WO2012036067A1

WO2012036067A1 - Rolling bearing

Info

Publication number: WO2012036067A1
Application number: PCT/JP2011/070467
Authority: WO
Inventors: 充浩中山
Original assignee: Ntn株式会社
Priority date: 2010-09-14
Filing date: 2011-09-08
Publication date: 2012-03-22
Also published as: JP2012062915A

Abstract

The present invention inexpensively inhibits cracks from occurring from the circumferential groove of a steel-material-made outer ring in a rolling bearing. After subjecting the outer ring (11) to a heat treatment, a chemical polishing treatment is performed in the circumferential groove (11b) of the outer ring. The thermal oxide layer formed in the circumferential groove (11b) by the heat treatment is removed by the chemical polishing treatment. By removing the thermal oxide layer, which increases sensitivity to cracks, the occurrence of cracks originating from the circumferential groove (11b) is inhibited. No sharp increase in cost is incurred, because the chemical polishing treatment is all that has to be performed.

Description

Rolling bearing

The present invention relates to a rolling bearing in which a concave portion such as a circumferential groove is formed on the outer diameter surface of an outer ring, and more particularly to a rolling bearing in which cracks from the concave portion are suppressed.
The present invention also relates to a method for manufacturing an outer ring of a rolling bearing in which the occurrence of cracks from a recess is suppressed.

As in Patent Document 1, a rolling bearing having a circumferential groove formed on the outer diameter surface of the outer ring is known. Such a circumferential groove is used to engage the snap ring to lock the entire rolling bearing to a housing or the like.
Moreover, when each component of a rolling bearing consists of steel materials, it is also known that each component is generally heat-treated as in the same document.

Here, when heat-treating the component of the rolling bearing, a thermal oxide film (so-called black skin) is generated on the outer surface of the component including the peripheral groove of the outer ring.
It is empirically known that if this kind of thermal oxide film generated in the peripheral groove of the outer ring is left, cracking from the peripheral groove is promoted (so-called crack sensitivity is increased).
Further, when turning the circumferential groove, a turning line may be generated in the circumferential groove, and there is a possibility that a crack may be generated starting from such a turning line.

By the way, in the case of a rolling bearing in which a circumferential groove is formed in the outer ring, a design in which the thickness between the bottom of the circumferential groove on the outer diameter surface of the outer ring and the rolling surface of the inner diameter surface is the thinnest part of the entire bearing is common. Therefore, the static strength of the bearing is often determined by the strength of the thinnest portion.
Therefore, if the state where the crack from the circumferential groove to the thinnest part is likely to occur due to the thermal oxide film or the turning line as described above, the static strength of the bearing may be greatly reduced.

On the other hand, if an enormous amount of money is spent to remove the thermal oxide film or the like, the manufacturing cost of the bearing rises, which is not preferable.
Such a problem is not limited to the circumferential groove, but is common in the case where a recess is formed in the outer ring.

JP 2004-332833 A

Therefore, the problem to be solved by the present invention is to suppress the occurrence of cracks from the concave portion of the outer ring made of a steel material at a low cost for the rolling bearing.

In order to solve the above-described problems, in the present invention, in a rolling bearing having an outer ring made of a steel material having a concave portion such as a circumferential groove formed on the outer diameter surface, the outer ring is chemically treated at least in the concave portion after heat treatment. A structure that has been polished is employed.

By chemically polishing the inside of the recess such as the circumferential groove, the thermal oxide film is removed and the turning line becomes smooth, so that the generation of cracks starting from the inside of the recess is suppressed. Since only chemical polishing is performed, a large-scale apparatus or the like is unnecessary, and costs can be reduced.
Since the occurrence of cracks is suppressed and the bearing strength is improved, the dimensional freedom of the design of the rolling bearing is also increased.

Incidentally, the outer ring may be subjected to chemical polishing other than the recesses, and when the inner ring is made of a steel material, it may be subjected to chemical polishing.
The outer ring may be subjected to a chemical polishing process at least in the recesses and then all or a part of the outer ring may be ground except for the recesses.

The type of heat treatment of the outer ring is not particularly limited, but any of those involving carburization of steel materials, those involving nitriding, and those involving refinement of crystal grains is preferable.
Although the kind of rolling bearing is not specifically limited, Any of an angular ball bearing, a cylindrical roller bearing, or a tapered roller bearing is preferable. Although its use is not particularly limited, it is preferably used for automobile transmission, axle or steering.

Considering this method in a method, a step of heat-treating an outer ring made of a steel material having a rolling surface formed on an inner diameter surface and a recess formed on an outer diameter surface, and then chemically polishing at least the inside of the recess of the outer ring. It is understood that the manufacturing method of the outer ring of the rolling bearing includes a step and then a step of grinding all or part of the outer ring other than the recess.

Since the rolling bearing according to the present invention is configured as described above, it has become possible to suppress the occurrence of cracks from the concave portion of the outer ring made of a steel material at a low cost.

Cross-sectional view of the rolling bearing of the embodiment Sectional drawing of outer ring of rolling bearing of embodiment An enlarged cross-sectional view schematically showing the state of adhesion of the thermal oxide film on the outer ring before chemical polishing treatment Schematic diagram showing the thrust fracture load measurement test Chart showing measurement results of thrust breaking load Schematic diagram showing the measurement test of radial breaking load Chart showing measurement results of radial breaking load

Embodiments of the present invention will be described below with reference to the drawings.
As shown in FIGS. 1 and 2, the deep groove ball bearing 10 of the embodiment includes a large-diameter cylindrical outer ring 11, a small-diameter cylindrical inner ring 12, a plurality of balls 13 as rolling elements, a cage 14, and the like. .
This type of deep groove ball bearing 10 is used in various applications such as for automobile transmissions, axles or steering.

The outer ring 11 of the deep groove ball bearing 10 is formed with a deep groove rolling surface 11a on the inner diameter surface, and the inner ring 12 coaxial with the outer ring 11 is formed with a deep groove rolling surface 12a on the outer diameter surface. Between these facing rolling surfaces 11a and 12a, each ball 13 is held by a cage 14 and is movably interposed.

A circumferential groove 11 b is further formed on the outer diameter surface of the outer ring 11 of the deep groove ball bearing 10. The deep groove ball bearing 10 can be fixed to a housing or the like by engaging (externally fitting) a snap ring R (retaining ring) as shown in FIG.

Here, the outer ring 11 and the inner ring 12 of the deep groove ball bearing 10 are made of a known steel material. The outer ring 11 and the inner ring 12 are subjected to a known heat treatment on the entirety thereof, and then a known chemical polishing process is further performed on a specific portion.

The type of heat treatment is not particularly limited, and examples include those involving carburization of steel materials, those involving nitriding, those involving carbonitriding, and those involving crystal grain refinement. The type of chemical polishing treatment is not particularly limited, and any method such as using hydrogen peroxide can be applied.

FIG. 3 shows the state of the outer ring 11 before the chemical polishing process is performed. As shown in the figure, the thermal oxide film L is particularly likely to remain in the portion excluding the rolling surface 11a on the inner diameter surface of the outer ring 11 and in the circumferential groove 11b on the outer diameter surface of the outer ring 11 and the chamfered portion 11c. ing.

From the state of FIG. 3, at least the thermal oxide film L in the circumferential groove 11 b is removed by the above-described chemical polishing treatment, and preferably, the chamfered portion 11 c and the thermal oxide film L on the inner diameter surface are also removed. If there is a turning line in the circumferential groove 11b, it is removed simultaneously by chemical polishing.
Thereafter, a part or all of the rolling surface 11a, the width surface (end surface), and the outer diameter surface (excluding the circumferential groove) of the outer ring 11 may be processed to the target dimensions by grinding.
Similarly, a part or all of the inner ring 12 may be chemically polished to remove the thermal oxide film, and part or all of the inner ring 12 may be processed to a target dimension by grinding.

The deep groove ball bearing 10 thus completed is smoothed by removing the thermal oxide film and the turning lines in the circumferential groove 11b of the outer ring 11. Therefore, the generation of cracks starting from the circumferential groove 11b is suppressed.
In this case, since only chemical polishing is performed after the heat treatment, generation of cracks can be suppressed at low cost.

In the above embodiment, the deep groove ball bearing 10 is exemplified as the rolling bearing, but the present invention is applicable to all rolling bearings such as a cylindrical roller bearing and a tapered roller bearing.
In the above embodiment, the inner ring 12 is heat treated and chemically polished using a steel material. However, the inner ring 12 may not be chemically polished, and the inner ring 12 may not be a steel material.
Furthermore, in the embodiment, the outer ring 11 provided with the peripheral groove 11b on the outer diameter surface is exemplified, but the present invention can be applied to all the outer ring 11 provided with a recess on the outer diameter surface.

Next, the features of the present invention will be further clarified by giving examples and comparative examples.
The outer ring 11 having the structure shown in FIG. 2 is subjected to chemical polishing treatment in the peripheral groove 11b after heat treatment in the same manner as in the above embodiment (Example 1), and is not subjected to chemical polishing treatment after heat treatment (Comparative Example 1). Prepared.

[Thrust breaking test]
As shown in FIG. 4, the outer ring 11 of Example 1 and Comparative Example 1 was assembled with the inner ring 12 and the ball 13 to complete a deep groove ball bearing. Then, the outer ring 11 was fixed to the housing H by attaching a snap ring R to the circumferential groove 11b.
Furthermore, the shaft S was attached from the upper part of the inner ring 12, an axial load indicated by an arrow was given to the shaft S, and the thrust breaking strength (thrust breaking load [kN]) of the outer ring 11 was measured. The results are shown in FIG.
As is clear from FIG. 5, Example 1 was confirmed to have an improvement in fracture strength of about 30% as seen from Comparative Example 1.

(Radial fracture test)
As shown in FIG. 6, the outer ring 11 of Example 1 and Comparative Example 1 was placed on the measuring table B, applied with a pusher P from above, and applied with a radial load indicated by an arrow, and its radial breaking strength (radial breaking) Load [kN]) was measured. The results are shown in FIG.
As is clear from FIG. 7, Example 1 was confirmed to have an improvement in fracture strength of about 20% as seen from Comparative Example 1.

It is considered that the improvement of the fracture strength in Example 1 as described above is caused by a decrease in so-called crack sensitivity due to the removal of the thermal oxide film and the like in the peripheral groove 11b.

DESCRIPTION OF SYMBOLS 10 Deep groove ball bearing 11 Embodiment 11 Outer ring 11a Rolling surface 11b Circumferential groove 11c Chamfer 12 Inner ring 12a Rolling surface 13 Ball 14 Cage L Thermal oxide film R Snap ring H Housing S Shaft B Measuring base P Pusher

Claims

An outer ring made of a steel material in which a rolling surface is formed on the inner diameter surface and a recess is formed on the outer diameter surface;
An inner ring disposed coaxially with the outer ring and having a rolling surface formed on the outer diameter surface thereof,
A plurality of rolling elements arranged so as to be able to roll between the facing rolling surfaces of the outer ring and the inner ring,
The outer ring is a rolling bearing in which at least the inside of the outer ring is subjected to a chemical polishing process after being heat-treated.
2. The rolling bearing according to claim 1, wherein at least the inside of the outer ring is subjected to a chemical polishing treatment and then all or a part of the outer ring other than the recess is ground.
The rolling bearing according to claim 1 or 2, wherein the concave portion of the outer ring is a circumferential groove capable of engaging with a snap ring for locking the entire rolling bearing to another member.
The rolling bearing according to any one of claims 1 to 3, wherein the heat treatment of the outer ring is a heat treatment involving carburization of a steel material.
The rolling bearing according to any one of claims 1 to 4, wherein the heat treatment of the outer ring is a heat treatment involving nitriding of a steel material.
The rolling bearing according to claim 4 or 5, wherein the heat treatment of the outer ring is a heat treatment accompanied by refinement of crystal grains of the steel material.
The rolling bearing according to any one of claims 1 to 6, which is a deep groove ball bearing, an angular ball bearing, a cylindrical roller bearing, or a tapered roller bearing.
The rolling bearing according to any one of claims 1 to 7, wherein the rolling bearing is for an automobile transmission, an axle, or a steering.
A step of heat-treating an outer ring made of a steel material in which a rolling surface is formed on the inner diameter surface and a recess is formed on the outer diameter surface;
Next, a step of chemically polishing at least the inside of the recess of the outer ring,
And a step of grinding all or part of the outer ring other than the recesses, and a method for manufacturing the outer ring of the rolling bearing.