WO2014038814A1 - Composition adhésive - Google Patents
Composition adhésive Download PDFInfo
- Publication number
- WO2014038814A1 WO2014038814A1 PCT/KR2013/007748 KR2013007748W WO2014038814A1 WO 2014038814 A1 WO2014038814 A1 WO 2014038814A1 KR 2013007748 W KR2013007748 W KR 2013007748W WO 2014038814 A1 WO2014038814 A1 WO 2014038814A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- weight
- acrylic copolymer
- parts
- group
- adhesive composition
- Prior art date
Abstract
La présente invention concerne une composition adhésive, et, plus particulièrement, une composition adhésive ayant des propriétés à la flexion améliorées en raison d'un soulagement des contraintes, permettant ainsi d'empêcher une fuite légère provoquée par la concentration des contraintes et ayant également une excellente durabilité et supprimant de façon efficace la corrosion d'une couche métallique sans contenir d'agent anticorrosion supplémentaire, la composition comprenant un copolymère à base acryle ayant un groupe alcool primaire, un copolymère à base acryle ayant un groupe alcool secondaire, un agent de réticulation à base de toluène diisocyanate et un agent de réticulation à base d'isocyanate aliphatique pour soulager les contraintes.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR10-2012-0097731 | 2012-09-04 | ||
KR20120097731 | 2012-09-04 | ||
KR10-2013-0101599 | 2013-08-27 | ||
KR1020130101599A KR20140031116A (ko) | 2012-09-04 | 2013-08-27 | 점착제 조성물 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2014038814A1 true WO2014038814A1 (fr) | 2014-03-13 |
Family
ID=50237379
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/KR2013/007748 WO2014038814A1 (fr) | 2012-09-04 | 2013-08-29 | Composition adhésive |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2014038814A1 (fr) |
Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2011231288A (ja) * | 2010-04-30 | 2011-11-17 | Nitto Denko Corp | 光学フィルム用粘着剤層、その製造方法、粘着型光学フィルム、及び画像表示装置 |
JP2011231189A (ja) * | 2010-04-26 | 2011-11-17 | Nippon Carbide Ind Co Inc | 偏光板用粘着剤組成物、並びにそれを用いた粘着剤付偏光板及び液晶表示装置 |
JP2012118301A (ja) * | 2010-12-01 | 2012-06-21 | Toyo Ink Sc Holdings Co Ltd | 光学フィルム並びに偏光板。 |
KR20120076267A (ko) * | 2010-12-29 | 2012-07-09 | 제일모직주식회사 | 점착제 조성물 및 이를 이용한 광학 부재 |
US20120316294A1 (en) * | 2011-06-08 | 2012-12-13 | Hiroshi Ogawa | Adhesive composition and optical member using the same |
-
2013
- 2013-08-29 WO PCT/KR2013/007748 patent/WO2014038814A1/fr active Application Filing
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP2011231189A (ja) * | 2010-04-26 | 2011-11-17 | Nippon Carbide Ind Co Inc | 偏光板用粘着剤組成物、並びにそれを用いた粘着剤付偏光板及び液晶表示装置 |
JP2011231288A (ja) * | 2010-04-30 | 2011-11-17 | Nitto Denko Corp | 光学フィルム用粘着剤層、その製造方法、粘着型光学フィルム、及び画像表示装置 |
JP2012118301A (ja) * | 2010-12-01 | 2012-06-21 | Toyo Ink Sc Holdings Co Ltd | 光学フィルム並びに偏光板。 |
KR20120076267A (ko) * | 2010-12-29 | 2012-07-09 | 제일모직주식회사 | 점착제 조성물 및 이를 이용한 광학 부재 |
US20120316294A1 (en) * | 2011-06-08 | 2012-12-13 | Hiroshi Ogawa | Adhesive composition and optical member using the same |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2013085132A1 (fr) | Composition adhésive photodurcissable, et dispositif d'affichage l'utilisant | |
WO2016032108A1 (fr) | Film adhésif et élément d'affichage utilisant celui-ci | |
WO2010002198A2 (fr) | Composition adhesive, film protecteur destine a une plaque de polarisation, plaque de polarisation et ecran a cristaux liquides | |
WO2012111963A2 (fr) | Film substrat et méthode de fabrication de celui-ci | |
WO2018056710A1 (fr) | Composition optique adhésive transparente, film optique adhésif transparent en comprenant, et dispositif d'affichage à écran plat | |
WO2014204215A1 (fr) | Composition d'adhésif | |
WO2014204250A1 (fr) | Composition d'adhésif | |
WO2017010765A1 (fr) | Composé | |
WO2014204217A1 (fr) | Composition d'adhésif | |
WO2009131393A2 (fr) | Composition adhésive et plaques polarisantes et écrans à cristaux liquides utilisant une telle composition | |
WO2012128594A2 (fr) | Composition adhésive pour un film optique | |
WO2018056675A2 (fr) | Composition adhésive transparente optique, film adhésif transparent optique la comprenant, et dispositif d'affichage à écran plat | |
WO2021060876A1 (fr) | Composition adhésive acrylique, plaque polarisante et dispositif d'affichage | |
WO2014038810A1 (fr) | Composition adhésive | |
WO2015099279A1 (fr) | Composition adhésive contenant un agent anti-statique ionique | |
WO2014038815A1 (fr) | Composition adhésive | |
WO2018062775A1 (fr) | Composition adhésive et feuille adhésive utilisant celle-ci | |
WO2014027766A1 (fr) | Composition adhésive à base d'acryle | |
WO2014038814A1 (fr) | Composition adhésive | |
WO2020091450A1 (fr) | Composition adhésive, film optique la comprenant, et élément électronique organique et dispositif d'affichage les comprenant tous les deux | |
WO2019132455A1 (fr) | Composition adhésive et film protecteur l'utilisant | |
WO2020111821A1 (fr) | Composition de revêtement | |
WO2020067613A1 (fr) | Composition adhésive acrylique, plaque polarisante et dispositif d'affichage | |
WO2023096413A1 (fr) | Adhésif | |
WO2023132578A1 (fr) | Composition adhésive, feuille adhésive et film optique |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 13835226 Country of ref document: EP Kind code of ref document: A1 |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 13835226 Country of ref document: EP Kind code of ref document: A1 |