WO2015032851A3 - Silicon-bridged pillared silicate compounds and process for their production - Google Patents
Silicon-bridged pillared silicate compounds and process for their production Download PDFInfo
- Publication number
- WO2015032851A3 WO2015032851A3 PCT/EP2014/068822 EP2014068822W WO2015032851A3 WO 2015032851 A3 WO2015032851 A3 WO 2015032851A3 EP 2014068822 W EP2014068822 W EP 2014068822W WO 2015032851 A3 WO2015032851 A3 WO 2015032851A3
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- silicon
- silicate
- pillared
- bridged
- production
- Prior art date
Abstract
The present invention relates to a process for the preparation of a pillared silicate compound comprising a layered silicate structure and bridging silicon atoms located between adjacent silicate layers of the silicate structure, wherein said bridging silicon atoms form at least one covalent bond to each of the adjacent silicate layers, said process comprising (1) providing one or more layered silicates; (2) adding said one or more layered silicates to a solvent system, wherein the resulting mixture has a pH of 5 or less; and (3) subjecting the mixture obtained in step (2) to solvothermal conditions; wherein no silicon-containing compound according to formula (I) R4-mSi[-(SiR2)n-R]m (I) is used at any point of the process up to and including step (3), wherein m is 1, 2, 3, or 4, and n is an integer greater than or equal to 0, wherein when n is equal to 0, one or more residues R are leaving groups, and wherein none of the residues R contains Si, as well as to a pillared silicate compound per se, preferably as obtained and/or obtainable according to the inventive process as well as to the use of the inventive compounds. A further process is disclosed wherein a sulfur oxoacid is present in step (2), and wherein a silicon-containing compound may or may not be used.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN2013083045 | 2013-09-06 | ||
CNPCT/CN2013/083045 | 2013-09-06 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2015032851A2 WO2015032851A2 (en) | 2015-03-12 |
WO2015032851A3 true WO2015032851A3 (en) | 2015-06-04 |
Family
ID=51492947
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/EP2014/068822 WO2015032851A2 (en) | 2013-09-06 | 2014-09-04 | Silicon-bridged pillared silicate compounds and process for their production |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2015032851A2 (en) |
Families Citing this family (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2016128917A1 (en) | 2015-02-12 | 2016-08-18 | Basf Se | Process for the preparation of a dealuminated zeolitic material having the bea framework structure |
MX2017014148A (en) | 2015-05-04 | 2018-03-15 | Basf Se | Process for the preparation of melonal. |
MX2018000606A (en) | 2015-07-15 | 2018-05-28 | Basf Se | Process for preparing an arylpropene. |
CN105536864B (en) * | 2016-01-13 | 2018-05-04 | 太原理工大学 | The preparation method of ZSM-5/EU-1 composite molecular screens with core shell structure feature |
CN110577239B (en) * | 2019-09-03 | 2020-08-04 | 华北电力大学 | Method for preparing two-dimensional metal oxide nanosheet by utilizing interlayer confinement strategy |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5980849A (en) * | 1996-09-09 | 1999-11-09 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Mesopore material, laminar silicic acid, and method of manufacturing mesopore material and laminar silicic acid |
JP2008137857A (en) * | 2006-12-03 | 2008-06-19 | National Institute Of Advanced Industrial & Technology | Method for producing high silica nanoporous body by acid-treating crystalline layered silicate at high temperature, and the high silica nanoporous body |
US20110319250A1 (en) * | 2009-03-03 | 2011-12-29 | Tokyo Institute Of Technology | Process For The Preparation Of Pillared Silicates |
US20120004332A1 (en) * | 2010-07-02 | 2012-01-05 | Tokyo Institute Of Technology | Metal-Bridged Pillared Silicate Compounds And Process For Their Production |
-
2014
- 2014-09-04 WO PCT/EP2014/068822 patent/WO2015032851A2/en active Application Filing
Patent Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US5980849A (en) * | 1996-09-09 | 1999-11-09 | Kabushiki Kaisha Toyota Chuo Kenkyusho | Mesopore material, laminar silicic acid, and method of manufacturing mesopore material and laminar silicic acid |
JP2008137857A (en) * | 2006-12-03 | 2008-06-19 | National Institute Of Advanced Industrial & Technology | Method for producing high silica nanoporous body by acid-treating crystalline layered silicate at high temperature, and the high silica nanoporous body |
US20110319250A1 (en) * | 2009-03-03 | 2011-12-29 | Tokyo Institute Of Technology | Process For The Preparation Of Pillared Silicates |
US20120004332A1 (en) * | 2010-07-02 | 2012-01-05 | Tokyo Institute Of Technology | Metal-Bridged Pillared Silicate Compounds And Process For Their Production |
Non-Patent Citations (3)
Title |
---|
FENG-SHOU XIAO ET AL: "Interlayer-Expanded Microporous Titanosilicate Catalysts with Functionalized Hydroxyl Groups", CHEMCATCHEM, vol. 3, no. 9, 11 July 2011 (2011-07-11), pages 1442 - 1446, XP055155851, ISSN: 1867-3880, DOI: 10.1002/cctc.201100144 * |
HERMANN GIES ET AL: "Interlayer Expansion of the Hydrous Layer Silicate RUB-36 to a Functionalized, Microporous Framework Silicate: Crystal Structure Analysis and Physical and Chemical Characterization", CHEMISTRY OF MATERIALS, vol. 24, no. 8, 24 April 2012 (2012-04-24), pages 1536 - 1545, XP055153244, ISSN: 0897-4756, DOI: 10.1021/cm300525u * |
TAKUJI IKEDA ET AL: "Structure Analysis of Si-Atom Pillared Lamellar Silicates Having Micropore Structure by Powder X-ray Diffraction", JOURNAL OF PHYSICAL CHEMISTRY C, vol. 114, no. 8, 4 March 2010 (2010-03-04), pages 3466 - 3476, XP055153252, ISSN: 1932-7447, DOI: 10.1021/jp912026n * |
Also Published As
Publication number | Publication date |
---|---|
WO2015032851A2 (en) | 2015-03-12 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2015032851A3 (en) | Silicon-bridged pillared silicate compounds and process for their production | |
WO2009108173A3 (en) | Methods for formation of substrate elements | |
WO2012057517A3 (en) | Compound semiconductor device and method for manufacturing a compound semiconductor | |
WO2015039723A8 (en) | Polycyclic phenylpyridine iridium complexes and derivatives thereof for oleds | |
WO2012113860A3 (en) | Phenalene-1-one derivatives, method for producing same and use thereof | |
WO2012103055A3 (en) | Molecular sieve adsorbent blends and uses thereof | |
WO2014108538A3 (en) | Layers or three-dimensional shaped bodies having two regions of different primary and/or secondary structure and method for production thereof | |
TW200703473A (en) | Doping mixture for doping semiconductors | |
MX2016002432A (en) | Hybrid organic/inorganic thin films and method of manufacturing same. | |
WO2014014542A3 (en) | High performance silicon based coating compositions | |
WO2010080242A3 (en) | Uzm-27 family of crystalline aluminosilicate compositions, a method of preparing the compositions and methods of using the compositions | |
WO2014121040A8 (en) | Flap modulators | |
FR2973936B1 (en) | METHOD OF SELECTIVE GROWTH ON SEMICONDUCTOR STRUCTURE | |
WO2012061037A3 (en) | Method for preparing small crystal ssz-32 | |
WO2010144393A3 (en) | Liquid crystal compositions | |
WO2014049052A3 (en) | Optoelectronic component and method for producing an optoelectronic component | |
WO2012015999A3 (en) | Process for the preparation of imatinib mesylate | |
WO2012071102A3 (en) | Method for buffering a chemical or biological composition | |
WO2013152277A3 (en) | Moenomycin analogs, methods of synthesis, and uses thereof | |
MX2020009096A (en) | 3d ceramic structures. | |
MY175376A (en) | Modified chabazite adsorbent compositions, methods of making and using them | |
MY165453A (en) | Drill having a coating | |
WO2014121055A3 (en) | Flap modulators | |
MX2017015113A (en) | Method for the manufacture of calcium silicate hydrate used as hardening accelerator in concrete and cement-based materials, calcium silicate hydrate manufactured with said method. | |
WO2013186082A3 (en) | Method for producing indium oxide-containing layers |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 14761332 Country of ref document: EP Kind code of ref document: A2 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 14761332 Country of ref document: EP Kind code of ref document: A2 |