WO2014111321A1 - Procédé pour la post-réticulation de surface de superabsorbants - Google Patents

Procédé pour la post-réticulation de surface de superabsorbants Download PDF

Info

Publication number
WO2014111321A1
WO2014111321A1 PCT/EP2014/050425 EP2014050425W WO2014111321A1 WO 2014111321 A1 WO2014111321 A1 WO 2014111321A1 EP 2014050425 W EP2014050425 W EP 2014050425W WO 2014111321 A1 WO2014111321 A1 WO 2014111321A1
Authority
WO
WIPO (PCT)
Prior art keywords
superabsorbent
water
weight
crosslinking
polymer
Prior art date
Application number
PCT/EP2014/050425
Other languages
English (en)
Inventor
Joseph Grill
Olaf Hoeller
Original Assignee
Basf Se
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Basf Se filed Critical Basf Se
Publication of WO2014111321A1 publication Critical patent/WO2014111321A1/fr

Abstract

L'invention porte sur un procédé pour la réticulation de surface de superabsorbants, dans lequel l'ajout de tensioactif éther de polyglycol et d'alcool gras à la solution de réticulation de surface permet d'améliorer la qualité de la réticulation de surface sans présenter d'effets négatifs de réduction de tension superficielle de liquides dans des produits d'hygiène comprenant le superabsorbant réticulé en surface.
PCT/EP2014/050425 2013-01-21 2014-01-13 Procédé pour la post-réticulation de surface de superabsorbants WO2014111321A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
US201361754658P 2013-01-21 2013-01-21
US61/754,658 2013-01-21

Publications (1)

Publication Number Publication Date
WO2014111321A1 true WO2014111321A1 (fr) 2014-07-24

Family

ID=49956177

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2014/050425 WO2014111321A1 (fr) 2013-01-21 2014-01-13 Procédé pour la post-réticulation de surface de superabsorbants

Country Status (1)

Country Link
WO (1) WO2014111321A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170281422A1 (en) * 2016-03-30 2017-10-05 Basf Se Ultrathin fluid-absorbent article

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0509708A1 (fr) * 1991-04-13 1992-10-21 The Dow Chemical Company Particules de résine absorbante ayant une surface réticulée et revêtues de tensio-actif et procédé de préparation
WO1995027739A1 (fr) * 1994-04-11 1995-10-19 Hoechst Celanese Corporation Polymeres super-absorbants et produits fabriques avec eux
US7473739B2 (en) * 2004-02-05 2009-01-06 Nippon Shokubai Co., Ltd. Particulate water absorbent agent and production method thereof, and water absorbent article

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP0509708A1 (fr) * 1991-04-13 1992-10-21 The Dow Chemical Company Particules de résine absorbante ayant une surface réticulée et revêtues de tensio-actif et procédé de préparation
WO1995027739A1 (fr) * 1994-04-11 1995-10-19 Hoechst Celanese Corporation Polymeres super-absorbants et produits fabriques avec eux
US7473739B2 (en) * 2004-02-05 2009-01-06 Nippon Shokubai Co., Ltd. Particulate water absorbent agent and production method thereof, and water absorbent article

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20170281422A1 (en) * 2016-03-30 2017-10-05 Basf Se Ultrathin fluid-absorbent article
US10806640B2 (en) * 2016-03-30 2020-10-20 Basf Se Ultrathin fluid-absorbent article

Similar Documents

Publication Publication Date Title
EP2134772B1 (fr) Procédé de fabrication de superabsorbants réticulés en surface et réhumidifiés
US9585798B2 (en) Water absorbent storage layers
US8017549B2 (en) Superabsorbents having superior permeability and conveying properties
EP2235093B1 (fr) Procédé pour produire des superabsorbants réticulés en surface
US8410233B2 (en) Method for producing superabsorbers with a low residual monomer content
US20100247916A1 (en) Process for Producing Surface Postcrosslinked Water-Absorbing Polymer Particles
US20110118114A1 (en) Color stable superabsorbent
US20120157634A1 (en) Soft Particulate Superabsorbent and Use Thereof
US20130260988A1 (en) Color-Stable Superabsorbent
US8076436B2 (en) Method for the production of superabsorbers
US8703876B2 (en) Process for producing water absorbing polymer particles with improved color stability
US20150306272A1 (en) Odour-inhibiting superabsorber
US8742024B2 (en) Mixture of surface postcrosslinked superabsorbers with different surface postcrosslinking
US20130256593A1 (en) Color-Stable Superabsorbent
US8497337B2 (en) Process for producing water-absorbing polymer particles with improved color stability
US9833769B2 (en) Process for producing water-absorbing polymer particles with high free swell rate
US10427135B2 (en) Aminopolycarboxylic acids useful as processing aids in the manufacture of superabsorbents
JP2013505313A (ja) 色安定性の超吸収剤
JP2013504674A (ja) 色安定性の超吸収剤
US20120157302A1 (en) Process For Producing Triclosan-Coated Superabsorbents
WO2008055856A1 (fr) Procédé de fabrication de superabsorbants
US11813589B2 (en) Superabsorbent complexed with aluminum ions
WO2013182469A2 (fr) Superabsorbant limitant les odeurs
WO2014111321A1 (fr) Procédé pour la post-réticulation de surface de superabsorbants

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14700359

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14700359

Country of ref document: EP

Kind code of ref document: A1