WO2013149699A1 - High-pressure radical ethylene polymerization process in which ethylene is polymerized with a specific polyunsaturated olefin grade - Google Patents
High-pressure radical ethylene polymerization process in which ethylene is polymerized with a specific polyunsaturated olefin grade Download PDFInfo
- Publication number
- WO2013149699A1 WO2013149699A1 PCT/EP2013/000726 EP2013000726W WO2013149699A1 WO 2013149699 A1 WO2013149699 A1 WO 2013149699A1 EP 2013000726 W EP2013000726 W EP 2013000726W WO 2013149699 A1 WO2013149699 A1 WO 2013149699A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- polyunsaturated olefin
- ethylene
- grade
- polyunsaturated
- polymerized
- Prior art date
Abstract
Description
Claims