WO2014041409A2 - Method for manufacturing steel casts - Google Patents
Method for manufacturing steel casts Download PDFInfo
- Publication number
- WO2014041409A2 WO2014041409A2 PCT/IB2013/001904 IB2013001904W WO2014041409A2 WO 2014041409 A2 WO2014041409 A2 WO 2014041409A2 IB 2013001904 W IB2013001904 W IB 2013001904W WO 2014041409 A2 WO2014041409 A2 WO 2014041409A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- reinforcement insert
- micro
- steel
- mold
- melting
- Prior art date
Abstract
Description
Claims