WO2013083655A2 - Pressure vessel with controlled vessel weight/gas weight ratio - Google Patents
Pressure vessel with controlled vessel weight/gas weight ratio Download PDFInfo
- Publication number
- WO2013083655A2 WO2013083655A2 PCT/EP2012/074564 EP2012074564W WO2013083655A2 WO 2013083655 A2 WO2013083655 A2 WO 2013083655A2 EP 2012074564 W EP2012074564 W EP 2012074564W WO 2013083655 A2 WO2013083655 A2 WO 2013083655A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- pressure vessel
- vessel
- liner
- fuel
- composite
- Prior art date
Abstract
Description
Claims