WO2013085480A1 - Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation - Google Patents

Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation Download PDF

Info

Publication number
WO2013085480A1
WO2013085480A1 PCT/US2011/063231 US2011063231W WO2013085480A1 WO 2013085480 A1 WO2013085480 A1 WO 2013085480A1 US 2011063231 W US2011063231 W US 2011063231W WO 2013085480 A1 WO2013085480 A1 WO 2013085480A1
Authority
WO
WIPO (PCT)
Prior art keywords
spacer
glass
spacers
panel
sheet
Prior art date
Application number
PCT/US2011/063231
Other languages
English (en)
Inventor
William RAGGIO
Original Assignee
Rayotek Scientific, Inc.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Rayotek Scientific, Inc. filed Critical Rayotek Scientific, Inc.
Priority to PCT/US2011/063231 priority Critical patent/WO2013085480A1/fr
Publication of WO2013085480A1 publication Critical patent/WO2013085480A1/fr

Abstract

Un panneau en verre isolé sous vide (VIG) selon l'invention comprend des premier et second panneaux en verre et un élément d'espacement est disposé entre les panneaux. L'élément d'espacement est de forme polygonale et traité en renversant et en polissant en les arrondissant tous les coins de l'élément d'espacement et en formant une empreinte de contact circulaire sur les faces latérales opposées de l'élément d'espacement. Les états de rupture de la surface de l'élément d'espacement sont mesurés au moyen d'un équipement de mesure plat optique. L'élément d'espacement est traité thermiquement pour assurer son renforcement. Les éléments d'espacement peuvent être revêtus d'un matériau de revêtement comprenant des particules ayant une taille moyenne inférieure à environ 1 micron. Le matériau de revêtement peut être des particules de polytétrafluoroéthylène.
PCT/US2011/063231 2011-12-05 2011-12-05 Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation WO2013085480A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/US2011/063231 WO2013085480A1 (fr) 2011-12-05 2011-12-05 Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/US2011/063231 WO2013085480A1 (fr) 2011-12-05 2011-12-05 Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation

Publications (1)

Publication Number Publication Date
WO2013085480A1 true WO2013085480A1 (fr) 2013-06-13

Family

ID=48574701

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/US2011/063231 WO2013085480A1 (fr) 2011-12-05 2011-12-05 Panneau en verre isolé sous vide avec des éléments d'espacement à caractéristiques améliorées et son procédé de formation

Country Status (1)

Country Link
WO (1) WO2013085480A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10253550B1 (en) 2015-10-30 2019-04-09 Corning Incorporated Vacuum insulated glass units and methodology for manufacturing the same
WO2019161864A1 (fr) * 2018-02-22 2019-08-29 Vkr Holding A/S Unités de verre d'isolation sous vide basées sur des représentations topographiques
EP4119513A4 (fr) * 2020-03-13 2024-02-28 Nippon Sheet Glass Co Ltd Panneau de verre multicouche sous vide

Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US49167A (en) * 1865-08-01 Improvement in window-glass
US4653680A (en) * 1985-04-25 1987-03-31 Regan Barrie F Apparatus for breaking semiconductor wafers and the like
US5517260A (en) * 1994-03-28 1996-05-14 Vari-Site, Inc. Ophthalmic lens having a progressive multifocal zone and method of manufacturing same
US5721050A (en) * 1993-06-03 1998-02-24 Saint Gobain Vitrage International Glass polyhedrons
US5769297A (en) * 1994-07-20 1998-06-23 Loomis; James W. Apparatus and method for dicing semiconductor wafers
US20010049031A1 (en) * 1999-03-04 2001-12-06 Christopher H. Bajorek Glass substrate for magnetic media and method of making the same
US6420002B1 (en) * 1999-08-18 2002-07-16 Guardian Industries Corp. Vacuum IG unit with spacer/pillar getter
US6677024B2 (en) * 1998-04-29 2004-01-13 Saint-Gobain Glass France Glass spacer
US20070082179A1 (en) * 2005-10-07 2007-04-12 Wade James J Method and apparatus for forming optical articles
US20090280415A1 (en) * 2004-09-13 2009-11-12 Hoya Corporation Transparent substrate for mask blank and mask blank
US20090324858A1 (en) * 2006-12-22 2009-12-31 Futech Gmbh Insulating glazing element, its manufacture and use
US20100323277A1 (en) * 2003-03-27 2010-12-23 Robert Roberts Isotropic nano crystallites of polytetrafluoroethylene (ptfe) resin and products thereof that are biaxially planar oriented and form stable
US20110147219A1 (en) * 2009-12-22 2011-06-23 Rolls-Royce Plc Hydrophobic surface

Patent Citations (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US49167A (en) * 1865-08-01 Improvement in window-glass
US4653680A (en) * 1985-04-25 1987-03-31 Regan Barrie F Apparatus for breaking semiconductor wafers and the like
US5721050A (en) * 1993-06-03 1998-02-24 Saint Gobain Vitrage International Glass polyhedrons
US5517260A (en) * 1994-03-28 1996-05-14 Vari-Site, Inc. Ophthalmic lens having a progressive multifocal zone and method of manufacturing same
US5769297A (en) * 1994-07-20 1998-06-23 Loomis; James W. Apparatus and method for dicing semiconductor wafers
US6677024B2 (en) * 1998-04-29 2004-01-13 Saint-Gobain Glass France Glass spacer
US20010049031A1 (en) * 1999-03-04 2001-12-06 Christopher H. Bajorek Glass substrate for magnetic media and method of making the same
US6420002B1 (en) * 1999-08-18 2002-07-16 Guardian Industries Corp. Vacuum IG unit with spacer/pillar getter
US20100323277A1 (en) * 2003-03-27 2010-12-23 Robert Roberts Isotropic nano crystallites of polytetrafluoroethylene (ptfe) resin and products thereof that are biaxially planar oriented and form stable
US20090280415A1 (en) * 2004-09-13 2009-11-12 Hoya Corporation Transparent substrate for mask blank and mask blank
US20070082179A1 (en) * 2005-10-07 2007-04-12 Wade James J Method and apparatus for forming optical articles
US20090324858A1 (en) * 2006-12-22 2009-12-31 Futech Gmbh Insulating glazing element, its manufacture and use
US20110147219A1 (en) * 2009-12-22 2011-06-23 Rolls-Royce Plc Hydrophobic surface

Non-Patent Citations (2)

* Cited by examiner, † Cited by third party
Title
KOCER: "Mechanical deformations in a vacuum glazing; a finite element modeling study", PROCEEDINGS ABSTRACT, 20 June 2011 (2011-06-20), Retrieved from the Internet <URL:http://www.gpd.fi/Global/GPD/Finland/Finland%202011/Accepted%20Abstarcts/IGU/Cenk%20Kocer.pdf> [retrieved on 20120403] *
WEINLADER ET AL.: "VIG - Vacuum Insulation Glass", VIG - VACUUM INSULATION GLASS, December 2005 (2005-12-01), Retrieved from the Internet <URL:http://www.bine.info/fileadmin/content/Publikationen/Projekt-Infos/Zusatzinfos/2008-01_Fachartikel.pdf> [retrieved on 20120403] *

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10253550B1 (en) 2015-10-30 2019-04-09 Corning Incorporated Vacuum insulated glass units and methodology for manufacturing the same
WO2019161864A1 (fr) * 2018-02-22 2019-08-29 Vkr Holding A/S Unités de verre d'isolation sous vide basées sur des représentations topographiques
WO2019161865A1 (fr) * 2018-02-22 2019-08-29 Vkr Holding A/S Unités de verre isolant sous vide basées sur des représentations topographiques
US11047167B2 (en) 2018-02-22 2021-06-29 Vkr Holding A/S Vacuum insulating glass units based on topographic representations
US11261651B2 (en) 2018-02-22 2022-03-01 Vkr Holding A/S Vacuum insulating glass units based on topographic representations
EP4119513A4 (fr) * 2020-03-13 2024-02-28 Nippon Sheet Glass Co Ltd Panneau de verre multicouche sous vide

Similar Documents

Publication Publication Date Title
US9410358B2 (en) Vacuum insulated glass panel with spacers coated with micro particles and method of forming same
US9187947B2 (en) Method of forming a vacuum insulated glass panel spacer
US9840436B2 (en) Methods for measuring the asymmetry of a glass-sheet manufacturing process
US11208346B2 (en) Processes of making glass with textured surface and 3-D shape
EP2855388B1 (fr) Article en verre de couverture
US9484473B2 (en) Anti-reflection glass substrate
TWI579251B (zh) 玻璃的酸強化
Collins et al. Transparent evacuated insulation
KR102531946B1 (ko) 변형된 곡률을 위한 화학적으로-강화된 얇은 유리 기판 신규 패러다임 및 제조 방법
EP2202208A1 (fr) Substrat de verre et son procédé de fabrication
KR102426303B1 (ko) 엔지니어링된 응력 프로파일을 갖는 유리계 제품 및 이의 제조 방법
EP3345877B1 (fr) Procédé de fabrication de plaque de verre, plaque de verre, procédé de fabrication d&#39;article en verre, article en verre
KR20220007890A (ko) 높은 굽힘 강도의 박형 유리 기판 및 이의 제조 방법
WO2013085480A1 (fr) Panneau en verre isolé sous vide avec des éléments d&#39;espacement à caractéristiques améliorées et son procédé de formation
US20190248702A1 (en) Glass article and method for producing the same
US20210331961A1 (en) Enhanced strength of glass by combining redraw and chemical thinning processes
Collins et al. Design of support pillar arrays in flat evacuated windows
Lawrence et al. A two-stage ceramic tile grout sealing process using a high power diode laser—II. Mechanical, chemical and physical properties
WO2000066868A1 (fr) Piliers ecarteurs avec depot cda pour vitrage a vide isolant
KR20210031477A (ko) 마이크로일렉트로닉스(microelectronics) 제조를 위한 캐리어
CN107857479B (zh) 玻璃板
US20200307173A1 (en) Methods for producing laminate glass articles
US20230076143A1 (en) Textured glass-based articles
Turner et al. Limits to performance of evacuated glazing
Sheth et al. Peculiar wear behavior of soda lime silicate glass in humid air and its implications

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11876934

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 11876934

Country of ref document: EP

Kind code of ref document: A1