WO2011133999A1 - Crystallisation facilitators for the synthesis of metal organic frameworks - Google Patents
Crystallisation facilitators for the synthesis of metal organic frameworks Download PDFInfo
- Publication number
- WO2011133999A1 WO2011133999A1 PCT/AU2010/001056 AU2010001056W WO2011133999A1 WO 2011133999 A1 WO2011133999 A1 WO 2011133999A1 AU 2010001056 W AU2010001056 W AU 2010001056W WO 2011133999 A1 WO2011133999 A1 WO 2011133999A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- crystallisation
- facilitator
- organic framework
- mof
- Prior art date
Abstract
Description
Claims