WO2013155367A1 - Alumina forming bimetallic tube for refinery process furnaces and method of making and using - Google Patents
Alumina forming bimetallic tube for refinery process furnaces and method of making and using Download PDFInfo
- Publication number
- WO2013155367A1 WO2013155367A1 PCT/US2013/036290 US2013036290W WO2013155367A1 WO 2013155367 A1 WO2013155367 A1 WO 2013155367A1 US 2013036290 W US2013036290 W US 2013036290W WO 2013155367 A1 WO2013155367 A1 WO 2013155367A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- tube layer
- inner tube
- layer
- alumina
- bimetallic
- Prior art date
Abstract
Description
Claims