WO2015020874A1 - Bulles ultrarésistantes pour matériaux légers à résistance et à ténacité élevées - Google Patents

Bulles ultrarésistantes pour matériaux légers à résistance et à ténacité élevées Download PDF

Info

Publication number
WO2015020874A1
WO2015020874A1 PCT/US2014/049138 US2014049138W WO2015020874A1 WO 2015020874 A1 WO2015020874 A1 WO 2015020874A1 US 2014049138 W US2014049138 W US 2014049138W WO 2015020874 A1 WO2015020874 A1 WO 2015020874A1
Authority
WO
WIPO (PCT)
Prior art keywords
bubbles
spherical bubbles
shell
spherical
polymer
Prior art date
Application number
PCT/US2014/049138
Other languages
English (en)
Inventor
Daeyeon Lee
Original Assignee
The Trustees Of The University Of Pennsylvania
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by The Trustees Of The University Of Pennsylvania filed Critical The Trustees Of The University Of Pennsylvania
Publication of WO2015020874A1 publication Critical patent/WO2015020874A1/fr

Abstract

La présente invention concerne des bulles non sphériques stables et un composite comprenant lesdites bulles non sphériques stables ainsi qu'un polymère. Les bulles non sphériques stables présentent une coque encapsulant un gaz. L'invention concerne également des procédés associés permettant de préparer les bulles non sphériques stables et ledit composite.
PCT/US2014/049138 2013-08-07 2014-07-31 Bulles ultrarésistantes pour matériaux légers à résistance et à ténacité élevées WO2015020874A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201361863028P 2013-08-07 2013-08-07
US61/863,028 2013-08-07

Publications (1)

Publication Number Publication Date
WO2015020874A1 true WO2015020874A1 (fr) 2015-02-12

Family

ID=52461845

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/049138 WO2015020874A1 (fr) 2013-08-07 2014-07-31 Bulles ultrarésistantes pour matériaux légers à résistance et à ténacité élevées

Country Status (1)

Country Link
WO (1) WO2015020874A1 (fr)

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5278194A (en) * 1993-03-25 1994-01-11 Microsome Environmentall dispersible syntactic foam
US20080213593A1 (en) * 2005-01-21 2008-09-04 President And Fellows Of Harvard College Systems And Methods For Forming Fluidic Droplets Encapsulated In Particles Such As Colloidal Particles
US20100310746A1 (en) * 2006-08-17 2010-12-09 Nestec S.A. Aqueous foams, food products and a method of producing same

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US5278194A (en) * 1993-03-25 1994-01-11 Microsome Environmentall dispersible syntactic foam
US20080213593A1 (en) * 2005-01-21 2008-09-04 President And Fellows Of Harvard College Systems And Methods For Forming Fluidic Droplets Encapsulated In Particles Such As Colloidal Particles
US20100310746A1 (en) * 2006-08-17 2010-12-09 Nestec S.A. Aqueous foams, food products and a method of producing same

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
SUBRAMANIAM ET AL.: "Colloid Science Non-sphericl bubbles", NATURE, vol. 438, 2005, pages 930. PG 930 *

Similar Documents

Publication Publication Date Title
Shahbazi et al. Directional freeze‐casting: A bioinspired method to assemble multifunctional aligned porous structures for advanced applications
Xu et al. 3D printing for polymer/particle-based processing: A review
Salimian et al. A review on aerogel: 3D nanoporous structured fillers in polymer‐based nanocomposites
Yaraghi et al. Biomimetic structural materials: inspiration from design and assembly
Liang et al. Ca2+ enhanced nacre-inspired montmorillonite–alginate film with superior mechanical, transparent, fire retardancy, and shape memory properties
Su et al. Micromechanical properties of melamine–formaldehyde microcapsules by nanoindentation: Effect of size and shell thickness
Chen et al. Artificial wooden nacre: a high specific strength engineering material
de Hazan et al. Robotic deposition of 3d nanocomposite and ceramic fiber architectures via UV curable colloidal inks
Sun et al. Tough polymer aerogels incorporating a conformal inorganic coating for low flammability and durable hydrophobicity
Huo et al. Ultrastrong hierarchical porous materials via colloidal assembly and oxidation of metal particles
Liu et al. Superhydrophobic coatings prepared by the in situ growth of silicone nanofilaments on alkali-activated geopolymers surface
Gupta et al. Ice-templated porous nanocellulose-based materials: Current progress and opportunities for materials engineering
Wang et al. Intriguing morphology evolution from noncrosslinked poly (tert-butyl acrylate) seeds with polar functional groups in soap-free emulsion polymerization of styrene
Liu et al. Novel strategy to prepare hierarchically porous ceramic microspheres via a self-assembly method on tunable superamphiphobic surfaces
Gunasekaran et al. Rapid carbon dioxide foaming of 3D printed thermoplastic polyurethane elastomers
Park et al. Shape memory polymer composites embedded with hybrid ceramic microparticles
de Hazan Porous ceramics, ceramic/polymer, and metal‐doped ceramic/polymer nanocomposites via freeze casting of photo‐curable colloidal fluids
Chang et al. Fabrication of anisotropic poly (vinyl alcohol) scaffolds with controllable mechanical properties and structural recoverability under compression via a freeze-casting technique
Shahid et al. Macroporous ceramic monolith from nanoparticle–polyelectrolyte-stabilized pickering emulsions
Menne et al. Giant functional properties in porous electroceramics through additive manufacturing of capillary suspensions
Jin et al. Fabrication of pill-shaped polyimide aerogel particles using microfluidic flows
Chadha et al. Bioinspired techniques in freeze casting: a survey of processes, current advances, and future directions
Jalili et al. Liquid crystal-mediated 3D printing process to fabricate nano-ordered layered structures
Qi et al. Imparting Cellulose Acetate Films with hydrophobicity, high transparency, and self-cleaning function by constructing a Slippery Liquid-Infused Porous Surface
Zhang et al. Cuttlefish-bone-structure-like lamellar porous fiber-based ceramics with enhanced mechanical performances

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14834837

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14834837

Country of ref document: EP

Kind code of ref document: A1