida nas paredes do secador que esta com a temperatura em torno de 150 graus Celsius e ao entrar em contato com a parede desse a troca térmica existe evaporando a água e deixando o produto totalmente seco, apresentando um teor máximo de umídade de 1 %. [33] After the static tank has discharged the material which is transferred and stored in 30 m3 storage tq with agitation. For sectors that require dry material, the drying process has been elaborated in Drum Dryer dryers that receive the material with a maximum of 40% solids, this suspension is sprayed on the walls of the dryer that is around 150 degrees Celsius and when entering In contact with the wall of the heat exchange there is evaporating the water and leaving the product totally dry, presenting a maximum moisture content of 1%.
[34] A presente patente de invenção será melhor compreendida através da figura única anexa que representa um fluxograma do
processo,que segue abaixo. [34] The present patent will be better understood by the attached single figure which represents a flowchart of the process, which follows below.
DESCRIÇÃO DETALHADA DA INVENÇÃO DETAILED DESCRIPTION OF THE INVENTION
[35] De acordo com a figura 1 , o produto a ser utilizado como anti pitch na fabricação de celulose sendo esse o carbonato de cálcio precipitado conhecido como "lama de cal" gerado no sistema de caustificação do processo da indústria da celulose e produto obtido através do mesmo, compreende as seguintes etapas: [35] According to Figure 1, the product to be used as an anti-pitch in the manufacture of cellulose is the precipitated calcium carbonate known as "lime sludge" generated in the process pulping system of the pulp industry and product obtained. through it, it comprises the following steps:
a.- Preparação da Lama (concentração e micronização); a.- Mud preparation (concentration and micronization);
a1 .~ O lodo de carbonato é recebido em suspensão com 35% de sólidos onde recebe o policloreto de alumínio e em seguida é necessário concentrar as partículas através de uma centrífuga ate atingir 70% de sólidos {para uma boa eficiência da redução das partículas); a1. ~ Carbonate sludge is received in 35% solids suspension where it receives aluminum polychloride and then it is necessary to concentrate the particles through a centrifuge to 70% solids (for good particle reduction efficiency) ;
a2.- A suspensão recebida após a centrifugação vem em tubulação e é destinada a um tanque de mistura com alta rotação, de no máximo 800 rpm; a2.- The suspension received after centrifugation comes in tubing and is intended for a high-speed mixing tank of up to 800 rpm;
a3.- O material fica em agitação por um tempo entre 15 a 30 min, para estabilidade e homogeneização da lama com teor de sólidos em até 70%; a3.- The material is stirred for 15 to 30 min for stability and homogenization of the sludge with up to 70% solids content;
a4.- O produto é então enviado para o sistema de moagem com bomba diafragma para reduzir o tamanho da partícula, nessa fase o material recebe o poliacrilato de sódio e é passado por um moinho contínuo de alta performance atingindo um tamanho de partícula entre 2,0 a 3,0 microns. a4.- The product is then sent to the diaphragm pump grinding system to reduce particle size, at which stage the material receives the sodium polyacrylate and is passed through a high performance continuous mill reaching a particle size between 2, 0 to 3.0 microns.
e.- transporte e.- transportation
[36] O produto obtido através do processo acima descrito compreende as seguintes características: [36] The product obtained by the process described above comprises the following characteristics:
[37] Aspecto - fluido em suspensão [37] Appearance - Suspension Fluid
[38] Umídade - 30% no máximo
[39] Teor de carbonato de cálcio - 98,5% no mínimo [38] Humidity - 30% maximum [39] Calcium carbonate content - minimum 98,5%
[40] Teor de carbonato magnésio - 1 ,0% no mínimo [40] Magnesium carbonate content - not less than 1,0%
[41] Teor de Si02 - 0,1 % no máximo [41] Si0 2 content - maximum 0,1%
[42] Tamanho das partículas - 1 ,5 a 3 microns. [42] Particle size - 1.5 to 3 microns.
[43] Obs. - O produto gerado em suspensão pode ser aplicado tal qual, no entanto em alguns casos devido a distância o produto poderá ser seco em processo drum dryer e destinado ao seu uso em condições de forma de po seco com as seguintes condições físico químicas [43] Note - The product generated in suspension may be applied as it is, however in some cases due to distance the product may be drum dried and intended for use in dry powder conditions under the following conditions. physical chemicals
[44] Aspecto - seco em forma de po. [44] Appearance - dry powder.
[45] Umidade - 2% no máximo. [45] Humidity - 2% maximum.
[46] Teor de carbonato de cálcio - 98,5% no mínimo. [46] Calcium carbonate content - 98,5% minimum.
[47] Teor de carbonato magnésio - 1 ,0% no mínimo. [47] Magnesium carbonate content - not less than 1,0%.
[48] Teor de Si02 - 0,1 % no máximo. [48] Si0 2 content - maximum 0,1%.
[49] Tamanho das partículas - 1 ,5 a 3 microns. [49] Particle size - 1.5 to 3 microns.
[50] Através de análises efetuadas em institutos como Universidade [50] Through analyzes conducted at institutes such as University
Federal de Viçosa e São Carlos foram obtidos os valores citados. Federal de Viçosa and São Carlos the obtained values were obtained.
[51] Também segue anexo os estudos de aplicação como anti pitch e sua performance , estudo esse realizado na Universidade federal de [51] Also attached are application studies such as anti pitch and its performance, a study conducted at the Federal University of
Viçosa, (anexo 2)no qual prova a funcionalidade do produto como agente anti pitch. Viçosa, (annex 2) which proves the functionality of the product as an anti pitch agent.
[52] Também se apresenta os laudos de análise de composição química e distribuição de tamanho de partículas efetuados na Universidade Federal de São Carlos. [52] Also presented are the reports on analysis of chemical composition and particle size distribution made at the Federal University of São Carlos.
EXEMPLO DE OBTENÇÃO OBTAINING EXAMPLE
[53] A seguir será apresentado um exemplo de aplicação do invento para ilustrar a viabilidade prática. É apresentado com suficientes detalhes para que um "expertise" versado no assunto possa reproduzi- lo com facilidade.
[54] Este exemplo não implica em limitar a abrangência do invento. RESULTADO OBTIDO [53] An exemplary application of the invention will be presented below to illustrate practical viability. It is presented in sufficient detail so that a knowledgeable expert can easily reproduce it. [54] This example does not imply limiting the scope of the invention. RESULTS OBTAINED
[55] Segue anexo trabalho do desenvolvimento de aplicação em desempenho realizado na Universidade de Viçosa através de relatório técnico. [55] The following is an attached work on performance application development at the University of Viçosa through a technical report.
APLICAÇÃO INDUSTRIAL DO PRODUTO OBTIDO INDUSTRIAL APPLICATION OF PRODUCT OBTAINED
- Vantagens obtidas com o invento: Advantages obtained with the invention:
[56] Com o Produto a ser utilizado como anti pitch na fabricação de celulose sendo esse o carbonato de cálcio precipitado conhecido como "lama de cal" gerado no sistema de caustificação do processo da indústria da celulose e produto obtido através do mesmo, os mesmos oferecem as seguintes e extraordinárias vantagens: [56] With the Product being used as an anti-pitch in the manufacture of pulp, which is the precipitated calcium carbonate known as "lime sludge" generated in the pulp industry process caustic system and product obtained therefrom. offer the following extraordinary advantages:
- Melhoria contínua do sistema produtivo da indústria de celulose; - Continuous improvement of the pulp industry production system;
- Preservação ambiental direta pela não emissão de resíduo e redução de extração mineral natural (talco); - Direct environmental preservation by the non emission of waste and reduction of natural mineral extraction (talc);
- Sustentabilidade do processo de celulose; - Sustainability of the pulp process;
- Vantagem económica significativa; - significant economic advantage;
[57] - Ciclo fechado. [57] - Closed loop.
[58] A abrangência da presente patente de invenção, não deve ser limitada ao exemplo, mas sim, aos termos definidos nas reivindicações e seus equivalentes.
[58] The scope of the present invention should not be limited to the example but to the terms defined in the claims and their equivalents.
Claims
REIVINDICAÇÕES
1 - PRODUTO A SER UTILIZADO COMO ANTI PITCH NA FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFfCAÇÃO DO PROCESSO DA INDÚSTRIA DA CELULOSE, caracterizado pela preparação da lama (concentração e micronização). 1 - PRODUCT TO BE USED AS ANTI PITCH IN THE MANUFACTURE OF CELLULOSE BEING THAT PRECIPITATED CALCIUM CARBONATE KNOWN AS THE "LIME MUD" GENERATED IN THE CELLULOSE INDUSTRY PROCESS SYSTEM, characterized by the preparation of the mud (micron concentration and concentration).
2 - PRODUTO A SER UTILIZADO COMO ANTI PITCH NA FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFICAÇÃO DO PROCESSO DA INDÚSTRIA DA CELULOSE, caracterizado pelo fato do lodo de carbonato ser recebido em suspensão com 35% de sólidos onde recebe o policloreto de alumínio e em seguida ser necessário concentrar as partículas através de uma centrífuga ate atingir 70% de sólidos (para uma boa eficiência da redução das partículas). 2 - PRODUCT TO BE USED AS ANTI PITCH IN THE MANUFACTURE OF CELLULOSIS BEING THIS PRECIPITATED CALCIUM CARBONATE KNOWN AS THE "CALM OF LAMM" GENERATED IN THE CELLULOSIS INDUSTRY PROCESS SYSTEM, characterized by the fact that the carbonate sludge suspension is received. 35% solids where it receives aluminum polychloride and then it is necessary to concentrate the particles through a centrifuge to 70% solids (for good particle reduction efficiency).
3 ~ PRODUTO A SER UTILIZADO COMO ANTI PITCH NA FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFICAÇÃO DO PROCESSO DA INDÚSTRIA DA CELULOSE, caracterizado pelo fato da suspensão recebida após a centrifugação vir em tubulação e ser destinada a um tanque de mistura com alta rotação, de no máximo 800 rpm. 3 ~ PRODUCT TO BE USED AS ANTI PITCH IN THE MANUFACTURE OF CELLULOSE BEING THIS PRECIPITATED CALCIUM CARBONATE KNOWN AS THE "CAL LAMM" GENERATED IN THE CELLULOSE INDUSTRY PROCESS SYSTEM, characterized by the fact that the suspension received after centrifugation has come after centrifugation pipe and be intended for a high-speed mixing tank of a maximum of 800 rpm.
4 - PRODUTO A SER UTILIZADO COMO ANTI PITCH NA FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFICAÇÃO DO PROCESSO DA INDÚSTRIA DA CELULOSE, caracterizado pelo fato do material ficar em agitação por um tempo entre 15 a 30 min. para estabilidade e
homogeneização da lama com teor de sólidos em até 70%. 4 - PRODUCT TO BE USED AS ANTI PITCH IN THE MANUFACTURE OF CELLULOSE BEING THAT PRECIPITATED CALCIUM CARBONATE KNOWN AS THE "CAL LIME" GENERATED IN THE CELLULOSE INDUSTRY PROCESS SYSTEM, characterized by the fact that the material is in agitation for a while between 15 to 30 min. for stability and homogenization of sludge with solids content up to 70%.
5 - PRODUTO A SER UTILIZADO COMO ANTI PITCH NA FABRICAÇÃO DE CELULOSE SENDO ESSE O CARBONATO DE CÁLCIO PRECIPITADO CONHECIDO COMO "LAMA DE CAL" GERADO NO SISTEMA DE CAUSTIFICAÇAO DO PROCESSO DA INDÚSTRIA DA CELULOSE, caracterizado pelo fato do produto ser enviado para o sistema de moagem com bomba diafragma para reduzir o tamanho da partícula, recebendo nessa fase o material o poliacriiato de sódio e é passado por um moinho contínuo de alta performance atingindo um tamanho de partícula entre 2,0 a 3,0 microns.
5 - PRODUCT TO BE USED AS ANTI PITCH IN THE MANUFACTURE OF CELLULOSE WITH THAT PRECIPITATED CALCIUM CARBONATE KNOWN AS THE "CAL LIME" GENERATED IN THE CELLULOSIS INDUSTRY PROCESS SYSTEM, characterized by the fact that the product system is shipped to the system diaphragm pump milling to reduce particle size, the material receiving sodium polyacryate at this stage and passed through a high performance continuous mill reaching a particle size of between 2.0 to 3.0 microns.