WO2014053341A1 - Hydraulic composition - Google Patents
Hydraulic composition Download PDFInfo
- Publication number
- WO2014053341A1 WO2014053341A1 PCT/EP2013/069652 EP2013069652W WO2014053341A1 WO 2014053341 A1 WO2014053341 A1 WO 2014053341A1 EP 2013069652 W EP2013069652 W EP 2013069652W WO 2014053341 A1 WO2014053341 A1 WO 2014053341A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- composition
- mortar
- composition according
- alcohol
- Prior art date
Abstract
Description
Claims