WO2012097140A2 - Panneaux de construction composites comportant des revêtements thermoplastiques et des mats fibreux prérevêtus d'un revêtement cimentaire - Google Patents
Panneaux de construction composites comportant des revêtements thermoplastiques et des mats fibreux prérevêtus d'un revêtement cimentaire Download PDFInfo
- Publication number
- WO2012097140A2 WO2012097140A2 PCT/US2012/021065 US2012021065W WO2012097140A2 WO 2012097140 A2 WO2012097140 A2 WO 2012097140A2 US 2012021065 W US2012021065 W US 2012021065W WO 2012097140 A2 WO2012097140 A2 WO 2012097140A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- coating
- cementitious
- thermoplastic
- board
- composite
- Prior art date
Abstract
L'invention concerne un élément de construction de type panneau de construction composite. Ledit panneau comprend une partie centrale en gypse durci et un mat fibreux qui est prérevêtu d'une couche cimentaire. Un revêtement thermoplastique est ensuite appliqué par-dessus la couche cimentaire. Des additifs peuvent être ajoutés à une ou plusieurs des couches pour de meilleures caractéristiques de performance. L'invention concerne également diverses techniques de fabrication visant à appliquer un revêtement thermoplastique thermofusible sur la couche cimentaire.
Priority Applications (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
EP12734285.5A EP2663452A4 (fr) | 2011-01-14 | 2012-01-12 | Panneaux de construction composites comportant des revêtements thermoplastiques et des mats fibreux prérevêtus d'un revêtement cimentaire |
CA2824508A CA2824508C (fr) | 2011-01-14 | 2012-01-12 | Panneaux de construction composites comportant des revetements thermoplastiques et des mats fibreux prerevetus d'un revetement cimentaire |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US13/006,691 US9346244B2 (en) | 2008-08-29 | 2011-01-14 | Composite building boards with thermoplastic coatings and cementitious precoated fibrous mats |
US13/006,691 | 2011-01-14 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2012097140A2 true WO2012097140A2 (fr) | 2012-07-19 |
WO2012097140A3 WO2012097140A3 (fr) | 2012-12-27 |
Family
ID=46507663
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2012/021065 WO2012097140A2 (fr) | 2011-01-14 | 2012-01-12 | Panneaux de construction composites comportant des revêtements thermoplastiques et des mats fibreux prérevêtus d'un revêtement cimentaire |
Country Status (3)
Country | Link |
---|---|
EP (1) | EP2663452A4 (fr) |
CA (1) | CA2824508C (fr) |
WO (1) | WO2012097140A2 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017189726A1 (fr) * | 2016-04-29 | 2017-11-02 | Certainteed Gypsum, Inc. | Ensemble de construction contenant un film de revêtement faisant barrière contre l'eau et procédé de fabrication de l'ensemble de construction |
Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2806811A (en) | 1954-12-31 | 1957-09-17 | United States Gypsum Co | Paper-covered gypsum board |
US20100005543A1 (en) | 2008-06-25 | 2010-01-07 | Athenix Corporation | Toxin genes and methods for their use |
WO2010025207A1 (fr) | 2008-08-29 | 2010-03-04 | Certainteed Gypsum, Inc. | Panneaux de construction composites revêtus de matière plastique et leur procédé de fabrication |
Family Cites Families (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
AU531527B2 (en) * | 1979-05-30 | 1983-08-25 | Bpb Industries Ltd. | Cementitious building board |
US6331028B1 (en) * | 2000-10-17 | 2001-12-18 | Advance Usa, Inc. | Fiber-reinforced composite structure |
US6524679B2 (en) * | 2001-06-06 | 2003-02-25 | Bpb, Plc | Glass reinforced gypsum board |
US7745357B2 (en) * | 2004-03-12 | 2010-06-29 | Georgia-Pacific Gypsum Llc | Use of pre-coated mat for preparing gypsum board |
US7829488B2 (en) * | 2008-01-22 | 2010-11-09 | Johns Manville | Non-woven glass fiber mat faced gypsum board and process of manufacture |
US20090208714A1 (en) * | 2008-02-18 | 2009-08-20 | Georgia-Pacific Gypsum Llc | Pre-coated non-woven mat-faced gypsum panel |
US9346244B2 (en) * | 2008-08-29 | 2016-05-24 | Certainteed Gypsum, Inc. | Composite building boards with thermoplastic coatings and cementitious precoated fibrous mats |
-
2012
- 2012-01-12 WO PCT/US2012/021065 patent/WO2012097140A2/fr active Application Filing
- 2012-01-12 CA CA2824508A patent/CA2824508C/fr active Active
- 2012-01-12 EP EP12734285.5A patent/EP2663452A4/fr not_active Withdrawn
Patent Citations (3)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US2806811A (en) | 1954-12-31 | 1957-09-17 | United States Gypsum Co | Paper-covered gypsum board |
US20100005543A1 (en) | 2008-06-25 | 2010-01-07 | Athenix Corporation | Toxin genes and methods for their use |
WO2010025207A1 (fr) | 2008-08-29 | 2010-03-04 | Certainteed Gypsum, Inc. | Panneaux de construction composites revêtus de matière plastique et leur procédé de fabrication |
Non-Patent Citations (1)
Title |
---|
See also references of EP2663452A4 |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
WO2017189726A1 (fr) * | 2016-04-29 | 2017-11-02 | Certainteed Gypsum, Inc. | Ensemble de construction contenant un film de revêtement faisant barrière contre l'eau et procédé de fabrication de l'ensemble de construction |
US10472293B2 (en) | 2016-04-29 | 2019-11-12 | Certainteed Gypsum, Inc. | Building assembly containing a water barrier coating film and method of making the building assembly |
Also Published As
Publication number | Publication date |
---|---|
EP2663452A4 (fr) | 2014-07-09 |
CA2824508A1 (fr) | 2012-07-19 |
CA2824508C (fr) | 2019-07-30 |
EP2663452A2 (fr) | 2013-11-20 |
WO2012097140A3 (fr) | 2012-12-27 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US10767368B2 (en) | Plastic coated composite building boards and method of making same | |
US9346244B2 (en) | Composite building boards with thermoplastic coatings and cementitious precoated fibrous mats | |
US20210114333A1 (en) | Prepregs, cores, composites and articles including repellent materials | |
US7842629B2 (en) | Non-woven glass fiber mat faced gypsum board and process of manufacture | |
US9186869B2 (en) | Composite floor underlayment with thermoplastic coatings | |
US8128767B2 (en) | Process for manufacturing gypsum board faced with non-woven glass fiber mat | |
EP1800853B1 (fr) | Matériau pour plaque | |
US20170218635A1 (en) | Stucco support structures and stucco walls | |
CA2824508C (fr) | Panneaux de construction composites comportant des revetements thermoplastiques et des mats fibreux prerevetus d'un revetement cimentaire | |
CA2818143C (fr) | Sous-couche de plancher composite avec revetements thermoplastiques |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 12734285 Country of ref document: EP Kind code of ref document: A2 |
|
ENP | Entry into the national phase in: |
Ref document number: 2824508 Country of ref document: CA |
|
NENP | Non-entry into the national phase in: |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2012734285 Country of ref document: EP |