WO2012029977A1 - Chromate-free coated metal plate - Google Patents
Chromate-free coated metal plate Download PDFInfo
- Publication number
- WO2012029977A1 WO2012029977A1 PCT/JP2011/070302 JP2011070302W WO2012029977A1 WO 2012029977 A1 WO2012029977 A1 WO 2012029977A1 JP 2011070302 W JP2011070302 W JP 2011070302W WO 2012029977 A1 WO2012029977 A1 WO 2012029977A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal plate
- coating film
- chromate
- particles
- polyolefin resin
- Prior art date
Abstract
Description
耐食性や耐傷付き性を向上させる技術の一つとして無機酸化物粒子を、有機樹脂を造膜成分とした塗膜に添加する技術が知られている。しかし、無機酸化物粒子の添加は塗膜の伸び特性を低下させてしまうため、加工性と耐食性、耐傷付き性を両立させることは、従来難しい課題であった。
また、耐傷付き性を向上させる技術の一つとしてポリオレフィン樹脂粒子やフッ素樹脂粒子、二硫化モリブデン粒子等の潤滑剤を塗膜に添加する技術も知られている。しかし、クロメートフリーで、且つ塗装金属板としては比較的薄膜の10μm以下の塗膜においては、これら潤滑剤の添加条件によっては、大幅に耐食性が低下する場合があることが新たに判明した。
そこで、本発明者らはこれらの課題を克服すべく鋭意検討を重ねてきた結果、有機樹脂を造膜成分とした塗膜に、特定の粒子形状を持った2種類の粒子径範囲の異なるシリカ粒子を分散添加することで、加工性を低下させることなく、耐食性、耐傷付き性を大幅に改善できるとの知見を得た。
加えて、塗膜に添加する潤滑剤としてはポリオレフィン樹脂粒子が好適であり、ポリオレフィン樹脂粒子の平均粒子径を限定し、更に塗膜厚とこのポリオレフィン樹脂粒子の平均粒子径の比を特定の範囲に制御することで耐食性を低下させることなく、大幅に耐傷付き性を改善できるとの知見を得た。
これらの知見を組み合わせることで、クロメートフリーであり、10μm以下の薄膜塗装金属板において、相反する性能である加工性と耐食性、耐傷付き性を高次元で両立させることに成功した。 In general, workability, corrosion resistance, and scratch resistance are technically conflicting performances. In order to ensure workability, it is important that the coating film covering the surface of the metal plate follows the deformation such as elongation that occurs when the metal plate is molded without cracking or peeling. is there. This is because if the coating film is cracked or peeled off, the design appearance may be remarkably impaired. In order to improve the followability of the coating film against deformation of the metal plate, it is preferable to use a relatively soft and excellent organic resin as a film-forming component of the coating film, but with only a soft organic resin, corrosion resistance and It is difficult to ensure scratch resistance.
As one of the techniques for improving the corrosion resistance and scratch resistance, there is known a technique of adding inorganic oxide particles to a coating film using an organic resin as a film-forming component. However, since the addition of inorganic oxide particles reduces the elongation characteristics of the coating film, it has been difficult to achieve both workability, corrosion resistance, and scratch resistance.
In addition, as one technique for improving the scratch resistance, a technique of adding a lubricant such as polyolefin resin particles, fluororesin particles, molybdenum disulfide particles or the like to the coating film is also known. However, it has been newly found that the corrosion resistance of a paint film that is chromate-free and relatively thin as a coated metal plate and is 10 μm or less may be significantly reduced depending on the conditions of addition of these lubricants.
Accordingly, as a result of intensive investigations to overcome these problems, the present inventors have obtained a silica film having a specific particle shape and two different particle diameter ranges on a coating film containing an organic resin as a film-forming component. It was found that by adding and dispersing the particles, the corrosion resistance and scratch resistance can be greatly improved without degrading the workability.
In addition, polyolefin resin particles are suitable as a lubricant to be added to the coating film, the average particle diameter of the polyolefin resin particles is limited, and the ratio of the coating film thickness to the average particle diameter of the polyolefin resin particles is in a specific range. It has been found that the scratch resistance can be greatly improved without reducing the corrosion resistance.
By combining these findings, we succeeded in achieving high compatibility between workability, corrosion resistance, and scratch resistance, which are chromate-free and thin film coated metal plates of 10 μm or less, which are contradictory properties.
前記ポリオレフィン樹脂粒子(D)の平均粒子径をaμm、前記塗膜(α)の厚みをbμmとしたとき、0.5≦a≦3、2≦b≦10、0.1≦a/b≦0.8を満足し、
前記シリカ粒子(C)が、平均粒子径5~50nmの球状シリカ粒子(C1)と平均粒子径0.3~5μmの球状シリカ粒子(C2)の両方を含有することを特徴とする、クロメートフリー塗装金属板。 [1] A chromate-free coated metal plate having a coating film (α) comprising an organic resin (A) as a film-forming component and containing silica particles (C) and polyolefin resin particles (D) on at least one surface of the metal plate. There,
When the average particle diameter of the polyolefin resin particles (D) is a μm and the thickness of the coating film (α) is b μm, 0.5 ≦ a ≦ 3, 2 ≦ b ≦ 10, 0.1 ≦ a / b ≦ 0.8 satisfied,
Chromate-free, characterized in that the silica particles (C) contain both spherical silica particles (C1) having an average particle size of 5 to 50 nm and spherical silica particles (C2) having an average particle size of 0.3 to 5 μm. Painted metal plate.
前記ポリオレフィン樹脂粒子(D)の平均粒子径が0.5~3μmであり、
前記シリカ粒子(C)が、平均粒子径5~50nmの球状シリカ粒子(C1)と平均粒子径0.3~5μmの球状シリカ粒子(C2)の両方を含有することを特徴とする、水系塗料組成物(X)。 [15] A water-based coating composition (X) containing an organic resin (A), silica particles (C), and polyolefin resin particles (D),
The polyolefin resin particles (D) have an average particle diameter of 0.5 to 3 μm,
The water-based paint characterized in that the silica particles (C) contain both spherical silica particles (C1) having an average particle diameter of 5 to 50 nm and spherical silica particles (C2) having an average particle diameter of 0.3 to 5 μm. Composition (X).
メラミン樹脂(B1)はメラミンとホルムアルデヒドとを縮合して得られる生成物のメチロール基の一部またはすべてをメタノール、エタノール、ブタノールなどの低級アルコールでエーテル化した樹脂である。 The organic resin (A) is preferably a resin cured with a curing agent (B) in order to improve scratch resistance and corrosion resistance. The curing agent (B) is not particularly limited as long as it cures the organic resin (A), and examples thereof include a melamine resin (B1) and a polyisocyanate compound.
The melamine resin (B1) is a resin obtained by etherifying a part or all of methylol groups of a product obtained by condensing melamine and formaldehyde with a lower alcohol such as methanol, ethanol, or butanol.
すなわち、「耐アブレージョン性」を有する塗装鋼板であっても、必ずしも「耐傷付き性」を満足するとは言えない。例えば、上記の麟片状シリカを用いる場合には、後で述べる様に球状シリカのようにシリカ粒子が転がりながら被接触物との接触を避けるという作用効果を得ることがでず、摩擦抵抗が大きくなる。このため麟片状シリカは耐アブレージョン性の確保には有用であるが耐傷付き性に対する効果は期待出来ない。 Further, it is known that there is a term “ablation resistance” in relation to scratch resistance. The difference between "ablation resistance" and "scratch resistance" is not always clearly defined, but "ablation resistance" is generally used when a processed product is transported in a cardboard box. This refers to wear scars (scratches caused by repeated wear at a relatively low surface pressure) caused by rubbing the workpiece and cardboard with vibration. On the other hand, “scratch resistance” generally covers “all” with scratches that occur during handling, pressing, and transportation of steel sheets. Therefore, from such a viewpoint, “ablation resistance” is included in “scratch resistance”.
That is, even a coated steel sheet having “abrasion resistance” does not necessarily satisfy “scratch resistance”. For example, in the case where the above scaly silica is used, the effect of avoiding contact with the contacted object while the silica particles roll as in the case of spherical silica cannot be obtained as will be described later, and the frictional resistance is low. growing. For this reason, scaly silica is useful for ensuring abrasion resistance, but an effect on scratch resistance cannot be expected.
使用した金属板の種類を、表1に示す。めっきを施した金属板の基材には、板厚0.5mmの軟鋼板を使用した。SUS板についてはフェライト系ステンレス鋼板(鋼成分:C;0.008質量%、Si;0.07質量%、Mn;0.15質量%、P;0.011質量%、S;0.009質量%、Al;0.067質量%、Cr;17.3質量%、Mo;1.51質量%、N;0.0051質量%、Ti;0.22質量%、残部Feおよび不可避的不純物)を使用した。金属板は表面をアルカリ脱脂処理、水洗乾燥して使用した。 (1) Metal plate Table 1 shows the types of metal plates used. A mild steel plate having a thickness of 0.5 mm was used as the base material of the plated metal plate. For SUS plate, ferritic stainless steel plate (steel component: C; 0.008 mass%, Si; 0.07 mass%, Mn; 0.15 mass%, P; 0.011 mass%, S; 0.009 mass) %, Al: 0.067% by mass, Cr: 17.3% by mass, Mo: 1.51% by mass, N: 0.0051% by mass, Ti: 0.22% by mass, balance Fe and inevitable impurities) used. The metal plate was used after subjecting the surface to alkaline degreasing treatment, washing with water and drying.
下地処理層を形成するためのコーティング剤は、有機樹脂(表2)、シランカップリング剤(表3)、ポリフェノール化合物(表4)を表5に示す配合量(固形分質量%)で配合し、塗料用分散機を用いて攪拌することで調整した。上記(1)で準備した金属板の表面に該コーティング剤を100mg/m2の付着量になるようにロールコーターで塗装し、到達板温度70℃の条件で乾燥させることで、必要に応じて下地処理層(β1~β9)を形成させた。 (2) Ground treatment layer The coating agent for forming the ground treatment layer is an organic resin (Table 2), a silane coupling agent (Table 3), and a polyphenol compound (Table 4) as shown in Table 5 (solid content). (Mass%), and it adjusted by stirring using the disperser for coating materials. The coating agent is applied to the surface of the metal plate prepared in (1) above with a roll coater so as to have an adhesion amount of 100 mg / m 2 , and dried under the condition of a reaching plate temperature of 70 ° C. Base treatment layers (β1 to β9) were formed.
塗膜を形成するための塗料組成物は、有機樹脂(A)(下記製造例1~5および表6)、硬化剤(B)(表7)、シリカ粒子(C)(表8)、ポリオレフィン樹脂粒子(D)(表9)、着色顔料(E)(表10)、アクリル樹脂、シリコーン樹脂から選ばれる少なくとも1種の樹脂粒子(F)(表11)を、表12~表22に示す配合量(固形分質量%)で配合し、塗料用分散機を用いて攪拌することで調整した。前記(2)で形成した下地処理層(下地処理層がない場合は前記(1)で準備した金属板)の上層に、上記塗料組成物を所定の膜厚になるようにロールコーターで塗装し、所定の到達板焼付温度で加熱乾燥し、塗膜を形成させた。 (3) Coating film The coating composition for forming the coating film is composed of an organic resin (A) (Production Examples 1 to 5 and Table 6 below), a curing agent (B) (Table 7), silica particles (C) ( Table 12), polyolefin resin particles (D) (Table 9), colored pigments (E) (Table 10), at least one resin particle (F) (Table 11) selected from acrylic resins and silicone resins ~ Blended in the blending amount shown in Table 22 (solid content mass%), and adjusted by stirring using a paint disperser. The coating composition is applied to the upper layer of the base treatment layer formed in (2) above (the metal plate prepared in (1) if there is no base treatment layer) with a roll coater so as to have a predetermined film thickness. The film was heated and dried at a predetermined reaching plate baking temperature to form a coating film.
攪拌機、コンデンサー、温度計を具備した反応容器にテレフタル酸199部、イソフタル酸232部、アジピン酸199部、5−ナトリウムスルホイソフタル酸33部、エチレングリコール312部、2,2−ジメチル−1,3−プロパンジオール125部、1,5−ペンタンジオール187部、テトラブチルチタネート0.41部を仕込み、160℃から230℃まで4時間かけてエステル化反応を行った。次いで系内を徐々に減圧していき、20分かけて5mmHgまで減圧し、さらに0.3mmHg以下の真空下、260℃にて40分間重縮合反応を行った。得られた共重合ポリエステル樹脂100部に、ブチルセロソルブ20部、メチルエチルケトン42部を投入した後、80℃で2時間攪拌溶解を行い、更に213gのイオン交換水を投入し、水分散を行った。その後、加熱しながら溶剤を留去、200メッシュのナイロンメッシュでろ過し、固形分濃度30%のポリエステル樹脂水分散体(A1)を得た。 <Organic resin production example 1>
In a reaction vessel equipped with a stirrer, condenser and thermometer, 199 parts of terephthalic acid, 232 parts of isophthalic acid, 199 parts of adipic acid, 33 parts of 5-sodium sulfoisophthalic acid, 312 parts of ethylene glycol, 2,2-dimethyl-1,3 -125 parts of propanediol, 187 parts of 1,5-pentanediol and 0.41 part of tetrabutyl titanate were charged, and the esterification reaction was performed from 160 ° C to 230 ° C over 4 hours. Next, the pressure in the system was gradually reduced, the pressure was reduced to 5 mmHg over 20 minutes, and a polycondensation reaction was performed at 260 ° C. for 40 minutes under a vacuum of 0.3 mmHg or less. After adding 20 parts of butyl cellosolve and 42 parts of methyl ethyl ketone to 100 parts of the obtained copolyester resin, the mixture was stirred and dissolved at 80 ° C. for 2 hours, and further 213 g of ion-exchanged water was added to perform water dispersion. Thereafter, the solvent was distilled off while heating, followed by filtration through a 200 mesh nylon mesh to obtain a polyester resin aqueous dispersion (A1) having a solid content concentration of 30%.
攪拌機、コンデンサー、温度計を具備した反応容器にテレフタル酸199部、イソフタル酸266部、アジピン酸199部、エチレングリコール312部、2,2−ジメチル−1,3−プロパンジオール125部、1,5−ペンタンジオール187部、テトラブチルチタネート0.41部を仕込み、160℃から230℃まで4時間かけてエステル化反応を行った。次いで系内を徐々に減圧していき、20分かけて5mmHgまで減圧し、さらに0.3mmHg以下の真空下、260℃にて40分間重縮合反応を行った。窒素気流下、220℃まで冷却し、無水トリメリット酸を23部、エチレングリコールビスアンヒドロトリメリテート16部を投入し、30分間反応を行った。得られた共重合ポリエステル樹脂100部、ブチルセロソルブ20部、メチルエチルケトン42部を投入した後、80℃で2時間攪拌溶解を行い、イソプロピルアルコール23部、トリエチルアミン3.5部を投入し、213部のイオン交換水で水分散を行った。その後、加熱しながら溶剤を留去、200メッシュのナイロンメッシュでろ過し、固形分濃度30%のポリエステル樹脂水分散体(A2)を得た。 <Organic resin production example 2>
In a reaction vessel equipped with a stirrer, condenser and thermometer, 199 parts terephthalic acid, 266 parts isophthalic acid, 199 parts adipic acid, 312 parts ethylene glycol, 125 parts 2,2-dimethyl-1,3-propanediol, 1,5 -187 parts of pentanediol and 0.41 part of tetrabutyl titanate were charged, and the esterification reaction was carried out from 160 ° C to 230 ° C over 4 hours. Next, the pressure in the system was gradually reduced, the pressure was reduced to 5 mmHg over 20 minutes, and a polycondensation reaction was performed at 260 ° C. for 40 minutes under a vacuum of 0.3 mmHg or less. The mixture was cooled to 220 ° C. in a nitrogen stream, and 23 parts of trimellitic anhydride and 16 parts of ethylene glycol bisanhydrotrimellitate were added and reacted for 30 minutes. 100 parts of the obtained copolyester resin, 20 parts of butyl cellosolve and 42 parts of methyl ethyl ketone were added, and then stirred and dissolved at 80 ° C. for 2 hours. Then, 23 parts of isopropyl alcohol and 3.5 parts of triethylamine were added, and 213 parts of ions were added. Water dispersion was performed with exchange water. Thereafter, the solvent was distilled off while heating, and the mixture was filtered through a 200 mesh nylon mesh to obtain a polyester resin aqueous dispersion (A2) having a solid content concentration of 30%.
攪拌機、コンデンサー、温度計を具備した反応容器にテレフタル酸199部、イソフタル酸232部、アジピン酸199部、5−ナトリウムスルホイソフタル酸33部、エチレングリコール250部、2,2−ジメチル−1,3−プロパンジオール125部、1,5−ペンタンジオール187部、ビスフェノールAエチレンオキサイド付加物62部、テトラブチルチタネート0.41部を仕込み、160℃から230℃まで4時間かけてエステル化反応を行った。次いで系内を徐々に減圧していき、20分かけて5mmHgまで減圧し、さらに0.3mmHg以下の真空下、260℃にて40分間重縮合反応を行った。得られた共重合ポリエステル樹脂100部に、ブチルセロソルブ20部、メチルエチルケトン42部を投入した後、80℃で2時間攪拌溶解を行い、更に213gのイオン交換水を投入し、水分散を行った。その後、加熱しながら溶剤を留去、200メッシュのナイロンメッシュでろ過し、固形分濃度30%のポリエステル樹脂水分散体(A3)を得た。 <Organic resin production example 3>
In a reaction vessel equipped with a stirrer, condenser and thermometer, 199 parts terephthalic acid, 232 parts isophthalic acid, 199 parts adipic acid, 33 parts 5-sodium sulfoisophthalic acid, 250 parts ethylene glycol, 2,2-dimethyl-1,3 -Propanediol 125 parts, 1,5-pentanediol 187 parts, bisphenol A ethylene oxide adduct 62 parts, tetrabutyl titanate 0.41 part were charged, and esterification was performed from 160 ° C to 230 ° C over 4 hours. . Next, the pressure in the system was gradually reduced, the pressure was reduced to 5 mmHg over 20 minutes, and a polycondensation reaction was performed at 260 ° C. for 40 minutes under a vacuum of 0.3 mmHg or less. After adding 20 parts of butyl cellosolve and 42 parts of methyl ethyl ketone to 100 parts of the obtained copolyester resin, the mixture was stirred and dissolved at 80 ° C. for 2 hours, and further 213 g of ion-exchanged water was added to perform water dispersion. Thereafter, the solvent was distilled off while heating, and the mixture was filtered through a 200 mesh nylon mesh to obtain a polyester resin aqueous dispersion (A3) having a solid content concentration of 30%.
末端にヒドロキシル基を有するアジピン酸と1,4−ブチレングリコールから合成された平均分子量900のポリエステルポリオール230部、2,2−ビス(ヒドロキシメチル)プロピオン酸15部をN−メチル2−ピロリドン100部に加え、80℃に加温して溶解させた。その後、ヘキサメチレンジイソシアネート100部を加え、110℃に加温して2時間反応させ、トリエチルアミンを11部加えて中和した。この溶液をエチレンジアミン5部とイオン交換水570部とを混合した水溶液に強攪拌下において滴下して、固形分濃度30%のポリウレタン樹脂水分散体(A4)を得た。 <Organic resin production example 4>
230 parts of an average molecular weight 900 polyester polyol synthesized from adipic acid having a hydroxyl group at the terminal and 1,4-butylene glycol, 15 parts of 2,2-bis (hydroxymethyl) propionic acid and 100 parts of N-methyl 2-pyrrolidone And dissolved by heating to 80 ° C. Thereafter, 100 parts of hexamethylene diisocyanate was added, heated to 110 ° C. and reacted for 2 hours, and 11 parts of triethylamine was added for neutralization. This solution was dropped into an aqueous solution in which 5 parts of ethylenediamine and 570 parts of ion-exchanged water were mixed under strong stirring to obtain a polyurethane resin aqueous dispersion (A4) having a solid content concentration of 30%.
末端にヒドロキシル基を有するアジピン酸と1,4−ブチレングリコールから合成された平均分子量900のポリエステルポリオール80部、平均分子量700のビスフェノールAプロピレンオキサイド3モル付加物120部、および2,2−ビス(ヒドロキシメチル)プロピオン酸12部をN−メチル2−ピロリドン100部に加え、80℃に加温して溶解させた。その後、ヘキサメチレンジイソシアネート100部を加え、110℃に加温して2時間反応させ、トリエチルアミンを11部加えて中和した。この溶液をエチレンジアミン5部とイオン交換水570部とを混合した水溶液に強攪拌下において滴下して、固形分濃度30%のポリウレタン樹脂(A5)を得た。 <Organic resin production example 5>
80 parts of a polyester polyol having an average molecular weight of 900 synthesized from adipic acid having a hydroxyl group at the terminal and 1,4-butylene glycol, 120 parts of a 3-mol adduct of bisphenol A propylene oxide having an average molecular weight of 700, and 2,2-bis ( 12 parts of hydroxymethyl) propionic acid was added to 100 parts of N-methyl 2-pyrrolidone and heated to 80 ° C. to dissolve. Thereafter, 100 parts of hexamethylene diisocyanate was added, heated to 110 ° C. and reacted for 2 hours, and 11 parts of triethylamine was added for neutralization. This solution was dropped into an aqueous solution in which 5 parts of ethylenediamine and 570 parts of ion-exchanged water were mixed under strong stirring to obtain a polyurethane resin (A5) having a solid content concentration of 30%.
上記(1)~(3)で作成した塗装金属板の塗膜構成および塗膜の膜厚、到達板温度、加熱乾燥時間、冷却方法(加熱乾燥後、直後に水没して急速冷却したものには水冷と記載し、加熱乾燥後自然放冷したものには放冷と記載)、水冷時の水冷水の温度を表12~表22に示す。また、前記ポリオレフィン樹脂粒子(D)の軟化点をTS℃、水冷時の前記金属板の板温度をTM℃、水冷水の水温度をTW℃としたときに、TM>TS、またはTW≧(TM−150)/4が成立するか否か(成立性と表記)も表12~表22に示す(成立するものには○、成立しないものには×と記載)。 (4) Painted metal plate Coating film composition of coated metal plate prepared in (1) to (3) above, coating film thickness, ultimate plate temperature, heating drying time, cooling method (submerged immediately after heating drying) Table 12 to Table 22 show the temperature of water-cooled water at the time of water cooling. Further, when the softening point of the polyolefin resin particles (D) is T S ° C, the plate temperature of the metal plate during water cooling is T M ° C, and the water temperature of the water-cooled water is T W ° C, T M > T S , or T W ≧ (T M -150) / 4 whether established (viability hereinafter) are also shown in Table 12 through Table 22 (according to those established ○, and × for those not satisfied) .
上記(4)で得られた塗装金属板(試験板)について、加工性、耐食性、耐傷付き性を下記に示す評価方法および評価基準にて評価した。その評価結果を表23~表29に示す。 (5) Evaluation test About the coating metal plate (test plate) obtained by said (4), workability, corrosion resistance, and damage resistance were evaluated by the evaluation method and evaluation criteria shown below. The evaluation results are shown in Tables 23 to 29.
試験板に180°折り曲げ加工を施し、折り曲げ部外側の外観を下記の評価基準で評価した。折り曲げ加工は20℃雰囲気中で、0.5mmのスペーサーを間に挟んで実施した(一般に1T曲げと呼ばれる)。
5:塗膜に亀裂等の不具合がなく、均一な外観である。塗膜が着色されている場合、均一な着色外観であり、色落ちも認められない。
4:塗膜に極僅かの亀裂が認められるが、ほぼ均一な外観である。塗膜が着色されている場合、やや色落ちが認められるが、ほぼ均一な着色外観である。(試験前の試験板を横に並べて何とか分かるレベル)。
3:塗膜に僅かの亀裂が認められため、やや不均一な外観である。塗膜が着色されている場合、やや色落ちが認められるが、ほぼ均一な着色外観である。(試験前の試験板を横に並べると容易に分かるレベル)。
2:塗膜に亀裂が認められ、不均一な外観である。塗膜が着色されている場合、色落ちが認められる(試験板のみ見て何とか分かるレベル)。
1:塗膜に亀裂が認められ、不均一な外観である。塗膜が着色されている場合、色落ちが著しい(試験板のみ見て容易に分かるレベル)。 (Processability)
The test plate was subjected to 180 ° bending, and the outer appearance of the bent portion was evaluated according to the following evaluation criteria. The bending process was performed in an atmosphere of 20 ° C. with a 0.5 mm spacer in between (generally referred to as 1T bending).
5: The coating film has no defects such as cracks and has a uniform appearance. When the coating film is colored, it has a uniform colored appearance and no color fading is observed.
4: Although a very slight crack is recognized in the coating film, it has a substantially uniform appearance. When the coating is colored, a slight color fading is observed, but the appearance is almost uniform. (The level that you can manage by arranging the test plates before the test side by side).
3: Since a slight crack is recognized in the coating film, it has a slightly non-uniform appearance. When the coating is colored, a slight color fading is observed, but the appearance is almost uniform. (The level that can be easily understood by arranging the test plates before the test side by side).
2: Cracks are observed in the coating film, and the appearance is uneven. When the coating is colored, color fading is observed (a level that can be understood by looking at only the test plate).
1: Cracks were observed in the coating film, and the appearance was uneven. When the coating is colored, the color fading is significant (a level that can be easily seen by looking at only the test plate).
試験板の端面をテープシールした後、JIS Z2371に準拠した塩水噴霧試験(SST)を120時間行い、錆発生状況を観察し、下記の評価基準で評価した。
5:錆発生なし。
4:錆発生面積が1%未満。
3:錆発生面積が1%以上、2.5%未満。
2:錆発生面積が2.5%以上、5%未満。
1:錆発生面積が5%以上。 (Corrosion resistance)
After tape-sealing the end face of the test plate, a salt spray test (SST) based on JIS Z2371 was performed for 120 hours, and the rust generation state was observed and evaluated according to the following evaluation criteria.
5: No rust generation.
4: Rust generation area is less than 1%.
3: Rust generation area is 1% or more and less than 2.5%.
2: Rust generation area is 2.5% or more and less than 5%.
1: Rust generation area is 5% or more.
試験板をラビングテスターに設置後、スチールウール(#0000)を49.03kPa(0.5kgf/cm2)および196.12kPa(2.0kgf/cm2)の荷重で10往復擦った後の皮膜状態を下記の評価基準で評価した。
5:擦り面に全く傷が付かない。
4:擦り面に極僅かに傷が付く(目を凝らして何とか擦り跡が判別できるレベル)。
3:擦り面に僅かに傷が付く(目を凝らすと容易に擦り跡が判別できるレベル)。
2:擦り面に明確な傷が付く(瞬時に擦り跡が判別できるレベル)。
1:擦り面の下地金属板が露出する。 (Scratch resistance)
After the test plate was placed on a rubbing tester, the steel wool (# 0000) was rubbed 10 times with a load of 49.03 kPa (0.5 kgf / cm 2 ) and 196.12 kPa (2.0 kgf / cm 2 ), and the coating state Was evaluated according to the following evaluation criteria.
5: The scratched surface is not scratched at all.
4: Scratches are slightly scratched on the rubbing surface (a level at which the rubbing marks can be discriminated with some attention).
3: Scratches are slightly scratched on the rubbing surface (a level at which the rubbing marks can be easily discerned when the eyes are closed).
2: Clear scratches on the rubbing surface (a level at which rubbing traces can be identified instantaneously).
1: The base metal plate of the rubbing surface is exposed.
Claims (15)
- 金属板の少なくとも片面に、有機樹脂(A)を造膜成分とし、シリカ粒子(C)、ポリオレフィン樹脂粒子(D)を含んでなる塗膜(α)を有するクロメートフリー塗装金属板であって、
前記ポリオレフィン樹脂粒子(D)の平均粒子径をaμm、前記塗膜(α)の厚みをbμmとしたとき、0.5≦a≦3、2≦b≦10、0.1≦a/b≦0.8を満足し、
前記シリカ粒子(C)が、平均粒子径5~50nmの球状シリカ粒子(C1)と平均粒子径0.3~5μmの球状シリカ粒子(C2)の両方を含有することを特徴とする、クロメートフリー塗装金属板。 A chromate-free coated metal plate having a coating film (α) comprising an organic resin (A) as a film-forming component, silica particles (C), and polyolefin resin particles (D) on at least one surface of the metal plate,
When the average particle diameter of the polyolefin resin particles (D) is a μm and the thickness of the coating film (α) is b μm, 0.5 ≦ a ≦ 3, 2 ≦ b ≦ 10, 0.1 ≦ a / b ≦ 0.8 satisfied,
Chromate-free, characterized in that the silica particles (C) contain both spherical silica particles (C1) having an average particle size of 5 to 50 nm and spherical silica particles (C2) having an average particle size of 0.3 to 5 μm. Painted metal plate. - 前記有機樹脂(A)が、構造中にスルホン酸基を含むポリエステル樹脂(Ae)を含有することを特徴とする、請求項1に記載のクロメートフリー塗装金属板。 The chromate-free painted metal plate according to claim 1, wherein the organic resin (A) contains a polyester resin (Ae) containing a sulfonic acid group in the structure.
- 前記有機樹脂(A)が、構造中にウレア基を含むポリウレタン樹脂(Au)をさらに含有することを特徴とする、請求項2に記載のクロメートフリー塗装金属板。 The chromate-free painted metal plate according to claim 2, wherein the organic resin (A) further contains a polyurethane resin (Au) having a urea group in its structure.
- 前記塗膜(α)が、着色顔料(E)をさらに含有することを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 The chromate-free painted metal sheet according to claim 1 or 2, wherein the coating film (α) further contains a color pigment (E).
- 前記ポリオレフィン樹脂粒子(D)の軟化点が125℃以上であることを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 The chromate-free painted metal sheet according to claim 1 or 2, wherein the polyolefin resin particles (D) have a softening point of 125 ° C or higher.
- 前記ポリオレフィン樹脂粒子(D)が、密度950kg/m3以上であり、且つ針入度法硬度が2以下である高密度ポリエチレン樹脂粒子(D1)であることを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 The polyolefin resin particles (D) are high-density polyethylene resin particles (D1) having a density of 950 kg / m 3 or more and a penetration hardness of 2 or less. Chromate-free painted metal plate as described in 1.
- 前記ポリオレフィン樹脂粒子(D)の平均分子量が3000~6000であることを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 The chromate-free painted metal plate according to claim 1 or 2, wherein the polyolefin resin particles (D) have an average molecular weight of 3000 to 6000.
- 前記ポリオレフィン樹脂粒子(D)の前記塗膜(α)中の含有量が0.5~10質量%であることを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 3. The chromate-free coated metal plate according to claim 1, wherein the content of the polyolefin resin particles (D) in the coating film (α) is 0.5 to 10% by mass.
- 前記球状シリカ粒子(C2)の平均粒子径をcμm、前記塗膜(α)の厚みをbμmとしたとき、0.1≦c/b≦0.7を満足することを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 When the average particle diameter of the spherical silica particles (C2) is c μm and the thickness of the coating film (α) is b μm, 0.1 ≦ c / b ≦ 0.7 is satisfied. The chromate-free painted metal plate according to 1 or 2.
- 前記有機樹脂(A)が硬化剤(B)によって硬化された樹脂であることを特徴とする、請求項1または2に記載のクロメートフリー塗装金属板。 The chromate-free painted metal plate according to claim 1 or 2, wherein the organic resin (A) is a resin cured by a curing agent (B).
- 前記硬化剤(B)がメラミン樹脂(B1)を含有することを特徴とする、請求項10に記載のクロメートフリー塗装金属板。 The chromate-free painted metal plate according to claim 10, wherein the curing agent (B) contains a melamine resin (B1).
- 請求項1または2に記載の前記塗膜(α)が、前記塗膜(α)の構成成分を含む水系塗料組成物(X)を、金属板の少なくとも片面に塗布、加熱乾燥することで形成されていることを特徴とする、クロメートフリー塗装金属板。 The said coating film ((alpha)) of Claim 1 or 2 forms by apply | coating the water-based coating composition (X) containing the structural component of the said coating film ((alpha)) to the at least single side | surface of a metal plate, and heat-drying. This is a chromate-free painted metal sheet.
- 前記水系塗料組成物(X)の加熱乾燥時の温度が前記金属板の到達板温で150~250℃の範囲にあり、且つ加熱乾燥時間が2.5~20秒の範囲にあることを特徴とする、請求項11に記載のクロメートフリー塗装金属板。 The temperature at the time of heating and drying of the water-based coating composition (X) is in the range of 150 to 250 ° C. as the ultimate plate temperature of the metal plate, and the heating and drying time is in the range of 2.5 to 20 seconds. The chromate-free painted metal plate according to claim 11.
- 前記水系塗料組成物(X)の加熱乾燥後に、さらに水冷工程があり、前記ポリオレフィン樹脂粒子(D)の軟化点をTS℃、水冷時の前記金属板の板温度をTM℃、水冷水の水温度をTW℃としたときに、TM>TS、TW≧(TM−150)/4を満足することを特徴とする、請求項11に記載のクロメートフリー塗装金属板。 After the water-based coating composition (X) is heated and dried, there is a further water cooling step. The polyolefin resin particles (D) have a softening point T S ° C, the metal plate temperature during water cooling is T M ° C, and water-cooled water. The chromate-free painted metal sheet according to claim 11, wherein T M > T S , T W ≧ (T M −150) / 4 when the water temperature of T is set to T W ° C.
- 有機樹脂(A)、シリカ粒子(C)、ポリオレフィン樹脂粒子(D)を含有する水系塗料組成物(X)であって、
前記ポリオレフィン樹脂粒子(D)の平均粒子径が0.5~3μmであり、
前記シリカ粒子(C)が、平均粒子径5~50nmの球状シリカ粒子(C1)と平均粒子径0.3~5μmの球状シリカ粒子(C2)の両方を含有することを特徴とする、水系塗料組成物(X)。 A water-based paint composition (X) containing an organic resin (A), silica particles (C), and polyolefin resin particles (D),
The polyolefin resin particles (D) have an average particle diameter of 0.5 to 3 μm,
The water-based paint characterized in that the silica particles (C) contain both spherical silica particles (C1) having an average particle diameter of 5 to 50 nm and spherical silica particles (C2) having an average particle diameter of 0.3 to 5 μm. Composition (X).