WO2014159724A1 - Extensible nonwoven fabric - Google Patents
Extensible nonwoven fabric Download PDFInfo
- Publication number
- WO2014159724A1 WO2014159724A1 PCT/US2014/024907 US2014024907W WO2014159724A1 WO 2014159724 A1 WO2014159724 A1 WO 2014159724A1 US 2014024907 W US2014024907 W US 2014024907W WO 2014159724 A1 WO2014159724 A1 WO 2014159724A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- fabric
- catalyzed polypropylene
- comparison
- fibers
- increase
- Prior art date
Abstract
Description
Claims