WO2011130017A2 - Multi-layer sin for functional and optical graded arc layers on crystalline solar cells - Google Patents
Multi-layer sin for functional and optical graded arc layers on crystalline solar cells Download PDFInfo
- Publication number
- WO2011130017A2 WO2011130017A2 PCT/US2011/030782 US2011030782W WO2011130017A2 WO 2011130017 A2 WO2011130017 A2 WO 2011130017A2 US 2011030782 W US2011030782 W US 2011030782W WO 2011130017 A2 WO2011130017 A2 WO 2011130017A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- layer
- sub
- passivation
- solar cell
- interface
- Prior art date
Abstract
Description
Claims