WO2013018059A2 - Self-cleaning, anti-smog, anti-mould photocatalytic powdered water based paint - Google Patents
Self-cleaning, anti-smog, anti-mould photocatalytic powdered water based paint Download PDFInfo
- Publication number
- WO2013018059A2 WO2013018059A2 PCT/IB2012/053968 IB2012053968W WO2013018059A2 WO 2013018059 A2 WO2013018059 A2 WO 2013018059A2 IB 2012053968 W IB2012053968 W IB 2012053968W WO 2013018059 A2 WO2013018059 A2 WO 2013018059A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- mixing
- photocatalytic
- paint
- mixer
- water
- Prior art date
Abstract
Description
Claims