WO2014087174A1 - Structures résistant aux explosions - Google Patents

Structures résistant aux explosions Download PDF

Info

Publication number
WO2014087174A1
WO2014087174A1 PCT/GB2013/053228 GB2013053228W WO2014087174A1 WO 2014087174 A1 WO2014087174 A1 WO 2014087174A1 GB 2013053228 W GB2013053228 W GB 2013053228W WO 2014087174 A1 WO2014087174 A1 WO 2014087174A1
Authority
WO
WIPO (PCT)
Prior art keywords
panel
wall
blast
curvature
mortar
Prior art date
Application number
PCT/GB2013/053228
Other languages
English (en)
Inventor
Faris Abed Al-Hafidh ALI
Original Assignee
University Of Ulster
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University Of Ulster filed Critical University Of Ulster
Publication of WO2014087174A1 publication Critical patent/WO2014087174A1/fr

Abstract

Panneau, paroi ou structure qui peut utiliser sa courbure afin de résister à des forces d'explosion. Un tel panneau possède une empreinte bidimensionnelle définie par une hauteur L et une courbure définie par un déplacement latéral maximum x dans une direction perpendiculaire à son empreinte et vers une source d'une explosion. La courbure est choisie dans le rayon d'action de 0,001≤ x/L ≤ 0,5 de manière à offrir une amélioration de la résistance aux explosions pour la même épaisseur de panneau.
PCT/GB2013/053228 2012-12-06 2013-12-06 Structures résistant aux explosions WO2014087174A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
GB1222002.6 2012-12-06
GB201222002 2012-12-06

Publications (1)

Publication Number Publication Date
WO2014087174A1 true WO2014087174A1 (fr) 2014-06-12

Family

ID=49817119

Family Applications (2)

Application Number Title Priority Date Filing Date
PCT/GB2013/053230 WO2014087176A1 (fr) 2012-12-06 2013-12-06 Détection d'explosion intelligente
PCT/GB2013/053228 WO2014087174A1 (fr) 2012-12-06 2013-12-06 Structures résistant aux explosions

Family Applications Before (1)

Application Number Title Priority Date Filing Date
PCT/GB2013/053230 WO2014087176A1 (fr) 2012-12-06 2013-12-06 Détection d'explosion intelligente

Country Status (3)

Country Link
US (1) US20150316358A1 (fr)
EP (1) EP2929281A1 (fr)
WO (2) WO2014087176A1 (fr)

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2569978C1 (ru) * 2014-07-25 2015-12-10 Российская Федерация, От Имени Которой Выступает Министерство Промышленности И Торговли Российской Федерации Защитная конструкция от фугасного воздействия взрыва
CN109424120A (zh) * 2017-08-23 2019-03-05 徐广鑫 一种钢结构墙板
US11313652B1 (en) 2021-02-25 2022-04-26 Government Of The United States, As Represented By The Secretary Of The Army Underbody kit
CN115519862A (zh) * 2021-06-24 2022-12-27 中国石油化工股份有限公司 抗气体爆炸结构及其制备方法

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10267600B1 (en) * 2016-09-02 2019-04-23 Honeywell Federal Manufacturing & Technologies, Llc Defeat system for vehicle attached improvised explosive devices
ES2684845B1 (es) * 2017-03-31 2019-06-20 Fhecor Ingenieros Consultores S A Sistema de proteccion anti-explosiones para barreras de amortiguamiento
PL430286A1 (pl) * 2019-06-19 2020-12-28 Innovative Radar Technologies Laboratory Spółka Z Ograniczoną Odpowiedzialnością Układ do pomiaru odkształceń oraz sposób pomiaru odkształceń
CN111809822B (zh) * 2019-08-08 2021-08-03 安徽谦谨建设有限公司 一种建筑外墙使用的具有脱落警示作用的干挂件
US11733005B2 (en) * 2019-08-28 2023-08-22 Disruptive Defenses, Llc Anti-ballistic barriers
CN115791228B (zh) * 2022-11-07 2023-08-08 南京理工大学 城市人防设施内爆炸效应的模拟实验装置

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1984407A (en) * 1933-06-27 1934-12-18 Geiger Eugenie Frey Bomb-proof building
US6298607B1 (en) * 1998-04-16 2001-10-09 The University Of Toledo Venting-membrane system to mitigate blast effects
WO2002039048A2 (fr) * 2000-11-09 2002-05-16 Vickers Omc (Proprietary) Limited Protection contre les mines avec charge reactive
WO2008039213A2 (fr) * 2005-11-30 2008-04-03 The Cooper Union For The Advancement Of Science And Art Structure protectrice et système protecteur
US20090266226A1 (en) * 2004-10-07 2009-10-29 Innovative Survivability Technologies Explosive round countermeasure system
US20110212320A1 (en) 2007-08-10 2011-09-01 Greenhill Antiballistics Corporation Composite Material
WO2013050783A1 (fr) 2011-10-05 2013-04-11 University Of Ulster Panneaux protecteurs

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US102015A (en) * 1870-04-19 Improved horse-power
IL202275A0 (en) * 2009-11-23 2010-11-30 Plasan Sasa Ltd A system for providing protection against an explosive threat

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US1984407A (en) * 1933-06-27 1934-12-18 Geiger Eugenie Frey Bomb-proof building
US6298607B1 (en) * 1998-04-16 2001-10-09 The University Of Toledo Venting-membrane system to mitigate blast effects
WO2002039048A2 (fr) * 2000-11-09 2002-05-16 Vickers Omc (Proprietary) Limited Protection contre les mines avec charge reactive
US20090266226A1 (en) * 2004-10-07 2009-10-29 Innovative Survivability Technologies Explosive round countermeasure system
WO2008039213A2 (fr) * 2005-11-30 2008-04-03 The Cooper Union For The Advancement Of Science And Art Structure protectrice et système protecteur
US20110212320A1 (en) 2007-08-10 2011-09-01 Greenhill Antiballistics Corporation Composite Material
WO2013050783A1 (fr) 2011-10-05 2013-04-11 University Of Ulster Panneaux protecteurs

Cited By (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
RU2569978C1 (ru) * 2014-07-25 2015-12-10 Российская Федерация, От Имени Которой Выступает Министерство Промышленности И Торговли Российской Федерации Защитная конструкция от фугасного воздействия взрыва
CN109424120A (zh) * 2017-08-23 2019-03-05 徐广鑫 一种钢结构墙板
CN109424120B (zh) * 2017-08-23 2020-11-03 徐广鑫 一种钢结构墙板
US11313652B1 (en) 2021-02-25 2022-04-26 Government Of The United States, As Represented By The Secretary Of The Army Underbody kit
CN115519862A (zh) * 2021-06-24 2022-12-27 中国石油化工股份有限公司 抗气体爆炸结构及其制备方法

Also Published As

Publication number Publication date
US20150316358A1 (en) 2015-11-05
WO2014087176A1 (fr) 2014-06-12
EP2929281A1 (fr) 2015-10-14

Similar Documents

Publication Publication Date Title
US20150316358A1 (en) Smart Blast Sensing
Goswami et al. Retrofitting materials for enhanced blast performance of Structures: Recent advancement and challenges ahead
US8453401B2 (en) Prestressed, strong foam glass tiles
Orton et al. Experimental testing of CFRP-strengthened reinforced concrete slab elements loaded by close-in blast
Anas et al. Experimental studies on blast performance of unreinforced masonry walls of clay bricks and concrete blocks: A state-of-the-art review
KR101250903B1 (ko) 알루미늄 폼 패널과 콘크리트판의 합성 방폭벽체, 그 시공방법 및 이를 이용한 방폭구조물
Liu et al. Blast testing of high performance geopolymer composite walls reinforced with steel wire mesh and aluminium foam
US20140273684A1 (en) Protective Panels
Alhadid et al. Critical overview of blast resistance of different concrete types
Rebentrost et al. Investigation of UHPFRC slabs under blast loads
Anas et al. Experimental studies on blast performance of unreinforced masonry walls: a state-of-the-art review
DK201200491A (en) Light weight composite armor with structural strength
KR100945204B1 (ko) 복합섬유를 이용한 초고인성 방폭 시멘트 복합체
Jung et al. Performance of SIFCON based HPFRCC under field blast load
Yamaguchi et al. Blast resistance of double-layered reinforced concrete slabs composed of precast thin plates
Cavili et al. Ductal–a high-performance material for resistance to blasts and impacts
CN108331204B (zh) 一种多层框架结构公共建筑的填充墙泄爆结构
Anas et al. Explosion load induced response of structural concrete columns under contact and close-range detonations: a state-of-the-art review
Sohel et al. Analysis and design of steel-concrete composite sandwich systems subjected to extreme loads
RU142251U1 (ru) Взрывоустойчивый навесной вентилируемый фасад
Tauma et al. Impact and blast resistance of slurry infiltrated fiber concrete (SIFCON): A comprehensive review
Makovicka Blast load of building structure
Kalman Use of steel fiber reinforced concrete for blast resistant design
Gandia Blast retrofit of unreinforced masonry walls using ECC shotcrete
Thakkar Blast-Resistant Ballistic Materials

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13810987

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13810987

Country of ref document: EP

Kind code of ref document: A1