WO2014085730A1 - Processes and apparatus for producing nanocellulose, and compositions and products produced therefrom - Google Patents
Processes and apparatus for producing nanocellulose, and compositions and products produced therefrom Download PDFInfo
- Publication number
- WO2014085730A1 WO2014085730A1 PCT/US2013/072442 US2013072442W WO2014085730A1 WO 2014085730 A1 WO2014085730 A1 WO 2014085730A1 US 2013072442 W US2013072442 W US 2013072442W WO 2014085730 A1 WO2014085730 A1 WO 2014085730A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nanocellulose
- cellulose
- lignin
- composition
- nanocellulose composition
- Prior art date
Abstract
Description
Claims