WO2014135626A1 - Production de polyamides par polymérisation hydrolytique et extractions multiples - Google Patents

Production de polyamides par polymérisation hydrolytique et extractions multiples Download PDF

Info

Publication number
WO2014135626A1
WO2014135626A1 PCT/EP2014/054325 EP2014054325W WO2014135626A1 WO 2014135626 A1 WO2014135626 A1 WO 2014135626A1 EP 2014054325 W EP2014054325 W EP 2014054325W WO 2014135626 A1 WO2014135626 A1 WO 2014135626A1
Authority
WO
WIPO (PCT)
Prior art keywords
polyamide
extractant
polymerization
extraction
water
Prior art date
Application number
PCT/EP2014/054325
Other languages
German (de)
English (en)
Inventor
Gad Kory
Silke Biedasek
Faissal-Ali El-Toufaili
Achim Stammer
Reinhard Lang
Dirk Meckelnburg
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Priority to EP14708048.5A priority Critical patent/EP2964691A1/fr
Priority to JP2015560687A priority patent/JP2016509118A/ja
Priority to BR112015021841A priority patent/BR112015021841A2/pt
Priority to CN201480024451.7A priority patent/CN105189608A/zh
Priority to KR1020157027985A priority patent/KR20150129791A/ko
Publication of WO2014135626A1 publication Critical patent/WO2014135626A1/fr

Abstract

La présente invention concerne un procédé de production de polyamides, comprenant une polymérisation hydrolytique et au moins deux étapes d'extraction qui ne sont pas effectuées immédiatement les unes à la suite des autres.
PCT/EP2014/054325 2013-03-07 2014-03-06 Production de polyamides par polymérisation hydrolytique et extractions multiples WO2014135626A1 (fr)

Priority Applications (5)

Application Number Priority Date Filing Date Title
EP14708048.5A EP2964691A1 (fr) 2013-03-07 2014-03-06 Production de polyamides par polymérisation hydrolytique et extractions multiples
JP2015560687A JP2016509118A (ja) 2013-03-07 2014-03-06 ポリアミドの加水分解重合および多段抽出による製造
BR112015021841A BR112015021841A2 (pt) 2013-03-07 2014-03-06 processo para preparação de poliamidas, poliamida e uso de uma poliamida
CN201480024451.7A CN105189608A (zh) 2013-03-07 2014-03-06 通过水解聚合和多次萃取制备聚酰胺
KR1020157027985A KR20150129791A (ko) 2013-03-07 2014-03-06 가수분해 중합 및 다중 추출에 의한 폴리아미드의 제조

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP13158182.9 2013-03-07
EP13158182 2013-03-07

Publications (1)

Publication Number Publication Date
WO2014135626A1 true WO2014135626A1 (fr) 2014-09-12

Family

ID=47827060

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2014/054325 WO2014135626A1 (fr) 2013-03-07 2014-03-06 Production de polyamides par polymérisation hydrolytique et extractions multiples

Country Status (6)

Country Link
EP (1) EP2964691A1 (fr)
JP (1) JP2016509118A (fr)
KR (1) KR20150129791A (fr)
CN (1) CN105189608A (fr)
BR (1) BR112015021841A2 (fr)
WO (1) WO2014135626A1 (fr)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2022029427A (ja) 2020-08-04 2022-02-17 信越化学工業株式会社 ネガ型感光性樹脂組成物、パターン形成方法、硬化被膜形成方法、層間絶縁膜、表面保護膜、及び電子部品
JP2022151614A (ja) 2021-03-23 2022-10-07 信越化学工業株式会社 ネガ型感光性樹脂組成物、パターン形成方法、硬化被膜形成方法、層間絶縁膜、表面保護膜、及び電子部品

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0117495A2 (fr) * 1983-02-26 1984-09-05 BASF Aktiengesellschaft Procédé pour la fabrication continue de polylactames
WO2009153340A1 (fr) * 2008-06-20 2009-12-23 Basf Se Procédé continu de séchage et post-condensation en plusieurs étapes d’un granulat de polyamide

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19801267B4 (de) * 1998-01-15 2005-03-24 Inventa-Fischer Gmbh Verfahren zur Herstellung von PA-6 Granulat und dessen Verwendung
CN102532526B (zh) * 2011-11-29 2013-11-06 湖南岳化化工股份有限公司 一种高粘度聚酰胺6连续聚合生产工艺

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0117495A2 (fr) * 1983-02-26 1984-09-05 BASF Aktiengesellschaft Procédé pour la fabrication continue de polylactames
WO2009153340A1 (fr) * 2008-06-20 2009-12-23 Basf Se Procédé continu de séchage et post-condensation en plusieurs étapes d’un granulat de polyamide

Also Published As

Publication number Publication date
JP2016509118A (ja) 2016-03-24
EP2964691A1 (fr) 2016-01-13
BR112015021841A2 (pt) 2017-07-18
CN105189608A (zh) 2015-12-23
KR20150129791A (ko) 2015-11-20

Similar Documents

Publication Publication Date Title
EP3143069A1 (fr) Production de polyamides par polymérisation hydrolytique suivie d'un traitement dans un malaxeur
EP2297228B1 (fr) Procédé continu de séchage et post-condensation en plusieurs étapes d un granulat de polyamide
EP2992035B1 (fr) Procédé de fabrication de polyamides de haute viscosité
US9200115B2 (en) Process for continuously preparing copolyamides from lactams and salts of diamines and dicarboxylic acids
US20160009869A1 (en) Preparation of polyamides by hydrolytic polymerization, postpolymerization and subsequent extraction
EP0288893B1 (fr) Polyamides à base de diamines/diacides modifiés par de l'alpha-amino-epsilon-caprolactame
US20140256905A1 (en) Preparation of polyamides by hydrolytic polymerization and subsequent devolatilization
DE3912767A1 (de) Verfahren zur kontinuierlichen herstellung von copolyamiden
EP1194473B1 (fr) Procede de production de polyamides a partir de lactames et d'extraits de polyamide
EP1054919A1 (fr) Procede en continu pour produire des polyamides a partir d'aminonitriles
EP2964691A1 (fr) Production de polyamides par polymérisation hydrolytique et extractions multiples
EP1723192B1 (fr) Procede de production en continu de polyamides
EP1165660B1 (fr) Procede de production de polyamide 6 a faible teneur en extrait, a haute stabilite de viscosite et a faible taux de remonomerisation
US20140256887A1 (en) Preparation of polyamides by hydrolytic polymierization and multiple extraction
DE19957663A1 (de) Verfahren zur kontinuierlichen Herstellung von Copolyamiden, die auf einem Lactam (I), einem Diamin (II) und einer Dicarbonsäure (III) basieren
WO2014135627A1 (fr) Fabrication de polyamides par polymérisation hydrolytique suivie d'un dégazage
EP0393544B1 (fr) Procédé de préparation en continu de nylon 4,6
WO2002094909A1 (fr) Procede de traitement d'oligoamides et de production de polyamide
WO2014006171A1 (fr) Procédé de purification de particules de polyamide
EP1687356B1 (fr) Procede de production en continu de polyamides à aptitudes à l'ecoulement ameliorees
WO2013076037A1 (fr) Procédé pour la production simplifiée de polyamide 6
EP1817361B1 (fr) Procede pour produire en continu des polyamides ayant des proprietes d'ecoulement ameliorees
DE102004027022A1 (de) Verfahren zur Abtrennung von Ammoniak und Wasser aus Lactam-haltigen Gemischen

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201480024451.7

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14708048

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
REEP Request for entry into the european phase

Ref document number: 2014708048

Country of ref document: EP

WWE Wipo information: entry into national phase

Ref document number: 2014708048

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2015560687

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

ENP Entry into the national phase

Ref document number: 20157027985

Country of ref document: KR

Kind code of ref document: A

REG Reference to national code

Ref country code: BR

Ref legal event code: B01A

Ref document number: 112015021841

Country of ref document: BR

ENP Entry into the national phase

Ref document number: 112015021841

Country of ref document: BR

Kind code of ref document: A2

Effective date: 20150905