WO2012021044A2 - Pore protected multi layered composite separator and the method for manufacturing the same - Google Patents
Pore protected multi layered composite separator and the method for manufacturing the same Download PDFInfo
- Publication number
- WO2012021044A2 WO2012021044A2 PCT/KR2011/005978 KR2011005978W WO2012021044A2 WO 2012021044 A2 WO2012021044 A2 WO 2012021044A2 KR 2011005978 W KR2011005978 W KR 2011005978W WO 2012021044 A2 WO2012021044 A2 WO 2012021044A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- solvent
- substrate
- pores
- coating solution
- coating
- Prior art date
Abstract
Description
Claims (5)
- A method for manufacturing a multi―layer composite porous film, comprising:(a) selecting a microporous film substrate;(b) preparing a coating solution that contains a polymer binder or the polymer binder and inorganic particles;(c) using a solvent with a boiling point of 35 to 250℃ to fill pores on at least one face of the microporous film substrate to protect the same;(d) applying the coating solution of operation (b) to the microporous film, of which the pores are filled and protected; and(e) removing the solvent filling the pores as well as the solvent contained in the coating solution, to thereby form the multi―layer composite porous film having a porous coating layer formed thereon.
- The method of claim 1, wherein the polymer resin is selected from polyphenyl sulfone, polysulfone, polyimide, polyamideimide, polyarylamide, polyarylate, polycarbonate, polyvinylidene fluoride and copolymers thereof, and has a melting point of 150℃ or higher.
- The method of claim 1, wherein the inorganic particles are one selected from calcium carbonate, alumina, aluminum hydroxide, silica, barium titanium oxide, magnesium oxide, magnesium hydroxide, talc, clay and titanium oxide, or a mixture of two or more thereof.
- The method of claim 1, wherein the solvent in operation (c) has a solubility defined by [Equation 1], which is lower than solubility of the solvent used for the coating solution in operation (b):[Equation 1]Solubility of solvent to polymer binder (%) = (initial weight ― weight after dissolution)/initial weight.
- The method of claim 1, wherein the multi―layer composite porous film has a permeability ratio defined by (a Gurley value after removal of a coating layer)/(a Gurley value of substrate)ㅧ100, of 200% or less.