WO2012091147A1

WO2012091147A1 - Piezoelectric material, piezoelectric element, liquid discharge head, ultrasonic motor, and dust removing device

Info

Publication number: WO2012091147A1
Application number: PCT/JP2011/080555
Authority: WO
Inventors: Jumpei Hayashi; Hisato Yabuta; Makoto Kubota; Mikio Shimada; Satoshi Wada; Ichiro Fujii; Ryuta MITSUI; Nobuhiro Kumada
Original assignee: Canon Kabushiki Kaisha; University Of Yamanashi
Priority date: 2010-12-28
Filing date: 2011-12-22
Publication date: 2012-07-05
Also published as: CN103298768A; US9306149B2; KR101541022B1; CN103298768B; EP2658826A1; EP2658826B1; JP5864168B2; KR20130111610A; JP2012148954A; US20130270965A1

Abstract

Provided is a piezoelectric material that achieves both high piezoelectric performance and high Curie temperature. In addition, provided are a piezoelectric element, a liquid discharge head, an ultrasonic motor, and a dust removing device, which use the piezoelectric material. The piezoelectric material includes a perovskite-type metal oxide that is expressed by the following general formula (1): xBaTiO₃-yBiFeO₃-zBi(M_0.5Ti_0.5)O₃ (1), where M represents at least one type of element selected from the group consisting of Mg and Ni, x satisfies 0.25≤x≤0.75, y satisfies 0.15≤y≤0.70, z satisfies 0.05≤z≤0.60, and x+y+z=1 is satisfied.

Description

DESCRIPTION

PIEZOELECTRIC MATERIAL , PIEZOELECTRIC ELEMENT, LIQUID DISCHARGE HEAD, ULTRASONIC MOTOR, AND

DUST REMOVING DEVICE

Technical Field

[0001] The present invention relates to a piezoelectric

material, and more particularly, to a lead-free piezoelectric material. The present invention also relates to a piezoelectric element, a liquid discharge head, an ultrasonic motor, and a dust removing device, which use the piezoelectric material.

Background Art

[0002] A commonly used piezoelectric material is an AB0₃-type perovskite metal oxide such as lead titanate zirconate (hereinafter, referred to as "PZT"). However, it is considered that PZT, which contains lead as an A-site element, may cause environmental problems. Therefore, a piezoelectric material with a lead-free perovskite- type metal oxide has been desired.

[0003] Barium titanate is known as a piezoelectric material with a lead-free perovskite-type metal oxide. Patent Literature 1 discloses barium titanate prepared by a resistance heating/two-step sintering technique. The patent literature describes that a ceramic with excellent piezoelectric property can be obtained when nano-sized barium titanate powder is sintered by the two-step sintering technique. However, the barium titanate has a problem that it is not suitable for device operation at high temperature because its Curie temperature is low at 125°C.

[0004] In addition, Non-Patent Literature 1 discloses a solid solution of barium titanate and bismuth ferrite as an attempt to increase the Curie temperature of barium titanate. However, as the solid solution amount of the bismuth ferrite increases, the Curie temperature increases while piezoelectric performance is conspicuously decreased.

[0005] In other words, it is difficult to achieve both high piezoelectric performance and high Curie temperature in a piezoelectric material of the lead-free perovskite- type metal oxide.

Citation List

Patent Literature

[0006] PTL 1: Japanese Patent Application Laid-Open No. 2008-

150247

[0007] NPL 1: "Journal of Applied Physics" 2008, Volume 87, Issue 2, pp.855-862

Summary of Invention

Technical Problem

[0008] he present invention has been made to address such a problem, and an object thereof is to provide a

piezoelectric material that can achieve both high piezoelectric performance and high Curie temperature. In addition, the present invention provides a

piezoelectric element, a liquid discharge head, an ultrasonic motor, and a dust removing device, which use the piezoelectric material.

Solution to Problem

[0009] According to the present invention, there is provided a piezoelectric material, including a perovskite-type metal oxide that is expressed by the following general formula (1): xBaTi0₃-yBiFe0₃-zBi (Mo.sTio.s) 0₃, where M represents at least one type of element selected from the group consisting of Mg and Ni, x satisfies

0.25<x<0.75, y satisfies 0.15<y<0.70, z satisfies

0.05≤z 0.60, and x+y+z=l is satisfied.

According to the present invention, there is provided a piezoelectric material, including a perovskite-type metal oxide that is expressed by the following general formula (2): xBaTi0₃-yBiFe0₃-zBi (M0.5T10.5) 0₃, where M represents at least one type of element selected from the group consisting of g and Ni, x satisfies 0.10<x<0.25, y satisfies 0.15<y<0.30, z satisfies

0.45≤z 0.75, and x+y+z=l is satisfied.

[0010 ] According to the present invention, there is provided a piezoelectric material, including a perovskite-type metal oxide that is expressed by the following general formula (3): lBaTi0₃-mBiFe0₃-nBi (M₀.₅Ti₀.5) 0₃, where represents at least one type of element selected from the group consisting of Mg and Ni, 1 satisfies 0<1<1, m satisfies 0<m<l, n satisfies 0<n<l, and l+m+n=l is satisfied, in which the piezoelectric material is a ceramic, and crystal grains of the ceramic have a diffuse phase transition structure.

[0011] According to the present invention, there is provided a piezoelectric element, including: a first electrode; a piezoelectric material; and a second electrode, in which the piezoelectric material includes the above- mentioned piezoelectric material.

[0012] A liquid discharge head according to the present

invention uses the above-mentioned piezoelectric element .

[0013] An ultrasonic motor according to the present invention uses the above-mentioned piezoelectric element.

[0014] A dust removing device according to the present

invention uses the above-mentioned piezoelectric element .

Advantageous Effects of Invention

[0015] According to the present invention, it is possible to provide a piezoelectric material that achieves both high piezoelectric performance and high Curie

temperature. Through the use of the piezoelectric material of the present invention, it is possible to provide a liquid discharge head having nozzle density and discharge performance equal to or higher than those in the case where a piezoelectric material including lead is used. Through the use of the piezoelectric material of the present invention, it is possible to provide an

ultrasonic motor having driving power and durability equal to or higher than those in the case where a piezoelectric material including lead is used.

Through the use of the piezoelectric material of the present invention, it is possible to provide a dust removing device having dust removing efficiency equal to or higher than that in the case where a

piezoelectric material including lead is used.

Brief Description of Drawings

] [FIGS. 1A and IB] FIGS. 1A and IB are phase diagrams illustrating an embodiment of a piezoelectric material of the present invention.

[FIGS. 2A to 2C]FIGS. 2A, 2B, and 2C are conceptual diagram of a microstructure inside crystal grains of the piezoelectric material of the present invention. [FIGS. 3A and 3B]FIGS. 3A and 3B are schematic diagrams illustrating an embodiment of a structure of a liquid discharge head of the present invention.

[FIGS. 4A and 4B]FIGS. 4A and 4B are schematic diagrams illustrating an embodiment of a structure of an

ultrasonic motor of the present invention.

[FIGS. 5A and 5B]FIGS. 5A and 5B are schematic diagrams illustrating an embodiment of a dust removing device of the present invention.

[FIG. 6A to 6C]FIGS. 6A, 6B and 6C are schematic diagrams illustrating a structure of a piezoelectric element of the present invention illustrated in FIGS. 5A and 5B.

[FIGS. 7A and 7B]FIGS. 7A and 7B are schematic diagrams illustrating a principle of vibration of the dust removing device of the present invention.

[FIG. 8] FIG. 8 is an X-ray diffraction pattern of Examples 3, 4, and 13 and Comparative Example 5.

[FIG. 9] FIG. 9 is a phase diagram illustrating a composition of the piezoelectric material of the present invention.

Description of Embodiments

[ 0017 ] Hereinafter, embodiments of the present invention are described.

According to the present invention, there is provided a piezoelectric material, including a perovskite-type metal oxide that is expressed by the following general formula (1): xBaTi0₃-yBiFe0₃-zBi (M0.5T10.5) 0₃ (1), where represents at least one type of element selected from the group consisting of g and Ni, x satisfies

0.25<x<0.75, y satisfies 0.15<y<0.70, z satisfies

0.05≤z≤0.60, and x+y+z=l is satisfied.

According to the present invention, there is also provided a piezoelectric material, including a

perovskite-type metal oxide that is expressed by the following general formula (2) : xBaTi0₃-yBiFe0₃- zBi ( ₀.5 i₀.5) 0₃ (2), where M represents at least one type of element selected from the group consisting of Mg and Ni, x satisfies 0.10≤x<0.25, y satisfies

0.15<y<0.30, z satisfies 0.45<z<0.75, and x+y+z=l is satisfied .

[0018] The perovskite-type metal oxide of the present

invention refers to a metal oxide having a perovskite- type structure that is ideally a cubic structure as described in Iwanami Physicochemical Dictionary, Fifth Edition (Iwanami Shoten, published on February 20, 1998) . The metal oxide having a perovskite-type structure is generally expressed by chemical formula of AB0₃. In the perovskite-type metal oxide, the elements A and B occupy specific positions in a form of ions in a unit cell, which are called A site and B site. For instance, in a cubic unit cell, the element A is positioned at a vertex of the cube while the element B is positioned at the body center. The element 0 occupies a face center position as an anion of oxygen. [0019] The metal oxide expressed by the general formula (1) refers to a solid solution of three perovskite-type metal oxides that are expressed by BaTi0₃, BiFe0₃, and Bi (M₀.₅Ti₀.5) 0₃. In the general formula (1), a metal element positioned at the A site is mainly Ba and Bi, and a metal element positioned at the B site is at least one type of element selected from the group consisting of Ti, Fe, Mg, and Ni.

[0020] In the general formula (1), an element content ratio between the A site and the B site is expressed as 1:1. However, even if the element content ratio is shifted slightly, a single phase state constituted of only the perovskite-type structure is included within the scope of the present invention. For instance, in a lead type piezoelectric material, it is well known that an actual B-site element ratio is often shifted from a

stoichiometric ratio when A-site Pb is excessively used or in a composite perovskite-type structure.

[0021] It is determined that the piezoelectric material is the perovskite-type structure from structure analysis using X-ray diffraction or electron diffraction, for example.

[0022] In the general formula (1), the range of x that

represents abundance of BaTi0₃ satisfies 0.25≤x≤0.75. Preferably, 0.25≤x≤0.55 is satisfied. In addition, in the general formula (2) , the range of x satisfies

0.10<x<0.25. If x is smaller than 0.10, a crystal phase other than the perovskite-type structure

(hereinafter, this crystal phase is referred to as a "secondary phase") may occur. On the other hand, if x is larger than 0.75, the Curie temperature becomes lower than 200°C, and thus piezoelectric property may disappear in a high temperature region. In this specification, the Curie temperature refers to the temperature at which ferroelectricity disappears. As a method of specifying the Curie temperature, there are a method of directly measuring the temperature at which ferroelectricity disappears while changing measuring temperature, and a method in which a dielectric

constant is measured by using micro alternating

magnetic field of a certain frequency while changing measuring temperature to thereby determine the

temperature at which the dielectric constant becomes maximum.

[0023] A desirable Curie temperature in piezoelectric material of the present invention is 200°C or higher and 500°C or lower, more preferably, 200°C or higher and 450°C or lower. If the Curie temperature is 200 °C or higher, it is possible to provide a material with little

characteristic variation when the material is used in a device. In addition, if the Curie temperature is 500 °C or lower, it is possible to provide a material that is easy to polarize when the material is used in an element .

[0024] In the general formula (1), the range of y representing abundance of BiFe0₃ satisfies 0.15≤y≤0.70. Preferably, 0.20≤y≤0.70 is satisfied. In addition, in the general formula (2), the range of y satisfies 0.15≤y≤0.30. If y is smaller than 0.15, there occurs a problem for the following reason, regardless of what value x takes. Specifically, if y is smaller than 0.15 and x is 0.5 or larger, the Curie temperature may be decreased. In addition, if x is smaller than 0.5, the secondary phase may be generated. On the other hand, if y is larger than 0.70, insulation property may be deteriorated.

[0025] In the general formula (1), the range of z representing abundance of Bi (Mo.sTio.s) 0₃ satisfies 0.05<z<0.60.

Preferably, 0.05≤z≤0.25 is satisfied. In addition, in the general formula (2), the range of z satisfies

0.45≤z≤0.75. If z is smaller than 0.05, there occurs a problem for the following reason, regardless of what value x takes. , Specifically, if z is smaller than 0.05 and x is 0.5 or larger, the Curie temperature may be decreased. In addition, if x is smaller than 0.5, the insulation property may be deteriorated. On the other hand, if z is larger than 0.75, the secondary phase may occur .

[0026] In the general formula (1), in Bi (M0.5T10.5) 0₃

represents at least one type of element selected from the group consisting of Mg and Ni . M may be only Mg or only Ni, or may include both Mg and Ni. Mg and Ni are divalent, and form a pseudo-trivalent ion with

tetravalent Ti, with the result that it is possible to achieve charge balance with trivalent Bi. In this case, it is preferred that a ratio between M and Ti be 1:1. In addition, in the general formula (1), element

contents of M and Ti in Bi (M0.5T10.5) O3 are both

expressed as 0.5. However, even if this element

content is shifted to a value in the range of 0.4 to 0.6, a single phase state constituted of only the perovskite-type structure is included in the scope of the present invention.

[0027] In addition, the piezoelectric material of the present invention may include characteristic adjustment

components and impurity components that are included in the manufacturing process.

[0028] In the general formula (1), M represents at least one type of element selected from the group consisting of Mg and Ni. When 0.25<x<0.75, 0.15<y<0.70, and

0.05≤z≤0.60 are satisfied, a piezoelectric constant d₃₃ ^* is 100 (pm/V) or larger, and the Curie temperature is 200°C or higher. Here, FIG. 1 is a phase diagram of one embodiment of the piezoelectric material of the present invention, and the above-mentioned ranges are expressed by a region A in this diagram.

[0029] In this specification, the piezoelectric constant d₃₃ ^* is a constant determined from electric field and

distortion gradient of an electric field distortion curve. Here, mark * is added for the following reason. The piezoelectric constant d₃₃ that is usually used shows piezoelectric property only in 33-direction. In contrast, in this calculation method, there is a slight possibility of contribution to directions other than the 33-direction. The piezoelectric material according to the present invention satisfies 0.25≤x≤0.55,

0.20<y<0.70, and 0.05<z<0.25 in the general formula (1)] In the general formula (1), M is at least one type of element selected from the group consisting of Mg and Ni When 0.25<x<0.55, 0.20<y<0.70, and 0.05<z<0.25 are satisfied, the piezoelectric constant d₃₃ ^* is 200 (pm/V) or larger, and the Curie temperature is 200 °C or higher Here, the above-mentioned ranges are expressed by a range B in FIG. 1.

] FIG. 9 illustrates the above-mentioned region A

indicating composition of the piezoelectric material of the present invention, and illustrates a range C that indicates composition of the piezoelectric material of the present invention similarly and is expressed by the general formula (2) . The piezoelectric material of the present invention having the composition corresponding to the range C expressed by the general formula (2) has a piezoelectric constant d₃₃ ^* of 100 (pm/V) or larger and a Curie temperature of 200 °C or higher.

] The piezoelectric material of the present invention contains at least one type selected from the group consisting of Mn and Cu, and hence insulation property and density of the piezoelectric material are improved. If the insulation property of the piezoelectric

material is improved, it is possible to endure a polarization process in which high electric field is applied. Thus, conversion efficiency between electric energy and mechanical energy is improved. In addition, if the density of the piezoelectric material is

improved, piezoelectric property and mechanical

strength are improved. ] It is preferred that the piezoelectric material according to the present invention contain at least one type of element selected from the group consisting of manganese (Mn) and copper (Cu) at 0.05 mass% or higher and 3.0 mass% or lower. If the amount of at least one type of element selected from the group consisting of Mn and Cu is smaller than 0.05 massl, improvement of insulation property and density may be decreased, and if the amount is larger than 3.0 mass%, the secondary phase may be generated.

] A raw material to be used for Mn and Cu contained in the piezoelectric material of the present invention is not limited particularly. In the case of Mn, a

divalent Mn compound or a tetravalent Mn compound may be used. Similarly, in the case of Cu, a monovalent Cu compound or a divalent Cu compound may be used. In addition, solid powder or liquid raw material may be used. Examples of Mn raw material include manganese oxide, manganese dioxide, manganese acetate, and manganese carbonate. Examples of Cu material include copper oxide and copper nitrate.

] In addition, positions of Mn and Cu contained in the piezoelectric material of the present invention are not limited particularly. Mn and Cu may be contained at the B site of the perovskite-type structure or may be contained as an oxide at a crystal grain boundary so that the same effect can be expected. As to the piezoelectric material according to the present invention, it is preferred that the piezoelectric material be a ceramic, that an average equivalent circular diameter of crystal grains of the ceramic is 500 nm or larger and 5 μπι or smaller, and that a maximum equivalent circular diameter of the crystal grains is 5 μιη or larger and 10 μπι or smaller.

] The term "ceramic" used herein refers to an aggregate (also referred to as bulk) of crystal particles sintered by thermal treatment, or the so-called polycrystal, in which the main component thereof is a metal oxide. The term also includes one processed after sintering. However, the term does not include any powder or powder-dispersed slurry.

[0037] The "equivalent circular diameter" used herein refers to a "projected area equivalent circular diameter" that is generally mentioned in a microscopic observation method and indicates a diameter of a circle having the same area as a projected area of the crystal grain. In the present invention, this method of measuring the equivalent circular diameter is not limited

particularly. For instance, the equivalent circular diameter can be determined by photographing a surface of the piezoelectric ceramic using a polarizing

microscope or a scanning electron microscope, and by performing image processing on the obtained

photographic image. An enlarging magnification when the equivalent circular diameter of the crystal grain is determined is, for example, approximately 5 to 5,000. An optical microscope and an electron microscope may be used selectively depending on the magnification. It is possible to determine the equivalent circular diameter not from an image of a surface of the ceramic but from an image of a polished surface or a cross-section.

[0038] The "average equivalent circular diameter" used herein refers to an average value of the equivalent circular diameter obtained by performing image processing on the photographic image obtained by photographing the

piezoelectric ceramic. The average value may be a volume average or a number average, but the number average is preferred.

[0039] The "maximum equivalent circular diameter" used herein refers to a maximum value of the equivalent circular diameter obtained by performing image processing on the photographic image obtained by photographing the piezoelectric ceramic.

[0040] It is preferred that the average equivalent circular

diameter of the crystal grains be 500 nm or larger and 5 μιη or smaller. In this range, there is a merit that a diffusion phase transition structure described later easily exists in the crystal grains of the

piezoelectric material. On the other hand, if the average equivalent circular diameter is smaller than 500 nm, the density may be decreased so that sufficient piezoelectric property cannot be obtained. In addition, if the average equivalent circular diameter is larger than 5 μιτι, mechanical strength may be deteriorated.

[0041] Further, it is preferred that the maximum equivalent

circular diameter of the crystal grains be 5 μπι or larger and 10 μπι or smaller. In this range, there is a merit that a diffusion phase transition structure described later easily exists in the crystal grains of the piezoelectric material. On the other hand, if the average equivalent circular diameter is smaller than 5 μπι, the density may be decreased so that sufficient piezoelectric property cannot be obtained. In addition, if the average equivalent circular diameter is larger than 10 μπι, mechanical strength may be deteriorated.

[0042] As to the piezoelectric material of the present

invention, it is preferred that the piezoelectric material be a ceramic and that crystal grains

constituting the ceramic have the diffusion phase transition structure.

[0043] If the structure analysis using a transmission type

electron microscope (TEM) is performed on the

piezoelectric material of the present invention, it is understood that a microstructure of the crystal grains is different depending on the composition region. FIGS. 2A to 2C are conceptual diagrams of the microstructure of the crystal grains in the piezoelectric material of the present invention, and the microstructure is described with reference to FIGS. 2A to 2C. As the microstructure of the crystal grains, there are three types: a composition region illustrated in FIG. 2A called a polar nano region (hereinafter, referred to as PNR) , in which a very local region with spontaneous polarizations of several nanometers in random

directions is dominant; a composition region

illustrated in FIG. 2B (hereinafter, referred to as a "domain region"), in which a region with spontaneous polarizations of several tens to several hundreds of nanometers in random directions is dominant; and a composition region illustrated in FIG. 2C, in which the PNR exists in the domain region. In the present

invention, the microstructure illustrated in FIG. 2C in which the PNR exists in the domain region is referred to as a "diffuse phase transition structure (Diffuse Phase Transition)". In addition, the region

illustrated in FIG. 2A is also called a relaxor region.

[0044] Next, what composition region this microstructure

exists in is described with reference to FIGS. 1A and IB.

[0045] The region in which the PNR is dominant exists in the range of y=0 and x≤0.5 and in the range of z=0 and x≥0.4 illustrated in FIGS. 1A and IB. Because coercive electric field is small in this region, there is a feature that good displacement response to the electric field is obtained. In addition, the piezoelectric property is apt to increase. However, frequency

dispersion of the dielectric constant is large, and hence the piezoelectric property becomes unstable with respect to the frequency even at a constant temperature. This is not preferred.

[0046] The domain region exists in the range of y=0 and x>0.5 and in the range of z=0 and x<0.4 illustrated in FIGS. 1A and IB. In this region, a structure of the domain to be an origin of the piezoelectric property is stable, and hence the piezoelectric property is stable at a constant temperature. However, because the coercive electric field is large, displacement response to an applied electric field may be slow. This is not preferred.

[0047] The diffusion phase transition structure exists in the region A illustrated in FIG. 1A. This region has both the feature that the piezoelectric property of the region in which the PNR is dominant is high and the feature that the piezoelectric property of the domain region is stable. This is preferred. As a specific characteristic, the piezoelectric property d₃₃ ^* is 100 (pm/V) or higher, and the Curie temperature is 200°C or higher .

[0048] The piezoelectric material of the present invention is a piezoelectric material made of a perovskite-type metal oxide expressed by the following general formula (3) :

lBaTi0₃-mBiFe0₃-nBi (M₀.₅Ti₀.5) 0₃ (3) ,

where M represents at least one type of element selected from the group consisting of Mg and Ni, 1 satisfies 0<1<1, m satisfies 0<m<l, n satisfies 0<n<l, and l+m+n=l is satisfied. Further, the piezoelectric material is a ceramic, and crystal grains of the ceramic have the diffusion phase transition structure.

[0049] Because the crystal grains have the diffusion phase transition structure, the piezoelectric property is high and stable, and further the Curie temperature is high .

[0050] In the general formula (3) , the element content ratio between the A site and the B site is expressed as 1:1. However, even if the element content ratio is shifted to approximately 0.9:1.1, the single phase state constituted of only the perovskite-type structure is included within the scope of the present invention.

[0051] In addition, a manufacturing method for the piezoelectric material of the present invention is not limited particularly.

[0052] When manufacturing a ceramic, it is possible to adopt a general method of sintering a solid powder of oxide, carbonate, nitrate, oxalate, and the like at a normal pressure. In addition, it is possible to use a method of cutting the sintered ceramic and overlaying the same to be adhered or a tape casting method of making ceramic powders in a sheet-like shape and overlaying the same so that a multilayered structure is achieved.

[0053] The raw material is made of a metal compound such as barium (Ba) compound, titanium (Ti) compound, bismuth (Bi) compound, iron (Fe) compound, magnesium (Mg) compound, nickel (Ni) compound, Mn compound, and Cu compound.

[0054 ] Examples of usable Ba compound include barium oxide, barium carbonate, barium oxalate, barium acetate, barium nitrate, and barium titanate.

[0055] Examples of usable Ti compound include titanium oxide.

[0056] Examples of usable Bi compound include bismuth oxide and bismuth nitrate.

[0057] Examples of usable Fe compound include iron oxide, iron chloride, and iron nitrate.

[0058 ] Examples of usable Mg compound include magnesium oxide, magnesium oxalate, magnesium chloride, and magnesium carbonate .

[0059] Examples of usable Ni compound include nickel oxide, nickel nitrate, nickel chloride, and nickel oxalate.

[0060] Examples of usable Mn compound include manganese

carbonate, manganese oxide, manganese dioxide, and manganese acetate.

[0061] Examples of usable Cu compound include copper oxide, copper nitrate, and copper sulfate.

[0062] In addition, the sintering method is not limited

particularly. Examples of the sintering method include a sintering method using an electric furnace, an electric heating method, a microwave sintering method, a millimeter wave sintering method, and a hot isostatic pressing (HIP) method.

[0063] The sintering temperature is not limited but is

preferably a temperature at which crystals of the piezoelectric ceramic can sufficiently grow. A

preferred sintering temperature is 800°C or higher and 1,150°C or lower, more preferably 900°C or higher and 1,030°C or lower. The piezoelectric ceramic sintered at a temperature in the above-mentioned range shows a good piezoelectric property.

[0064] In order to stabilize the characteristic of the

piezoelectric ceramic obtained by the sintering process, it is preferred to maintain the sintering temperature to be constant in the above-mentioned range to perform the sintering process for an hour or longer and 24 hour or shorter. A relative density of the sintered

piezoelectric ceramic is preferably 90% or higher, more preferably 95% or higher. This is because, if the relative density is lower than 90%, a relative

dielectric constant of the piezoelectric ceramic is conspicuously decreased, and the mechanical strength is also decreased. Examples of means for increasing relative density include a method of adding manganese or copper and a method of using the tape casting method to make a compact.

[0065] Hereinafter, a piezoelectric element using the

piezoelectric material of the present invention is described.

[0066] The piezoelectric element according to the present

invention is a piezoelectric element including at least a first electrode, a piezoelectric material, and a second electrode, and the piezoelectric material is the above-mentioned piezoelectric material.

[0067] The first electrode and the second electrode are each formed of a conductive layer having a thickness of about 5 nm to 2,000 nm. The material for the conductive layer is not particularly limited, and may be a material which is typically used in a

piezoelectric element. Examples of such material include metals such as Ti, Pt, Ta, Ir, Sr, In, Sn, Au, Al, Fe, Cr, Ni, Pd, Ag, and Cu, and oxides of these metals. Each of the first electrode and the second electrode may be formed of one kind of those materials, or may be obtained by laminating two or more kinds thereof. The first electrode and the second electrode may be formed of different materials, respectively.

[0068] A manufacturing method for the first electrode and the second electrode is not limited. The first electrode and the second electrode may be formed by baking a metal paste or by sputtering, vapor deposition, or the like. In addition, both the first electrode and the second electrode may be patterned in desired shapes for use .

[0069] FIGS. 3A and 3B are each a schematic view illustrating an embodiment of the construction of a liquid discharge head of the present invention. As illustrated in FIGS. 3A and 3B, the liquid discharge head of the present invention is a liquid discharge head including a piezoelectric element 101 of the present invention.

The piezoelectric element 101 is a piezoelectric element including at least a first electrode 1011, a piezoelectric material 1012, and a second electrode 1013. The piezoelectric material 1012 is patterned as required as illustrated in FIG. 3B.

FIG. 3B is a schematic view of the liquid discharge head. The liquid discharge head includes discharge ports 105, individual liquid chambers 102,

communicating holes 106 for connecting the individual liquid chambers 102 and the discharge ports 105, liquid chamber partition walls 104, a common liquid chamber 107, a diaphragm 103, and the piezoelectric elements 101. Each of the piezoelectric elements 101, which is of a rectangular shape in FIG. 3B, may be of a shape except the rectangular shape such as an elliptical shape, a circular shape, or a parallelogram shape. In general, the piezoelectric material 1012 are each of a shape in conformity with the shape of the individual liquid chamber 102.

[0070] he vicinity of the piezoelectric element 101 included in the liquid discharge head of the present invention is described in detail with reference to FIG. 3A. FIG. 3A is a sectional view of the piezoelectric element in the width direction of the liquid discharge head illustrated in FIG. 3B. The sectional shape of the piezoelectric element 101, which is illustrated in a rectangular shape, may be a trapezoidal shape or a reverse trapezoidal shape. In FIG. 3A, the first electrode 1011 is used as the lower electrode, and the second electrode 1013 is used as the upper electrode. However, the arrangement of the first electrode 1011 and the second electrode 1013 is not limited to the foregoing. For example, the first electrode 1011 may be used as the lower electrode, or may be used as the upper electrode. Similarly, the second electrode 1013 may be used as the upper electrode, or may be used as the lower electrode. In addition, a buffer layer 108 may be present between the diaphragm 103 and the lower electrode .

[0071] Note that, those differences in name are caused by a manufacturing method for the device and an effect of the present invention can be obtained in any case.

[0072] In the liquid discharge head, the diaphragm 103

vertically fluctuates owing to the expansion and contraction of the piezoelectric material 1012 to apply a pressure to liquid in the individual liquid chamber

102. As a result, the liquid is discharged from the discharge port 105. The liquid discharge head of the present invention can be used in a printer application or the manufacture of an electronic device.

[0073] The diaphragm 103 has a thickness of 1.0 \i or more and 15 μηι or less, preferably 1.5 μπι or more and 8 μιη or less. A material for the diaphragm, which is not limited, is preferably Si. Si for the diaphragm may be doped with B or P. In addition, the buffer layer and the electrode layer on the diaphragm may serve as part of the diaphragm.

[0074] The buffer layer 108 has a thickness of 5 nm or more and 300 nm or less, preferably 10 nm or more and 200 nm or less.

[0075] The size of the discharge port 105 is 5 μπι or more and 40 μπι or less in terms of a equivalent circular

diameter. The shape of the discharge port 105 may be a circular shape, or may be a star shape, a square shape, or a triangular shape.

[0076] Next, an ultrasonic motor using the piezoelectric

element of the present invention is described.

[0077] FIGS. 4A and 4B are schematic views illustrating an embodiment of the construction of the ultrasonic motor of the present invention.

[0078] FIG. 4A illustrates an ultrasonic motor in which the piezoelectric element of the present invention is formed of a single plate. The ultrasonic motor

includes a transducer 201, a rotor 202 brought into contact with the sliding surface of the transducer 201 by virtue of a pressure applied from a pressurizing spring (not shown) , and an output axis 203 provided so as to be integral with the rotor 202. The transducer 201 is formed of a metal elastic ring 2011, a

piezoelectric element 2012 of the present invention, and an organic adhesive 2013 for bonding the

piezoelectric element 2012 to the elastic ring 2011 (such as an epoxy- or cyanoacrylate-based adhesive) . The piezoelectric element 2012 of the present invention is formed of a piezoelectric material interposed between a first electrode (not shown) and a second electrode (not shown) .

[0079] The application of two alternating voltages different from each other in phase by n/2 to the piezoelectric element of the present invention results in the

generation of a bending travelling wave in the

transducer 201, and hence each point on the sliding surface of the transducer 201 undergoes an elliptical motion. When the rotor 202 is brought into press contact with the sliding surface of the transducer 201, the rotor 202 receives a frictional force from the transducer 201 to rotate in the direction opposite to the bending travelling wave. A body to be driven (not shown) is joined to the output axis 203, and is driven by the rotary force of the rotor 202.

[0080] he application of a voltage to the piezoelectric

material results in the expansion and contraction of the piezoelectric material due to a piezoelectric transverse effect. When an elastic body such as a metal is joined to the piezoelectric element, the elastic body is bent by the expansion and contraction of the piezoelectric material. The ultrasonic motor of the kind described here utilizes the principle.

[0081] ext, an ultrasonic motor including a piezoelectric element having a laminated structure is illustrated in FIG. 4B. A transducer 204 is formed of a laminated piezoelectric element 2042 interposed between tubular metal elastic bodies 2041. The laminated piezoelectric element 2042 is an element formed of multiple laminated piezoelectric materials (not shown) , and includes a first electrode and a second electrode on its outer surface of lamination, and inner electrodes on its inner surface of lamination. The metal elastic bodies 2041 are fastened with bolts so that the piezoelectric element 2042 may be interposed between and fixed by the bodies. Thus, the transducer 204 is formed.

[0082] The application of alternating voltages different from each other in phase to the piezoelectric element 2042 causes the transducer 204 to excite two vibrations orthogonal to each other. The two vibrations are synthesized to form a circular vibration for driving the tip portion of the transducer 204. Note that, a constricted circumferential groove is formed in the upper portion of the transducer 204 to enlarge the displacement of the vibration for driving.

[0083]A rotor 205 is brought into contact with the transducer 204 under a pressure from a spring 206 for

pressurization to obtain a frictional force for driving. The rotor 205 is rotatably supported by a bearing.

[0084] Next, a dust removing device using the piezoelectric

element of the present invention is described.

[0085] FIGS. 5A and 5B are schematic diagrams illustrating an embodiment of the dust removing device of the present invention. A dust removing device 310 includes a plate-like piezoelectric element 330 and a diaphragm 320. The material of the diaphragm 320 is not limited. In the case where the dust removing device 310 is used for an optical device, a transparent material or a reflective material can be used as the material of the diaphragm 320. The piezoelectric element 330 includes a piezoelectric material 331, a first electrode 332, and a second electrode 333.

[0086] FIGS. 6A to 6C are schematic diagrams illustrating a

structure of the piezoelectric element 330 illustrated in FIGS. 5A and 5B. FIGS. 6A and 6C illustrate a front surface structure and a rear surface structure of the piezoelectric element 330, respectively. FIG. 6B illustrates a side surface structure. As illustrated in FIGS. 6A to 6C, the piezoelectric element 330

includes the piezoelectric material 331, the first electrode 332, and the second electrode 333. The first electrode 332 and the second electrode 333 are disposed so as to be opposed to the plate surfaces of the piezoelectric material 331. In FIG. 6C, the front surface of the piezoelectric element 330 on which the first electrode 332 is disposed is referred to as a first electrode surface 336. In FIG. 6A, the front surface of the piezoelectric element 330 on which the second electrode 333 is disposed is referred to as a second electrode surface 337.

[0087] Here, the electrode surface in the present invention means a surface of the piezoelectric element on which the electrode is disposed. For instance, as

illustrated in FIGS. 6A to 6C, the first electrode 332 may extend around to the second electrode surface 337.

[0088]As illustrated in FIGS. 5A and 5B, as for the

piezoelectric element 330 and the diaphragm 320, the plate surface of the diaphragm 320 is fixed to the first electrode surface 336 of the piezoelectric element 330. When the piezoelectric element 330 is driven, a stress is generated between the piezoelectric element 330 and the diaphragm 320, so that out-of-plane vibration is generated in the diaphragm. The dust removing device 310 of the present invention is a device that removes foreign matters such as dust sticking to the surface of the diaphragm 320 by the out-of-plane vibration of the diaphragm 320. The out- of-plane vibration means elastic vibration in which the diaphragm moves in the optical axis direction, namely in the thickness direction of the diaphragm.

[0089] FIGS. 7A and 7B are schematic diagrams illustrating a vibration principle of the dust removing device 310 of the present invention. FIG. 7A illustrates a state in which alternating electric fields having the same phase are applied to a pair of left and right piezoelectric elements 330 so that the out-of-plane vibration is generated in the diaphragm 320. The polarization direction of the piezoelectric ceramic forming the pair of left and right piezoelectric elements 330 is the same as the thickness direction of the piezoelectric elements 330, and the dust removing device 310 is driven by the seventh vibrational mode. FIG. 7B illustrates a state in which alternating voltages having opposite phases by 180 degrees are applied to the pair of left and right piezoelectric elements 330 so that the out-of-plane vibration is generated in the diaphragm 320. The dust removing device 310 is driven by the sixth vibrational mode. The dust removing device 310 of the present invention is a device that can effectively remove dust sticking to the surface of the diaphragm by using at least two vibrational modes selectively.

[0090] As described above, the piezoelectric element of the present invention is suitably applicable to the liguid discharge head , the ultrasonic motor, and the dust removing device.

[0091] The present invention provides a novel piezoelectric material that can achieve both high piezoelectric performance and high Curie temperature. Note that, the piezoelectric material of the present invention can be used in various applications such as material for capacitors, material for memories, and material for sensors, utilizing its characteristic as dielectric.

[0092] Through the use of the piezoelectric material of the present invention, it is possible to provide the liquid discharge head having the same or higher nozzle density and discharge force than the case where the

piezoelectric material containing lead is used.

[0093] Through the use of the piezoelectric material of the present invention, it is possible to provide the ultrasonic motor having the same or higher driving force and durability than the case where the

piezoelectric material containing lead is used. [0094] hrough the use of the piezoelectric material of the present invention, it is possible to provide the dust removing device having the same or higher dust-removing efficiency than the case where the piezoelectric material containing lead is used.

[0095] The piezoelectric material of the present invention can be used in such a device as an ultrasonic transducer, a piezoelectric actuator, a piezoelectric sensor, and a ferroelectric memory, as well as the liquid discharge head and the motor.

[0096] Hereinafter, the piezoelectric material of the present invention is described more specifically by way of examples. However, the present invention is not limited by the following examples.

[0097] (Example of BaTi0₃-BiFe0₃-Bi (Mg₀.₅Ti₀.5) 0₃) (Examples 1 to 16, and Comparative Examples 1 to 6)

(Manufacturing method)

As raw materials, barium titanate (manufactured by Sakai Chemical Industry Co., Ltd.; grain size is 100 nm) , bismuth oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.999%), iron oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), magnesium oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), and titanium oxide (manufactured by Ishihara Sangyo Kaisha, Ltd.; purity is 99.9%) were used.

Composition of Table 1 was achieved by weighing, ethanol was used as solvent, and wet mixing was

performed in a ball mill for 24 hours. After that, drying was performed at 80 °C, and the mixed powder was calcined at a temperature of 800 to 900°C for 6 hours. The calcined powder was crushed and the ball mill wet mixing was performed again using ethanol as solvent for 16 hours. After that, polyvinyl alcohol (PVA) was added by 2 mass% as a binder, the ball mill mixing was performed for 1 hour, and then drying was performed at 80°C so that granulated powder was obtained. Next, the obtained granulated powder was crushed and particle size selection was performed with a sieve of 250 μπι mesh. The obtained powder after the particle size selection was filled in a mold and was pressed uniaxially by 200 Pa pressure, so as to make a disc^¬ like compact having a diameter of 10 mm.

Then, the binder was removed from the obtained compact at 700°C for 10 hours, and the compact was sintered at a temperature of 900 to 1,000°C for 6 hours so that a sintered body was obtained. After that, the obtained sintered body was polished to have a thickness of 0.4 mm.

[0098] (Structure evaluation)

The composition of the polished sintered body was evaluated by X-ray fluorescence analysis (XRF) in which a calibration curve is formed by ICP weight analysis. A crystal structure of the sintered body was evaluated by 2Θ-Θ measurement of the X-ray diffraction (XRD) . In addition, detailed structure analysis was performed using a TEM.

Density of the sintered body was evaluated by

Archimedes method. The relative density was determined as a ratio of a measure value of the density to a theoretical density determined from the crystal

structure analysis of the X-ray diffraction measurement. The average equivalent circular diameter and the

maximum equivalent circular diameter of the crystal grains of the sintered body were observed by the SE , and the average equivalent circular diameter was

determined as the number average.

[0099] (Electric characteristic evaluation)

In order to evaluate electric characteristic of the polished sintered body, the sintered body was processed in a strip shape having a thickness of 0.4 mm, a length of 15 mm, and a width of 4 mm, and silver electrodes were formed on the front and back surface so as to make a piezoelectric element.

The piezoelectric property was evaluated by determining the piezoelectric constant d₃₃ ^* from the electric field and the distortion gradient of the electric field distortion curve. As a distortion value, a value when an electric field of 60 kV/cm was applied was adopted, and the piezoelectric constant was calculated.

In addition, the Curie temperature was determined from a peak position of temperature characteristic of the dielectric constant. The temperature characteristic of the dielectric constant was determined by measuring the dielectric constant at 1 MHz every 10°C while

increasing temperature at 3°C per minute.

] Results of those evaluations are shown in Table 1. In Table 1, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Mg₀.₅Ti₀.5) 0₃,

respectively. In the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o", and a state in which the secondary phase exists is indicated by "χ" .

[0102] From the result of the fluorescent X-ray analysis, it was found that the composition was as weighed after sintering, too. In the structure evaluation, it was found that only the perovskite-type structure existed in examples except for Comparative Example 6 from the X-ray diffraction structure analysis (2Θ-Θ measurement) . Here, X-ray diffraction patterns of Examples 3, 4, and 13, and Comparative Example 5 are illustrated in FIG. 8. In addition, the density was 90% or higher as relative density in all having only the perovskite-type

structure. Further, in the samples of examples, the average equivalent circular diameter of crystal grains was 0.5 μπι or larger and 5.0 μιη or smaller, and the maximum equivalent circular diameter of crystal grains was 5.2 μπι or larger and 9.8 μπι or smaller. Then, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples of examples. As to comparative examples, the PNR was dominant in Comparative Examples 1, 2, 3, and 6, while the domain region was dominant in

Comparative Examples 4 and 5.

As to the electric characteristic, the piezoelectric constant d₃₃ ^* was 100 (pm/V) or larger, and the Curie temperature was 200 °C or higher in all the samples in the composition ranges of the examples.

[0103] (Examples 17 to 23: Materials containing Mn or Cu)

(Manufacturing method)

As raw materials, barium titanate (manufactured by

Sakai Chemical Industry Co., Ltd.; grain size is 100 nm) , bismuth oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.999%), iron oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), magnesium oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), titanium oxide (manufactured by Ishihara Sangyo Kaisha, Ltd.; purity is 99.9%), manganese

carbonate, and copper oxide were used. Composition of Table 2 was achieved by weighing, and the sintered body was manufactured by the same method as in Examples 1 to 16.

[0104] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 16, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0105] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 16.

[0106] Results of those evaluations are shown in Table 2. In Table 2, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Mg₀.₅Ti₀.5) 0₃,

respectively. In addition, Mn quantity and Cu quantity respectively indicate masses with respect to 100 parts by mass of xBaTi0₃-yBiFe0₃-zBi (Mgo.sTio.s) 0₃. Further, in the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o" .

[0108] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 94% or higher as relative density in all the samples, which is a higher value than that in Examples 1 to 16 without manganese or copper. Then, the average equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 1.0 μπι or larger and 4.2 μπι or smaller, and the maximum equivalent circular diameter was 5.4 μιη or larger and 9.9 μπι or smaller. Further, as a result of the structure analysis using the TE , the diffuse phase transition structure was confirmed in all the samples.

As to the electric characteristic, the piezoelectric constant d₃₃ ^* was 110 (pm/V) or larger, and the Curie temperature was 200 °C or higher in all the samples.

[0109] (Example of BaTi0₃-BiFe0₃-Bi (Nio.sTio.s) 0₃) (Examples 24 to 33, and Comparative Examples 7 to 10)

(Manufacturing method A: common sintering method) As raw materials, barium titanate (manufactured by Sakai Chemical Industry Co., Ltd.; grain size is 100 nm) , bismuth oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.999%), iron oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), nickel oxide

(manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), and titanium oxide (manufactured by Ishihara Sangyo Kaisha, Ltd.; purity is 99.9%) were used.

Composition of Table 3 was achieved by weighing, and wet mixing was performed in the ball mill for 24 hours using ethanol as a solvent. After that, drying was performed at 80°C, and the mixed powder was calcined at a temperature of 750 to 850°C for 6 hours.

The calcined powder was crushed, and wet mixing was performed again in the ball mill for 16 hours using ethanol as a solvent. Next, the mixed powder was dried at 80 °C, and then was calcined again at a temperature of 850 to 900°C for 6 hours. After that, PVA was added as a binder by 2 mass%, and the ball mill mixing was performed for 1 hour. After that, drying was performed at 80 °C, and then granulated powder was obtained.

Next, the obtained granulated powder was crushed, and particle size selection was performed with a sieve of 250 μιη mesh. The obtained powder after the particle size selection was filled in a mold and was pressed uniaxially by 200 MPa pressure, so as to make a disclike compact having a diameter of 10 mm.

Then, the binder was removed from the obtained compact at 500°C for 10 hours, and the compact was sintered at a temperature of 950 to 1,030°C for 6 hours so that a sintered body was obtained. After that, the obtained sintered body was polished to have a thickness of 0.4 mm.

(Manufacturing method B: tape casting method)

As raw materials, barium titanate (manufactured by Sakai Chemical Industry Co., Ltd.; grain size is 100 nm) , bismuth oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.999%), iron oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), nickel oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), and titanium oxide (manufactured by Ishihara Sangyo Kaisha, Ltd.; purity is 99.9%) were used.

Composition of Table 3 was achieved by weighing, and wet mixing was performed in the ball mill for 24 hours using ethanol as a solvent. After that, drying was performed at 80 °C, and the mixed powder was calcined at a temperature of 750 to 850°C for 6 hours.

The calcined powder was crushed, and wet mixing was performed again in the ball mill for 16 hours using ethanol as a solvent. Next, the mixed powder was dried at 80 °C, and then was calcined again at a temperature of 850 to 900°C for 6 hours. After that, mixed

solution of 55 vol% toluene and 45 vol% ethanol was added to the mixed powder to be 90 mass%. To this, polyvinyl pyrrolidone (PVP) having an average molecular weight of 400,000 as a binder and plasticizer (butyl phthalate) were added by 6 mass% each to the powder quantity. The wet mixing of this mixture was performed in the ball mill for 5 hours to make slurry.

Next, using a doctor blade device, the slurry was formed into a tape-like shape having a thickness of 40 to 45 μπι and was dried. Further, this tape was cut into pieces of 2x2 cm² size, and 40 pieces of them were laminated and were bonded by pressure of 100 kg/cm² (9.8 MPa) at 80 °C for 10 minutes so that a compact having a thickness of 1.8 mm was obtained.

Then, the binder was removed from the obtained compact at 650°C for 10 hours, and the compact was sintered at a temperature of 950 to 1,030°C for 6 hours so that a sintered body was obtained. After that, the obtained sintered body was polished to have a thickness of 0.4 mm.

[0111] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 23, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0112] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 23.

[0113] Results of those evaluations are shown in Table 3. In Table 3, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Ni₀.₅Ti₀.5) 0₃

respectively. In the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o", and a state in which the secondary phase exists is indicated by "χ".

[0115] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

In the structure evaluation, it was found from the X- ray diffraction structure analysis that only the perovskite-type structure existed in the examples except for Comparative Example 10. In addition, the density was 90% or higher as relative density in all having only the perovskite-type structure, and it is understood that the relative density increased as 97% or higher by using the tape casting method. Further, in the samples of the examples, the average equivalent circular diameter of crystal grains was 0.9 μκι or larger and 5.0 μπι or smaller, and the maximum

equivalent circular diameter of crystal grains was 6.1 μπι or larger and 9.8 μιη or smaller. Then, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples of the examples. As to the comparative

examples, the PNR was dominant in Comparative Examples 7 and 8, while the domain region was dominant in

Comparative Examples 9 and 10.

As to the electric characteristic, the piezoelectric constant d₃₃ ^* was 105 (pm/V) or larger, and the Curie temperature was 200°C or higher in all the samples in the composition ranges of the examples.

[0116] (Examples 34 to 39: Materials containing Mn or Cu)

(Manufacturing method)

As raw materials, barium titanate (manufactured by Sakai Chemical Industry Co., Ltd.; grain size is 100 nm) , bismuth oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.999%), iron oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), nickel oxide (manufactured by Rare Metallic Co., Ltd.; purity is 99.9%), titanium oxide (manufactured by Ishihara Sangyo Kaisha, Ltd.; purity is 99.9%), manganese carbonate, and copper oxide were used. Composition of Table 4 was achieved by weighing, and the sintered body was

manufactured by the same method as in Examples 1 to 33.

[0117] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 33, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0118] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 33.

[0119] Results of those evaluations are shown in Table 4. In Table 4, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Nio.sTio.s) 0₃,

respectively. In addition, n quantity and Cu quantity respectively indicate masses with respect to 100 parts by mass of xBaTi0₃-yBiFe0₃-zBi (Nio.sTio.s) 0₃. Further, in the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o" .

[0121] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 94% or higher as relative density in all the samples, which is a higher value than the samples in Examples 24 to 33, which were manufactured in the same method without manganese or copper. Then, the average equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 0.5 pm or larger and 4.0 \im or smaller, and the maximum equivalent circular diameter was 6.1 μπι or larger and 10.0 μπι or smaller. Further, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples.

As to the electric characteristic, the piezoelectric constant d₃₃ ^* was 100 (pm/V) or larger, and the Curie temperature was 200°C or higher in all the samples.

[0122] (Another example of BaTi0₃-BiFe0₃-Bi ( g₀.₅Ti₀.5) 0₃)

(Examples 40 to 45, and Comparative Example 11)

(Manufacturing method)

Through the use of the same raw materials as in

Examples 1 to 16, composition of Table 5 was achieved by weighing, and the sintered body was manufactured by the same method as in Examples 1 to 16.

[0123] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 39, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0124 ] (Electric characteristic evaluate) The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 39.

Results of those evaluations are shown in Table 5. In Table 5, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Mg₀.₅Tio.5) 0₃,

respectively. The crystal structure column indicates a state in which only the perovskite-type structure exists .

[0127] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

[0128] In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 90% or higher as relative density in all the samples. Then, the average

equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 3.9 μπι or larger and 7.5 μπι or smaller, and the maximum equivalent circular diameter was 8.4 μπι or larger and 13.7 μπι or smaller. Further, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples .

[0129] As to the electric characteristic, the piezoelectric

constant d₃₃ ^* was 100 (pm/V) or larger, and the Curie temperature was 200 °C or higher in all the samples.

[0130] (Examples 46 to 51: Materials containing Mn or Cu)

(Manufacturing method)

Through the use of the same raw materials as in

Examples 17 to 23, composition of Table 6 was achieved by weighing, and the sintered body was manufactured by the same method as in Examples 17 to 23.

[0131] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 45, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0132] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 45. Results of those evaluations are shown in Table 6. In Table 6, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Mg₀.₅Tio.5) 0₃,

respectively. In addition, Mn quantity and Cu quantity respectively indicate masses with respect to 100 parts by mass of xBaTi0₃-yBiFe0₃-zBi (Mgo.sTio.s) 0₃. Further, in the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o".

[0135] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

[0136] In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 94% or higher as relative density in all the samples, which is a higher value than that in Examples 40 to 45 without manganese or copper. Then, the average equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 3.1 μιη or larger and 6.5 μπι or smaller, and the maximum equivalent circular diameter was 8.2 μκι or larger and 10.0 μπι or smaller. Further, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples.

[0137] As to the electric characteristic, the piezoelectric

[0138] (Another example of BaTi0₃-BiFe0₃-Bi (Ni₀.₅Tio.5) 0₃)

(Examples 52 to 57, and Comparative Example 11)

(Manufacturing method)

Through the use of the same raw materials as in

Examples 24 to 33, composition of Table 7 was achieved by weighing, and the sintered body was manufactured by the same method as in Examples 24 to 33.

[0139] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 51, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0140] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 51.

Results of those evaluations are shown in Table 7. In Table 7, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Ni₀.₅Ti₀.5) 0₃,

respectively. In the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o" .

[0143] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

[0144] In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 90% or higher as relative density in all the samples. Then, the average

equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 3.4 μπι or larger and 7.9 μπι or smaller, and the maximum equivalent circular diameter was 7.2 μπι or larger and 14.6 μπι or smaller. Further, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples .

[0145] As to the electric characteristic, the piezoelectric

[0146] (Examples 58 to 63: Materials containing Mn or Cu)

(Manufacturing method)

Through the use of the same raw materials as in

Examples 34 to 39, composition of Table 8 was achieved by weighing, and the sintered body was manufactured by the same method as in Examples 34 to 39.

[0147] (Structure evaluation)

As to the polished sintered body, through the use of the same method as in Examples 1 to 57, the composition, the crystal structure, the density, and the average equivalent circular diameter and the maximum equivalent circular diameter of the crystal grains were evaluated.

[0148] (Electric characteristic evaluation)

The electric characteristic of the polished sintered body was evaluated by the same method as in Examples 1 to 57. Results of those evaluations are shown in Table 8. In Table 8, composition columns x, y, and z indicate molar ratios of BaTi0₃, BiFe0₃, and Bi (Ni₀.₅Ti₀.5) 0₃,

respectively. In addition, Mn quantity and Cu quantity respectively indicate masses with respect to 100 parts by mass of xBaTi0₃-yBiFe0₃-zBi (Nio.sTio.s) 0₃. Further, in the crystal structure column, a state in which only the perovskite-type structure exists is indicated by "o".

[0151] From a result of the fluorescent X-ray analysis, it was found that the composition was as weighed after

sintering, too.

[0152] In the structure evaluation, it was found that only the perovskite-type structure existed in all the samples from the X-ray diffraction structure analysis. In addition, the density was 94% or higher as relative density in all the samples, which is a higher value than that in Examples 52 to 57 without manganese or copper. Then, the average equivalent circular diameter and the maximum equivalent circular diameter of crystal grains were evaluated in all the samples. The average equivalent circular diameter was 2.8 μπι or larger and 6.5 μπι or smaller, and the maximum equivalent circular diameter was 6.2 μπι or larger and 9.8 pm or smaller. Further, as a result of the structure analysis using the TEM, the diffuse phase transition structure was confirmed in all the samples.

[0153] As to the electric characteristic, the piezoelectric constant d₃₃ ^* was 100 (pm/V) or larger, and the Curie temperature was 200°C or higher in all the samples.

[0154] (Liquid discharge head according to Example 8)

Through the use of the same piezoelectric material as in Example 8, a liquid discharge head illustrated in FIGS. 3A and 3B was prepared. Ink discharge from the liquid discharge head in response to input electric signals was confirmed.

[0155] (Ultrasonic motor according to Example 20)

Through the use of the same piezoelectric material as in Example 20, an ultrasonic motor illustrated in FIGS. 4A and 4B were prepared. The rotary behavior of the motor in response to application of an alternating voltage was confirmed.

[0156] (Dust removing device according to Example 30)

Through the use of the same piezoelectric material as in Example 30, a dust removing device illustrated in FIGS. 5A and 5B were prepared. When an alternating voltage was applied after spraying plastic beads, a satisfactory dust-removing rate was confirmed.

[0157] According to the present invention, it is possible to provide a piezoelectric material having high

piezoelectric performance without ingredients harmful to the environment. In addition, the present invention can provide the piezoelectric element, the liquid discharge head , the ultrasonic motor, and the dust removing device, which use the piezoelectric material. Reference Signs List

[0158] 101 piezoelectric element

102 individual liquid chamber

103 diaphragm

104 liquid chamber partition wall

105 discharge port

106 communicating hole

107 common liquid chamber

108 buffer layer

1011 first electrode

1012 piezoelectric material

1013 second electrode

201 transducer

202 rotor

203 output axis

204 transducer

205 rotor

206 spring

2011 elastic ring

2012 piezoelectric element

2013 organic adhesive

2041 metal elastic body

2042 laminated piezoelectric element

310 dust removing device

320 diaphragm

330 piezoelectric element 331 piezoelectric material

332 first electrode

333 second electrode

336 first electrode surface

337 second electrode surface

[0159] While the present invention has been described with reference to exemplary embodiments, it is to be understood that the invention is not limited to the disclosed exemplary embodiments. The scope of the following claims is to be accorded the broadest interpretation so as to encompass all such

modifications and equivalent structures and functions.

[0160] This application claims the benefit of Japanese Patent Application No. 2010-292819, filed December 28, 2010, and Japanese Patent Application No. 2011-194072, filed September 6, 2011, which are hereby incorporated by reference herein in their entirety.

Claims

[1] A piezoelectric material, comprising a perovskite-type metal oxide that is expressed by the following general formula (1) :

xBaTi0₃-yBiFe0₃-zBi ( ₀.₅Tio.5) 0₃ (1)

where M represents at least one type of element selected from the group consisting of Mg and Ni, x satisfies 0.25<x<0.75, y satisfies 0.15<y<0.70, z satisfies 0.05≤z≤0.60, and x+y+z=l is satisfied.

[2] The piezoelectric material according to claim 1,

wherein x satisfies 0.25≤x≤0.55, y satisfies

0.20≤y≤0.70, and z satisfies 0.05<z<0.25 in the general formula ( 1 ) .

[3] A piezoelectric material, comprising a perovskite-type metal oxide that is expressed by the following general formula (2 ) :

xBaTi0₃-yBiFe0₃-zBi ( ₀.₅Ti₀.5) 0₃ (2)

where M represents at least one type of element selected from the group consisting of Mg and Ni, x satisfies 0.10<x<0.25, y satisfies 0.15<y<0.30, z satisfies 0.45≤z≤0.75, and x+y+z=l is satisfied.

[4] The piezoelectric material according to any one of

claims 1 to 3, wherein the piezoelectric material contains at least one type of element selected from the group consisting of Mn and Cu at 0.05 mass% or higher and 3.0 massl or lower.

[5] The piezoelectric material according to any one of

claims 1 to 4,

wherein the piezoelectric material comprises a ceramic, wherein an average equivalent circular diameter of crystal grains of the ceramic is 500 nm or larger and 5 μπι or smaller, and

wherein a maximum equivalent circular diameter of the crystal grains is 5 μπ\ or larger and 10 μπι or smaller.

[6] The piezoelectric material according to any one of

claims 1 to 5, wherein the piezoelectric material comprises a ceramic, and

wherein crystal grains of the ceramic have a diffuse phase transition structure.

[7] A piezoelectric material, comprising a perovskite-type metal oxide that is expressed by the following general formula ( 3 ) :

lBaTi0₃-mBiFe0₃-nBi (M₀.₅Ti₀.5) 0₃ (3) ,

where M represents at least one type of element selected from the group consisting of Mg and Ni, 1 satisfies 0<1<1, m satisfies 0<m<l, n satisfies 0<n<l, and l+m+n=l is satisfied,

wherein the piezoelectric material comprises a ceramic, and

[8] A piezoelectric element, comprising:

a first electrode;

a piezoelectric material; and

a second electrode,

wherein the piezoelectric material comprises the piezoelectric material according to any one of claims 1 to 7.

[9] A liquid discharge head , comprising:

a liquid chamber comprising a vibration portion

including the piezoelectric element according to claim 8 ; and

a discharge port communicating to the liquid chamber.

[10] An ultrasonic motor, comprising:

a vibration body including the piezoelectric element according to claim 8; and

a moving body that is in contact with the vibration body.

[11] A dust removing device, comprising a vibration portion including the piezoelectric element according to claim 8.