WO2012019777A8 - Method for applying a paint system on a moving steel strip to form a coating, and steel strip thus produced - Google Patents

Method for applying a paint system on a moving steel strip to form a coating, and steel strip thus produced Download PDF

Info

Publication number
WO2012019777A8
WO2012019777A8 PCT/EP2011/004066 EP2011004066W WO2012019777A8 WO 2012019777 A8 WO2012019777 A8 WO 2012019777A8 EP 2011004066 W EP2011004066 W EP 2011004066W WO 2012019777 A8 WO2012019777 A8 WO 2012019777A8
Authority
WO
WIPO (PCT)
Prior art keywords
steel strip
paint system
coating
applying
produced
Prior art date
Application number
PCT/EP2011/004066
Other languages
French (fr)
Other versions
WO2012019777A1 (en
Inventor
Neil Mathieson Craik
Martin Simon Brunnock
Robert Gordon Ireson
Joel Michel Robert Rousseau
Sreedhara Sarma
Original Assignee
Tata Steel Uk Limited
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tata Steel Uk Limited filed Critical Tata Steel Uk Limited
Publication of WO2012019777A1 publication Critical patent/WO2012019777A1/en
Publication of WO2012019777A8 publication Critical patent/WO2012019777A8/en

Abstract

The invention relates to a method for applying a paint system on a moving metal strip to form a coating. According to the invention, the paint system is cured or dried using radiation, which paint system is applied on the moving steel strip passing through or leaving a Continuous Annealing Section at a strip speed of at least 160 m/min using a roller coating technique, and in that the paint system is cured or dried on the steel strip. The invention also relates to a steel strip having a coating layer of such a cured or dried paint system.
PCT/EP2011/004066 2010-08-12 2011-08-12 Method for applying a paint system on a moving steel strip to form a coating, and steel strip thus produced WO2012019777A1 (en)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP10008421.9 2010-08-12
EP10008421 2010-08-12

Publications (2)

Publication Number Publication Date
WO2012019777A1 WO2012019777A1 (en) 2012-02-16
WO2012019777A8 true WO2012019777A8 (en) 2012-04-19

Family

ID=43532767

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2011/004066 WO2012019777A1 (en) 2010-08-12 2011-08-12 Method for applying a paint system on a moving steel strip to form a coating, and steel strip thus produced

Country Status (1)

Country Link
WO (1) WO2012019777A1 (en)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE102014109548A1 (en) 2014-07-08 2016-01-14 Thyssenkrupp Ag Strip coating process for producing a semi-finished product having a surface structure
DE102018209553A1 (en) 2018-06-14 2019-12-19 Voestalpine Stahl Gmbh METHOD FOR PRODUCING LACQUER-COATED ELECTRIC TAPES AND LACQUER-COATED ELECTRIC TAPE
JP7213076B2 (en) * 2018-12-13 2023-01-26 Ｔｏｙｏ Ｔｉｒｅ株式会社 Coating method and manufacturing method for anti-vibration rubber for vehicle
WO2023111644A1 (en) * 2021-12-15 2023-06-22 Arcelormittal Method for managing coating gloss on a coil-coating line

Family Cites Families (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE19625548A1 (en) * 1996-06-26 1998-01-02 Schloemann Siemag Ag Combined hot dip galvanising and resin coating of metal strip
FR2755702B1 (en) * 1996-11-13 1998-12-11 Lorraine Laminage PROCESS FOR THE CONTINUOUS APPLICATION OF AN ORGANIC COATING ON A RUNNING METALLURGICAL PRODUCT AND DEVICE FOR ITS IMPLEMENTATION
KR20040081151A (en) * 2002-01-28 2004-09-20 제이에프이 스틸 가부시키가이샤 Method for producing coated steel sheet
KR100619638B1 (en) * 2002-05-14 2006-09-08 신닛뽄세이테쯔 카부시키카이샤 Coated metal material capable of being welded which is excellent in corrosion resistance of worked zone

Also Published As

Publication number Publication date
WO2012019777A1 (en) 2012-02-16

Similar Documents

Publication Publication Date Title
PL2360213T3 (en) Antifouling coating composition, antifouling coating film formed from the composition, coated object having the coating film on surface, and method of antifouling by forming the coating film
MX370513B (en) Coated body and method for coating a body.
MX366592B (en) Method for producing a metal sheet having zn-al-mg coatings, comprising the application of an acid solution and an adhesive, and corresponding metal sheet and assembly.
PL2161316T3 (en) Antifouling coating composition, process for producing the composition, antifouling coating film formed from the composition, coated object having the coating film on surface, and method of antifouling treatment by formation of the coating film
SG10201707903VA (en) Hot-dip zinc alloy coated steel sheet excellent in coating adhesion, and method for producing the same
EP3358036A4 (en) Hot-dip galvanized layer thickness control system and method for continuous thickness-varying strip material
WO2010144509A3 (en) Electrodeposited, nanolaminate coatings and claddings for corrosion protection
EP3290495A4 (en) Solid lubricant, lubricating coating agent for metal material, surface-treated metal material, and method for forming lubricating coating for metal material
EP2405035A4 (en) Composition for treating surface of metal, method for treating surface of metal using the composition, and coating film for treating surface of metal utilizing the composition and the method
EP3904552A4 (en) High-strength hot-dip galvanized steel sheet and method for manufacturing same
WO2013104530A3 (en) Method for passivating tinplate
PT2252673E (en) Method for adjusting the friction coefficient of a metallic workpiece
DE502006001936D1 (en) PREPARATION AND METHOD FOR APPLYING CORROSION PROTECTION LAYERS
WO2012048844A8 (en) A steel strip composite and a method for making the same
WO2012019777A8 (en) Method for applying a paint system on a moving steel strip to form a coating, and steel strip thus produced
EP3623435A4 (en) Aqueous coating composition and method for producing coated metal substrate
EP3290544A4 (en) Water-based lubricating coating agent for metal material, surface-treated metal material, and method for forming lubricating coating for metal material
EP3502299A4 (en) Hot-rolled galvanizing steel sheet having excellent galling resistance, formability and sealer-adhesion property and method for manufacturing same
EP2316578A4 (en) Roll coating apparatus and method for producing coated metal band
EP3628712A4 (en) Coating agent, method for producing coating film, primer treatment method, method for repairing concrete, and method for consturcting road
EP3613868A4 (en) High strength hot-dip galvanized steel sheet and production method therefor
EP2794955A4 (en) Conversion coating composition, surface treated steel sheet, and method for manufacturing the same
UA114627C2 (en) Method for producing a metal sheet having oiled zn-al-mg coatings, and corresponding metal sheet
EP3617151A4 (en) Metal compound nanoparticles, coating and film using same, method for manufacturing film, and method for manufacturing metal compound nanoparticles
SG11202100680WA (en) Antifouling paint composition, antifouling coating, substrate with antifouling coating, production method thereof, and repair method

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 11748267

Country of ref document: EP

Kind code of ref document: A1

DPE1 Request for preliminary examination filed after expiration of 19th month from priority date (pct application filed from 20040101)
NENP Non-entry into the national phase in:

Ref country code: DE

122 Ep: pct app. not ent. europ. phase

Ref document number: 11748267

Country of ref document: EP

Kind code of ref document: A1