WO2013174512A2

WO2013174512A2 - Electromagnetic stirring device

Info

Publication number: WO2013174512A2
Application number: PCT/EP2013/001507
Authority: WO
Inventors: Monte Stefano De; Stefano Spagnul
Original assignee: Ergolines Lab S.R.L.
Priority date: 2012-05-24
Filing date: 2013-05-22
Publication date: 2013-11-28
Also published as: CN104661772A; EP2855048A2; ITUD20120095A1; WO2013174512A3; RU2637456C2; RU2014152242A; US20150151355A1; US9550232B2; CN104661772B; EP2855048B1

Abstract

Electromagnetic stirring device of melted metallic materials inside a cooling chamber of a casting machine comprising a retaining body of induction coils that is a body composed of at least two reciprocally different portions.

Description

DESCRIPTION

ELECTROMAGNETIC STIRRING DEVICE

Technical field

The present invention relates to an electromagnetic stirring device (1 ) of melted metallic material inside a cooling chamber (30) of a casting machine (1 8) according to the characteristics of the pre-characterizing part of claim 1 .

This invention relates also to a casting machine (18) according to the characteristics of the pre-characterizing part of claim 17.

The present invention also relates to a casting process for the production of metallic material bars (16) according to the characteristics of the pre-characterizing part of claim 20.

Definitions

Herein description and in the appended claims the following terms must be intended according to the definitions given in the following.

With the expression "metallic bar" it is intended to include all types of products of a casting machine, e.g. billets, blooms or flat blooms with different shapes in section e.g. with square, rectangular, round, polygonal section.

With the expression "casting machine" it is intended to include both vertical casting machines and casting machines provided with bending.

Prior art

In the field of the execution of continuous casting plants of metallic materials, in general steels and metallic alloys, the recourse to electromagnetic stirring devices of the melted metallic material generally known with the name of stirrers, is known.

The stirrer produces a magnetic field generating a force inside the die or mould within which there is the melted metallic material inducing a rotating flow inside the melted bath obtaining a stirring effect of the same. In the die or mould occurs the cooling of the surface or skin of the metal bar that is generated in the die itself and, in correspondence with the outlet of the metal bar from the die or mould, it presents a solidified perimetrical zone or shell having a 10-30 mm thickness inside which there is a nucleus in which the metallic material is still at the melted state and that is progressively solidified when the metallic bar advances within a cooling chamber of the casting machine in which it is subject to the action of cooling groups that in general consist of sets of water sprayers. Applications of the stirrers both in correspondence with the die or mould within which the introduction of the melted metallic material occurs and applications of the stirrer at the cooling chamber of the casting machine to obtain qualitative improvements of the metallic bar structure to reduce the occurrence of deficiencies during the solidifying phase are known. The stirrer consists of a housing inside which some electrical windings are placed for the passage of the current that induces the electromagnetic stirring field and the housing presents an open duct within which the incandescent metallic bar in the formation process passes. For example the recourse to the stirrers contributes to reduce inclusions and surface and subcutaneous blowholes, cracks, porosity, segregation and contributes to improve the solidifying structures.

The prior art stirrers are usually mounted in fixed position determined on the basis of the characteristics of the casting machine and of the process according to a solution of compromise between the optimal different positions that would be required according to the process variations and to the sections of the cast metallic bars.

The Patent Application EP 2127783 A1 describes an electromagnetic stirrer that is intended to be installed around the steel discharger from the tundish to the mould of a continuous casting machine, in which the electromagnetic stirrer including a nucleus composed of two different circumferential portions around which a plurality of windings is wound.

The Patent Application US 2008/164004 A1 describes an electromagnetic stirrer that is intended to be installed along different billet portions in the process of production in a continuous casting machine.

Problems of the prior art

The stirrers that are applied inside the cooling chamber and that operate on the still melted nucleus present internally to the metal bar in the formation process have some drawbacks. First of all the position in which the stirrer is applied remains fixed for the whole process. Since its effect on the still melted nucleus depends strongly on the solidifying phase in which the metallic bar is found at the installation zone of the stirrer itself, it isn't possible keeping into account variations of the solidifying conditions that may happen for example due to variations in the casting temperatures of the melted metallic material in the die or mould, to the extraction speed of the bar in the formation process, to the section shrinkage along the casting line, to the composition of the metallic material, etc. Consequently in the prior art techniques the effectiveness of the stirrers applied in the cooling chamber is often compromised because the positioning of the stirrer along the bar in the formation process is the result of a compromise that does not keep into account the real conditions that may occur during the casting phase and that can change continuously.

Furthermore during the casting phase different drawbacks may occur that can damage gravely and irreparably the stirrers applied in the cooling chamber. For example during the casting may happen a phenomenon known with the name of break-out that involves the breakage of the skin or of the solid shell containing the metallic material nucleus still at the melted state. Consequently the melted metallic material nucleus exits from the bar in the formation process and outflows within the casting chamber with the consequence that it may run over the stirrer and definitively compromise its functionality for prolonged time periods. In fact in case of damage it will be necessary to remove the stirrer from the casting machine and to provide to its replacement or to its repair that could involve long times during which the functionality of the stirrer cannot be used. Further problems are liable to occur in case of interruption of the electrical energy feeding for the casting machine functioning. In this case the cooling devices of the stirrer interrupt the cooling liquid flow leaving the stirrer exposed to the heat coming from the metallic bar that remains blocked in the passage duct inside the stirrer with the risk of serious damages to the stirrer internal windings.

Furthermore the prior art techniques providing the presence of stirring devices within the casting chamber have problems from the point of view of the casting machine set-up times because their position should be modified according to the process parameters, e.g. according to the metal alloy that is cast, to the shape in section of the bar that is produced and to the size in section of the bar itself. However it is not always possible to ensure the correct positioning of the stirrers in correspondence with the estimated optimal point for the action of the stirrer and sometimes the optimal positioning of the stirrer must be wasted to increase the machine fitting-out times, involving, therefore, not-optimal results.

Furthermore the movement of the stirrers during the casting process is not possible because of the presence of the support mechanisms of the casting machine that would prevent their sliding because of the interference problems between the body of the stirrer and the same mechanisms.

Aim of the invention

The aim of this invention is to supply a stirrer intended to be applied within the cooling chamber of a casting machine that allows a greater effectiveness in the stirring action with respect to the stirring devices of the prior art.

Further aim of the present invention is to allow an effective positioning of the stirrer in the optimal operative zone according to the operative parameters of the casting in progress.

Further aim of the present invention is to supply a stirrer endowed with safety means that in emergency conditions allow to put in safety the stirrer itself in these conditions.

Concept of the invention

The aim is reached with the characteristics of the main claim. The sub-claims represent advantageous solutions.

Advantageous effects of the invention

The solution in accordance with the present invention, by the considerable creative contribution the effect of which constitutes an immediate and not-negligible technical progress, presents various advantages.

With the solution according to the present invention applied to a casting machine, obtaining products of the casting machine in the form of bars having the best quality with respect to the bars made by casting machines equipped with traditional stirrers, is possible.

Moreover with the solution according to the present invention obtaining a more protected stirrer with reference to emergency conditions that may happen inside the cooling chamber of the casting machine e.g. in the case of break-out, namely breakage of the skin or shell of the metal bar in the formation process, or interruption of the feeding electric current of the same casting machine apparatuses is possible.

Furthermore with the solution according to the present invention it is possible a faster fitting- out of the casting machine according to the process parameters, e.g. according to the metal alloy that is cast, to the shape in section of the bar that is produced and to the size in section of the same bar. A fast fitting-out of the machine has important implications from the economical point of view because prolonged stop times endanger the reaching of large production amounts with consequent minor exploitation of the production capacity of the casting machine and less results.

Description of the drawings

It is in the following described a solution realizable with reference to the included drawings to be considered namely non-limited example of the present invention in which:

Fig. 1 represents schematically a three-dimensional view of the stirrer made in conformity with the present invention in closing condition of the stirrer body.

Fig. 2 represents schematically a three-dimensional view of the stirrer of Fig. 1 in opening condition of the stirrer body.

Fig. 3 represents schematically a plan view of the stirrer of Fig. 1 in closing condition of the stirrer body.

Fig. 4 represents schematically a plan view of the stirrer of Fig. 3 in opening condition of the stirrer body.

Fig. 5 represents schematically a side-view of the stirrer of Fig. 3.

Fig. 6 represents schematically a plan view of the stirrer of Fig. 4 in which the body containing the induction windings has been partially sectioned to leave visible the inside of the same body.

Fig. 7 represents schematically a three-dimensional plan view of the stirrer of Fig. 1 in which the body containing the induction windings has been partially sectioned to leave visible the inside of the same body.

Fig. 8 represents schematically the application of the stirrer according to the present invention in a vertical casting machine in a first operating position in closing condition of the stirrer body.

Fig. 9 represents schematically the application of the stirrer according to the present invention in a vertical casting machine in the first position of Fig. 8 in condition of opening the body of the stirrer.

Fig. 10 represents schematically the application of the stirrer according to the present invention in a vertical casting machine in a second position in opening condition of the stirrer body.

Fig. 11 represents schematically the application of the stirrer according to the present invention in a vertical casting machine in the second position of Fig. 10 in closing condition of the stirrer body.

Fig. 12 represents schematically the application of the stirrer according to the present invention in a casting machine endowed with bending in a first operating position.

Fig. 13 represents schematically the application of the stirrer according to the present invention in a casting machine endowed with bending in a second operating position.

Fig. 14 represents schematically the application of the stirrer according to the present invention in a parking position.

Fig. 15 represents schematically the application of a couple of stirrers according to the present invention in a casting machine equipped with bending in which a first stirrer acts in correspondence with a first operating position and in which a second stirrer acts in correspondence with a second operating position.

Fig. 16 represents schematically the solidifying profile of a metallic bar in a casting machine endowed with bending.

Fig. 17 represents a chart showing the temperature profile of a metallic bar in a casting machine according to the distance from the meniscus.

Fig. 18 represents a chart showing the solidifying profile of a metallic bar in a casting machine according to the distance from the meniscus.

Fig. 19 represents schematically the application of a stirrer according to the present invention in a vertical casting machine in which also a possible embodiment of the movement system is shown.

Description of the invention

Referring to the figures (Fig. 1 , Fig. 2, Fig. 3, Fig. 4, Fig. 5) the present invention relates to an electromagnetic stirring device (1) of melted metallic material of the type usually called "stirrer". The electromagnetic stirring device (1) according to the present invention is intended to be applied (Fig. 12, Fig. 13, Fig. 14, Fig. 15) within a cooling chamber (30) of a casting machine (18). The application is intended both for vertical type casting machines (Fig. 8, Fig. 9, Fig. 10, Fig. 11) and for casting machines endowed with bending (Fig. 12, Fig. 13, Fig. 14, Fig. 15), namely those in which the melted metallic material is cast from a tundish (19) within a mould (14) placed below the tundish (19) and in which the metallic material bar (16) exits from the mould below according to a vertical exit direction and is then bent to come out horizontally from the casting machine (18) in correspondence with an extraction and straightening group (20) that provides both to the movement of the metallic material bar (16) and to its straightening to obtain rectilinear bars that may be, only as an example and without limitation within the aim of the present invention, billets, blooms or flat blooms with different shapes in section e.g. with square, rectangular, round, polygonal section. Herein description and in the appended claims with the expression "casting machine", therefore are meant both vertical casting machines and casting machines endowed with bending. The electromagnetic stirring device (1) applies a stirring force by means of application of a current generating an electromagnetic field through windings or induction coils (12). With illustrative aim and without limitations with the aim of the present invention the currents generating the electromagnetic field can be alternated currents of frequency between 5 and 50 Hertz with intensity between 300 and 1000 Ampere. The stirring force acts in correspondence with a partially solidified metallic material bar (16) that moves (Fig. 12, Fig. 13, Fig. 14, Fig. 15) within the cooling chamber (30). When the metallic material bar (16) exits from the mould (14) it is not yet in a complete solidified condition but the metallic material bar (16) consists (Fig. 16) of a shell (22) at the solid state enclosing a nucleus (23) at the melted state. The electromagnetic stirring device (1 ) acts and applies its action by means of the electromagnetic stirring field on the nucleus (23) at the melted state. The electromagnetic stirring device (1) includes (Fig. 1 , Fig. 2, Fig. 3, Fig. 4, Fig. 5) a retaining body (28) of the (Fig. 6, Fig. 7) induction coils (12) and the body (28) is supplied with a duct (27) inside the body itself intended to the passage of the metallic material bar (16). With the expression "internal duct" it s meant to comprise both a configuration in which the body constitutes a closed shape holding inside the duct, and a configuration in which the body constitutes a shape endowed with possible perimetrical openings and in which the body circumscribes the duct. The body is composed of portions (2, 3) intended to be moved by means of driving means (6) between at least two configurations and further the electromagnetic stirring device (1) is associated and/or associable to driving means (7, 8) of the electromagnetic stirring device (1) along the development in length of the metallic material bar (16). In particular the body (28) is composed of (Fig. 1 , Fig. 2, Fig. 3, Fig. 4, Fig. 5) at least two portions (2, 3). Though in the form of execution shown reference is made to a representative and illustrative solution in which there are two portions (2, 3), the present invention is not limited to this embodiment, the body (28) being able to be made also by means of the combination of a greater number of portions, e.g. three portions, four portions, etc. The portions can be both identical and different to one another provided that from their combination derives a body (28) suitable to surround even only partially the metallic material bar (16), if necessary also with open zones between one portion and the following portion in which the open zones have extension in length minor than the extension in length of the same portions. The preferred solution of the present invention, however, provides the recourse to two portions (2, 3).

The portions (2, 3) are intended to be moved by means of driving means (6) between at least two configurations of which:

- a first configuration is a configuration in which the at least two portions (2, 3) are reciprocally close to each other and the body (28) is essentially close and surrounds and defines a duct (27) internal to said body intended for the passage of said metallic material bar (16) for the action of said electromagnetic field on said metallic material bar (16);

- a second configuration is a configuration in which the at least two portions (2, 3) are reciprocally spaced and the body (28) is essentially opened and endowed with at least one opening (29), whose aim will be cleared in the following of the present description.

In the preferred solution of the present invention (Fig. 1 , Fig. 8, Fig. 12) the electromagnetic stirring device (1) includes coupling means (8) with a guide (7) intended for the movement of the electromagnetic stirring device (1) along such guide (7). The guide develops (Fig. 8, Fig. 12) in an essentially parallel direction with respect to the metallic material bar (16) that exits from the mould (14) and crosses the cooling chamber (30). The development in length of the guide (7) regards at least one portion of the total development of the metallic material bar (16) within the cooling chamber (30). The electromagnetic stirring device (1) is endowed with and/or is associable to movement motorized means intended for the movement (Fig. 9, Fig. 10) of the device itself along the guide (7) with positioning of the electromagnetic stirring device (1) in different operative positions along the guide (7) intended for the application of the stirring force in correspondence with different positions of the metallic material bar (16). It is understood, therefore, as the solution according to the present invention shows undoubted advantages from the point of view of the fitting-out times of the machine as the positioning of the device in the optimal position, estimated on the base for example of the shape and/or size of the bar, will be particularly fast, particularly at the time of production changes from a casting shape to another casting shape, without requiring the intervention of operators within the casting chamber for the correct positioning of the electromagnetic stirring device (1).

The portions (2, 3) of the body (28) contain (Fig. 6, Fig. 7) a series of induction coils (12). Each series of induction coils (12) can be composed of at least one of these induction coils (2), preferably two induction coils (12), even more preferably three induction coils (12). In the represented illustrative solution each portion (2, 3) includes a series of three induction coils (12) circumferentially placed around the center (31) of the body (28), but it will be evident that also solutions with a greater or minor number of induction coils (12) will be provided in function of the total size of the body (28) and/or of each portion (2, 3). For example in the case of casting machines designed for the execution of small size bars (billets) applications may be provided with one or two or three induction coils for each portion and in the case of casting machines designed for the execution of large size bars (blooms) applications may be provided with three or four or five induction coils for each portion. In similar way also in the case of execution of a body (28) subdivided in more than two portions, e.g. in three or four portions, the number of the coils housed in each portion may be decreasing on the increasing of the number of subdivision portions of the body. The induction coils (12) are preferably structured and configured according to a configuration with couples of induction coils which are opposite (12) with respect to the center (31) of the duct (27), the induction coils (12) being intended to constitute a multi-phase and multi-pole arrangement circumferentially located around the duct (28). If necessary it may be provided also the resort to some portions that are not endowed with coils at their inside but that are intended to constitute coupling elements with the portions endowed with induction coils. Preferably each of these induction coils (12) is composed of at least one pack (32) of windings, preferably two packs or three packs of windings placed adjacent to each other according to a radial direction (33) with respect to the center (31) of the duct (27). In the represented solution (Fig. 6) each of the induction coils (12) is composed of two packs (32) of windings placed one adjacent to the other and mounted on a support (13) housed within a closing housing (11) of the portion in its whole.

In the preferred solution of the present invention the body (28) is composed of two movable portions (2, 3) that are a first portion (2) and a second portion (3) reciprocally hinged at a hinging point (9) in correspondence with one end for the coupling between the two portions. Preferably the portions (2, 3) are reciprocally symmetrical semicircular portions.

In the shown realizable solution (Fig. 4, Fig. 5) the portions (2, 3) are supported by supporting arms (4, 5) intended to be moved by means of said driving means (6). For example in the shown solution a first portion (2) is supported by a first arm (4) and a second portion (3) is supported by a second arm (5). The driving means are preferably at least one driving piston acting on the arms (4, 5) and intended to apply a pushing and/or traction action of an arm (5, 6) with respect to another arm (4, 5). Even more preferably the driving means are at least one driving piston for each of said arms (4, 5) and the piston is intended to act in correspondence with one first end on the corresponding arm and at the opposite end of the piston itself on a supporting frame (34) of the arms (4, 5) in correspondence of the which there is also the hinging point (9).

Though in the form of execution shown the coupling means (8) are a trolley endowed with wheels intended to slide on a guide (7) in the form of a beam with "H" like profile, it will be evident that innumerable embodiments of the guide system of the electromagnetic stirring device (1 ) that are meant to be included in the aim of the appended claims are possible.

Advantageously the electromagnetic stirring device (1) according to the present invention can also include (Fig. 14) at least one protection housing (26) in correspondence with an end of the guide (7). the protection housing (26) being intended to house inside it the electromagnetic stirring device (1). This solution is particularly advantageous because in case of emergency events the electromagnetic stirring device (1) can be controlled by a control unit (21) for performing an emergency sequence intended to put in safety the same device. For example in case of the phenomenon known with the name of "breakout", namely in the case of breakage of the shell or skin (22) with outflow of the liquid fraction of the nucleus (23) within the casting chamber (30), the electromagnetic stirring device (1) can be controlled for the execution of an emergency procedure in which the portions (2, 3) are rapidly carried in the reciprocally spaced configuration and the electromagnetic stirring device (1) is carried within the protection housing (26) to protect it from squirts or melted material casts preserving its integrity. For example the protection housing (26) can be placed in correspondence with a last end (25) of the guide (7), namely at the last end (25) of the guide that is the opposite end with respect to a first end (24) placed near the mould (14) of the machine (18).

Independently on the presence or less of the protection housing (26) the solution according to the present invention allows important benefits from the point of view of the integrity of the electromagnetic stirring device (1) in the emergency situations because the reciprocal opening of the movable portions (2, 3) in itself already reduces the device heating by radiation. Furthermore the emergency phase can provide, once the reciprocal opening of the movable portions (2, 3 ) has happened, also the removal of the electromagnetic stirring device (1) from a zone subject to greater heat to a zone subject to less heat and less exposed to the risk of metal squirts, namely from a zone close to the mould to a zone far from the mould and at the most, if necessary but not necessarily, external to the same casting machine.

In the preferred solution of the present invention the body (28) is composed of two movable portions (2, 3) that are a first portion (2) and a second portion (3) reciprocally hinged at a hinging point (9) in correspondence with a coupling end between the two portions. Preferably the portions (2, 3) are reciprocally symmetrical semicircular portions.

Each portion (2, 3) will be endowed with at least one inlet and at least one outlet intended to the feeding of a cooling fluid of the induction coils (12) to discharge the heat coming from the bar (16). The cooling fluid can circulate internally to the portions (2, 3) according to a configuration in which the induction coils (12) are immersed in a flow of this cooling fluid which circulates between the at least one inlet and the at least one outlet and/or according to a configuration in which said cooling fluid circulates internally to a metallic conductor preferably made of copper which is a hollow conductor which is wound according to a circular shape to make such induction coils (12). The cooling fluid can be delivered to the portions (2, 3) by interconnection means (10) with a delivery duct of fluids.

The electromagnetic stirring device (1) can also comprise at least one temperature sensor (35), preferably at least one temperature sensor of (35) for each of the portions (2, 3), even more preferably a temperature sensor (35) for each of the induction coils (12). The temperature sensor (35) is intended for the measurement of temperature of the induction coils (12). Further the electromagnetic stirring device (1 ) can comprise also emergency opening means (37) of the portions (2, 3). The emergency opening means (37) being intended to move the portions (2, 3) from the first configuration in which the portions (2, 3) are reciprocally close to the second configuration in which the portions (2, 3) are reciprocally spaced. This solution is particularly advantageous in case of lack of suitable cooling fluid that could bring to a raising of the temperature with damage for the induction coils (12) or in case of interruption of the feeding of the electric power to the casting machine. In this condition usually is maintained only the circulation of the cooling fluid closely necessary to manage the maximum emergency conditions of this situation and, therefore, the electromagnetic stirring device (1) would be exposed to the heat coming from the bar (16) without suitable cooling. The opening of the portions would increase the distance of the coils from the incandescent bar preserving the same coils. Furthermore it may be provided also the release of braking devices of the device so that it, by gravity, will move to a position of the guide where the bar has a lower temperature. For example the emergency opening means (37) can include activation means intended to control said emergency opening means (37) following the exceeding of a temperature threshold measured by means of the temperature sensor/s (35). The activation means can be directly managed on the device to manage also the case of lack of electric power in the casting machine and/or can be managed by the control unit (21). The control unit (21) can be indifferently made in the form of a personal computer, a personal industrial computer or a programmable logic controller (PLC), a dedicated electronic card or equivalent means. The emergency opening means (37) can include, for example, pushing means in the form of elastic mechanical means and/or pushing springs and/or pushing means in the form of pushing piston operated by container of air or gas, possibly a noble gas.

This invention relates also to a casting machine (18) for the production of metallic material bars (16) in which the metallic material at the melted state is cast (Fig. 12) from a tundish (19) within a mould (14) placed below the tundish (19) and in which the metallic material bar (16) exits from the mould (14) below the same to come across a cooling chamber (30) and characterised in that it comprises at least one of the electromagnetic stirring devices (1) made according to the present invention within such cooling chamber (30). The casting machine (18) can comprise even more than one of the inventive electromagnetic stirring devices (1), e.g. at least two, for example two or three or more, of these electromagnetic stirring devices (1), each of these electromagnetic stirring devices (1) comprising the previously described coupling means (8) with a corresponding guide (7) or intended to be moved independently one from the other and/or coordinated with each other along a same common guide (7). This solution is advantageous because one of the electromagnetic stirring devices (1) can perform an action in the first section of the bar and the other can perform its action in the zone of the bar foot, namely the closest zone to the exit of the bar from the casting machine with the advantage that both can be placed in optimal position with respect to the casting parameters and further with the advantage that both can be carried in protected position in case of emergency.

This invention relates also to a casting process for the production of metallic material bars (16) comprising a casting phase in which the metallic material is cast within a mould (14) of the casting machine (18) for extracting the metallic material bar (16) from the mould (14), the metallic material bar (16) exiting from the mould (14) being partially solidified and moving within the cooling chamber (30). The process provides one or more stirring phases of the material at the melted state constituting the nucleus (23) of the metallic material bar (16) within the cooling chamber (30) and the stirring phase of the material at the melted state constituting such nucleus occurs by means of at least one of the inventive electromagnetic stirring devices (1).

The casting process can include at least one movement phase of one or more of these electromagnetic stirring devices (1) by said movement means (7, 8), for example along the respective guide (7), this movement phase happening before of the starting of this casting phase and/or during the casting phase.

In the casting process according to the present invention, the movement phase can provide the following steps for at least one of the inventive electromagnetic stirring devices (1):

- activation of the driving means (6) with movement of the at least two portions (2, 3) from the first configuration in which the at least two portions (2, 3) are reciprocally close to the second configuration in which the at least two portions (2, 3) are reciprocally spaced;

- activation of the motorized means of movement intended for the movement of the electromagnetic stirring device (1) along the guide (7) with displacement along this guide (7) of the electromagnetic stirring device (1) itself from a first operative position to a second operating position different with respect to this first operating position;

- activation of the driving means (6) with movement of the at least two portions (2, 3) from the second configuration in which the at least two portions (2, 3) are reciprocally spaced to the first configuration in which the at least two portions (2, 3) are reciprocally close.

In the casting process according to this invention such second operating position will be preferably determined at least for one of the electromagnetic stirring devices (1) referring to the distance (d) from the meniscus (15) and/or referring to an equivalent reference point of the casting machine. The meniscus (15) is the interface within the mould (14) constituting the starting of the formation of the bar (16) and corresponding to the level at which the metallic material poured at the melted state is maintained within the mould (14). The reckoning of the operative position will occur preferably on the base of parameters and data describing the casting process including estimated cooling curve of the metallic material bar (16) and/or shapes in section of the metallic material bar (16) and/or size in section of the metallic material bar (16) and/or casting or extraction speed and/or temperature of the metallic material within the mould (14) and/or temperature of the metallic material within the tundish (19) feeding the metallic material at the melted state within the mould (14) and/or temperature of the metallic material within the ladle (not represented) feeding the metallic material at the melted state within the tundish (19) and/or composition of the metallic material at the melted state and/or temperature of the cooling water of the metallic material at the melted state within the mould (14) and/or operative parameters of the casting process.

For example the optimal operative positions can be determined according to the estimation of the ratio between solid fraction and liquid fraction of the partially solidified metallic material bar (16) in correspondence with such operative positions, the solid fraction corresponding to the estimated extension of the shell (22) and the liquid fraction corresponding to the estimated extension of the nucleus (23). In particular (Fig. 18) following the line of solidus it can be seen as the reaching of the condition in which 100 % of solidifying occurs, in the illustrative chart, at a distance (d) of about fifteen metres from the meniscus (15). The solidifying profile can be estimated by a calculation according to the previously indicated parameters according to prior art and, once determined the percentage of solidus (or equivalently the percentage of liquidus or equivalently the ratio between liquid fraction and solid fraction or vice-versa) corresponding to the optimal position for applying the device (1), it will be possible to identify the corresponding optimal position expressed in terms of distance (d) from the meniscus (15), that in the chart (Fig. 18) is in the abscissas. Consequently it will be possible to provide to the movement of one or more devices (1) to place them in the optimal operative positions. In similar way also by means of the estimated temperature profile (Fig. 17) it will be possible to carry out an equivalent evaluation for determining the distance (d) from the meniscus (15) at which one or more devices (1) will be placed according to positions comprised between the exit position of the bar from the mould (14) and the position in which the closure of the solidifying cone occurs, namely the position in which the condition for solidifying the nucleus is reached.

For example at least one first of such operative positions may correspond to a determined value of the relation between solid fraction and liquid fraction in which the thickness of the shell (22) is between 20 % and 60 % with respect to the thickness of the metallic material bar (16), preferably between 30 % and 50%, even more preferably about 40 %.

For example at least one second of said operative positions corresponds to a value of the ratio between solid fraction and liquid fraction in which the thickness of the shell (22) is between 65 % and 85 % with respect to the thickness of the metallic material bar (16), preferably between 70 % and 80 % even more preferably about 75 %.

Example 1

The temperature (Fig. 17) and solidifying profiles (Fig. 18) are estimated starting from the casting parameters relative to the casting of a C40 type steel that is poured within a square mould with side of 160 mm with the following parameters:

Mould section: 160 x 160 mm Steel type: C40

Casting speed: 2.00 m/min Steel range: 401.92 kg/min

Metallurgic length: 14.90 m Temperature in tundish: 1522 °C

Liquidus temperature : 1492 °C Solidus temperature: 1439 °C

Cooling of first zone of the secondary cooling part with 65 l/min on 0.6 metres range

Cooling of second zone of the secondary cooling part with 110 l/min on 2.0 metres range Cooling of the third zone of the secondary cooling part with 58 l/min on 5.0 metres range On the solidifying profile (Fig. 18) the shell thickness is selected corresponding to a first position of application of one first of the electromagnetic stirring devices (1), for example in correspondence with a thickness shell equal to 40 %. It is obtained a first zone (Z1) that constitutes the optimal positioning zone of the first electromagnetic stirring device (1). This first zone (Z1) is identified as the zone comprised between a first value in abscissa that corresponds to the point of intersection between the horizontal straight line corresponding to the thickness of the shell of 40 % and the solid fraction line equal to 0.05 and a second value in abscissa that corresponds to the point of intersection between the horizontal straight line corresponding to the shell thickness of 40 % and the solid fraction line equal to 0.2. In the example represented the first zone (Z1) is approximately comprised between the points having a distance from the meniscus equal to 3 metres and 3.8 metres. The first optimal point (d1), namely the one corresponding to the position of the first electromagnetic stirring device (1) in correspondence with the point in which the estimated shell thickness is equal to 40% is the one corresponding to the point of intersection between the horizontal straight line corresponding to the shell thickness of 40 % and the solid fraction line equal to 0.1. In the example represented the first optimal point (d1) is approximately placed at a distance from the meniscus equal to 3.2 metres. During the casting this evaluation can be repeated in a continuous or discrete way in order to change the position of the first electromagnetic stirring device (1 ) according to the variation of one or more of the previously listed calculation parameters. Example 2

On the basis of the data reported for the example 1 , on the solidifying profile (Fig. 18) the shell thickness is selected corresponding to a second application position of a second one of the electromagnetic stirring devices (1), for example in correspondence with a shell thickness equal to 75 %. It is obtained a second zone (Z2) that constitutes the optimal positioning zone of the second electromagnetic stirring device (1). This second zone (Z2) is identified as the zone comprised between a first value in abscissa that corresponds to the point of intersection between the horizontal straight line corresponding to the shell thickness of 75 % and the solid fraction line equal to 0.05 and a second value in abscissa that corresponds to the point of intersection between the horizontal straight line corresponding to the shell thickness of 75 % and the solid fraction line equal to 0.2. In the example represented the second zone (Z2) is approximately comprised between the points having a distance from the meniscus equal to 8.4 metres and 10 metres. The second optimal point (d2), namely the one corresponding to the position of the second electromagnetic stirring device (1) in correspondence with the point in which the estimated shell thickness is equal to 75 % is the one corresponding to the point of intersection between the horizontal straight line corresponding to the shell thickness of 75 % and the solid fraction line equal to 0.1. In the example represented the second optimal point (d2) is approximately placed at a distance from the meniscus equal to 9.2 metres. During the casting this evaluation can be repeated in a continuous or discrete way in order to change the position of the second electromagnetic stirring device (1) according to the variation of one or more of the previously listed calculation parameters.

Example 3

On the basis of the example 2, the influence on the optimal positioning of the second electromagnetic stirring device (1) has been valued according to the type of steel and casting rate, estimating the corresponding solidifying sections and obtaining the results reported in the following in Table 1. Table 1

SQUARE SECTION 1 60

Steel Casting speed Optimal position d2

type [m/min] Distance from meniscusfm]

1.8 10.3

35KB

2.0 11.6

1.8 10.0

C40

2.0 11.4

1.8 10.6

lfiMnCrs

2.0 12.1

Example 4

On the basis of the example 2, the influence on the optimal positioning of the second electromagnetic stirring device (1) has been valued according to the type of steel and casting speed for a different size in section of the metallic bar that in this case has square section with a side of 180 mm instead than of 160 mm. By way of example it should be pointed out that in this case also other operative parameters change e.g. the cooling ranges to keep into account the greater size of the metallic material bar.

Cooling of first zone of the secondary cooling part with range of 82 l/min on 0.6 metres

Cooling of second zone of the secondary cooling part with range of 139 l/min on 2.0 metres Cooling of third zone of the secondary cooling part with range of 73 l/min on 5.0 metres estimating the corresponding solidifying profiles and obtaining the results reported in the following in Table 2

As it can be seen from the tables the optimal position of the electromagnetic stirring device (1 ) may change also considerably according to the steel type, to the casting speed, to the section of the metallic material bar. Therefore it is understood that the advantage of the electromagnetic stirring device (1 ) according to the present invention both in the case in which the movement is used during the first phase of the casting machine fitting-out, which is carried out in function of the type of steel that must be cast, and in the case in which the movement is used during the casting for adapting the position of the device itself with respect to the real casting parameters that can suffer also important variations with respect to the initially provided parameters. It follows that the consequences of the present invention in terms of speed of the fitting-out time of the machine and of quality of the produced steel are important.

Advantageously the operative positions are determined in a continuous way along the development of the metallic material bar (16) within the cooling chamber (30) according to the previously enunciated parameters and data describing the casting process and according to the presence of interference zones with accessories (17, 36) of the casting machine (18) precluding the positioning of the electromagnetic stirring devices (1 ) in correspondence with such interference zones. In fact though the solution according to the present invention allows to obtain a positioning in a continuous way along the bar in the process of solidifying it is necessary to observe that not all the positions are actually practicable because of the presence, for example, of sprayers (36) or rollers (17) that could interfere with the device (1 ). In addition to the safeguard of the coils (12) in the emergency conditions, therefore, the solution according to the present invention with portions (2, 3) which may be reciprocally spaced or drawn closer on the bar (16), also allows to obtain the maximum stirring effect in the condition with the portions (2, 3) drawn closer that corresponds to the highest filling factor of the duct (27) and at the same time allows the movement of the device between positions placed on opposite sides with respect to such accessories (17, 36) that preclude the positioning of the electromagnetic stirring devices (1) and that could be damaged by the passage of the same devices if they were not equipped with the opening system described. Furthermore in the casting process the stirring phase of the material at the melted state constituting the nucleus of the bar can happen by means of at least two of these electromagnetic stirring devices (1 ), this casting process comprising stirring phases of the material at the melted state constituting the nucleus in which:

- a first phase provides the disjoined action of these electromagnetic stirring devices (1) in reciprocally spaced operative positions (Fig. 15) along the total development of the metallic material bar (16) within the cooling chamber (30);

- a second phase provides the combined action of at least two of these electromagnetic stirring devices (1) in reciprocally close operative positions along the total development of the metallic material bar (16) within the cooling chamber (30), such at least two electromagnetic stirring devices (1) which operate in combination one next to the other with effect of combination and interaction of the respective Electromagnetic fields generating the stirring force,! each of these at least two electromagnetic stirring devices (1) being controlled with a generation signal of the electromagnetic field at a determined operative frequency, the operative frequencies of these electromagnetic stirring devices (1) in reciprocally close operative positions being selected from the group consisting of identical frequencies for all such electromagnetic stirring devices (1), slightly different frequencies for each of these electromagnetic stirring devices (1) with respect to the operative frequency of the adjacent electromagnetic stirring device (1), different frequencies for each of these electromagnetic stirring devices (1) with respect to the operative frequency of the adjacent electromagnetic stirring device (1).

The movement system (Fig. 19) according to one embodiment can include a motor (38) acting on a traction means (40) that for example can be made by a cable or equivalent means that are made pass in a series of pulleys (41) and to which a counterweight (39) is fixed in order to reduce the effort of the motor. This solution presents the advantage that allows to position the motor and the transmission devices in a protected position, at the most even outside of the casting chamber or anyway in a destined space situated within the same. In this way in case of problems, e.g. steel squirts due to a breakage of the skin of the bar, the motor and the transmission devices will be advantageously protected either due to the position far from the bar or to the possible presence of a protection space. It will be however evident that it will be possible to provide also other types of movement systems as, e.g. rack structures, telescopic systems that are considered as equivalent movement means with the aim of the present invention.

The connection of the electrical users of the electromagnetic stirring device (1) preferably occurs by means of a connection box (42) placed in protected position and preferably near the intermediate position with respect to the complete excursion of the movement of the electromagnetic stirring device (1) along the guide (7). The connection can happen by means of one or more electric cables (43) of flexible type in order to ensure the liberty of movement of the electromagnetic stirring device of (1) along the guide (7), possibly by means of the passage in a fairlead chain (not represented). In an absolutely! similar way the connection of the hydraulic users can happen by means of one or more flexible pipes for fluids (44) for feeding a cooling fluid of the induction coils (12) to discharge the heat coming from the bar (16).

The description of the present invention has been done with reference to figures enclosed in a form of preferred embodiment of the same, but it is evident that many possible alterations, changes and variants will be immediately clear to those skilled in the art of the sector in view of the previous description. So, it should be stressed that the invention is not limited by the previous description, but contains all alterations, changes and variants in accordance with the appended claims.

Used nomenclature

With reference to the identification numbers reported in the enclosed figures, it has been used the following nomenclature:

I . Stirrer device or electromagnetic stirring device

2. First portion

3. Second portion

4. First arm

5. Second arm

6. Driving means or piston

7. Guide

8. Coupling means

9. Hinging

10. Interconnection means

I I . Casing

12. Winding or induction coil

13. Support

14. Mould

15. Meniscus

16. Metallic bar or metallic material bar j

17. Roller

18. Casting machine

19. Tundish

20. Extraction and straightening group 21. Control unit

22. Solid fraction or shell or skin

23. Liquid fraction or nucleus

24. First end

25. Last end

26. Protection housing

27. Duct

28. Body

29. Opening

30. Cooling chamber

31. Center

32. Pack of windings

33. Radial direction

34. Frame

35. Temperature sensor

36. Sprayers

37. Opening means in emergency

38. Motor

39. Counterweight

40. Traction means

41. Pulley

42. Connection box

43. Electric cable

44. Flexible pipe for fluids | d. distance from the meniscus

Claims

1. Electromagnetic stirring device (1) of melted metallic materials inside a cooling chamber (30) of a casting machine (18) in which said electromagnetic stirring device (1) applies a stirring force by means of application of a current generating an electromagnetic field through induction coils (12), said stirring force acting in correspondence with a partially solidified metallic material bar (16) which moves within said cooling chamber (30), said metallic material bar (16) consisting of a shell (22) at the solid state enclosing a nucleus (23) at the melted state which is intended to be subject to the action of said stirring electromagnetic field, said electromagnetic stirring device (1) comprising a retaining body (28) of said induction coils (12), said body (28) being provided with a duct (27) internal to said body which is intended for the passage of said metallic material bar (16) in which said body (28) is composed of portions (2, 3) which are intended to be moved by means of driving means (6) between at least two configurations characterized in that said electromagnetic stirring device (1) is associated and/or associable to movement means (7, 8) to move said electromagnetic stirring device (1) along the development in length of said metallic material bar (16), said movement means (7, 8) being intended to the movement of said electromagnetic stirring device (1) along guide means developing in an essentially parallel direction with respect to said metallic material bar (16) at least for a portion of the total development in length of said metallic material bar (16) in different operative positions along said metallic material bar (16)

2. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to the previous claim characterized in that

said body (28) is composed of at least two of said portions (2, 3) which are portions intended to be moved by means of said driving means (6) between at least two configurations of which: j I

- a first configuration is a configuration in which said at least two portions (2, 3) are reciprocally close to each other and said body (28) is an essentially closed body which surrounds and defines said duct (27) internally with respect to said body which is intended for the passage of said metallic material bar (16) for the action of said electromagnetic field on said metallic material bar (16);

- a second configuration is a configuration in which said at least two portions (2, 3) are reciprocally spaced and said body (28) is an essentially opened body and it is provided with at least one opening (29).

3. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 1 to 2 characterized in that

said movement means (7, 8) include coupling means (8) intended to couple with said guide means (7) which are realized in the form of a guide (7), said movement means (7, 8) intended for the movement of said electromagnetic stirring device (1) along said guide (7), said guide developing in an essentially parallel direction with respect to said metallic material bar (16) at least for a portion of the total development in length of said metallic material bar (16) within said cooling chamber (30), said electromagnetic stirring device (1) being provided and/or associable to motorized means intended for the movement of said electromagnetic stirring device (1) along said guide (7) in different operative positions along said guide (7) which are intended for the application of said stirring force in correspondence with different positions of said metallic material bar (16).

4. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to the previous claim characterized in that

said motorized means are a motor (38) which operates on a traction means (40) passing in a series of pulleys (41), to said traction means a counterweight (39) being associated which is intended to reduce the effort of said motor (38), said traction means (40) being connected to said electromagnetic stirring device (1) for the transmission of the traction action applied by said motor (38).

5. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 1 to 4 characterized in that

said portions (2, 3) of said body (28) contain a series of said induction coils (12), said series of said induction coils (12) consisting of at least one of said induction coils (2), preferably two induction coils (12), even more preferably three induction coils (12), said induction coils (12) being structured and configured according to a configuration with couples of induction coils (12) which are opposite with respect to the center (31) of said duct (27), said induction coils (12) being intended to constitute a multi phase and multi pole arrangement which is circumferentially located around said duct (27).

6. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to the previous claim characterized in that

each of said induction coils (12) is composed of at least one pack (32) of windings, preferably two packs or three packs of windings which are placed adjacent to each other according to a radial direction (33) with respect to the center (31) of said duct (27).

7. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 1 to 6 characterized in that

said portions (2, 3) of said body (28) which are intended to be moved are two.

8. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to the previous claim characterized in that

said two portions (2, 3) are a first portion (2) and a second portion (3) which are reciprocally hinged at a hinging point (9).

9. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 7 to 8 characterized in that

said portions (2, 3) are reciprocally symmetrical semicircular portions.

10. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 1 to 9 characterized in that

said portions (2, 3) are supported by supporting arms (4, 5) which are intended to be moved by means of said driving means (6), said driving means being at least one driving piston acting on said arms (4, 5) and intended to apply a pushing and/or traction action of one of said arms (4, 5) with respect to another of said arms (4, 5), preferably said driving means being at least one operating piston for each of said arms (4, 5) which is intended to act in correspondence with a first end on the corresponding arm and at the opposite end of said piston on a supporting frame (34) of said arms (4, 5).

11. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 3 to 10 characterized in that

said movement means (7, 8) include a trolley which is provided with wheels which are intended to slide on said guide (7).

12. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 3 to 11 characterized in that

it includes at least one protection housing (26) in correspondence with an end of said guide (7), said protection housing (26) being intended to house inside of it said electromagnetic stirring device (1).

13. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 1 to 12 characterized in that

each of said portions (2, 3) comprises at least one inlet and at least one outlet which are intended to feed a cooling fluid of said induction coils (12), said cooling fluid being intended to circulate internally to said portions (2, 3) according to a configuration in which said induction coils (12) are immersed in a flow of said cooling fluid which circulates between said at least one inlet and said at least one outlet and/or according to a configuration in which said cooling fluid circulates internally to a metallic conductor preferably made of copper which is a hollow conductor which is wound according to a circular shape to make said induction coils (12).

14. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 2 to 13 characterized in that

it includes emergency opening means (37) of said portions (2, 3), said emergency opening means (37) being intended to move said portions (2, 3) from said first configuration in which said portions (2, 3) are reciprocally close to said second configuration in which said portions (2, 3) are reciprocally spaced.

15. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to the previous claim characterized in that said emergency opening means (37) include pushing means in the form of elastic mechanical means and/or pushing springs and/or pushing means in the form of pushing piston operated by a container of air or gas, possibly a noble gas.

16. Electromagnetic stirring device (1) of melted metallic materials in a casting machine (18) according to any of the previous claims 14 to 16 and according to claim 12 characterized in that said emergency opening means (37) include activation means, said activation means being intended to control said emergency opening means (37) following the detection of the lack of said cooling fluid and/or following the exceeding of a temperature threshold measured by means of at least one temperature sensor (35).

17. Casting machine (18) for the production of said metallic material bars (16) comprising said cooling chamber (30) characterized in that

it includes at least one of said electromagnetic stirring devices (1) made according to any of the previous claims 1 to 16.

18. Casting machine (18) for the production of said metallic material bars (16) according to the previous claim characterized in that

it includes at least two of said electromagnetic stirring devices (1 ), each of said electromagnetic stirring devices (1) being associated and/or associable to said movement means (7, 8) to move said electromagnetic stirring device (1) along the development in length of said metallic material bar (16).

19. Casting machine (18) for the production of said metallic material bars (16) according to the previous claim and comprising at least one of said electromagnetic stirring devices (1) made according to any of the previous claims 3 to 16 characterized in that

said electromagnetic stirring devices (1) are intended to be moved along the same guide (7) in an independent way with respect to each other and/or in a coordinated way with respect to each other.

20. Casting process for the production of said metallic material bars (16) comprising a casting phase in which said metallic material is poured within a mould (14) of said casting machine (18) to extract said metallic material bar (16) from said mould (14), said metallic material bar (16) exiting from said mould (14) being partially solidified and moving within said cooling chamber (30), said metallic material bar (16) consisting of a shell (22) at the solid state enclosing a nucleus (23) at the melted state, said casting process providing one or more stirring phases of the material at the melted state constituting said nucleus (23) characterized in that

said stirring phase of the material at the melted state constituting said nucleus occurs by means of at least one of said electromagnetic stirring devices (1) made according to any of the previous claims 1 to 16.

21. Casting process for the production of said metallic material bars (16) according to the previous claim characterized in that

it includes at least one movement phase of one or more of said electromagnetic stirring devices (1) by means of said movement means (7, 8), said movement phase occurring before the beginning of said casting phase and/or during said casting phase.

22. Casting process for the production of said metallic material bars (16) according to the previous claim in which said stirring phase of the material at the melted state occurs by means of at least one of said electromagnetic stirring devices (1) according to any of the previous claims 3 to 16 characterized in that

said movement phase provides the following steps for at least one of said electromagnetic stirring devices (1):

- activation of said driving means (6) with movement of said at least two portions (2, 3) from said first configuration in which said at least two portions (2, 3) are reciprocally close to said second configuration in which said at least two portions (2, 3) are reciprocally spaced;

- activation of said motorized means of movement intended for the movement of said electromagnetic stirring device (1) along said guide (7) with a displacement along said guide (7) of said electromagnetic stirring device (1) from a first operating position to a second operating position different with respect to said first operating position; - activation of said driving means (6) with movement of said at least two portions (2, 3) from said second configuration in which said at least two portions (2, 3) are reciprocally spaced to said first configuration in which said at least two portions (2, 3) are reciprocally close.

23. Casting process for the production of said metallic material bars (16) according to the previous claim characterized in that

said second operating position is determined at least for one of said electromagnetic stirring devices (1) referring to the distance (d) from the meniscus (15) corresponding to the level of said metallic material poured at the melted state within said mould (14), and/or referring to an equivalent reference point of said casting machine, on the basis of parameters and data describing said casting process including estimated cooling curve of said metallic material bar (16) and/or shape in section of said metallic material bar (16) and/or size in section of said metallic material bar (16) and/or casting or extraction speed and/or temperature of said metallic material within said mould (14) and/or temperature of said metallic material within a tundish (19) feeding said metallic material at the melted state within said mould (14) and/or temperature of said metallic material within a ladle feeding said metallic material at the melted state within said tundish (19) and/or composition of said metallic material at the melted state and/or temperature of the cooling water of said metallic material at the melted state within said mould (14) and/or operative parameters of said casting process.

24. Casting process for the production of said metallic material bars (16) according to the previous claim characterized in that

said operative positions are determined according to the estimation of the ratio between solid fraction and liquid fraction of said partially solidified metallic material bar (16) in correspondence with said operative positions and/or according to the thickness of said shell (22) in correspondence with said operative positions, said solid fraction corresponding to the estimated extension of said shell (22) and said liquid fraction corresponding to the estimated extension of said nucleus (23).

25. Casting process for the production of said metallic material bars (16) according to the previous claim characterized in that

at least one first of said operative positions corresponds to a position along said metallic material bar (16) in which the thickness of said shell (22) is between 20 % and 60 % with respect to the thickness of said metallic material bar (16), preferably between 30 % and 50%, even more preferably about 40 %.

26. Casting process for the production of said metallic material bars (16) according to claim 24 characterized in that

at least one second of said operative positions corresponds to a position along said metallic material bar (16) in which the thickness of said shell (22) is between 65 % and 85 % with respect to the thickness of said metallic material bar (16), preferably between 70 % and 80%, even more preferably about 75 %.

27. Casting process for the production of said metallic material bars (16) according to any of the previous claims 23 to 26 characterized in that

said operative positions are determined in a continuous way along the development in length of said metallic material bar (16) within said cooling chamber (30) depending on said parameters and data describing said casting process and according to the presence of interference zones with accessories (17, 36) of said casting machine (18) precluding the positioning of said electromagnetic stirring devices (1 ) in correspondence with said interference zones.

28. Casting process for the production of said metallic material bars (16) according to any of the previous claims 20 to 27 characterized in that

said stirring phase of the material at the melted state constituting said nucleus occurs by means of at least two of said electromagnetic stirring devices (1), said casting process comprising stirring phases of the material at the melted state constituting said nucleus in which:

- a first phase provides the separate action of said electromagnetic stirring devices (1) in operative positions which are reciprocally spaced along the total development of said metallic material bar (16) within said cooling chamber (30); - a second phase provides the combined action of at least two of said electromagnetic stirring devices (1) in reciprocally close operative positions along the total development of said metallic material bar (16) within said cooling chamber (30), said at least two electromagnetic stirring devices (1) operating in combination next to each other with a combination and interaction effect of the respective electromagnetic fields generating said stirring force, each of said at least two electromagnetic stirring devices (1) being controlled by a generation signal of said electromagnetic field at a determined operative frequency, the operative frequencies of said electromagnetic stirring devices (1) in reciprocally close operative positions being selected from the group consisting of identical frequencies for all said electromagnetic stirring devices (1 ), slightly different frequencies for each of said electromagnetic stirring devices (1) with respect to the operative frequency of the adjacent electromagnetic stirring device (1), different frequencies for each of said electromagnetic stirring devices (1) with respect to the operative frequency of the adjacent electromagnetic stirring device (1).