WO2014018615A1 - Optimal membrane electrochemical energy storage systems - Google Patents
Optimal membrane electrochemical energy storage systems Download PDFInfo
- Publication number
- WO2014018615A1 WO2014018615A1 PCT/US2013/051802 US2013051802W WO2014018615A1 WO 2014018615 A1 WO2014018615 A1 WO 2014018615A1 US 2013051802 W US2013051802 W US 2013051802W WO 2014018615 A1 WO2014018615 A1 WO 2014018615A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- flow battery
- active material
- electrolyte
- metal
- separator
- Prior art date
Abstract
Description
Claims