WO2014130318A2 - Essai de ténacité par émissions acoustiques pour pdc, pcbn ou d'autres inserts en matériaux durs ou extra-durs - Google Patents

Essai de ténacité par émissions acoustiques pour pdc, pcbn ou d'autres inserts en matériaux durs ou extra-durs Download PDF

Info

Publication number
WO2014130318A2
WO2014130318A2 PCT/US2014/016000 US2014016000W WO2014130318A2 WO 2014130318 A2 WO2014130318 A2 WO 2014130318A2 US 2014016000 W US2014016000 W US 2014016000W WO 2014130318 A2 WO2014130318 A2 WO 2014130318A2
Authority
WO
WIPO (PCT)
Prior art keywords
cutter
acoustic
load
test
acoustic event
Prior art date
Application number
PCT/US2014/016000
Other languages
English (en)
Other versions
WO2014130318A3 (fr
Inventor
Federico Bellin
Original Assignee
Varel International Ind., L.P.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from US13/774,886 external-priority patent/US20130166214A1/en
Application filed by Varel International Ind., L.P. filed Critical Varel International Ind., L.P.
Priority to CN201480009865.2A priority Critical patent/CN105008912A/zh
Priority to CA2900228A priority patent/CA2900228A1/fr
Priority to JP2015558875A priority patent/JP2016507756A/ja
Priority to KR1020157022476A priority patent/KR20150117670A/ko
Publication of WO2014130318A2 publication Critical patent/WO2014130318A2/fr
Publication of WO2014130318A3 publication Critical patent/WO2014130318A3/fr

Abstract

Un dispositif d'essai par émissions acoustiques selon l'invention comprend un couteau d'essai comprenant une première surface, un capteur acoustique, un pénétrateur couplé à la première surface, et une charge. La charge est appliquée sur le pénétrateur qui transfère la charge à la première surface. Le capteur acoustique est couplé au couteau d'essai afin de pouvoir communiquer avec ce dernier, et détecte un ou plusieurs événements acoustiques survenant dans ledit couteau d'essai. Un système d'essai par émissions acoustiques comprend un enregistreur de données couplé au dispositif d'essai. L'enregistreur de données enregistre les données provenant du dispositif d'essai. Sur la base des données reçues, la ténacité du couteau d'essai est déterminée de manière objective et peut être classée par comparaison à la ténacité d'autres couteaux d'essai. La charge augmente jusqu'à une charge de crête, est maintenue durant une période de temps puis diminue. Des couteaux du même type que les couteaux d'essai ont une ténacité similaire.
PCT/US2014/016000 2013-02-22 2014-02-12 Essai de ténacité par émissions acoustiques pour pdc, pcbn ou d'autres inserts en matériaux durs ou extra-durs WO2014130318A2 (fr)

Priority Applications (4)

Application Number Priority Date Filing Date Title
CN201480009865.2A CN105008912A (zh) 2013-02-22 2014-02-12 用于pdc、pcbn或其它硬或超硬材料插入件的声发射韧性测试
CA2900228A CA2900228A1 (fr) 2013-02-22 2014-02-12 Essai de tenacite par emissions acoustiques pour pdc, pcbn ou d'autres inserts en materiaux durs ou extra-durs
JP2015558875A JP2016507756A (ja) 2013-02-22 2014-02-12 Ｐｄｃ、ｐｃｂｎ又は他の高硬又は超硬材料インサート用の音響放射靱性試験
KR1020157022476A KR20150117670A (ko) 2013-02-22 2014-02-12 Pdc, pcbn 또는 다른 경질 또는 초경질 물질 인서트를 위한 음향 방출 인성 시험

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US13/774,886 2013-02-22
US13/774,886 US20130166214A1 (en) 2010-04-06 2013-02-22 Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts

Publications (2)

Publication Number Publication Date
WO2014130318A2 true WO2014130318A2 (fr) 2014-08-28
WO2014130318A3 WO2014130318A3 (fr) 2014-10-16

Family

ID=51391956

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2014/016000 WO2014130318A2 (fr) 2013-02-22 2014-02-12 Essai de ténacité par émissions acoustiques pour pdc, pcbn ou d'autres inserts en matériaux durs ou extra-durs

Country Status (5)

Country Link
JP (1) JP2016507756A (fr)
KR (1) KR20150117670A (fr)
CN (1) CN105008912A (fr)
CA (1) CA2900228A1 (fr)
WO (1) WO2014130318A2 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4658245A (en) * 1983-04-29 1987-04-14 The Warner & Swasey Company Tool condition and failure monitoring apparatus and method
US4918616A (en) * 1984-05-18 1990-04-17 Omron Tateisi Electronics Co. Tool monitoring system
US20110246102A1 (en) * 2010-04-06 2011-10-06 Varel Europe S.A.S. Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts
US20110239765A1 (en) * 2010-04-06 2011-10-06 Varel Europe S.A.S. Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US4658245A (en) * 1983-04-29 1987-04-14 The Warner & Swasey Company Tool condition and failure monitoring apparatus and method
US4918616A (en) * 1984-05-18 1990-04-17 Omron Tateisi Electronics Co. Tool monitoring system
US20110246102A1 (en) * 2010-04-06 2011-10-06 Varel Europe S.A.S. Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts
US20110239765A1 (en) * 2010-04-06 2011-10-06 Varel Europe S.A.S. Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts

Also Published As

Publication number Publication date
JP2016507756A (ja) 2016-03-10
CA2900228A1 (fr) 2014-08-28
CN105008912A (zh) 2015-10-28
WO2014130318A3 (fr) 2014-10-16
KR20150117670A (ko) 2015-10-20

Similar Documents

Publication Publication Date Title
US8397572B2 (en) Acoustic emission toughness testing for PDC, PCBN, or other hard or superhard materials
US8322217B2 (en) Acoustic emission toughness testing for PDC, PCBN, or other hard or superhard material inserts
US8596124B2 (en) Acoustic emission toughness testing having smaller noise ratio
US8365599B2 (en) Acoustic emission toughness testing for PDC, PCBN, or other hard or superhard materials
US9086348B2 (en) Downhole acoustic emission formation sampling
US9297731B2 (en) Acoustic emission toughness testing for PDC, PCBN, or other hard or superhard material inserts
US20130166214A1 (en) Acoustic Emission Toughness Testing For PDC, PCBN, Or Other Hard Or Superhard Material Inserts
WO2014130318A2 (fr) Essai de ténacité par émissions acoustiques pour pdc, pcbn ou d'autres inserts en matériaux durs ou extra-durs

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14754297

Country of ref document: EP

Kind code of ref document: A2

ENP Entry into the national phase

Ref document number: 2900228

Country of ref document: CA

ENP Entry into the national phase

Ref document number: 2015558875

Country of ref document: JP

Kind code of ref document: A

Ref document number: 20157022476

Country of ref document: KR

Kind code of ref document: A

ENP Entry into the national phase

Ref document number: 2015140138

Country of ref document: RU

Kind code of ref document: A

122 Ep: pct application non-entry in european phase

Ref document number: 14754297

Country of ref document: EP

Kind code of ref document: A2