WO2011146615A2 - Novel metal-containing zeolite beta for nox reduction and methods of making the same - Google Patents
Novel metal-containing zeolite beta for nox reduction and methods of making the same Download PDFInfo
- Publication number
- WO2011146615A2 WO2011146615A2 PCT/US2011/036997 US2011036997W WO2011146615A2 WO 2011146615 A2 WO2011146615 A2 WO 2011146615A2 US 2011036997 W US2011036997 W US 2011036997W WO 2011146615 A2 WO2011146615 A2 WO 2011146615A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- zeolite beta
- metal
- beta
- iron
- containing zeolite
- Prior art date
Abstract
Description
Claims